CN104231819A - Sterilization interior wall latex paint - Google Patents
Sterilization interior wall latex paint Download PDFInfo
- Publication number
- CN104231819A CN104231819A CN201410445448.4A CN201410445448A CN104231819A CN 104231819 A CN104231819 A CN 104231819A CN 201410445448 A CN201410445448 A CN 201410445448A CN 104231819 A CN104231819 A CN 104231819A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- wall latex
- latex paint
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses sterilization interior wall latex paint which is prepared from the following raw materials in parts by weight: 32-40 parts of pure acrylic emulsion, 1-2 parts of inositol hexaphosphate, 0.6-1 part of 1,2-benzo-iothiazolin-3-one, 2-3 parts of bamboo carbon powder, 3-4 parts of absolute ethyl alcohol, 2-3 parts of xanthan gum, 1-2 parts of cocoamidopropyl betaine, 25-30 parts of talcum powder, 1-2 parts of beta-hydroxyethyl ethylene diamine, 4-7 parts of filming aid and 24-30 parts of deionized water. The sterilization interior wall latex paint disclosed by the invention is good in antibacterial and sterilization properties, and the weather resistance and the stability of a paint film are improved; due to adoption of the filming aid, the surface tension of the paint film is greatly reduced, the filming property is improved, and the stability of the paint film is further improved.
Description
?
Technical field
The present invention relates generally to paint field, particularly relates to a kind of bactericidal inner wall latex paint.
Background technology
Take acrylate copolymer emulsion as a large class synthetic resin emulsion coating of representative.Emulsion paint is water-dispersible paint, and it take synthetic resin emulsion as base-material, and filler adds the coating that various auxiliary agent is refined after grinding distribution.Emulsion paint has possessed the many merits different from conventional wall coating materials, and as being easy to brushing, drying is rapid, paint film is water-fast, scrub resistance is good; Water-soluble interior wall emulsion paint is pollution-free, nontoxic, without disaster hidden-trouble, be easy to brushing, drying rapidly, paint film is water-fast, scrub resistance good, and color is soft.Water-soluble interior wall emulsion paint, using water as dispersion medium, the problem of environmental pollution that organic solvent-free poisonous gas brings, good permeability, avoids the film foaming disadvantage caused because of film internal and external temperature pressure difference, is applicable to undried new metope application.
Summary of the invention
The object of the invention is just to provide a kind of bactericidal inner wall latex paint.
The present invention is achieved by the following technical solutions:
A kind of bactericidal inner wall latex paint, it is made up of the raw material of following weight parts:
Pure-acrylic emulsion 32-40, myo-Inositol hexaphosphate 1-2, BIT 0.6-1, bamboo charcoal powder 2-3, dehydrated alcohol 3-4, xanthan gum 2-3, AMONYL 380LC 1-2, talcum powder 25-30, beta-hydroxyethyl quadrol 1-2, film coalescence aid 4-7, deionized water 24-30;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 20-30, vinyl acetate 3-5, ethoxylated alkyl ammonium sulfate 1-2, aluminium dihydrogen phosphate 2-3, ammonium persulphate 0.5-2, deionized water 10-20;
Ethoxylated alkyl ammonium sulfate is joined in above-mentioned deionized water, stirs to obtain premixed liquid;
Vinyl acetate is heated to 40-50 DEG C, adds aluminium dihydrogen phosphate, insulated and stirred mixing 20-30 minute, join in above-mentioned premixed liquid, 200-300 rev/min of dispersed with stirring 3-5 minute, obtains dispersion liquid;
Joined by ammonium persulphate in organosilicon crylic acid latex, mix with above-mentioned dispersion liquid after being uniformly mixed, abundant ball milling, obtains described film coalescence aid.
A preparation method for bactericidal inner wall latex paint, comprises the following steps:
(1) bamboo charcoal powder is mixed with talcum powder, add xanthan gum, at 50-60 DEG C, be uniformly mixed 4-6 minute, be cooled to normal temperature;
(2) BIT is joined in dehydrated alcohol, stir;
(3) mixed with each raw material of residue by above-mentioned dispersion liquid, 1600-2000 rev/min of dispersed with stirring 30-40 minute, obtains described bactericidal inner wall latex paint.
