CN104119746A - 一种彩色岩片的制备方法 - Google Patents

一种彩色岩片的制备方法 Download PDF

Info

Publication number
CN104119746A
CN104119746A CN201410352160.2A CN201410352160A CN104119746A CN 104119746 A CN104119746 A CN 104119746A CN 201410352160 A CN201410352160 A CN 201410352160A CN 104119746 A CN104119746 A CN 104119746A
Authority
CN
China
Prior art keywords
color
preparation
thickness
coating
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410352160.2A
Other languages
English (en)
Inventor
王新
巢启
钟勤
刘齐
程峰
孙美娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi Qili New Materials Science And Technology Co Ltd
Original Assignee
Guangxi Qili New Materials Science And Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi Qili New Materials Science And Technology Co Ltd filed Critical Guangxi Qili New Materials Science And Technology Co Ltd
Priority to CN201410352160.2A priority Critical patent/CN104119746A/zh
Publication of CN104119746A publication Critical patent/CN104119746A/zh
Pending legal-status Critical Current

Abstract

本发明公开的是一种彩色岩片的制备方法。目前的彩片制备采用在覆盖塑料膜或特氟龙膜平台表面涂膜、干燥、起膜的制备方法，存在彩片厚度与产能不可兼得的问题。本发明采用在花岗岩板、耐磨地板或者玻璃板等硬质光滑平板上涂膜、干燥、起膜的制备方法，可将彩片厚度控制在0.05到0.25mm之间，且只需多铺设涂膜用光滑硬质平板，在自然条件下便可实现大批量产出彩片，能有效地解决厚度与产能不可兼得的问题。本发明制备的彩片具有厚度薄、产能高的优点，有效推动了彩片制造行业的生产技术发展。

