CN104059349A - 一种具有耐油性能的橡胶 - Google Patents
一种具有耐油性能的橡胶 Download PDFInfo
- Publication number
- CN104059349A CN104059349A CN201410292114.8A CN201410292114A CN104059349A CN 104059349 A CN104059349 A CN 104059349A CN 201410292114 A CN201410292114 A CN 201410292114A CN 104059349 A CN104059349 A CN 104059349A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- rubber
- aging agent
- ursol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种具有耐油性能的橡胶,本发明属于橡胶领域。本发明的具有耐油性能的橡胶包括下述重量份数的组分:氯醇橡胶80-1800份、氟硅橡胶50-180份、纳米氧化锌3-10份、硬脂酸2-4份、炭黑N100 15-30份、石蜡2-5份、古马隆树脂4-15份、硫磺2-10份、防老剂1-5份、碳酸钙1-8份、羟基硅油1-6份、氢硅油1-5份、白炭黑2-5份、二甲基硅油1-5份、邻苯二甲酸二丁酯2-4份、二乙基二硫代氨基甲酸锌1-4份、2-硫醇基咪唑啉2-4份。本发明的有益效果在于,采用上述的配方所得到的耐油橡胶,具有耐油性能好、耐高温、耐腐蚀等优点,能够有效满足生产生活中的需要。
Description
技术领域
本发明涉及一种具有耐油性能的橡胶,属于橡胶领域。
背景技术
橡胶是一种有弹性的聚合物。橡胶可以从一些植物的树汁中取得,也可以是人造的,两者皆有相当多的应用及产品,例如轮胎、垫圈等,遂成为重要经济作物。橡胶的种植主要集中在东南亚地区,如泰国、马来西亚、印度尼西亚。橡胶按原料分为天然橡胶和合成橡胶。按形态分为块状生胶、乳胶、液体橡胶和粉末橡胶。乳胶为橡胶的胶体状水分散体;液体橡胶为橡胶的低聚物,未硫化前一般为粘稠的液体;粉末橡胶是将乳胶加工成粉末状,以利配料和加工制作。20世纪60年代开发的热塑性橡胶,无需化学硫化,而采用热塑性塑料的加工方法成形。橡胶按使用又分为通用型和特种型两类。是绝缘体,不容易导电,但如果沾水或不同的温度的话,有可能变成导体。
耐油橡胶是指耐非极性油类的氟橡胶,氟橡胶是指分子结构中含有氟原子的合成橡胶。通常以共聚物中含氟单元的氟原子数目来表示,如氟橡胶23,是偏二氟乙烯同三氟氯乙烯的共聚物。氟橡胶耐高温、耐油、耐化学腐蚀。耐油是指耐燃油、耐混合燃油、耐酸性氧化燃油、耐矿物油、耐合成润滑油、耐合成氢类润滑油、耐聚亚烷基二醇(PAG)合成润滑油、耐有机酯合成润滑油、耐含硅的合成润滑油、耐含氟元素油、耐聚苯基醚液体、耐氯代氢液体。耐油橡胶具有如此多的优点,因此需要发明一种耐油橡胶,以满足人们生产生活的需要。
发明内容
本发明所要解决的技术问题是提供一种具有耐油性能的橡胶。
为解决上述技术问题,本发明采用的技术方案是:一种具有耐油性能的橡胶,该具有耐油性能的橡胶包括下述重量份数的组分:氯醇橡胶80-1800份、氟硅橡胶50-180份、纳米氧化锌3-10份、硬脂酸2-4份、炭黑N100 15-30份、石蜡2-5份、古马隆树脂4-15份、硫磺2-10份、防老剂1-5份、碳酸钙1-8份、羟基硅油1-6份、氢硅油1-5份、白炭黑2-5份、二甲基硅油1-5份、邻苯二甲酸二丁酯2-4份、二乙基二硫代氨基甲酸锌1-4份、2-硫醇基咪唑啉2-4份。
优选的,上述的耐油橡胶包括下述重量份数的组分:
