CN104087168A - 一种水乳型再生胶改性沥青防水涂料制备方法 - Google Patents
一种水乳型再生胶改性沥青防水涂料制备方法 Download PDFInfo
- Publication number
- CN104087168A CN104087168A CN201410272818.9A CN201410272818A CN104087168A CN 104087168 A CN104087168 A CN 104087168A CN 201410272818 A CN201410272818 A CN 201410272818A CN 104087168 A CN104087168 A CN 104087168A
- Authority
- CN
- China
- Prior art keywords
- water
- raw material
- added
- type reclaimed
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种水乳型再生胶改性沥青防水涂料制备方法,涉及涉及化工技术领域,由以下组分的原料组成,石油沥青380-400份、橡胶粉25-35份、肥皂1.6-2份、水玻璃3-4份、烧碱1.5-1.7份、填料90-110份、水390-410份。本发明的有益效果是:本发明制备方便简单,原料易得,设备投资少,便于操作,制备的水乳型再生胶改性沥青防水涂料,环保无污染,纯度高,使用效果好,耐高温性强,安全可靠。
Description
技术领域
本发明涉及化工技术领域,具体涉及一种水乳型再生胶改性沥青防水涂料制备方法。
背景技术
防水涂料是指用于防止水侵入和渗漏的涂料,防水涂料经固化后形成的防水薄膜具有一定的延伸性、弹塑性、抗裂性、抗渗性及耐候性,能起到防水、防渗和保护作用,防水涂料有良好的温度适应性,操作简便,易于维修与维护,市场上的防水材料有两大类:一是聚氨酯类防水涂料,这类材料一般是由聚氨脂与煤焦油作为原材料制成,它所挥发的焦油气毒性大,且不容易清除,因此于2000年在中国被禁止使用,尚在销售的聚氨脂防水涂料,是用沥青代替煤焦油作为原料,但在使用这种涂料时,一般采用含有甲苯、二甲苯等有机溶剂来稀释,因而也含有毒性;同时施工不便便、综合造价高,工期短长,环保性也比较差,但是即便是拥有如此多的缺点,但是由于目前防水涂料生产的技术匮乏,因此可选度很低,市场上使用的大多数还是此种类型的防水涂料。
发明内容
本发明所要解决的技术问题在于提供一种无毒环保,制备工艺简单的水乳型再生胶改性沥青防水涂料制备方法。
本发明所要解决的技术问题采用以下技术方案来实现:
一种水乳型再生胶改性沥青防水涂料,其特征在于,由以下组分的原料组成:
各原料的优选组分为:
所述原料中的填料为滑石粉。
本发明的另一目的是制备本发明水乳型再生胶改性沥青防水涂料的制备方法,其特征在于:包括以下工艺步骤,
a.将原料中的水按照配方量的50%加入混合搅拌机中,然后进行加热至沸腾,然后将原料中的烧碱加入其中,搅拌至溶解。
b.当步骤a中的烧碱溶解完后,继续进行搅拌,按照配方量将原料中的肥皂盒水玻璃投放入混合搅拌机中,然后将温度升至40-50℃,充分搅拌均匀后,即得到清澈的阴离子乳化剂,在温度为60-80℃之间储存备用。
c.选取一熔化釜,按照配方量将原料中的石油沥青加入至熔化釜内进行加热熔化后,脱水,过滤去除杂质。
d.将步骤c中的熔化釜内的反应物进行冷却直至温度为90-110℃后,按照配方量将原料中的橡胶粉、填料加入熔化釜内,再将步骤b制得的阴离子乳化剂加入内部,充分搅拌均匀后将温度升至180-200℃,保温1h。
e.将原料中的剩余水加入步骤d中的熔化釜内部,搅拌均匀后,稀释固含量为50%的黏稠状液体即为本发明所要制备的水乳型再生胶改性沥青防水涂料,冷却后放料,采用塑料桶或者铁桶密封包装储存。