Advantage of the present invention is:
Emulsion paint of the present invention has good antibacterial sterilising, and can improve weathering resistance and the stability of paint film, the film coalescence aid added greatly reduces coating surface tension force, improves film-forming properties, further increases the stability of paint film.
Embodiment
Embodiment 1
A kind of bactericidal inner wall latex paint, it is made up of the raw material of following weight parts (kilogram):
Pure-acrylic emulsion 40, myo-Inositol hexaphosphate 1, BIT 0.6, bamboo charcoal powder 2, dehydrated alcohol 3, xanthan gum 2, AMONYL 380LC 1, talcum powder 30, beta-hydroxyethyl quadrol 1, film coalescence aid 7, deionized water 30;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 30, vinyl acetate 3, ethoxylated alkyl ammonium sulfate 1, aluminium dihydrogen phosphate 3, ammonium persulphate 0.5, deionized water 20;
Ethoxylated alkyl ammonium sulfate is joined in above-mentioned deionized water, stirs to obtain premixed liquid;
Vinyl acetate is heated to 50 DEG C, adds aluminium dihydrogen phosphate, insulated and stirred mixes 30 minutes, joins in above-mentioned premixed liquid, and 300 revs/min of dispersed with stirring 3 minutes, obtain dispersion liquid;
Joined by ammonium persulphate in organosilicon crylic acid latex, mix with above-mentioned dispersion liquid after being uniformly mixed, abundant ball milling, obtains described film coalescence aid.
A preparation method for bactericidal inner wall latex paint, comprises the following steps:
(1) bamboo charcoal powder is mixed with talcum powder, add xanthan gum, at 60 DEG C, be uniformly mixed 6 minutes, be cooled to normal temperature;
(2) BIT is joined in dehydrated alcohol, stir;
(3) mixed with each raw material of residue by above-mentioned dispersion liquid, 2000 revs/min of dispersed with stirring 40 minutes, obtain described bactericidal inner wall latex paint.
Performance test:
Paint film appearance is smooth, good without lump, good hand touch, glossiness;
Abrasion resistance is tested: pass through for 5000 times, paint film is without breakage;
Artificial ageing resistance test: 2000 hours non-foaming, do not peel off, flawless;
Water tolerance: 140h paint film is without breakage;
Alkali resistance: 120h paint film is without breakage.
Claims (2)
1. a bactericidal inner wall latex paint, is characterized in that what it was made up of the raw material of following weight parts:
Pure-acrylic emulsion 32-40, myo-Inositol hexaphosphate 1-2, BIT 0.6-1, bamboo charcoal powder 2-3, dehydrated alcohol 3-4, xanthan gum 2-3, AMONYL 380LC 1-2, talcum powder 25-30, beta-hydroxyethyl quadrol 1-2, film coalescence aid 4-7, deionized water 24-30;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 20-30, vinyl acetate 3-5, ethoxylated alkyl ammonium sulfate 1-2, aluminium dihydrogen phosphate 2-3, ammonium persulphate 0.5-2, deionized water 10-20;
Ethoxylated alkyl ammonium sulfate is joined in above-mentioned deionized water, stirs to obtain premixed liquid;
Vinyl acetate is heated to 40-50 DEG C, adds aluminium dihydrogen phosphate, insulated and stirred mixing 20-30 minute, join in above-mentioned premixed liquid, 200-300 rev/min of dispersed with stirring 3-5 minute, obtains dispersion liquid;
Joined by ammonium persulphate in organosilicon crylic acid latex, mix with above-mentioned dispersion liquid after being uniformly mixed, abundant ball milling, obtains described film coalescence aid.
2. a preparation method for bactericidal inner wall latex paint as claimed in claim 1, is characterized in that comprising the following steps:
(1) bamboo charcoal powder is mixed with talcum powder, add xanthan gum, at 50-60 DEG C, be uniformly mixed 4-6 minute, be cooled to normal temperature;
(2) BIT is joined in dehydrated alcohol, stir;
(3) mixed with each raw material of residue by above-mentioned dispersion liquid, 1600-2000 rev/min of dispersed with stirring 30-40 minute, obtains described bactericidal inner wall latex paint.