氯醇橡胶 100-160份 氟硅橡胶80-160份
纳米氧化锌 2-9份 硬脂酸1-3份
炭黑N100 18-45份 石蜡2-4份
古马隆树脂 4-12份 硫磺2-9份
防老剂 1-4份 碳酸钙2-6份
羟基硅油 1-4份 氢硅油 1-4份
白炭黑 1-5份 二甲基硅油 1-4份
邻苯二甲酸二丁酯 1-3份 二乙基二硫代氨基甲酸锌1-3份
2-硫醇基咪唑啉1-3份。
更优选的,上述的耐油橡胶包括下述重量份数的组分:
氯醇橡胶 140份 氟硅橡胶120份
纳米氧化锌 6份 硬脂酸2份
炭黑N100 35份 石蜡3份
古马隆树脂 8份 硫磺6份
防老剂 2份 碳酸钙4份
羟基硅油 2份 氢硅油 3份
白炭黑 4份 二甲基硅油 2份
邻苯二甲酸二丁酯 2份 二乙基二硫代氨基甲酸锌2份
2-硫醇基咪唑啉2份。
上述的防老剂为为6-乙氧基-2,2,4-三甲基-1,2二氢化喹啉、2,2,4-三甲基1,2-二氢化喹聚合体、二芳基仲胺类防老剂、对苯二胺类中的至少一种。
上述的防老剂为N-苯基-α-苯胺、N-苯基-N’-异丙基-对苯二胺、N-N’-二苯基-对苯二胺、防老剂4020的至少一种。
上述的防老剂为N-苯基-α-苯胺、N-N’-二苯基-对苯二胺,两者的重量份数比为1-3:1。
上述的防老剂为N-苯基-α-苯胺、N-N’-二苯基-对苯二胺,两者的重量份数比为2:1。上述的石蜡中包括低熔点石蜡、高熔点石蜡,低熔点石蜡与高熔点石蜡的重量份比1:2。
上述的橡胶还包括抗氧剂,所述的抗氧剂的重量份数为1-5份。
上述的抗氧剂的重量份数为3份。
本发明的有益效果在于,采用上述的配方所得到的耐油橡胶,具有耐油性能好、耐高温、耐腐蚀等优点,能够有效满足生产生活中的需要。
具体实施方式
实施例1
氯醇橡胶 140份 氟硅橡胶120份
纳米氧化锌 6份 硬脂酸2份
炭黑N100 35份 石蜡3份
古马隆树脂 8份 硫磺6份
防老剂 2份 碳酸钙4份
羟基硅油 2份 氢硅油 3份
白炭黑 4份 二甲基硅油 2份
邻苯二甲酸二丁酯 2份 二乙基二硫代氨基甲酸锌2份
2-硫醇基咪唑啉2份 抗氧剂3份。
防老剂为N-苯基-α-苯胺、N-N’-二苯基-对苯二胺,两者的重量份数比为2:
1;
石蜡中包括低熔点石蜡、高熔点石蜡,低熔点石蜡与高熔点石蜡的重量份数比为1:2。
当然上述说明并非是对本发明的限制,本发明也并不限于上述举例,本技术领域的普通技术人员,在本发明的实质范围内,作出的变化、改变、添加或替换,都应属于本发明的保护范围。
Claims (5)
1.一种具有耐油性能的橡胶,其特征在于,所述的耐油橡胶包括下述重量份数的组分:
氯醇橡胶80-1800份、氟硅橡胶50-180份、纳米氧化锌3-10份、硬脂酸2-4份、炭黑N100 15-30份、石蜡2-5份、古马隆树脂4-15份、硫磺2-10份、防老剂1-5份、碳酸钙1-8份、羟基硅油1-6份、氢硅油1-5份、白炭黑2-5份、二甲基硅油1-5份、邻苯二甲酸二丁酯2-4份、二乙基二硫代氨基甲酸锌1-4份、2-硫醇基咪唑啉2-4份。
2.如权利要求1所述的一种耐油橡胶,其特征在于,所述的防老剂为6-乙氧基-2,2,4-三甲基-1,2二氢化喹啉、2,2,4-三甲基1,2-二氢化喹聚合体、二芳基仲胺类防老剂、对苯二胺类中的至少一种。
3.如权利要求1所述的一种耐油橡胶,其特征在于,所述的防老剂为N-苯基-α-苯胺、N-苯基-N’-异丙基-对苯二胺、N-N’-二苯基-对苯二胺、防老剂4020的至少一种。
4.如权利要求1所述的一种耐油橡胶,其特征在于,所述的防老剂为N-苯基-α-苯胺、N-N’-二苯基-对苯二胺,两者的重量份数比为1-3:1。
5.如权利要求1所述的一种耐油橡胶,其特征在于,所述的防老剂为N-苯基-α-苯
胺、N-N’-二苯基-对苯二胺,两者的重量份数比为2:1。