CN104059307A - 遇海水膨胀橡胶止水条的材料质量配方比及其生产工艺 - Google Patents

遇海水膨胀橡胶止水条的材料质量配方比及其生产工艺 Download PDF

Info

Publication number
CN104059307A
CN104059307A CN201310087839.9A CN201310087839A CN104059307A CN 104059307 A CN104059307 A CN 104059307A CN 201310087839 A CN201310087839 A CN 201310087839A CN 104059307 A CN104059307 A CN 104059307A
Authority
CN
China
Prior art keywords
seawater
parts
sealing rod
production technique
quality
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310087839.9A
Other languages
English (en)
Inventor
胡建生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hebei Ke Xin Special Rubber Plastic Co Ltd
Original Assignee
Hebei Ke Xin Special Rubber Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hebei Ke Xin Special Rubber Plastic Co Ltd filed Critical Hebei Ke Xin Special Rubber Plastic Co Ltd
Priority to CN201310087839.9A priority Critical patent/CN104059307A/zh
Publication of CN104059307A publication Critical patent/CN104059307A/zh
Pending legal-status Critical Current

Abstract

遇海水膨胀橡胶止水条的材料质量配方比及其生产工艺，它涉及止水条技术领域，它的质量配方比为：丁基橡胶85-125份、氯化聚乙烯2-8份、膨润土20-36份、吸水性树脂10-30份、环烷油80-120份、着色剂1-5份。它能起到遇海水膨胀的作用，且膨胀倍率可调，效果明显，实用性强。

Description

遇海水膨胀橡胶止水条的材料质量配方比及其生产工艺
技术领域：
本发明涉及止水条技术领域，具体涉及一种科橡牌PN-H型遇海水膨胀橡胶止水条的材料质量配方比及其生产工艺。
背景技术：
依据现有技术：1.中华人民共和国国家标准，《离分子防水材料》GB/T18173.3—2002第三部分遇水膨胀橡胶，2.中华人民共和国建筑业行业标准JG/T141—2001，3.中华人民共和国国家标准地下防水工程质量验收规范GB50208—2002，以上3个标准中的遇水膨胀橡胶经近些年实际应用证实其优点遇水膨胀，以水止水。实用于地下防水工程，混凝土毛细缝，施工缝中。但是对于沿海地区及地下水含矿物质及含盐类较严重的环境却失去其膨胀的优点，实验证明以上标准的止水条浸泡在海水中，几乎膨胀倍率为零，起不到遇水膨胀以水止水的效果。
发明内容：
本发明的目的是提供遇海水膨胀橡胶止水条的材料质量配方比及其生产工艺，它能起到遇海水膨胀的作用，且膨胀倍率可调，效果明显，实用性强。
为了解决背景技术所存在的问题，本发明是采用以下质量配方比：丁基橡胶 85-125份、氯化聚乙烯 2-8份、膨润土 20-36份、吸水性树脂 10-30份、环烷油 80-120份、着色剂 1-5份。
本发明的生产工艺为：在密炼机内将配方中所有原料分步骤放入，进行密炼，均匀倒出后，人工压制成25X50mm的片条，通过挤出机制成所需尺寸，用包装膜隔离纸包装、初检、装箱、检测、出厂。
本发明具有以下有益效果：它能起到遇海水膨胀的作用，且膨胀倍率可调，效果明显，实用性强。
具体实施方式：
本具体实施方式采用以下质量配方比：丁基橡胶 85-125份、氯化聚乙烯 2-8份、膨润土 20-36份、吸水性树脂 10-30份、环烷油 80-120份、着色剂 1-5份。
本具体实施方式的生产工艺为：在密炼机内将配方中所有原料分步骤放入，进行密炼，均匀倒出后，人工压制成25X50mm的片条，通过挤出机制成所需尺寸，用包装膜隔离纸包装、初检、装箱、检测、出厂。
遇海水膨胀橡胶止水条的安装包含中止水条的安装和遇水膨胀止水条隧道的安装。
本具体实施方式中止水条的安装方法为：
1、需粘帖固定止水条的施工缝，后浇缝的界面应保持干燥、平整，施工前须清除界面上的浮渣、尘土及杂物；
2、止水条安装部位确定后，用高强度锚钉或水泥钉将止水条固定在安装的部位；
3、止水条必须与混凝土界面紧密接触固定牢实，防止止水条脱离界面而失去抗渗的作用。
本具体实施方式中遇水膨胀止水条隧道安装方法为：
1、参照“止水胶条安装方法”；
2、在衬砌浇注混凝土前，已出现的纵（水平）向或横（环）向施工缝界面上均安装止水条；
3、对于横（环）施工缝，最佳方法是由施工单位在需安装止水条的部位，预留一条与止水条断面一致的定位凹槽，早浇注下一道混凝土前，将止水条粘帖镶嵌在预留槽中。
本具体实施方式能起到遇海水膨胀的作用，且膨胀倍率可调，效果明显，实用性强。

Claims (2)

1.遇海水膨胀橡胶止水条的材料质量配方比及其生产工艺，其特征在于它的质量配方比为：丁基橡胶 85-125份、氯化聚乙烯 2-8份、膨润土 20-36份、吸水性树脂 10-30份、环烷油 80-120份、着色剂 1-5份。
2.根据权利要求1所述的遇海水膨胀橡胶止水条的材料质量配方比及其生产工艺，其特征在于它的生产工艺为：在密炼机内将配方中所有原料分步骤放入，进行密炼，均匀倒出后，人工压制成25X50mm的片条，通过挤出机制成所需尺寸，用包装膜隔离纸包装、初检、装箱、检测、出厂。
CN201310087839.9A 2013-03-19 2013-03-19 遇海水膨胀橡胶止水条的材料质量配方比及其生产工艺 Pending CN104059307A (zh)