CN103773142B - A kind of equipment Environmentally-frieantirust antirust paint and preparation method thereof - Google Patents
A kind of equipment Environmentally-frieantirust antirust paint and preparation method thereof Download PDFInfo
- Publication number
- CN103773142B CN103773142B CN201410024071.5A CN201410024071A CN103773142B CN 103773142 B CN103773142 B CN 103773142B CN 201410024071 A CN201410024071 A CN 201410024071A CN 103773142 B CN103773142 B CN 103773142B
- Authority
- CN
- China
- Prior art keywords
- parts
- antirust paint
- preparation
- environmentally
- clorafin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a kind of equipment Environmentally-frieantirust antirust paint and preparation method thereof, this coating in mass parts containing following composition: polyvinyl butyral resin 19 ~ 30 parts, organosilicon-modified acrylate emulsion 10 ~ 20 parts, toluene sulfonic acide 0.3 ~ 0.6 part, clorafin 0.04 ~ 0.08 part, zinc-chrome yellow 2 ~ 5 parts, iron mica 2 ~ 5 parts, tripolyphosphate calcium 2 ~ 5 parts, aluminum phosphate 1 ~ 3 part, wilkinite 2 ~ 4 parts, nepheline 3 ~ 6 parts, carbon black 0.6 ~ 1.5 part, silicone emulsion 0.07 ~ 0.12 part, dibutyl phthalate 0.2 ~ 0.5 part, 0.2 ~ 0.4 part, diatomite, urethane 0.1 ~ 0.3 part, 32 ~ 45 parts, water.Coating safety non-toxic provided by the invention, sticking power is high, and rustless property, wear resisting property and shock resistance are good, can also remove the objectionable impuritiess such as the free formaldehyde in air, benzene, VOC.
Description
Technical field
The present invention relates to paint field, particularly relate to a kind of equipment Environmentally-frieantirust antirust paint and preparation method thereof.
Background technology
Equipment refers to and can supply enterprise's life-time service aborning, and substantially in Reusability keeps original physical form and the means of labor of function and the general name of material goods.Equipment is generally made of metal, and its surface scribbles coating.But existing coating is mostly containing organic solvent, and have toxicity, meanwhile, its rustless property is poor, and sticking power is not high, easily peels off, and resistance to impact shock is low.
Summary of the invention
the technical problem solved:for the shortcoming that existing installation exists with coating, the invention provides a kind of equipment Environmentally-frieantirust antirust paint and preparation method thereof.
technical scheme:a kind of equipment Environmentally-frieantirust antirust paint, in mass parts containing following composition: polyvinyl butyral resin 19 ~ 30 parts, organosilicon-modified acrylate emulsion 10 ~ 20 parts, toluene sulfonic acide 0.3 ~ 0.6 part, clorafin 0.04 ~ 0.08 part, zinc-chrome yellow 2 ~ 5 parts, iron mica 2 ~ 5 parts, tripolyphosphate calcium 2 ~ 5 parts, aluminum phosphate 1 ~ 3 part, wilkinite 2 ~ 4 parts, nepheline 3 ~ 6 parts, carbon black 0.6 ~ 1.5 part, silicone emulsion 0.07 ~ 0.12 part, dibutyl phthalate 0.2 ~ 0.5 part, 0.2 ~ 0.4 part, diatomite, urethane 0.1 ~ 0.3 part, 32 ~ 45 parts, water.
A kind of equipment Environmentally-frieantirust antirust paint described above, in mass parts containing following composition: polyvinyl butyral resin 25 parts, organosilicon-modified acrylate emulsion 15 parts, toluene sulfonic acide 0.45 part, clorafin 0.06 part, zinc-chrome yellow 3.5 parts, iron mica 3.5 parts, tripolyphosphate calcium 3.5 parts, aluminum phosphate 2 parts, wilkinite 3 parts, nepheline 4.5 parts, carbon black 1.1 parts, silicone emulsion 0.1 part, dibutyl phthalate 0.35 part, 0.3 part, diatomite, urethane 0.2 part, 38 parts, water.
The preparation process of a kind of equipment Environmentally-frieantirust antirust paint described above is as follows: first add in high speed agitator by clorafin, zinc-chrome yellow, iron mica, tripolyphosphate calcium, aluminum phosphate, wilkinite, nepheline, carbon black, silicone emulsion, dibutyl phthalate, diatomite, urethane and water, stir 0.5 ~ 1h, obtain mixture; Again polyvinyl butyral resin and organosilicon-modified acrylate emulsion are mixed 1 ~ 1.5h at temperature is 40 ~ 50 DEG C, then mix with said mixture, toluene sulfonic acide, get product.
beneficial effect:a kind of equipment Environmentally-frieantirust antirust paint provided by the invention and preparation method thereof, this coating safety non-toxic, sticking power is high, and rustless property, wear resisting property and shock resistance are good, can also remove the objectionable impuritiess such as the free formaldehyde in air, benzene, VOC.
