CN104108945A - Soybean milk/volcanic ash composite lightweight partition plate and manufacturing method thereof - Google Patents
Soybean milk/volcanic ash composite lightweight partition plate and manufacturing method thereof Download PDFInfo
- Publication number
- CN104108945A CN104108945A CN201410272065.1A CN201410272065A CN104108945A CN 104108945 A CN104108945 A CN 104108945A CN 201410272065 A CN201410272065 A CN 201410272065A CN 104108945 A CN104108945 A CN 104108945A
- Authority
- CN
- China
- Prior art keywords
- parts
- volcanic ash
- partition plate
- add
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a soybean milk/volcanic ash composite lightweight partition plate, which is characterized by being composed of the following raw materials in parts by weight: 10 to 13 parts of cement, 12 to 14 parts of bottom ash prepared by burning city household garbage, 14 to 18 parts of geopolymer, 18 to 20 parts of volcanic ash, 0.4 to 0.8 part of cellulose ether, 0.3 to 0.7 part of polypropylene short fiber, 0.7 to 2.2 parts of dicumyl peroxide, 15 to 17 parts of soybean milk, 1 to 2 parts of sodium lignosulfonate, 17 to 20 parts of calcium carbide slag, 2 to 3 parts of hydrogenated rosin glycerin ester, 15 to 17 parts of soybean straw, 12 to 15 parts of poplar twig, 6 to 9 parts of hemp seed oil, 3 to 6 parts of auxiliary agent, and a proper amount of water. The added soybean milk helps to form uniformly-distributed pores in a partition plate, and thus the thermal insulation effect of the partition plate is further improved. The partition plate can be widely applied to house decoration and the onsite practicability of the partition plate is very good.
Description
Technical field
The present invention relates to building material field, be specifically related to compound light cellular partition board of a kind of soya-bean milk/volcanic ash and preparation method thereof.
Background technology
Light cellular partition board is comprised of various industrial waste residues such as innoxious phosphogypsum, lightweight slag, flyash, a kind of novel energy-conserving walling material forming through the maintenance of frequency conversion steam pressurized, the walling that it is a kind of external form as the cassette ceiling, but there is male and female falcon groove on its both sides, during installation, only sheet material need be erected, male and female falcon is coated after a small amount of filleting mortar assembled.It has the advantages such as quality is light, intensity is high, multiple environmental protection, heat insulating, sound insulation, breathing damping, fire prevention, rapid construction, reduction body of wall cost, so enjoy favor in architecture indoor finishing field, however the shortcomings such as the light cellular partition board ultimate compression strength of using is in the market low, tensile strength weak, anti-cracking performance and hanging ability is not good, production cost is high, sound-insulating weak effect.
Summary of the invention
Object of the present invention is just to provide compound light cellular partition board of a kind of soya-bean milk/volcanic ash and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
The light cellular partition board that a kind of soya-bean milk/volcanic ash is compound, it is characterized in that, by the raw material of following weight part, made: cement 10-13, burning city domestic garbage bottom ash 12-14, geopolymer 14-18, volcanic ash 18-20, ether of cellulose 0.4-0.8, polypropene staple 0.3-0.7, dicumyl peroxide 0.7-2.2, soya-bean milk 15-17, sodium lignosulfonate 1-2, carbide slag 17-20, hydrogenated rosin glyceride 2-3, soybean stalk 15-17, branch of poplar 12-15, Hemp Seed oil 6-9, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made by following raw materials in part by weight: volcanic ash 6-9, Sodium sulfate anhydrous.min(99) 2-5, magnesium chloride 3-5, magnesium oxide 2-4, polyvinyl alcohol 0.2-0.5, Starso 0.03-0.07, sodium aluminate 0.05-0.6, tartrate 0.8-2.1, organosilicon crylic acid latex 2.1-4.3, 2-imidazolidone 0.04-0.09, silicon carbide 1-3, accelerant CZ 0.03-0.05, Syzygium aromaticum stem oil 1.2-3.2, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
Described geopolymer is the novel inorganic silicon-aluminum gelatinized material in a kind of structure with the network-like keyed jointing structure of space three-dimensional, does not adopt " two mills one burn " calcining process of consumption of natural resource and the energy in preparation technology, does not substantially discharge CO
2.The starting material wide material sources of geopolymer, easy to prepare, energy consumption is little, has higher mechanical property and very excellent resistance to elevated temperatures simultaneously, broken through the use range of traditional portland and alkali slag cement.The present invention, by geopolymer replacing partial cement, not only can reduce cost energy-conserving and environment-protective, and can not weaken again the pectisation of cement.
