CN104087072A - Water-resistant paint - Google Patents
Water-resistant paint Download PDFInfo
- Publication number
- CN104087072A CN104087072A CN201410337787.0A CN201410337787A CN104087072A CN 104087072 A CN104087072 A CN 104087072A CN 201410337787 A CN201410337787 A CN 201410337787A CN 104087072 A CN104087072 A CN 104087072A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- resistant paint
- calcium carbonate
- sodium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-resistant paint which comprises the following components in parts by weight: 20-40 parts of butadiene-styrene latex, 40-60 parts of dibutyl phthalate, 10-20 parts of sodium silicate, 10-16 parts of magnesium silicate, 4-8 parts of potassium silicate, 4-8 parts of sodium sulfate, 2-4 parts of zinc oxide, 8-12 parts of zinc dihydrogen phosphate and 10-20 parts of calcium carbonate. The water-resistant paint is simple to manufacture, has the advantages of accurate chroma after being coated, high water resistance and high durability, and can effectively resist water after being used for a long time.
Description
Technical field
The present invention relates to polymeric material field, be specifically related to a kind of waterproof paint.
Background technology
Coating is a kind of material, and this material can be coated in article surface by different construction technologies, forms and adheres to firmly, has some strength, continuous solid film.The film common name film forming like this, claims again paint film or coating.Belong to organic chemical industry's macromolecular material, the film forming belongs to macromolecular compound type.According to the classification of current Chemicals of modern times, coating belongs to fine chemical product.Modern coating is progressively becoming the polyfunctional engineering materials of a class, is an important industry in chemical industry.Current coating function ratio is on the market more single, can not meet people's demand.
Summary of the invention
Object of the present invention provides a kind of waterproof paint, solves one or more in above-mentioned prior art problem.
According to an aspect of the present invention, a kind of waterproof paint, comprise the component of following weight part: 20～40 parts of styrene-butadiene latexes, 40～60 parts of dibutyl phthalates, 10～20 parts of water glass, 10～16 parts of Magnesium Silicate q-agents, 4～8 parts of potassium silicates, 4～8 parts, sodium sulfate, 2～4 parts, zinc oxide, 8～12 parts of primary zinc phosphates, 10～20 parts, calcium carbonate.
A kind of waterproof paint provided by the invention, makes simply, smears rear colourity accurate, and water-repellancy is strong, and good endurance is used also effectively waterproof over a long time.
Embodiment
Embodiment 1
A kind of waterproof paint, comprises the component of following weight part: 20 parts of styrene-butadiene latexes, 40 parts of dibutyl phthalates, 10 parts of water glass, 10 parts of Magnesium Silicate q-agents, 4 parts of potassium silicates, 4 parts, sodium sulfate, 2 parts, zinc oxide, 8 parts of primary zinc phosphates, 10 parts, calcium carbonate; Above-mentioned component is fully dissolved, mix.
Embodiment 2
A kind of waterproof paint, comprises the component of following weight part: 30 parts of styrene-butadiene latexes, 50 parts of dibutyl phthalates, 15 parts of water glass, 13 parts of Magnesium Silicate q-agents, 6 parts of potassium silicates, 6 parts, sodium sulfate, 3 parts, zinc oxide, 10 parts of primary zinc phosphates, 15 parts, calcium carbonate; Above-mentioned component is fully dissolved, mix.
Embodiment 3
A kind of waterproof paint, comprises the component of following weight part: 40 parts of styrene-butadiene latexes, 60 parts of dibutyl phthalates, 20 parts of water glass, 16 parts of Magnesium Silicate q-agents, 8 parts of potassium silicates, 8 parts, sodium sulfate, 4 parts, zinc oxide, 12 parts of primary zinc phosphates, 20 parts, calcium carbonate; Above-mentioned component is fully dissolved, mix.
The above is only optimal way of the present invention; it should be pointed out that to those skilled in the art, without departing from the concept of the premise of the invention; can also make some similar distortion and improvement, within these also should be considered as protection scope of the present invention.
Claims (1)
1. a waterproof paint, it is characterized in that, comprise the component of following weight part: 20～40 parts of styrene-butadiene latexes, 40～60 parts of dibutyl phthalates, 10～20 parts of water glass, 10～16 parts of Magnesium Silicate q-agents, 4～8 parts of potassium silicates, 4～8 parts, sodium sulfate, 2～4 parts, zinc oxide, 8～12 parts of primary zinc phosphates, 10～20 parts, calcium carbonate.