CN104075993A - 一种乳胶纤维板层间剥离强度的测定方法 - Google Patents

一种乳胶纤维板层间剥离强度的测定方法 Download PDF

Info

Publication number
CN104075993A
CN104075993A CN201410271146.XA CN201410271146A CN104075993A CN 104075993 A CN104075993 A CN 104075993A CN 201410271146 A CN201410271146 A CN 201410271146A CN 104075993 A CN104075993 A CN 104075993A
Authority
CN
China
Prior art keywords
stainless steel
ring
sample
small sample
pressing plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410271146.XA
Other languages
English (en)
Other versions
CN104075993B (zh
Inventor
龙建友
胡海洋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG WALKKING SPECIAL FIBREBOARD TECHNOLOGY Co Ltd
Original Assignee
GUANGDONG WALKKING SPECIAL FIBREBOARD TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG WALKKING SPECIAL FIBREBOARD TECHNOLOGY Co Ltd filed Critical GUANGDONG WALKKING SPECIAL FIBREBOARD TECHNOLOGY Co Ltd
Priority to CN201410271146.XA priority Critical patent/CN104075993B/zh
Publication of CN104075993A publication Critical patent/CN104075993A/zh
Application granted granted Critical
Publication of CN104075993B publication Critical patent/CN104075993B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种乳胶纤维板层间剥离强度的测定方法。取乳胶纤维板成品经过温度、相对湿度环境条件下做恒温恒湿平衡处理，两面贴上印刷双面胶，然后用裁断机、环型模具冲裁出标准尺寸的环型小试样，剥去其印刷双面胶的保护纸，将其一侧粘附于不锈钢圆环片上，另外一侧粘附在不锈钢实心圆片上，将贴有不锈钢圆环片和不锈钢实心圆片的环型小试样放在耐破强度试验机的下压盘上，用手转动转盘，使上压盘与下压盘夹紧，油压表显示压力为200Psi；然后松开上压盘，装上不锈钢环套，不锈钢环套套在不锈钢实心圆片上，再次用手转动转盘，使上压盘与下压盘夹紧，油压表显示压力100Psi，再按动面板的测试键，当环形小试样剥离发生后，直接读取显示剥离强度的数据。

