CN104231850A - Antimicrobial anticorrosive powder paint - Google Patents
Antimicrobial anticorrosive powder paint Download PDFInfo
- Publication number
- CN104231850A CN104231850A CN201410416739.0A CN201410416739A CN104231850A CN 104231850 A CN104231850 A CN 104231850A CN 201410416739 A CN201410416739 A CN 201410416739A CN 104231850 A CN104231850 A CN 104231850A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- sizing agent
- paint
- copper sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antimicrobial anticorrosive powder paint which is prepared from the following raw materials in parts by weight: 33-40 parts of epoxy resin, 1-2 parts of polyethylene wax, 1-2 parts of zinc oxide, 0.3-0.5 part of silicon micropowder, 1-2 parts of polyisocyanate, 0.1-0.3 part of benzoin, 1-3 parts of castor oil, 2-3 parts of benzotriazole, 1-5 parts of sodium tripolyphosphate, 4-6 parts of light calcium carbonate, 1-2 parts of ethyl cellulose, 13-16 parts of gum, 1-2 parts of wollastonite, 3-5 parts of tributyl phosphate, 1-2 parts of copper sulfate, 10-20 parts of bacon rubber, 1-2 parts of epoxy soybean oil, 1-2 parts of cobalt naphthenate and 4-8 parts of compound adhesive. The paint is simple in manufacturing technique and convenient to use; the application method is common electrostatic spraying; and under the actions of copper sulfate and other antimicrobial agents, the paint has favorable inhibiting and killing actions on multiple bacteria and fungi after being applied.
Description
Technical field
The present invention relates to art of powder coatings, is exactly a kind of Antimicrobial preservative powder coating.
Background technology
Powder coating is a kind of novel not containing solvent 100% solid powdery coating.There is solvent-free, pollution-free, recyclable, environmental protection, the saving energy and resource, reduce labor intensity and film physical strength high.And Mierocrystalline cellulose must apply in coating is a lot, the effect of coating toughness can be played.
Summary of the invention
The object of the present invention is to provide a kind of Antimicrobial preservative powder coating.
Above-mentioned purpose is realized by following scheme:
A kind of Antimicrobial preservative powder coating, is characterized in that: it is obtained by the raw material of following weight parts:
Epoxy resin 33-40, polyethylene wax 1-2, zinc oxide 1-2, silicon powder 0.3-0.5, polyisocyanates 1-2, st-yrax 0.1-0.3, Viscotrol C 1-3, benzotriazole 2-3, tripoly phosphate sodium STPP 1-5, light calcium carbonate 4-6, ethyl cellulose 1-2, gummy 13-16, wollastonite 1-2, tributyl phosphate 3-5, copper sulfate 1-2, smoke sheet rubber 10-20, epoxy soybean oil 1-2, cobalt naphthenate 1-2, composite sizing agent 4-8;
Composite sizing agent is obtained by the raw material of following weight parts:
Styrene-butadiene rubber(SBR) 4-6; st-yrax 0.1-0.5, acetone 1-2, pine tar 1-2, resol 0.8-0.9, Hydroxylated acrylic resin 1-2, zinc powder 0.1-0.2, silica 1-2, uric acid 0.1-0.5, Walocel MT 20.000PV 1-2, antioxidant 1076 1-2, polyether-ether-ketone 1-2;
The preparation method of composite sizing agent is: after each raw material blending, in 80-90 DEG C of mixing 10-20min, after taking-up, pulverizes, crosses 100-200 mesh sieve, to obtain final product.
Described a kind of Antimicrobial preservative powder coating, is characterized in that:
Preparation method comprises the following steps:
(1) all materials take by proportioning, are placed in high-speed mixer, mixing 3-6min;
(2) two spiral shell forcing machine is adopted, 110-125
oabout C extrudes;
(3) extruding tablet through pulverizing, crossing 200-300 mesh sieve, to obtain final product.
Beneficial effect of the present invention is:
Coating manufacture craft of the present invention is simple, and easy to use, coating process is general electrostatic spraying, by the effect of the antiseptic-germicides such as copper sulfate, after making application of the present invention, has good suppression and killing action to various bacteria and fungi.
Embodiment
A kind of Antimicrobial preservative powder coating, it is obtained by the raw material of following weight (kg):
Epoxy resin 40, polyethylene wax 2, zinc oxide 1, silicon powder 0.5, polyisocyanates 1, st-yrax 0.3, Viscotrol C 3, benzotriazole 2, tripoly phosphate sodium STPP 1, light calcium carbonate 6, ethyl cellulose 2, natural gum 15, wollastonite 2, tributyl phosphate 3, copper sulfate 2, smoke sheet rubber 10, epoxy soybean oil 2, cobalt naphthenate 1, composite sizing agent 6;
Composite sizing agent is obtained by the raw material of following weight (kg):
Styrene-butadiene rubber(SBR) 6, st-yrax 0.1, acetone 2, pine tar 1, resol 0.9, Hydroxylated acrylic resin 2, zinc powder 0.2, silicon-dioxide 2, uric acid 0.5, Walocel MT 20.000PV 2, antioxidant 1076 1, polyether-ether-ketone 2;
The preparation method of composite sizing agent is: after each raw material blending, in 90 DEG C of mixing 20min, after taking-up, pulverizes, crosses 100 mesh sieves, to obtain final product.
Described a kind of Antimicrobial preservative powder coating, is characterized in that:
Preparation method comprises the following steps:
(1) all materials take by proportioning, are placed in high-speed mixer, mixing 5min;
(2) two spiral shell forcing machine is adopted, 125
oabout C extrudes;
(3) extruding tablet through pulverizing, crossing 300 mesh sieves, to obtain final product.
The coating process of the present embodiment product is general electrostatic spraying, condition of cure: 200
oc/12-15min, gained coating is level and smooth, complete, and the artificial accelerated aging time is>=1500h.
Claims (2)
1. an Antimicrobial preservative powder coating, is characterized in that: it is obtained by the raw material of following weight parts:
Epoxy resin 33-40, polyethylene wax 1-2, zinc oxide 1-2, silicon powder 0.3-0.5, polyisocyanates 1-2, st-yrax 0.1-0.3, Viscotrol C 1-3, benzotriazole 2-3, tripoly phosphate sodium STPP 1-5, light calcium carbonate 4-6, ethyl cellulose 1-2, gummy 13-16, wollastonite 1-2, tributyl phosphate 3-5, copper sulfate 1-2, smoke sheet rubber 10-20, epoxy soybean oil 1-2, cobalt naphthenate 1-2, composite sizing agent 4-8;
Composite sizing agent is obtained by the raw material of following weight parts:
Styrene-butadiene rubber(SBR) 4-6; st-yrax 0.1-0.5, acetone 1-2, pine tar 1-2, resol 0.8-0.9, Hydroxylated acrylic resin 1-2, zinc powder 0.1-0.2, silica 1-2, uric acid 0.1-0.5, Walocel MT 20.000PV 1-2, antioxidant 1076 1-2, polyether-ether-ketone 1-2;
The preparation method of composite sizing agent is: after each raw material blending, in 80-90 DEG C of mixing 10-20min, after taking-up, pulverizes, crosses 100-200 mesh sieve, to obtain final product.
2. a kind of Antimicrobial preservative powder coating according to claim 1, is characterized in that:
Preparation method comprises the following steps:
(1) all materials take by proportioning, are placed in high-speed mixer, mixing 3-6min;
(2) two spiral shell forcing machine is adopted, 110-125
oabout C extrudes;
(3) extruding tablet through pulverizing, crossing 200-300 mesh sieve, to obtain final product.