The preparation method of the light cellular partition board that described a kind of soya-bean milk/volcanic ash is compound, is characterized in that comprising the following steps:
(1) soybean stalk, branch of poplar are sent in charring furnace, at 485-605 ℃, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form Hemp Seed oil under condition, then add hydrogenated rosin glyceride stirring and evenly mixing to the powder of gained in air blast;
(2) get geopolymer and put into the hydrochloric acid soln of 8-12% and soak 4-5 hour, filter and take out, use clear water repetitive scrubbing, dry, be added to the water, meanwhile, add burning city domestic garbage bottom ash, grinding obtains slurry;
(3) volcanic ash, carbide slag are calcined at 600-828 ℃ after 3-6 hour and taken out, pulverize, add polypropene staple to stir 4-8 minute;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, obtain.
The present invention has following beneficial effect: the present invention, by increasing soya-bean milk, is conducive to form equally distributed pore in partition plate, has further promoted the heat insulating effect of partition plate, can be widely used in house decoration partition wall use, and product practical is good.
Embodiment
The described compound light cellular partition board of a kind of soya-bean milk/volcanic ash, it is characterized in that, by the raw material of following weight part, made: cement 12, burning city domestic garbage bottom ash 13, geopolymer 14, volcanic ash 18, ether of cellulose 0.7, polypropene staple 0.3, dicumyl peroxide 0.7, soya-bean milk 15, sodium lignosulfonate 1, carbide slag 17, hydrogenated rosin glyceride 2, soybean stalk 15, branch of poplar 12, Hemp Seed oil 6, auxiliary agent 3, suitable quantity of water.
Described auxiliary agent is made by following raw materials in part by weight: volcanic ash 6, Sodium sulfate anhydrous.min(99) 2, magnesium chloride 3, magnesium oxide 2, polyvinyl alcohol 0.3, Starso 0.03, sodium aluminate 0.4, tartrate 0.8, organosilicon crylic acid latex 2.6,2-imidazolidone 0.04, silicon carbide 1, accelerant CZ 0.03, Syzygium aromaticum stem oil 1.2, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter, at 2-5mm, is dried and be get final product.
Making method comprises the following steps:
(1) soybean stalk, branch of poplar are sent in charring furnace, at 485-605 ℃, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form Hemp Seed oil under condition, then add hydrogenated rosin glyceride stirring and evenly mixing to the powder of gained in air blast;
(2) get geopolymer and put into the hydrochloric acid soln of 8-12% and soak 4-5 hour, filter and take out, use clear water repetitive scrubbing, dry, be added to the water, meanwhile, add burning city domestic garbage bottom ash, grinding obtains slurry;
(3) volcanic ash, carbide slag are calcined at 600-828 ℃ after 3-6 hour and taken out, pulverize, add polypropene staple to stir 4-8 minute;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, obtain.
The technical indicator of processing the light cellular partition board obtaining by above-described embodiment is as follows:
(1) unit weight: 536kg/m
3;
(2) ultimate compression strength: 5.03MPa;
(3) high temperature resistant, flat appearance is smooth;
(4) shock resistance: 0.5 meter of 30kg drop, flawless.
Claims (2)
1. the light cellular partition board that soya-bean milk/volcanic ash is compound, it is characterized in that, by the raw material of following weight part, made: cement 10-13, burning city domestic garbage bottom ash 12-14, geopolymer 14-18, volcanic ash 18-20, ether of cellulose 0.4-0.8, polypropene staple 0.3-0.7, dicumyl peroxide 0.7-2.2, soya-bean milk 15-17, sodium lignosulfonate 1-2, carbide slag 17-20, hydrogenated rosin glyceride 2-3, soybean stalk 15-17, branch of poplar 12-15, Hemp Seed oil 6-9, auxiliary agent 3-6, suitable quantity of water, described auxiliary agent is made by following raw materials in part by weight: volcanic ash 6-9, Sodium sulfate anhydrous.min(99) 2-5, magnesium chloride 3-5, magnesium oxide 2-4, polyvinyl alcohol 0.2-0.5, Starso 0.03-0.07, sodium aluminate 0.05-0.6, tartrate 0.8-2.1, organosilicon crylic acid latex 2.1-4.3, 2-imidazolidone 0.04-0.09, silicon carbide 1-3, accelerant CZ 0.03-0.05, Syzygium aromaticum stem oil 1.2-3.2, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
2. the making method of the compound light cellular partition board of a kind of soya-bean milk/volcanic ash according to claim 1, is characterized in that comprising the following steps:
(1) soybean stalk, branch of poplar are sent in charring furnace, at 485-605 ℃, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form Hemp Seed oil under condition, then add hydrogenated rosin glyceride stirring and evenly mixing to the powder of gained in air blast;
(2) get geopolymer and put into the hydrochloric acid soln of 8-12% and soak 4-5 hour, filter and take out, use clear water repetitive scrubbing, dry, be added to the water, meanwhile, add burning city domestic garbage bottom ash, grinding obtains slurry;
(3) volcanic ash, carbide slag are calcined at 600-828 ℃ after 3-6 hour and taken out, pulverize, add polypropene staple to stir 4-8 minute;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water stirring and evenly mixing and obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, obtain.