本发明的有益效果是:本发明制备方便简单,原料易得,设备投资少,便于操作,制备的水乳型再生胶改性沥青防水涂料,环保无污染,纯度高,使用效果好,耐高温性强,安全可靠。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
一种水乳型再生胶改性沥青防水涂料,由以下组分的原料组成:
制备本发明水乳型再生胶改性沥青防水涂料的方法,包括以下工艺步骤:
a.将原料中的水按照配方量的50%加入混合搅拌机中,然后进行加热至沸腾,然后将原料中的烧碱加入其中,搅拌至溶解。
b.当步骤a中的烧碱溶解完后,继续进行搅拌,按照配方量将原料中的肥皂盒水玻璃投放入混合搅拌机中,然后将温度升至40-50℃,充分搅拌均匀后,即得到清澈的阴离子乳化剂,在温度为60-80℃之间储存备用。
c.选取一熔化釜,按照配方量将原料中的石油沥青加入至熔化釜内进行加热熔化后,脱水,过滤去除杂质。
d.将步骤c中的熔化釜内的反应物进行冷却直至温度为90-110℃后,按照配方量将原料中的橡胶粉、滑石粉加入熔化釜内,再将步骤b制得的阴离子乳化剂加入内部,充分搅拌均匀后将温度升至180-200℃,保温1h。
e.将原料中的剩余水加入步骤d中的熔化釜内部,搅拌均匀后,稀释固含量为50%的黏稠状液体即为本发明所要制备的水乳型再生胶改性沥青防水涂料,冷却后放料,采用塑料桶或者铁桶密封包装储存。
实施例2
一种水乳型再生胶改性沥青防水涂料,由以下组分的原料组成:
制备本发明水乳型再生胶改性沥青防水涂料的方法,包括以下工艺步骤:
a.将原料中的水按照配方量的50%加入混合搅拌机中,然后进行加热至沸腾,然后将原料中的烧碱加入其中,搅拌至溶解。
b.当步骤a中的烧碱溶解完后,继续进行搅拌,按照配方量将原料中的肥皂盒水玻璃投放入混合搅拌机中,然后将温度升至40-50℃,充分搅拌均匀后,即得到清澈的阴离子乳化剂,在温度为60-80℃之间储存备用。
c.选取一熔化釜,按照配方量将原料中的石油沥青加入至熔化釜内进行加热熔化后,脱水,过滤去除杂质。
d.将步骤c中的熔化釜内的反应物进行冷却直至温度为90-110℃后,按照配方量将原料中的橡胶粉、滑石粉加入熔化釜内,再将步骤b制得的阴离子乳化剂加入内部,充分搅拌均匀后将温度升至180-200℃,保温1h。
e.将原料中的剩余水加入步骤d中的熔化釜内部,搅拌均匀后,稀释固含量为50%的黏稠状液体即为本发明所要制备的水乳型再生胶改性沥青防水涂料,冷却后放料,采用塑料桶或者铁桶密封包装储存。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种水乳型再生胶改性沥青防水涂料,其特征在于,由以下组分的原料组成:
。
2.根据权利要求1所述的一种水乳型再生胶改性沥青防水涂料,其特征在于:优选的原料组分为:
。
3.根据权利要求1所述的一种水乳型再生胶改性沥青防水涂料,其特征在于:所述原料中的填料为滑石粉。
4.根据权利要求1-2所述的一种水乳型再生胶改性沥青防水涂料的制备方法,其特征在于:包括以下步骤,
a.将原料中的水按照配方量的50%加入混合搅拌机中,然后进行加热至沸腾,然后将原料中的烧碱加入其中,搅拌至溶解。
b.当步骤a中的烧碱溶解完后,继续进行搅拌,按照配方量将原料中的肥皂盒水玻璃投放入混合搅拌机中,然后将温度升至40-50℃,充分搅拌均匀后,即得到清澈的阴离子乳化剂,在温度为60-80℃之间储存备用。
c.选取一熔化釜,按照配方量将原料中的石油沥青加入至熔化釜内进行 加热熔化后,脱水,过滤去除杂质。
d.将步骤c中的熔化釜内的反应物进行冷却直至温度为90-110℃后,按照配方量将原料中的橡胶粉、填料加入熔化釜内,再将步骤b制得的阴离子乳化剂加入内部,充分搅拌均匀后将温度升至180-200℃,保温1h。
e.将原料中的剩余水加入步骤d中的熔化釜内部,搅拌均匀后,稀释固含量为50%的黏稠状液体即为本发明所要制备的水乳型再生胶改性沥青防水涂料,冷却后放料,采用塑料桶或者铁桶密封包装储存。