CN104046181A - Environment-friendly diatom ooze latex paint - Google Patents
Environment-friendly diatom ooze latex paint Download PDFInfo
- Publication number
- CN104046181A CN104046181A CN201410218788.3A CN201410218788A CN104046181A CN 104046181 A CN104046181 A CN 104046181A CN 201410218788 A CN201410218788 A CN 201410218788A CN 104046181 A CN104046181 A CN 104046181A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatom ooze
- stirring
- minute
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an environment-friendly diatom ooze latex paint, which is composed of the following raw materials by weight: 36-40 parts of pure acrylic emulsion, 4-7 parts of diatom ooze, 2-4 parts of isopropanol, 2-3 parts of dimethyl sulfoxide, 1-2 parts of sodium monofluorophosphate, 1-2 parts of dimethylethanolamine, 1-2 parts of fatty alcohol polyoxyethylene ether ammonium sulfate, 2-3 parts of zinc white, 5-10 parts of titanium white powder, 25-30 parts of light calcium carbonate, 4-6 parts of a composite auxiliary agent and 30-35 parts of deionized water. The diatom ooze added into the latex paint provided by the invention can effectively remove harmful substances such as free formaldehyde, benzene and ammonia in the air, and other and odors generated by pets, smoking and garbage, and purify the indoor air; and the diatom ooze does not generate static electricity or absorb dust, and can carry out metope self-cleaning.
Description
Technical field
The present invention relates generally to paint field, relates in particular to a kind of environmental protection diatom ooze emulsion paint.
Background technology
A large class synthetic resin emulsion coating taking acrylate copolymer emulsion as representative.Emulsion paint is water-dispersible paint, and it is taking synthetic resin emulsion as base-material, and filler adds the refining coating forming of various auxiliary agents after grinding distribution.Emulsion paint has possessed the many merits different from traditional wallcovering, as be easy to brushing, dry rapidly, paint film is water-fast, scrub resistance is good etc.;
Emulsion paint is water-borne coatings, and their paint film property is more far better than solvent based coating, and the organic solvent that accounts for solvent based coating half has here been replaced by water, and therefore the toxicity problem of organic solvent, has been solved thoroughly by emulsion paint substantially.
Summary of the invention
The object of the invention is just to provide a kind of environmental protection diatom ooze emulsion paint.
The present invention is achieved by the following technical solutions:
A kind of environmental protection diatom ooze emulsion paint, it is made up of the raw material of following weight parts:
Pure-acrylic emulsion 36-40, diatom ooze 4-7, Virahol 2-4, dimethyl sulfoxide (DMSO) 2-3, sodium monoflurophosphate 1-2, dimethylethanolamine 1-2, ethoxylated alkyl ammonium sulfate 1-2, zinc white 2-3, titanium dioxide 5-10, light calcium carbonate 25-30, composite assistant 4-6, deionized water 30-35;
Described composite assistant is made up of the raw material of following weight parts:
VAE emulsion 15-20, aluminium colloidal sol 5-7, pyrrolidone hydroxy acid sodium 1-2, zinc-amino acid chelate 0.2-1, Vltra tears 2-3, carrageenin 0.2-1, dimethyl fumarate 1-2;
Above-mentioned dimethyl fumarate is joined in aluminium colloidal sol, at 70-80 DEG C, be uniformly mixed 2-3 minute, add zinc-amino acid chelate, 100-200 rev/min of dispersed with stirring 3-5 minute;
Vltra tears is mixed with carrageenin, after stirring, join in VAE emulsion, stir;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 200-300 rev/min of dispersed with stirring 10-20 minute, obtains described composite assistant.
A preparation method for environmental protection diatom ooze emulsion paint, comprises the following steps:
(1) diatom ooze is joined in Virahol, at 50-60 DEG C, be uniformly mixed 3-6 minute, must expect a;
(2) ethoxylated alkyl ammonium sulfate is joined in above-mentioned deionized water, join in above-mentioned material a after stirring, 100-200 rev/min of dispersed with stirring 4-6 minute, adds dimethylethanolamine, stirs, and must expect b;
(3) will remain each raw material and mix, and add pan feeding b after stirring, 1200-1600 rev/min of dispersed with stirring 30-40 minute, obtains described environmental protection diatom ooze emulsion paint.
