CN104119680A - 一种耐压抗开裂耐火电缆绝缘材料 - Google Patents
一种耐压抗开裂耐火电缆绝缘材料 Download PDFInfo
- Publication number
- CN104119680A CN104119680A CN201410332479.9A CN201410332479A CN104119680A CN 104119680 A CN104119680 A CN 104119680A CN 201410332479 A CN201410332479 A CN 201410332479A CN 104119680 A CN104119680 A CN 104119680A
- Authority
- CN
- China
- Prior art keywords
- insulating material
- aluminium hydroxide
- silicon rubber
- cable insulating
- additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种耐压抗开裂耐火电缆绝缘材料,其由以下质量组分的原料组成:氢氧化铝70%~85%,硅橡胶10%~20%、添加剂5~10%,所述添加剂包括96级SiO2微粉、防爆纤维和复合树脂。本发明采用氢氧化铝微细粉作为主要材料,取材广泛,成本较低,同时采用直径不大于3mm硅橡胶颗粒做填料,增强耐火绝缘材料的韧性和拉伸强度,改善材料的耐高低温性能,另外,添加有特制的添加剂,该添加剂中含有SiO2微粉、防爆纤维和复合树脂,进一步提高了耐压、抗开裂及耐火性能。
Description
技术领域
本发明涉及耐火电缆的绝缘材料。
背景技术
耐火电缆绝缘层材料是耐火电缆最重要的组成部分,它的性能和质量直接影响耐火电缆的应用环境、使用寿命、耐火等级和安全状况,每年由于火材或高温引起的电缆损坏而造成的救援损失和直接财产损失十分巨大,传统的电缆绝缘层材料主要以云母带和氧化镁为主,近年来高温陶瓷化绝缘材料和聚合物阻燃材料也有少量应用和技术报道,但在实际生产、安装施工成本和技术性能等方面存在严重缺陷,推广和应用十分缓慢。
发明内容
本发明所要解决的技术问题就是提供一种电缆绝缘材料,耐压、抗开裂及耐火性能好,施工成本低,便于推广应用。
为解决上述技术问题,本发明采用如下技术方案:一种耐压抗开裂耐火电缆绝缘材料,其由以下质量组分的原料组成:氢氧化铝70%~85%,硅橡胶10%~20%、添加剂5~10%,所述添加剂包括96级SiO2微粉、防爆纤维和复合树脂。
优选的,所述硅橡胶为直径不大于3mm的颗粒。
优选的,所述氢氧化铝采用含量85%以上的500-800目微细粉。
优选的,由以下质量组分的原料组成:氢氧化铝80%,硅橡胶15%、添加剂5%。
优选的,由以下质量组分的原料组成:氢氧化铝70%,硅橡胶20%、添加剂10%。
优选的,由以下质量组分的原料组成:氢氧化铝85%,硅橡胶10%、添加剂5%。
本发明采用氢氧化铝微细粉作为主要材料,取材广泛,成本较低,同时采用直径不大于3mm硅橡胶颗粒做填料,增强耐火绝缘材料的韧性和拉伸强度,改善材料的耐高低温性能,另外,添加有特制的添加剂,该添加剂中含有SiO2微粉、防爆纤维和复合树脂,进一步提高了耐压、抗开裂及耐火性能。
具体实施方式
本发明提供了一种耐压抗开裂耐火电缆绝缘材料,其由以下质量组分的原料组成:氢氧化铝70%~85%,硅橡胶10%~20%、添加剂5~10%,所述添加剂包括96级SiO2微粉、防爆纤维和复合树脂。其中,所述硅橡胶为直径不大于3mm的颗粒,所述氢氧化铝采用含量85%以上的500-800目微细粉,去除铁、钠杂质,使铁离子、钠离子两者总含量少于0.5%。
以下结合具体实施例对本发明做进一步说明。
实施例1,由以下质量组分的原料组成:氢氧化铝80%,硅橡胶15%、添加剂5%,添加剂中96级SiO2微粉、防爆纤维和复合树脂间质量比例为4:3:3。
实施例2,由以下质量组分的原料组成:氢氧化铝70%,硅橡胶20%、添加剂10%。其中,添加剂中除了96级SiO2微粉、防爆纤维和复合树脂,还添加有三聚磷酸钠和木质素磷酸镁,配合SiO2微粉、防爆纤维和复合树脂,进一步防止耐火材料发生收缩、开裂的现象。而且添加剂中96级SiO2微粉、防爆纤维、复合树脂、三聚磷酸钠和木质素磷酸镁间质量比例为3:2:2::1.5:1.5。
实施例3,由以下质量组分的原料组成:氢氧化铝85%,硅橡胶10%、添加剂5%。
上述耐压抗开裂耐火电缆绝缘材料的制备方法为,将氢氧化铝、硅橡胶和添加剂按质量配比混合均匀,然后加入结合剂,所述结合剂由无水葡萄糖、硼砂、托品和工业盐组成,所述结合剂的添加质量占氢氧化铝、硅橡胶和添加剂总质量的3~6%。所述结合剂按质量百分比由以下组分组成:无水葡萄糖:86wt%;硼砂:5wt%;乌洛托品:4.5wt%;工业盐:4.5wt%。该结合剂结合能好,能将氢氧化铝、硅橡胶和添加剂有机结合。
Claims (6)
1.一种耐压抗开裂耐火电缆绝缘材料,其特征在于由以下质量组分的原料组成:氢氧化铝70%~85%,硅橡胶10%~20%、添加剂5~10%,所述添加剂包括96级SiO2微粉、防爆纤维和复合树脂。
2.根据权利要求1所述的一种耐压抗开裂耐火电缆绝缘材料,其特征在于:所述硅橡胶为直径不大于3mm的颗粒。
3.根据权利要求1所述的一种耐压抗开裂耐火电缆绝缘材料,其特征在于:所述氢氧化铝采用含量85%以上的500-800目微细粉。
4.根据权利要求1至3任意一项所述的一种耐压抗开裂耐火电缆绝缘材料,其特征在于:由以下质量组分的原料组成:氢氧化铝80%,硅橡胶15%、添加剂5%。
5.根据权利要求1至3任意一项所述的一种耐压抗开裂耐火电缆绝缘材料,其特征在于:由以下质量组分的原料组成:氢氧化铝70%,硅橡胶20%、添加剂10%。
6.根据权利要求1至3任意一项所述的一种耐压抗开裂耐火电缆绝缘材料,其特征在于:由以下质量组分的原料组成:氢氧化铝85%,硅橡胶10%、添加剂5%。