Description

一种彩色岩片的制备方法
技术领域
本发明涉及的是一种彩色岩片的制备方法，属于建筑新材料领域。
背景技术
随着仿石涂料市场需求日益增大，作为其关键组分的彩色岩片（以下简称彩片）的市场需求也越来越大。
然而，当前传统制备方法主要以人工为主，先将乳胶漆在覆盖塑料膜或特氟龙膜的平台表面滚涂成膜，自然干燥后以手撕膜的方式使薄膜与塑料膜或特氟龙膜分离，将所得涂膜在低温下放入碎片机进行碎片和筛分得到彩片。这种制备方法虽然成本较低，却只能制作0.15-0.5mm厚度的彩片，因为太薄的涂膜撕不起膜。较先进的制备方法是用一套专用设备在特氟龙膜上涂膜，经烘干后吹膜即可起膜，并制得厚度为0.05-0.15mm的彩片。但受限于设备和工艺流程的设计，该制备方法生产效率较低，每台设备日均产能仅有200-300kg，导致生产成本很高。因此，寻求一种生产成本低，生产效率高的彩色岩片生产方法，就是本发明致力于要解决的问题，
经检索，目前还没有采用花岗岩板、耐磨地板或者玻璃板等硬质光滑平板作为浆料成膜底板的彩片制备方法的相关专利信息。
发明内容
本发明的目的是提供一种厚度薄、产能高的彩片制备方法，解决当前制备方法彩片厚度与产能不可兼得的问题。 
上述发明目的通过以下技术方案实现：一种彩色岩片的制备方法，彩片配方主要由下述重量份原料组成：乳液20-50份，羟乙基纤维素醚0.002-0.005份，助剂0.002-0.005份，填料20-50份，水20-50份。
所述的乳液为市售固含量为48%的耐强碱改性型VAE乳液；
所述的羟乙基纤维素醚是市售的一种冷溶性非离子型纤维素醚；
所述助剂为市售制备乳胶漆的常用助剂；
所述填料为市售300-400目双飞粉和钛白粉中的一种或两种任意比例的混合物。
上述一种彩色岩片的制备方法，采取下述方法制备：
（1） 按照比例将各种原料称取好制备成乳胶漆备用；
（2） 将乳胶漆在花岗岩板、耐磨地板或玻璃板等任意一种硬质光滑平板上均匀涂膜，涂膜厚度为0.05-0.25mm。
（3） 将膜在自然环境下干燥15-30min；
（4） 采用铲刀或刮刀起膜；
（5） 把所起薄膜在-5℃以下低温下放入碎片机进行碎片和筛分即可得到彩片。
采取上述措施的本发明，是在花岗岩板、耐磨地板或者玻璃板等硬质光滑平板上涂膜，涂膜干燥后手工铲膜即可起膜，并可将彩片厚度控制在0.05到0.25mm之间，而且只需多铺设涂膜用光滑硬质平板，在自然条件下便可实现大批量的产出彩片。本发明制备的彩片具有厚度薄、产能高的优点，有效推动了彩片制造行业的生产技术发展。
具体实施方式
实施例1
配方一：乳液50份，羟乙基纤维素醚0.002份，助剂0.002份，填料20份，水20份。
制备方法如下：
（1）按照配方比例将各种原料称取好制备成乳胶漆备用；
（2）将乳胶漆在花岗岩板的光滑平面上均匀涂膜，涂膜厚度为0.05-0.25mm；
（3）将膜在自然环境下干燥30min；
（4）采用铲刀起膜；
（5）把所起薄膜在-10℃的低温下放入碎片机进行碎片和筛分即可得到厚度为0.05-0.25mm彩片。
实施例2
配方二：乳液20份，羟乙基纤维素醚0.005份，助剂0.005份，填料50份，水50份。
制备方法如下：
（1）按照配方比例将各种原料称取好制备成乳胶漆备用；
（2）将乳胶漆在耐磨地板的光滑平面上均匀涂膜，涂膜厚度为0.05-0.25mm；
（3）将膜在自然环境下干燥15min；
（4）采用刮刀起膜；
（5）把所起薄膜在-8℃的低温下放入碎片机进行碎片和筛分即可得到厚度为0.05-0.25mm彩片。
实施例3
配方三：乳液30份，羟乙基纤维素醚0.003份，助剂0.004份，填料30份，水40份。
制备方法如下：
（1）按照配方比例将各种原料称取好制备成乳胶漆备用；
（2）将乳胶漆在花岗岩板光滑平面上均匀涂膜，涂膜厚度为0.05-0.25mm；
（3）将膜在自然环境下干燥20min；
（4）采用刮刀起膜；
（5）把所起薄膜在-12℃的低温下放入碎片机进行碎片和筛分即可得到厚度为0.05-0.25mm彩片。
实施例4
配方四：乳液40份，羟乙基纤维素醚0.004份，助剂0.003份，填料40份，水30份。
制备方法如下：
（1）按照配方比例将各种原料称取好制备成乳胶漆备用；
（2）将乳胶漆在玻璃板平滑表面上均匀涂膜，涂膜厚度为0.05-0.25mm；
（3）将涂膜在自然环境下风干25min；
（4）采用铲刀起膜；
（5）把所起薄膜在-15℃的低温下放入碎片机进行碎片和筛分即可得到厚度为0.05-0.25mm彩片。

Claims (1)

1.一种彩色岩片的制备方法，彩片配方主要由下述重量份原料组成：乳液20-50份，羟乙基纤维素醚0.002-0.005份，助剂0.002-0.005份，填料20-50份，水20-50份；其特征是所述的制备方法包括下述具体步骤： 
（1）按照配方比例将各种原料称取好制备成乳胶漆备用；
（2）将乳胶漆在花岗岩板、耐磨地板或玻璃板等任意一种硬质光滑平板上均匀涂膜，涂膜厚度为0.05-0.25mm；
（3）将膜在自然环境下干燥15-30min；
（4）采用铲刀或刮刀起膜；
（5）把所起薄膜在-5℃以下低温放入碎片机进行碎片和筛分即可得到彩片。
CN201410352160.2A 2014-07-23 2014-07-23 一种彩色岩片的制备方法 Pending CN104119746A (zh)