CN104046181B - A kind of environmental protection diatom ooze emulsion paint - Google Patents
A kind of environmental protection diatom ooze emulsion paint Download PDFInfo
- Publication number
- CN104046181B CN104046181B CN201410218788.3A CN201410218788A CN104046181B CN 104046181 B CN104046181 B CN 104046181B CN 201410218788 A CN201410218788 A CN 201410218788A CN 104046181 B CN104046181 B CN 104046181B
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- stirring
- raw material
- environmental protection
- emulsion paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of environmental protection diatom ooze emulsion paint, it is made up of the raw material of following weight parts: pure-acrylic emulsion 36-40, diatom ooze 4-7, isopropanol 2-4, dimethyl sulfoxide 2-3, sodium monofluorophosphate 1-2, dimethylethanolamine 1-2, ethoxylated alkyl ammonium sulfate 1-2, zinc white 2-3, titanium dioxide 5-10, precipitated calcium carbonate 25-30, composite assistant 4-6, deionized water 30-35; The diatom ooze that the emulsion paint of the present invention adds can effectively remove the harmful substances such as the free formaldehyde in air, benzene, ammonia and because of abnormal smells from the patient produced by house pet, smoking, rubbish, purify the air of a room, diatom ooze does not produce electrostatic, does not inhale dust simultaneously, it is possible to carry out metope self-cleaning.
Description
Technical field
The invention mainly relates to paint field, particularly relate to a kind of environmental protection diatom ooze emulsion paint.
Background technology
The big class synthetic resin emulsion coating being representative with acrylate copolymer emulsion. Emulsion paint is water-dispersible paint, and it is with synthetic resin emulsion for base material, and filler adds the coating that various auxiliary agent is refined after grinding distribution. Emulsion paint has possessed the many merits different from conventional wall coating materials, as be prone to brushing, dry rapidly, paint film is water-fast, scrub resistance is good;
Emulsion paint is water paint, and their paint film property is more far better than solvent based coating, and the organic solvent accounting for solvent based coating half here be instead of by water, and therefore the toxicity problem of organic solvent, is substantially solved thoroughly by emulsion paint.
Summary of the invention
The object of the invention is just to provide a kind of environmental protection diatom ooze emulsion paint.
The present invention is achieved by the following technical solutions:
A kind of environmental protection diatom ooze emulsion paint, it is made up of the raw material of following weight parts:
Pure-acrylic emulsion 36-40, diatom ooze 4-7, isopropanol 2-4, dimethyl sulfoxide 2-3, sodium monofluorophosphate 1-2, dimethylethanolamine 1-2, ethoxylated alkyl ammonium sulfate 1-2, zinc white 2-3, titanium dioxide 5-10, precipitated calcium carbonate 25-30, composite assistant 4-6, deionized water 30-35;
Described composite assistant is made up of the raw material of following weight parts:
VAE emulsion 15-20, Alumina gel 5-7, ketopyrrolidine hydroxy acid sodium 1-2, zinc-amino acid chelate 0.2-1, hydroxypropyl methyl cellulose 2-3, carrageenan 0.2-1, dimethyl fumarate 1-2;
Above-mentioned dimethyl fumarate is joined in Alumina gel, at 70-80 DEG C stirring mixing 2-3 minute, add zinc-amino acid chelate, 100-200 rev/min dispersed with stirring 3-5 minute;
Hydroxypropyl methyl cellulose is mixed with carrageenan, is stirring evenly and then adding in VAE emulsion, stirs;
By each raw material after above-mentioned process with remain each raw material mix, 200-300 rev/min dispersed with stirring 10-20 minute, obtain described composite assistant.
The preparation method of a kind of environmental protection diatom ooze emulsion paint, comprises the following steps:
(1) joining in isopropanol by diatom ooze, at 50-60 DEG C, stirring mixing 3-6 minute, must expect a;
(2) ethoxylated alkyl ammonium sulfate is joined in above-mentioned deionized water, is stirring evenly and then adding in above-mentioned material a, 100-200 rev/min dispersed with stirring 4-6 minute, add dimethylethanolamine, stir, b must be expected;
(3) mixing of each raw material will be remained, be stirring evenly and then adding into and expect b, 1200-1600 rev/min dispersed with stirring 30-40 minute, obtain described environmental protection diatom ooze emulsion paint.
