CN104046168A - High adhesion latex paint - Google Patents
High adhesion latex paint Download PDFInfo
- Publication number
- CN104046168A CN104046168A CN201410218789.8A CN201410218789A CN104046168A CN 104046168 A CN104046168 A CN 104046168A CN 201410218789 A CN201410218789 A CN 201410218789A CN 104046168 A CN104046168 A CN 104046168A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- raw material
- minute
- mentioned
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high adhesion latex paint, which is composed of the following raw materials by weight: 35-40 parts of pure acrylic emulsion, 2-3 parts of barium metaborate, 1-2 parts of coco fatty acid diethanol amide, 1-2 parts of hexadecyl trimethyl ammonium bromide, 0.6-1 parts of isopropyl myristate, 1-2 parts of 2-mercapto benzimidazole, 1-2 parts of N,N-diethylaniline, 4-6 parts of ethanol, 2-3 parts of sodium hexametaphosphate, 10-14 parts of titanium dioxide, 20-25 parts of nano calcium carbonate, 6-8 parts of composite additive, and 25-40 parts of deionized water. The latex paint provided by the invention has the advantages of good material compatibility, firm film, smooth surface, strong adhesion to the substrate, and strong scrub resistance and stain resistance; and the added composite additive greatly improves the film forming effect, enhances the adhesion, and improves the stability of the paint film.
Description
Technical field
The present invention relates generally to paint field, relates in particular to a kind of high emulsion paint that adheres to.
Background technology
A large class synthetic resin emulsion coating taking acrylate copolymer emulsion as representative.Emulsion paint is water-dispersible paint, and it is taking synthetic resin emulsion as base-material, and filler adds the refining coating forming of various auxiliary agents after grinding distribution.Emulsion paint has possessed the many merits different from traditional wallcovering, as be easy to brushing, dry rapidly, paint film is water-fast, scrub resistance is good etc.;
Emulsion paint is water-borne coatings, and their paint film property is more far better than solvent based coating, and the organic solvent that accounts for solvent based coating half has here been replaced by water, and therefore the toxicity problem of organic solvent, has been solved thoroughly by emulsion paint substantially.
Summary of the invention
The object of the invention is just to provide a kind of high emulsion paint that adheres to.
The present invention is achieved by the following technical solutions:
A kind of high emulsion paint that adheres to, it is made up of the raw material of following weight parts:
Pure-acrylic emulsion 35-40, barium metaborate 2-3, lauric acid amide of ethanol 1-2, cetyl trimethylammonium bromide 1-2, Isopropyl myristate 0.6-1,2-thiol group benzimidazolyl 1-2, N, N-Diethyl Aniline 1-2, ethanol 4-6, Sodium hexametaphosphate 99 2-3, titanium dioxide 10-14, nano-calcium carbonate 20-25, composite assistant 6-8, deionized water 25-40;
Described composite assistant is made up of the raw material of following weight parts:
VAE emulsion 15-20, aluminium colloidal sol 5-7, pyrrolidone hydroxy acid sodium 1-2, zinc-amino acid chelate 0.2-1, Vltra tears 2-3, carrageenin 0.2-1, dimethyl fumarate 1-2;
Above-mentioned dimethyl fumarate is joined in aluminium colloidal sol, at 70-80 DEG C, be uniformly mixed 2-3 minute, add zinc-amino acid chelate, 100-200 rev/min of dispersed with stirring 3-5 minute;
Vltra tears is mixed with carrageenin, after stirring, join in VAE emulsion, stir;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 200-300 rev/min of dispersed with stirring 10-20 minute, obtains described composite assistant.
A high preparation method who adheres to emulsion paint, comprises the following steps:
(1) 2-thiol group benzimidazolyl is joined in above-mentioned ethanol, after fully stirring, add N, N-Diethyl Aniline, stirs;
(2) Sodium hexametaphosphate 99 is joined in above-mentioned deionized water, after stirring, add Isopropyl myristate, be uniformly mixed 3-4 minute, add titanium dioxide, cetyl trimethylammonium bromide, 300-500 rev/min of dispersed with stirring 10-15 minute;
(3) above-mentioned each raw material after treatment is mixed with the each raw material of residue, 1600-2000 rev/min of dispersed with stirring 30-40 minute, obtains described height and adheres to emulsion paint.
Advantage of the present invention is:
The consistency of the each raw material of emulsion paint of the present invention is good, and paint film is firm, smooth surface, and to the strong adhesion of base material, scrubbing resistance, resistance to soiling are strong, and the composite assistant adding has improved film-formation result greatly, has strengthened cohesiveness, has improved the stability of paint film.
