CN104046144B - A kind of clean taste emulsion paint - Google Patents
A kind of clean taste emulsion paint Download PDFInfo
- Publication number
- CN104046144B CN104046144B CN201410222888.3A CN201410222888A CN104046144B CN 104046144 B CN104046144 B CN 104046144B CN 201410222888 A CN201410222888 A CN 201410222888A CN 104046144 B CN104046144 B CN 104046144B
- Authority
- CN
- China
- Prior art keywords
- raw material
- stirred
- emulsion paint
- minute
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a kind of clean taste emulsion paint, and it is made up of the raw material of following weight parts: benzene emulsion 41-50, pamorusa oil 1-2, ricinolic acid 0.5-1, Sodium hexametaphosphate 99 1-2, lauric acid amide of ethanol 1-2, casein food grade 1-2, bamboo charcoal powder 2-3, citric acid 0.4-1,2-thiol group benzimidazolyl 1-2, urea 1-2, mica powder 10-16, light calcium carbonate 20-30, film coalescence aid 4-6, deionized water 33-40; The emulsion paint of the present invention not only construction effect good, hide that ability is good, environmental protection, taste is pure and fresh, nontoxic, cost is lower, and the time used is permanent, can not go mouldy, can reach graceful, pure and fresh, naturally fit up effect.
Description
Technical field
The present invention relates generally to paint field, particularly relates to a kind of clean taste emulsion paint.
Background technology
Take acrylate copolymer emulsion as a big class synthetic resin emulsion coating of representative. Emulsion paint is water-dispersible paint, and it take synthetic resin emulsion as base-material, and filler adds the coating that various auxiliary agent is refined and become after grinding distribution. Emulsion paint has possessed the numerous advantages different from conventional wall coating materials, and as being easy to brushing, drying is rapid, paint film is water-fast, scrub resistance is good; Water-soluble interior wall emulsion paint is pollution-free, nontoxic, without disaster hidden-trouble, be easy to brushing, dry rapidly, paint film is water-fast, scrub resistance good, and color is soft. Water-soluble interior wall emulsion paint, using water as dispersion medium, the problem of environmental pollution that organic solvent-free poisonous gas brings, good permeability, avoids the film foaming disadvantage caused because of film internal and external temperature pressure difference, is applicable to the new metope application not parched.
Summary of the invention
The object of the invention is just to provide a kind of clean taste emulsion paint.
The present invention is achieved by the following technical solutions:
A kind of clean taste emulsion paint, it is made up of the raw material of following weight parts:
Benzene emulsion 41-50, pamorusa oil 1-2, ricinolic acid 0.5-1, Sodium hexametaphosphate 99 1-2, lauric acid amide of ethanol 1-2, casein food grade 1-2, bamboo charcoal powder 2-3, citric acid 0.4-1,2-thiol group benzimidazolyl 1-2, urea 1-2, mica powder 10-16, light calcium carbonate 20-30, film coalescence aid 4-6, deionized water 33-40;
Described film coalescence aid is made up of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 21-30, cetomacrogol 1000 3-5, plant sterol 1-2, hydroxypropylguar gum 2-3, amino acid chelated magnesium 1-2, polyvinylpyrrolidone 1-2, boric acid 0.1-0.2;
Above-mentioned cetomacrogol 1000 is heated to 38-40 DEG C, adds amino acid chelated magnesium, be stirred to normal temperature, add boric acid, be uniformly mixed;
The 40-50% getting above-mentioned acrylate and vinyl acetate emulsion weight mixes with hydroxypropylguar gum, at 50-60 DEG C insulated and stirred 10-15 minute, adds plant sterol, is stirred to normal temperature;
Being mixed with each raw material of residue by each raw material after above-mentioned process, 200-300 rev/min is uniformly mixed 20-30 minute, obtains described film coalescence aid.
A preparation method for clean taste emulsion paint, comprises the following steps:
(1) by above-mentioned pamorusa oil, ricinolic acid, citric acid mixing, stirring after evenly and add 2-thiol group benzimidazolyl, 300-400 rev/min is stirred 5-10 minute;
(2) joining in deionized water by Sodium hexametaphosphate 99, stir after evenly and add lauric acid amide of ethanol, bamboo charcoal powder, 200-300 rev/min is stirred 3-5 minute;
(3) by each for each starting material left after above-mentioned process raw material mix, 1400-1500 rev/min dispersed with stirring 30-40 minute, obtain described emulsion paint.