Embodiment
embodiment 1
The present embodiment provides a kind of equipment Environmentally-frieantirust antirust paint, in mass parts containing following composition: polyvinyl butyral resin 30 parts, organosilicon-modified acrylate emulsion 20 parts, toluene sulfonic acide 0.6 part, clorafin 0.08 part, zinc-chrome yellow 5 parts, iron mica 5 parts, tripolyphosphate calcium 5 parts, aluminum phosphate 3 parts, wilkinite 4 parts, nepheline 6 parts, carbon black 1.5 parts, silicone emulsion 0.12 part, dibutyl phthalate 0.5 part, 0.4 part, diatomite, urethane 0.3 part, 45 parts, water.
A kind of preparation process of equipment Environmentally-frieantirust antirust paint is as follows: first add in high speed agitator by clorafin, zinc-chrome yellow, iron mica, tripolyphosphate calcium, aluminum phosphate, wilkinite, nepheline, carbon black, silicone emulsion, dibutyl phthalate, diatomite, urethane and water, stir 1h, obtain mixture; Again polyvinyl butyral resin and organosilicon-modified acrylate emulsion are mixed 1.5h at temperature is 50 DEG C, then mix with said mixture, toluene sulfonic acide, get product.
The sticking power of the coating that the present embodiment provides is 1 grade, and wear resistance (knockout) is 2.76L/ μm, and salt fog resistance (1000h) is non-foaming, non-corrosive.
embodiment 2
The present embodiment provides a kind of equipment Environmentally-frieantirust antirust paint, in mass parts containing following composition: polyvinyl butyral resin 19 parts, organosilicon-modified acrylate emulsion 10 parts, toluene sulfonic acide 0.3 part, clorafin 0.04 part, zinc-chrome yellow 2 parts, iron mica 2 parts, tripolyphosphate calcium 2 parts, aluminum phosphate 1 part, wilkinite 2 parts, nepheline 3 parts, carbon black 0.6 part, silicone emulsion 0.07 part, dibutyl phthalate 0.2 part, 0.2 part, diatomite, urethane 0.1 part, 32 parts, water.
A kind of preparation process of equipment Environmentally-frieantirust antirust paint is as follows: first add in high speed agitator by clorafin, zinc-chrome yellow, iron mica, tripolyphosphate calcium, aluminum phosphate, wilkinite, nepheline, carbon black, silicone emulsion, dibutyl phthalate, diatomite, urethane and water, stir 0.5h, obtain mixture; Again polyvinyl butyral resin and organosilicon-modified acrylate emulsion are mixed 1h at temperature is 40 DEG C, then mix with said mixture, toluene sulfonic acide, get product.
The sticking power of the coating that the present embodiment provides is 1 grade, and wear resistance (knockout) is 2.85L/ μm, and salt fog resistance (1100h) is non-foaming, non-corrosive.
embodiment 3
The present embodiment provides a kind of equipment Environmentally-frieantirust antirust paint, in mass parts containing following composition: polyvinyl butyral resin 25 parts, organosilicon-modified acrylate emulsion 15 parts, toluene sulfonic acide 0.45 part, clorafin 0.06 part, zinc-chrome yellow 3.5 parts, iron mica 3.5 parts, tripolyphosphate calcium 3.5 parts, aluminum phosphate 2 parts, wilkinite 3 parts, nepheline 4.5 parts, carbon black 1.1 parts, silicone emulsion 0.1 part, dibutyl phthalate 0.35 part, 0.3 part, diatomite, urethane 0.2 part, 38 parts, water.
A kind of preparation process of equipment Environmentally-frieantirust antirust paint is as follows: first add in high speed agitator by clorafin, zinc-chrome yellow, iron mica, tripolyphosphate calcium, aluminum phosphate, wilkinite, nepheline, carbon black, silicone emulsion, dibutyl phthalate, diatomite, urethane and water, stir 0.5h, obtain mixture; Again polyvinyl butyral resin and organosilicon-modified acrylate emulsion are mixed 1h at temperature is 45 DEG C, then mix with said mixture, toluene sulfonic acide, get product.
The sticking power of the coating that the present embodiment provides is 1 grade, and wear resistance (knockout) is 2.96L/ μm, and salt fog resistance (1150h) is non-foaming, non-corrosive.
Above the embodiment of the present invention is described in detail, for one of ordinary skill in the art, according to the thought of the embodiment of the present invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (1)
1. the preparation method of an equipment Environmentally-frieantirust antirust paint, it is characterized in that the preparation process of the method is as follows: first add in high speed agitator by clorafin, zinc-chrome yellow, iron mica, tripolyphosphate calcium, aluminum phosphate, wilkinite, nepheline, carbon black, silicone emulsion, dibutyl phthalate, diatomite, urethane and water, stir 0.5 ~ 1h, obtain mixture; Again polyvinyl butyral resin and organosilicon-modified acrylate emulsion are mixed 1 ~ 1.5h at temperature is 40 ~ 50 DEG C, then mix with said mixture, toluene sulfonic acide, get product.