Description

一种乳胶纤维板层间剥离强度的测定方法
技术领域：
本发明属于乳胶纤维板制造领域，具体涉及一种乳胶纤维板层间剥离强度的测定方法。
背景技术：
在乳胶纤维板的生产过程中，对产品的层间剥离强度进行检测，以确定产品纤维间的结合强度，并将其作为评估产品质量好坏的重要项目之一。
经对现有技术文献检索发现：现有的可以用于乳胶纤维板层间剥离强度的测试方法：《鞋类内底试验方法层间剥离强度》(GB/T3903.8-2005)和《制鞋纸板》(GB/T22803-2008)中的“层间剥离强度的测定”。
以上两种方法均可以对乳胶纤维板层间剥离强度进行检测，但是，第一种方法操作耗用时间较长(例如：对试样进行环境调节要花24小时，试样两表面涂粘合剂干燥需20分钟)；第二种方法在取样时分纵横向试样，在操作时沿试样长度预先剥开50mm，未剥开部分与拉伸方向呈T型，这样对操作有一定难度，而且纵横向试样的检测结果差异大，不能保证检测精确度，另外，此方法对厚度在1.5mm(含)以下鞋内底板、主跟板的层间剥离强度的检测不作要求。
因此，需要有一种能够快速、简便、全面、精确地对生产过程中乳胶纤维板层间剥离强度进行检测的方法。
发明内容：
本发明的目的是提供一种能够快速、简便、全面、精确地对生产过程中乳胶纤维板层间剥离强度进行检测的方法，该方法能使乳胶纤维板层间剥离强度进行量化，在确保产品层间剥离强度，满足用户需要的前提下，促进生产工艺的改进，从而降低生产成本。
本发明的乳胶纤维板层间剥离强度进行检测的方法，其特征在于，包括以下步骤：
取乳胶纤维板成品经过温度(23±2)℃、相对湿度50％±2％环境条件下做恒温恒湿平衡处理，然后将平衡后的样品两面贴上印刷双面胶，然后利用裁断机、环型模具冲裁出标准尺寸的环型小试样，剥去环型小试样上的印刷双面胶的保护纸，将环型小试样一侧粘附于不锈钢圆环片上，另外一侧粘附在不锈钢实心圆片上，将贴有不锈钢圆环片和不锈钢实心圆片的环型小试样放在耐破强度试验机的下压盘上，用手转动转盘，使上压盘与下压盘夹紧，油压表显示压力为200Psi；然后松开上压盘，装上不锈钢环套，不锈钢环套套在不锈钢实心圆片上，再次用手转动转盘，使上压盘与下压盘夹紧，油压表显示压力100Psi，再按动面板的测试键，当环形小试样剥离发生后，直接读取显示剥离强度的数据，单位为kgf/cm2，取下环形小试样，测试完毕，该数据即为乳胶纤维板层间剥离强度。
本发明操作快速、便捷，在数分钟内便可以出结果，能为乳胶纤维板生产厂家及时控制产品质量提供科学的数据支持。
附图说明：
图1层间剥离强度测试方法测试工具示意图；
其中：1、不锈钢环套；2、不锈钢实心圆片；3、不锈钢圆环片；4、圆环片座。
图2是圆环片座的示意图。
具体实施方式：
以下是对本发明的进一步说明，而不是对本发明的限制。
实施例1：
如图1和图2所示，本实施例的乳胶纤维板层间剥离强度的测定方法，具体包括以下步骤
1、取无外观缺陷的厚度为1.5mm的乳胶纤维板成品A4规格样品1片。
2、经在温度(23±2)℃、相对湿度50％±2％环境条件下做恒温恒湿平衡水分处理。
3、将平衡后的样品用切纸刀裁切出一小块，尺寸比试样尺寸稍大，然后将小块样品两面用印刷双面胶贴牢。
4、将贴有印刷双面胶的小块样品放置在裁断机上，再在样品上放置环型模具，操作裁断机对样品进行裁切，裁出标准尺寸的环型小试样。然后取出裁切好的环型小试样，取得的试样是为的环状。
5、接着将不锈钢圆环片3放入圆环片座4的凸出面，圆环片3的内环孔卡入圆环片座4的凸出部，去掉环状小试样一面的印刷双面胶保护纸，将环状小试样贴在不锈钢圆环片3上；然后将贴有环状小试样的不锈钢圆环片3取出，将圆环片座4翻过来，凹面向上，将不锈钢实心圆片2卡入圆环片座4凹面内；将贴在不锈钢圆环片3上的环状小试样的另一面印刷双面胶保护纸去掉，然后将其贴在卡入圆环片座4凹面内的不锈钢实心圆片2上；取出贴有不锈钢圆环片3和不锈钢实心圆片2的环状小试样待用。
6、将贴有不锈钢圆环片3和不锈钢实心圆片2的环状小试样放在耐破强度试验机(如国产CC-606)的下压盘上，用手转动转盘，使上压盘与下压盘夹紧，油压表显示压力为200Psi；过一定时间后，松开上压盘，装上不锈钢环套1，不锈钢环套1套在不锈钢实心圆片2上；再次用手转动转盘，使上压盘与下压盘夹紧，油压表显示压力为100Psi；一定时间(30S)过后，按动面板的测试键；当环状小试样剥离发生后，直接读取显示剥离强度的数据，10.85kgf/cm2，并作好记录；取下小试样，测试完毕，按面板的归零键，以便下一次的测试。
本实施例的乳胶纤维板剥离强度为10.85kgf/cm2(约1.06MPa)，与《鞋类内底试验方法层间剥离强度》(GB/T3903.8-2005)测定的基本一致，由此说明，按照本发明的方法可以测定乳胶纤维板剥离强度。

Claims (1)

1.一种乳胶纤维板层间剥离强度进行检测的方法，其特征在于，包括以下步骤：
取乳胶纤维板成品经过温度23±2℃、相对湿度50％±2％环境条件下做恒温恒湿平衡处理，然后将平衡后的样品两面贴上印刷双面胶，然后利用裁断机、环型模具冲裁出标准尺寸的环型小试样，剥去环型小试样上的印刷双面胶的保护纸，将环型小试样一侧粘附于不锈钢圆环片上，另外一侧粘附在不锈钢实心圆片上，将贴有不锈钢圆环片和不锈钢实心圆片的环型小试样放在耐破强度试验机的下压盘上，用手转动转盘，使上压盘与下压盘夹紧，油压表显示压力为200Psi；然后松开上压盘，装上不锈钢环套，不锈钢环套套在不锈钢实心圆片上，再次用手转动转盘，使上压盘与下压盘夹紧，油压表显示压力100Psi，再按动面板的测试键，当环形小试样剥离发生后，直接读取显示剥离强度的数据，单位为kgf/cm2，取下环形小试样，测试完毕，该数据即为乳胶纤维板层间剥离强度。
CN201410271146.XA 2014-06-17 2014-06-17 一种乳胶纤维板层间剥离强度的测定方法 Active CN104075993B (zh)