Embodiment
Embodiment 1
A kind of high emulsion paint that adheres to, it by following weight parts (kilogram) raw material form:
Pure-acrylic emulsion 35-40, barium metaborate 3, lauric acid amide of ethanol 2, cetyl trimethylammonium bromide 2, Isopropyl myristate 0.6,2-thiol group benzimidazolyl 1, N, N-Diethyl Aniline 1, ethanol 6, Sodium hexametaphosphate 99 2, titanium dioxide 14, nano-calcium carbonate 25, composite assistant 6, deionized water 40;
Described composite assistant is made up of the raw material of following weight parts:
VAE emulsion 20, aluminium colloidal sol 7, pyrrolidone hydroxy acid sodium 1, zinc-amino acid chelate 0.2, Vltra tears 3, carrageenin 0.2, dimethyl fumarate 1;
Above-mentioned dimethyl fumarate is joined in aluminium colloidal sol, at 80 DEG C, be uniformly mixed 3 minutes, add zinc-amino acid chelate, 200 revs/min of dispersed with stirring 3 minutes;
Vltra tears is mixed with carrageenin, after stirring, join in VAE emulsion, stir;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 300 revs/min of dispersed with stirring 20 minutes, obtain described composite assistant.
A high preparation method who adheres to emulsion paint, comprises the following steps:
(1) 2-thiol group benzimidazolyl is joined in above-mentioned ethanol, after fully stirring, add N, N-Diethyl Aniline, stirs;
(2) Sodium hexametaphosphate 99 is joined in above-mentioned deionized water, after stirring, add Isopropyl myristate, be uniformly mixed 3 minutes, add titanium dioxide, cetyl trimethylammonium bromide, 500 revs/min of dispersed with stirring 15 minutes;
(3) above-mentioned each raw material after treatment is mixed with the each raw material of residue, 2000 revs/min of dispersed with stirring 40 minutes, obtain described height and adhere to emulsion paint.
Performance test:
Paint film appearance is smooth, good without lump, good hand touch, glossiness;
Abrasion resistance test: pass through for 5000 times, paint film is without breakage;
Artificial ageing resistance test: 2000 hours non-foaming, do not peel off, flawless;
Water tolerance: 140h paint film is without breakage;
Alkali resistance: 120h paint film is without breakage.
Claims (2)
1. the high emulsion paint that adheres to, is characterized in that what it was made up of the raw material of following weight parts:
Pure-acrylic emulsion 35-40, barium metaborate 2-3, lauric acid amide of ethanol 1-2, cetyl trimethylammonium bromide 1-2, Isopropyl myristate 0.6-1,2-thiol group benzimidazolyl 1-2, N, N-Diethyl Aniline 1-2, ethanol 4-6, Sodium hexametaphosphate 99 2-3, titanium dioxide 10-14, nano-calcium carbonate 20-25, composite assistant 6-8, deionized water 25-40;
Described composite assistant is made up of the raw material of following weight parts:
VAE emulsion 15-20, aluminium colloidal sol 5-7, pyrrolidone hydroxy acid sodium 1-2, zinc-amino acid chelate 0.2-1, Vltra tears 2-3, carrageenin 0.2-1, dimethyl fumarate 1-2;
Above-mentioned dimethyl fumarate is joined in aluminium colloidal sol, at 70-80 DEG C, be uniformly mixed 2-3 minute, add zinc-amino acid chelate, 100-200 rev/min of dispersed with stirring 3-5 minute;
Vltra tears is mixed with carrageenin, after stirring, join in VAE emulsion, stir;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 200-300 rev/min of dispersed with stirring 10-20 minute, obtains described composite assistant.
2. height as claimed in claim 1 adheres to a preparation method for emulsion paint, it is characterized in that comprising the following steps:
(1) 2-thiol group benzimidazolyl is joined in above-mentioned ethanol, after fully stirring, add N, N-Diethyl Aniline, stirs;
(2) Sodium hexametaphosphate 99 is joined in above-mentioned deionized water, after stirring, add Isopropyl myristate, be uniformly mixed 3-4 minute, add titanium dioxide, cetyl trimethylammonium bromide, 300-500 rev/min of dispersed with stirring 10-15 minute;
(3) above-mentioned each raw material after treatment is mixed with the each raw material of residue, 1600-2000 rev/min of dispersed with stirring 30-40 minute, obtains described height and adheres to emulsion paint.