CN104212175A - 一种耐火硅橡胶电力电缆料用改性云母及其制备方法 - Google Patents

一种耐火硅橡胶电力电缆料用改性云母及其制备方法 Download PDF

Info

Publication number
CN104212175A
CN104212175A CN201410415557.1A CN201410415557A CN104212175A CN 104212175 A CN104212175 A CN 104212175A CN 201410415557 A CN201410415557 A CN 201410415557A CN 104212175 A CN104212175 A CN 104212175A
Authority
CN
China
Prior art keywords
parts
mica
fire
silicon rubber
modified mica
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410415557.1A
Other languages
English (en)
Inventor
荔建荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI JI'AN SPECIAL WIRE AND CABLE MANUFACTURING Co Ltd
Original Assignee
ANHUI JI'AN SPECIAL WIRE AND CABLE MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI JI'AN SPECIAL WIRE AND CABLE MANUFACTURING Co Ltd filed Critical ANHUI JI'AN SPECIAL WIRE AND CABLE MANUFACTURING Co Ltd
Priority to CN201410415557.1A priority Critical patent/CN104212175A/zh
Publication of CN104212175A publication Critical patent/CN104212175A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐火硅橡胶电力电缆料用改性云母及其制备方法。其由以下重量份的原料制成：云母75-85、烟片胶15-20、六氯环三磷腈10-15、中空微珠16-22、三甲硅基甲基膦酸二甲酯6-9、高硼硼酸钙11-17、勃姆石10-15、五氯硬脂酸甲酯3-6、甲基三丁酮肟基硅烷2-4、四甲基氢氧化铵1-2、乙酰丙酮钒2-3、胡莫柳酯1.5-2.5、N-叔丁基-2-苯并噻唑次磺酰胺1-2、助剂2.5-4.5。本发明改性后的云母与硅橡胶相容性好，填充功能高，填充后的硅橡胶复合材料具有耐火性能稳定，绝缘性能高，机械性能好的特点，同时具有优良的阻燃性、自熄性、耐臭氧和耐大气老化等性能，安全性能高。