Advantage of the present invention is:
The smell that the diatom ooze that emulsion paint of the present invention adds can effectively be removed the objectionable impuritiess such as airborne free formaldehyde, benzene, ammonia and produce because of pet, smoking, rubbish, purify the air of a room, simultaneously diatom ooze does not produce static, does not inhale dust, can carry out metope self-cleaning.
Embodiment
Embodiment 1
A kind of environmental protection diatom ooze emulsion paint, it by following weight parts (kilogram) raw material form:
Pure-acrylic emulsion 40, diatom ooze 4, Virahol 4, dimethyl sulfoxide (DMSO) 3, sodium monoflurophosphate 1, dimethylethanolamine 1, ethoxylated alkyl ammonium sulfate 1, zinc white 3, titanium dioxide 10, light calcium carbonate 30, composite assistant 4, deionized water 35;
Described composite assistant is made up of the raw material of following weight parts:
VAE emulsion 20, aluminium colloidal sol 7, pyrrolidone hydroxy acid sodium 2, zinc-amino acid chelate 0.2, Vltra tears 3, carrageenin 0.2, dimethyl fumarate 2;
Above-mentioned dimethyl fumarate is joined in aluminium colloidal sol, at 80 DEG C, be uniformly mixed 3 minutes, add zinc-amino acid chelate, 200 revs/min of dispersed with stirring 3 minutes;
Vltra tears is mixed with carrageenin, after stirring, join in VAE emulsion, stir;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 200 revs/min of dispersed with stirring 20 minutes, obtain described composite assistant.
A preparation method for environmental protection diatom ooze emulsion paint, comprises the following steps:
(1) diatom ooze is joined in Virahol, be uniformly mixed 6 minutes at 60 DEG C, must expect a;
(2) ethoxylated alkyl ammonium sulfate is joined in above-mentioned deionized water, join in above-mentioned material a after stirring, 200 revs/min of dispersed with stirring 6 minutes, add dimethylethanolamine, stir, and must expect b;
(3) will remain each raw material and mix, and add pan feeding b after stirring, 1600 revs/min of dispersed with stirring 40 minutes, obtain described environmental protection diatom ooze emulsion paint.
Performance test:
Paint film appearance is smooth, good without lump, good hand touch, glossiness;
Abrasion resistance test: pass through for 5000 times, paint film is without breakage;
Artificial ageing resistance test: 2000 hours non-foaming, do not peel off, flawless;
Water tolerance: 140h paint film is without breakage;
Alkali resistance: 120h paint film is without breakage.
Claims (2)
1. an environmental protection diatom ooze emulsion paint, is characterized in that what it was made up of the raw material of following weight parts:
Pure-acrylic emulsion 36-40, diatom ooze 4-7, Virahol 2-4, dimethyl sulfoxide (DMSO) 2-3, sodium monoflurophosphate 1-2, dimethylethanolamine 1-2, ethoxylated alkyl ammonium sulfate 1-2, zinc white 2-3, titanium dioxide 5-10, light calcium carbonate 25-30, composite assistant 4-6, deionized water 30-35;
Described composite assistant is made up of the raw material of following weight parts:
VAE emulsion 15-20, aluminium colloidal sol 5-7, pyrrolidone hydroxy acid sodium 1-2, zinc-amino acid chelate 0.2-1, Vltra tears 2-3, carrageenin 0.2-1, dimethyl fumarate 1-2;
Above-mentioned dimethyl fumarate is joined in aluminium colloidal sol, at 70-80 DEG C, be uniformly mixed 2-3 minute, add zinc-amino acid chelate, 100-200 rev/min of dispersed with stirring 3-5 minute;
Vltra tears is mixed with carrageenin, after stirring, join in VAE emulsion, stir;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 200-300 rev/min of dispersed with stirring 10-20 minute, obtains described composite assistant.
2. a preparation method for environmental protection diatom ooze emulsion paint as claimed in claim 1, is characterized in that comprising the following steps:
(1) diatom ooze is joined in Virahol, at 50-60 DEG C, be uniformly mixed 3-6 minute, must expect a;
(2) ethoxylated alkyl ammonium sulfate is joined in above-mentioned deionized water, join in above-mentioned material a after stirring, 100-200 rev/min of dispersed with stirring 4-6 minute, adds dimethylethanolamine, stirs, and must expect b;
(3) will remain each raw material and mix, and add pan feeding b after stirring, 1200-1600 rev/min of dispersed with stirring 30-40 minute, obtains described environmental protection diatom ooze emulsion paint.