CN104087070A - Anti-corrosion coating - Google Patents
Anti-corrosion coating Download PDFInfo
- Publication number
- CN104087070A CN104087070A CN201410337907.7A CN201410337907A CN104087070A CN 104087070 A CN104087070 A CN 104087070A CN 201410337907 A CN201410337907 A CN 201410337907A CN 104087070 A CN104087070 A CN 104087070A
- Authority
- CN
- China
- Prior art keywords
- parts
- ethylene glycol
- corrosion coating
- tributyl phosphates
- talcum powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-corrosion coating comprising the following components in parts by weight: 8-12 parts of epoxy-acrylic acid, 2-4 parts of iron oxide, 2-4 parts of talcum powder, 4-8 parts of strontium chromate, 6-9 parts of tributyl phosphate, 2-8 parts of ethylene glycol-butyl ether, 8-16 parts of carboxymethyl cellulose sodium, 4-8 parts of dibutyl phthalate, 2-6 parts of ethylene glycol, 8-12 parts of ammonium phosphate, 4-12 parts of sodium nitrate, 6-8 parts of tributyl phosphate and 2-4 parts of methanol. The anti-corrosion coating disclosed by the invention is low in cost and simple in manufacturing process, and can be used for effectively preventing acid and alkali corrosion.
Description
Technical field
The present invention relates to polymeric material field, be specifically related to anticorrosive coating.
Background technology
Coating is a kind of material, and this material can be coated in article surface by different construction technologies, forms and adheres to firmly, has some strength, continuous solid film.The film common name film forming like this, claims again paint film or coating.Belong to organic chemical industry's macromolecular material, the film forming belongs to macromolecular compound type.According to the classification of current Chemicals of modern times, coating belongs to fine chemical product.Modern coating is progressively becoming the polyfunctional engineering materials of a class, is an important industry in chemical industry.Current coating function ratio is on the market more single, can not meet people's demand.
Summary of the invention
Object of the present invention provides anticorrosive coating, solves one or more in above-mentioned prior art problem.
According to an aspect of the present invention, anticorrosive coating, comprise following weight part component: Huan Yang ?8～12 parts, vinylformic acid, 2～4 parts of ferric oxide, 2～4 parts of talcum powder, 4～8 parts of strontium yellows, 6～9 parts of tributyl phosphates, 2～8 parts of ethylene glycol monobutyl ethers, 8～16 parts of sodium cellulose glycolates, 4～8 parts of dibutyl phthalates, 2～6 parts of ethylene glycol, 8～12 parts, ammonium phosphate, 4～12 parts of SODIUMNITRATE, 6～8 parts of tributyl phosphates, 2～4 parts of methyl alcohol.
Anticorrosive coating provided by the invention, cost is low, and manufacture craft is simple, can be to effectively preventing acid and alkali corrosion.
Embodiment
Embodiment 1
Anticorrosive coating, comprise following weight part component: Huan Yang ?8 parts, vinylformic acid, 2 parts of ferric oxide, 2 parts of talcum powder, 4 parts of strontium yellows, 6 parts of tributyl phosphates, 2 parts of ethylene glycol monobutyl ethers, 8 parts of sodium cellulose glycolates, 4 parts of dibutyl phthalates, 2 parts of ethylene glycol, 8 parts, ammonium phosphate, 4 parts of SODIUMNITRATE, 6 parts of tributyl phosphates, 2 parts of methyl alcohol; Above-mentioned component is fully dissolved, mix.
Embodiment 2
Anticorrosive coating, comprise following weight part component: Huan Yang ?10 parts, vinylformic acid, 3 parts of ferric oxide, 3 parts of talcum powder, 6 parts of strontium yellows, 8 parts of tributyl phosphates, 5 parts of ethylene glycol monobutyl ethers, 12 parts of sodium cellulose glycolates, 6 parts of dibutyl phthalates, 4 parts of ethylene glycol, 10 parts, ammonium phosphate, 8 parts of SODIUMNITRATE, 7 parts of tributyl phosphates, 3 parts of methyl alcohol; Above-mentioned component is fully dissolved, mix.
Embodiment 3
Anticorrosive coating, comprise following weight part component: Huan Yang ?12 parts, vinylformic acid, 4 parts of ferric oxide, 4 parts of talcum powder, 8 parts of strontium yellows, 9 parts of tributyl phosphates, 8 parts of ethylene glycol monobutyl ethers, 16 parts of sodium cellulose glycolates, 8 parts of dibutyl phthalates, 6 parts of ethylene glycol, 12 parts, ammonium phosphate, 12 parts of SODIUMNITRATE, 8 parts of tributyl phosphates, 4 parts of methyl alcohol; Above-mentioned component is fully dissolved, mix.
The above is only optimal way of the present invention; it should be pointed out that to those skilled in the art, without departing from the concept of the premise of the invention; can also make some similar distortion and improvement, within these also should be considered as protection scope of the present invention.
Claims (1)
1. anticorrosive coating, is characterized in that, comprise following weight part component: Huan Yang ?8～12 parts, vinylformic acid, 2～4 parts of ferric oxide, 2～4 parts of talcum powder, 4～8 parts of strontium yellows, 6～9 parts of tributyl phosphates, 2～8 parts of ethylene glycol monobutyl ethers, 8～16 parts of sodium cellulose glycolates, 4～8 parts of dibutyl phthalates, 2～6 parts of ethylene glycol, 8～12 parts, ammonium phosphate, 4～12 parts of SODIUMNITRATE, 6～8 parts of tributyl phosphates, 2～4 parts of methyl alcohol.