CN104073680A - 一种硅锡黄铜合金 - Google Patents
一种硅锡黄铜合金 Download PDFInfo
- Publication number
- CN104073680A CN104073680A CN201410334370.9A CN201410334370A CN104073680A CN 104073680 A CN104073680 A CN 104073680A CN 201410334370 A CN201410334370 A CN 201410334370A CN 104073680 A CN104073680 A CN 104073680A
- Authority
- CN
- China
- Prior art keywords
- silicon
- tin
- lead
- brass
- brass alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种硅锡黄铜合金。其特征在于，硅锡黄铜合金组成含量为66～75wt%铜、0.4～3.3wt%硅、0.5～1.0wt%铬、0.03～1.1wt%锡、0.1～0.66wt%镍、0.001～0.11wt%钛，铅≤0.2wt%，余量为锌以及不可避免杂质，不可避免杂质总量不大于0.2wt%。本发明通过用硅替代铅来提高合金的切削性能和锻造性能，用锡来提高合金的切削性能和抗脱锌腐蚀性能，用钛来细化晶粒。本发明与铅黄铜相比，含铅微量，尽可能消除铅在生产和使用过程中对人体和环境的危害。本发明与现有含硅环保黄铜相比，切削性能显著提高，而且成本较低。
Description
技术领域
本发明涉及一种硅锡黄铜合金。
背景技术
黄铜具有美观的外表和优异的性能，在仪器仪表、电子电气、日用五金、水暖阀门等领域中大量应用，其中尤以 HPb59-1 生产、应用量最大。目前锻造用黄铜大多含锌为 35～45 wt%，属于 α+β 双相黄铜。这类黄铜在高温下塑性极好，因此适合于热锻加工。为了改善锻造后机加工和切削性能，在这种黄铜中加入少量铅（约 0.8 ～ 3.5%），从而为加工形状复杂的日用品和水暖阀门零部件带来了便利。
发明内容
针对现有技术中存在的问题，本发明的目的在于提供一种硅锡黄铜合金的技术方案。
所述的一种硅锡黄铜合金，其特征在于，硅锡黄铜合金组成含量为66～75wt%铜、0.4～3.3 wt% 硅、0.5～1.0wt% 铬、0.03～1.1 wt% 锡、0.1～0.66wt% 镍、0.001～0.11 wt% 钛，铅≤0.2wt%，余量为锌以及不可避免杂质，不可避免杂质总量不大于0.2wt%。
所述的一种硅锡黄铜合金，其特征在于，硅锡黄铜合金组成含量为69～72wt%铜、0.8～2.9 wt% 硅、0.6～0.9 wt% 铬、0.08～1.05 wt% 锡、0.15～0.61wt% 镍、0.005～0.10 wt% 钛，铅≤0.15wt%，余量为锌以及不可避免杂质，不可避免杂质总量不大于0.18wt%。
所述的一种硅锡黄铜合金，其特征在于，硅锡黄铜合金组成含量为70～71wt%铜、1.0～2.7 wt% 硅、0.65～0.85 wt% 铬、0.10～1.03 wt% 锡、0.20～0.56wt% 镍、0.008～0.08 wt% 钛，铅≤0.13wt%，余量为锌以及不可避免杂质，不可避免杂质总量不大于0.15wt%。
本发明通过用硅替代铅来提高合金的切削性能和锻造性能，用锡来提高合金的切削性能和抗脱锌腐蚀性能，用钛来细化晶粒。本发明与铅黄铜相比，含铅微量，尽可能消除铅在生产和使用过程中对人体和环境的危害。本发明与现有含硅环保黄铜相比，切削性能显著提高，而且成本较低。并且本合金化学组份简单，易于回收和再生利用。本合金生产工艺简单，可利用现有铅黄铜的生产设备制造，不需要增加新的设备。
具体实施方式
实施例1
一种硅锡黄铜合金，硅锡黄铜合金组成含量为66～75wt%铜、0.4～3.3 wt% 硅、0.5～1.0wt% 铬、0.03～1.1 wt% 锡、0.1～0.66wt% 镍、0.001～0.11 wt% 钛，铅≤0.2wt%，余量为锌以及不可避免杂质，不可避免杂质总量不大于0.2wt%。
实施例2
一种硅锡黄铜合金，其特征在于，硅锡黄铜合金组成含量为69～72wt%铜、0.8～2.9 wt% 硅、0.6～0.9 wt% 铬、0.08～1.05 wt% 锡、0.15～0.61wt% 镍、0.005～0.10 wt% 钛，铅≤0.15wt%，余量为锌以及不可避免杂质，不可避免杂质总量不大于0.18wt%。
实施例3
一种硅锡黄铜合金，其特征在于，硅锡黄铜合金组成含量为70～71wt%铜、1.0～2.7 wt% 硅、0.65～0.85 wt% 铬、0.10～1.03 wt% 锡、0.20～0.56wt% 镍、0.008～0.08 wt% 钛，铅≤0.13wt%，余量为锌以及不可避免杂质，不可避免杂质总量不大于0.15wt%。
Claims (3)
1.一种硅锡黄铜合金，其特征在于，硅锡黄铜合金组成含量为66～75wt%铜、0.4～3.3 wt% 硅、0.5～1.0wt% 铬、0.03～1.1 wt% 锡、0.1～0.66wt% 镍、0.001～0.11 wt% 钛，铅≤0.2wt%，余量为锌以及不可避免杂质，不可避免杂质总量不大于0.2wt%。
2.根据权利要求1所述的一种硅锡黄铜合金，其特征在于，硅锡黄铜合金组成含量为69～72wt%铜、0.8～2.9 wt% 硅、0.6～0.9 wt% 铬、0.08～1.05 wt% 锡、0.15～0.61wt% 镍、0.005～0.10 wt% 钛，铅≤0.15wt%，余量为锌以及不可避免杂质，不可避免杂质总量不大于0.18wt%。
3.根据权利要求1所述的一种硅锡黄铜合金，其特征在于，硅锡黄铜合金组成含量为70～71wt%铜、1.0～2.7 wt% 硅、0.65～0.85 wt% 铬、0.10～1.03 wt% 锡、0.20～0.56wt% 镍、0.008～0.08 wt% 钛，铅≤0.13wt%，余量为锌以及不可避免杂质，不可避免杂质总量不大于0.15wt%。