It is an advantage of the invention that:
The emulsion paint of the present invention not only construction effect good, hide that ability is good, environmental protection, taste is pure and fresh, nontoxic, cost is lower, and the time used is permanent, can not go mouldy, can reach graceful, pure and fresh, naturally fit up effect.
Embodiment
Embodiment 1
A kind of clean taste emulsion paint, it is made up of the raw material of following weight parts (kilogram):
Benzene emulsion 50, pamorusa oil 1, ricinolic acid 0.5, Sodium hexametaphosphate 99 1, lauric acid amide of ethanol 2, casein food grade 1, bamboo charcoal powder 3, citric acid 0.4,2-thiol group benzimidazolyl 1, urea 1-2, mica powder 16, light calcium carbonate 30, film coalescence aid 4, deionized water 40;
Described film coalescence aid is made up of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 30, cetomacrogol 1000 3, plant sterol 2, hydroxypropylguar gum 3, amino acid chelated magnesium 2, polyvinylpyrrolidone 2, boric acid 0.2;
Above-mentioned cetomacrogol 1000 is heated to 40 DEG C, adds amino acid chelated magnesium, be stirred to normal temperature, add boric acid, be uniformly mixed;
Get above-mentioned acrylate and vinyl acetate emulsion weight 50% mixes with hydroxypropylguar gum, and at 60 DEG C, insulated and stirred 15 minutes, add plant sterol, are stirred to normal temperature;
Being mixed with each raw material of residue by each raw material after above-mentioned process, 300 revs/min are uniformly mixed 30 minutes, obtain described film coalescence aid.
A preparation method for clean taste emulsion paint, comprises the following steps:
(1) by above-mentioned pamorusa oil, ricinolic acid, citric acid mixing, stirring after evenly and add 2-thiol group benzimidazolyl, 400 revs/min are stirred 10 minutes;
(2) joining in deionized water by Sodium hexametaphosphate 99, stir after evenly and add lauric acid amide of ethanol, bamboo charcoal powder, 300 revs/min are stirred 5 minutes;
(3) being mixed by each for each starting material left after above-mentioned process raw material, 1500 revs/min of dispersed with stirring 30 minutes, obtain described emulsion paint.
Performance test:
Paint film appearance is smooth, good without lump, good hand touch, glossiness;
Abrasion resistance is tested: passing through for 5000 times, paint film is without breakage;
Artificial ageing resistance test: 2000 hours non-foaming, do not peel off, flawless;
Water tolerance: 140h paint film is without breakage;
Alkali resistance: 120h paint film is without breakage.
Claims (2)
1. a clean taste emulsion paint, it is characterised in that it is made up of the raw material of following weight parts:
Benzene emulsion 41-50, pamorusa oil 1-2, ricinolic acid 0.5-1, Sodium hexametaphosphate 99 1-2, lauric acid amide of ethanol 1-2, casein food grade 1-2, bamboo charcoal powder 2-3, citric acid 0.4-1,2-thiol group benzimidazolyl 1-2, urea 1-2, mica powder 10-16, light calcium carbonate 20-30, film coalescence aid 4-6, deionized water 33-40;
Described film coalescence aid is made up of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 21-30, cetomacrogol 1000 3-5, plant sterol 1-2, hydroxypropylguar gum 2-3, amino acid chelated magnesium 1-2, polyvinylpyrrolidone 1-2, boric acid 0.1-0.2;
Above-mentioned cetomacrogol 1000 is heated to 38-40 DEG C, adds amino acid chelated magnesium, be stirred to normal temperature, add boric acid, be uniformly mixed;
The 40-50% getting above-mentioned acrylate and vinyl acetate emulsion weight mixes with hydroxypropylguar gum, at 50-60 DEG C insulated and stirred 10-15 minute, adds plant sterol, is stirred to normal temperature;
Being mixed with each raw material of residue by each raw material after above-mentioned process, 200-300 rev/min is uniformly mixed 20-30 minute, obtains described film coalescence aid.
2. the preparation method of a clean taste emulsion paint as claimed in claim 1, it is characterised in that comprise the following steps:
(1) by above-mentioned pamorusa oil, ricinolic acid, citric acid mixing, stirring after evenly and add 2-thiol group benzimidazolyl, 300-400 rev/min is stirred 5-10 minute;
(2) joining in deionized water by Sodium hexametaphosphate 99, stir after evenly and add lauric acid amide of ethanol, bamboo charcoal powder, 200-300 rev/min is stirred 3-5 minute;
(3) by the material that obtains after above-mentioned process and residue each raw material mixing, 1400-1500 rev/min dispersed with stirring 30-40 minute, obtain described emulsion paint.