CN104513535A - Waterproof paint - Google Patents
Waterproof paint Download PDFInfo
- Publication number
- CN104513535A CN104513535A CN201310457362.9A CN201310457362A CN104513535A CN 104513535 A CN104513535 A CN 104513535A CN 201310457362 A CN201310457362 A CN 201310457362A CN 104513535 A CN104513535 A CN 104513535A
- Authority
- CN
- China
- Prior art keywords
- waterproof paint
- emulsion
- agent
- water
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof paint. The waterproof paint comprises following ingredients, by mass, 30 to 50% of styrene-acrylic emulsion, 20 to 30% of quartz sand, 20 to 25% of cement, 0 to 5% of heavy calcium, 1 to 5% of an anti-aging agent, 0 to 5% of an antifoaming agent, 0 to 5% of talc powder, 3 to 5% of titanium dioxide, 5 to 10% of polyvinyl alcohol, 1 to 5% of sodium hexametaphosphate, and 10% of water. An anti-settling agent, which is a high molecular ionic compound is used, and can be dispersed in a plurality of solvent based coatings. The emulsion is acrylic acid modified emulsion, and possesses excellent water resistance and alkali resistance.
Description
Technical field
A kind of waterproof paint of the present invention has superpower fire resistance characteristic, can be immersed in non-scale in water, foaming for a long time.The invention belongs to the category of chemistry painting industry.
Background technology
Waterproof paint water resistance is in the past lower and cost value is higher, and because add organic solvent, has certain pollution, the present invention adopts acrylic acid modified emulsion to adhere to reinforcer, improves the water resistance of coating, also has superpower erosion resistance, non-scale is not afraid of collision, strong adhesion.
Summary of the invention
A kind of waterproof paint, component and mass ratio are: the benzene emulsion of 30 ~ 50%, the quartz sand of 20 ~ 30%, the cement of 20-25; The coarse whiting of 0 ~ 5%, the anti-aging agent of 1 ~ 5%, the defoamer of 0 ~ 5%, the talcum powder of 0 ~ 5%, the titanium dioxide of 3 ~ 5%, the polyvinyl alcohol of 5 ~ 10%, the Sodium hexametaphosphate 99 of 1 ~ 5%, the water of 10%.The anti-settling agent used is a kind of macroion type compound, can be scattered in all kinds of SOLVENTS type coating.Emulsion be acrylic acid modified emulsion, there is high water-alkali resistance effect.
embodiment
A kind of concrete component of waterproof paint, the mass ratio of each component and concrete production technique are as follows:
By recipe requirements add one by one raw material to be mixed evenly after slowly add a small amount of film coalescence aid so that film-formation result is better in the process of coating in film forming, film forming is more fine and close, but necessarily slowly adds at the process medium velocity added.To be mixed evenly after add appropriate flow agent and thickening material, to improve the application property of coating in construction process, increase the construction thickness of paint film individual layer in construction, improve the quality of coating and the decorative effect after improving construction.Until indices all detect qualified after barrelling wait for dispatch from the factory.
Claims (3)
1. a waterproof paint, component and mass ratio are: the benzene emulsion of 30 ~ 50%, the quartz sand of 20 ~ 30%, the cement of 20-25; The coarse whiting of 0 ~ 5%, the anti-aging agent of 1 ~ 5%, the defoamer of 0 ~ 5%, the talcum powder of 0 ~ 5%, the titanium dioxide of 3 ~ 5%, the polyvinyl alcohol of 5 ~ 10%, the Sodium hexametaphosphate 99 of 1 ~ 5%, the water of 10%.
2. according to claim 1, a kind of waterproof paint, is characterized in that, the anti-settling agent that a kind of waterproof paint is used is a kind of macroion type compound, can be scattered in all kinds of SOLVENTS type coating.
3. according to claim 1, a kind of superpower coating, is characterized in that the emulsion in a kind of Superstrong waterproof paint is acrylic acid modified emulsion, has high water-alkali resistance effect.