Description

一种耐火硅橡胶电力电缆料用改性云母及其制备方法
技术领域
本发明涉及一种耐火硅橡胶电力电缆料用改性云母及其制备方法，属于无机填料技术领域。
背景技术
云母为天然层状片形结晶结构的铝钾硅酸盐矿物，其具有击穿电压高，介电常数大，耐电弧性好、硬度高，耐酸碱，耐热性能好以及对紫外光的高吸收性能，广泛应用于塑料、橡胶等高聚物基复合材料的无机填料。但现有的云母不仅与有机高聚物间相容性差，而且填充功能较低，使得云母的应用范围具有局限性。因此，必须对其进行一定的改性处理。
发明内容
本发明目的在于提供一种耐火硅橡胶电力电缆料用改性云母及其制备方法，改性后的云母填充性能好，可以显著提高硅橡胶电缆料的机械强度、耐火性能、和绝缘性能。
为实现上述目的，本发明采用如下技术方案：
一种耐火硅橡胶电力电缆料用改性云母，由以下重量份的原料制成：云母75-85、烟片胶15-20、六氯环三磷腈10-15、中空微珠16-22、三甲硅基甲基膦酸二甲酯6-9、高硼硼酸钙11-17、勃姆石10-15、五氯硬脂酸甲酯3-6、甲基三丁酮肟基硅烷2-4、四甲基氢氧化铵1-2、乙酰丙酮钒2-3、胡莫柳酯1.5-2.5、N-叔丁基-2-苯并噻唑次磺酰胺1-2、助剂2.5-4.5；
所述助剂由以下重量份的原料混合而成：二苯甲烷双马来酰亚胺3-4、双(叔丁基过氧化异丙基)苯2-3、松香季戊四醇酯4-5、乙基苯基二硫代氨基甲酸锌2-3、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯1-2、双咪唑烷基脲2-4、N-苯基-2-萘胺1-2、4,4'-亚丁基双(6-叔丁基-3-甲基苯酚)1.5-2.5、辛酸亚锡1-2。
本发明的耐火硅橡胶电力电缆料用改性云母的制备方法，包括以下步骤：首先将云母、高硼硼酸钙、勃姆石混合均匀，粉碎至平均粒度为3-6μm的细粉，再投入高速混合机内，加入烟片胶、六氯环三磷腈、中空微珠、三甲硅基甲基膦酸二甲酯、甲基三丁酮肟基硅烷，1500-2000r/min高速混合至料温达到70-80℃时，加入余下原料，800-1200r/min高速混合至料温达到90-100℃时，然后将物料输送到冷混机中，冷却至35-45℃，出料，烘干，粉碎，过筛，包装即可。
本发明的有益效果：
本发明改性后的云母与硅橡胶相容性好，填充功能高，填充后的硅橡胶复合材料具有耐火性能稳定，绝缘性能高，机械性能好的特点，同时具有优良的阻燃性、自熄性、耐臭氧和耐大气老化等性能，安全性能高。
具体实施方式
一种耐火硅橡胶电力电缆料用改性云母，由以下重量(kg)的原料制成：云母80、烟片胶18、六氯环三磷腈12、中空微珠18、三甲硅基甲基膦酸二甲酯7、高硼硼酸钙16、勃姆石12、五氯硬脂酸甲酯4.5、甲基三丁酮肟基硅烷3、四甲基氢氧化铵1.5、乙酰丙酮钒2.5、胡莫柳酯2、N-叔丁基-2-苯并噻唑次磺酰胺1.5、助剂3.5；
所述助剂由以下重量(kg)的原料混合而成：二苯甲烷双马来酰亚胺3.5、双(叔丁基过氧化异丙基)苯2。5、松香季戊四醇酯4、乙基苯基二硫代氨基甲酸锌2、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯1.5、双咪唑烷基脲3、N-苯基-2-萘胺1、4,4'-亚丁基双(6-叔丁基-3-甲基苯酚)2、辛酸亚锡1.5。
耐火硅橡胶电力电缆料用改性云母的制备方法，包括以下步骤：首先将云母、高硼硼酸钙、勃姆石混合均匀，粉碎至平均粒度为3-6μm的细粉，再投入高速混合机内，加入烟片胶、六氯环三磷腈、中空微珠、三甲硅基甲基膦酸二甲酯、甲基三丁酮肟基硅烷，1500-2000r/min高速混合至料温达到70-80℃时，加入余下原料，800-1200r/min高速混合至料温达到90-100℃时，然后将物料输送到冷混机中，冷却至35-45℃，出料，烘干，粉碎，过筛，包装即可。
上述实施例制得的改性云母用于填充耐火硅橡胶电力电缆料的性能测试结果如下表所示：
表1  填充改性云母的耐火硅橡胶电力电缆料的性能测试结果

Claims (2)

1.一种耐火硅橡胶电力电缆料用改性云母，其特征在于，由以下重量份的原料制成：云母75-85、烟片胶15-20、六氯环三磷腈 10-15、中空微珠16-22、三甲硅基甲基膦酸二甲酯6-9、高硼硼酸钙11-17、勃姆石10-15、五氯硬脂酸甲酯3-6、甲基三丁酮肟基硅烷2-4、四甲基氢氧化铵1-2、乙酰丙酮钒2-3、胡莫柳酯1.5-2.5、N-叔丁基-2-苯并噻唑次磺酰胺1-2、助剂2.5-4.5；
    所述助剂由以下重量份的原料混合而成：二苯甲烷双马来酰亚胺3-4、双(叔丁基过氧化异丙基)苯2-3、松香季戊四醇酯4-5、乙基苯基二硫代氨基甲酸锌2-3、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯1-2、双咪唑烷基脲2-4、N-苯基-2-萘胺1-2、4,4'-亚丁基双(6-叔丁基-3-甲基苯酚)1.5-2.5、辛酸亚锡1-2。
2.一种如权利要求1所述的耐火硅橡胶电力电缆料用改性云母的制备方法，其特征在于包括以下步骤：首先将云母、高硼硼酸钙、勃姆石混合均匀，粉碎至平均粒度为3-6μm的细粉，再投入高速混合机内，加入烟片胶、六氯环三磷腈、中空微珠、三甲硅基甲基膦酸二甲酯、甲基三丁酮肟基硅烷，1500-2000r/min高速混合至料温达到70-80℃时，加入余下原料，800-1200r/min高速混合至料温达到90-100℃时，然后将物料输送到冷混机中，冷却至35-45℃，出料，烘干，粉碎，过筛，包装即可。
CN201410415557.1A 2014-08-21 2014-08-21 一种耐火硅橡胶电力电缆料用改性云母及其制备方法 Pending CN104212175A (zh)