The invention have the advantage that
The diatom ooze that the emulsion paint of the present invention adds can effectively remove the harmful substances such as the free formaldehyde in air, benzene, ammonia and because of abnormal smells from the patient produced by house pet, smoking, rubbish, purify the air of a room, diatom ooze does not produce electrostatic, does not inhale dust simultaneously, it is possible to carry out metope self-cleaning.
Detailed description of the invention
Embodiment 1
A kind of environmental protection diatom ooze emulsion paint, it is made up of the raw material of following weight parts (kilogram):
Pure-acrylic emulsion 40, diatom ooze 4, isopropanol 4, dimethyl sulfoxide 3, sodium monofluorophosphate 1, dimethylethanolamine 1, ethoxylated alkyl ammonium sulfate 1, zinc white 3, titanium dioxide 10, precipitated calcium carbonate 30, composite assistant 4, deionized water 35;
Described composite assistant is made up of the raw material of following weight parts:
VAE emulsion 20, Alumina gel 7, ketopyrrolidine hydroxy acid sodium 2, zinc-amino acid chelate 0.2, hydroxypropyl methyl cellulose 3, carrageenan 0.2, dimethyl fumarate 2;
Above-mentioned dimethyl fumarate is joined in Alumina gel, stirring mixing 3 minutes at 80 DEG C, add zinc-amino acid chelate, 200 revs/min of dispersed with stirring 3 minutes;
Hydroxypropyl methyl cellulose is mixed with carrageenan, is stirring evenly and then adding in VAE emulsion, stirs;
Each raw material after above-mentioned process is mixed with remaining each raw material, 200 revs/min of dispersed with stirring 20 minutes, obtain described composite assistant.
The preparation method of a kind of environmental protection diatom ooze emulsion paint, comprises the following steps:
(1) joining in isopropanol by diatom ooze, at 60 DEG C, stirring mixing 6 minutes, must expect a;
(2) ethoxylated alkyl ammonium sulfate is joined in above-mentioned deionized water, be stirring evenly and then adding in above-mentioned material a, 200 revs/min of dispersed with stirring 6 minutes, add dimethylethanolamine, stir, b must be expected;
(3) mixing of each raw material will be remained, be stirring evenly and then adding into material b, 1600 revs/min of dispersed with stirring 40 minutes, obtain described environmental protection diatom ooze emulsion paint.
Performance test:
Paint film appearance is smooth, good without lump, good hand touch, glossiness;
Abrasion resistance is tested: passing through for 5000 times, paint film is without breakage;
Artificial ageing resistance test: 2000 hours non-foaming, do not peel off, flawless;
Resistance to water: 140h paint film is without breakage;
Alkali resistance: 120h paint film is without breakage.
Claims (2)
1. an environmental protection diatom ooze emulsion paint, it is characterised in that it is made up of the raw material of following weight parts: pure-acrylic emulsion 40, diatom ooze 4, isopropanol 4, dimethyl sulfoxide 3, sodium monofluorophosphate 1, dimethylethanolamine 1, ethoxylated alkyl ammonium sulfate 1, zinc white 3, titanium dioxide 10, precipitated calcium carbonate 30, composite assistant 4, deionized water 35;
Described composite assistant is made up of the raw material of following weight parts:
VAE emulsion 20, Alumina gel 7, ketopyrrolidine hydroxy acid sodium 2, zinc-amino acid chelate 0.2, hydroxypropyl methyl cellulose 3, carrageenan 0.2, dimethyl fumarate 2; Above-mentioned dimethyl fumarate is joined in Alumina gel, at 70-80 DEG C stirring mixing 2-3 minute, add zinc-amino acid chelate, 100-200 rev/min dispersed with stirring 3-5 minute;Hydroxypropyl methyl cellulose is mixed with carrageenan, is stirring evenly and then adding in VAE emulsion, stirs; By each raw material after above-mentioned process with remain each raw material mix, 200-300 rev/min dispersed with stirring 10-20 minute, obtain described composite assistant.
2. the preparation method of an environmental protection diatom ooze emulsion paint as claimed in claim 1, it is characterised in that comprise the following steps:
(1) joining in isopropanol by diatom ooze, at 60 DEG C, stirring mixing 6 minutes, must expect a;
(2) ethoxylated alkyl ammonium sulfate is joined in above-mentioned deionized water, be stirring evenly and then adding in above-mentioned material a, 200 revs/min of dispersed with stirring 6 minutes, add dimethylethanolamine, stir, b must be expected;
(3) mixing of each raw material will be remained, be stirring evenly and then adding into material b, 1600 revs/min of dispersed with stirring 40 minutes, obtain described environmental protection diatom ooze emulsion paint.