CN104026088A - 环保海竿坠及其制备方法 - Google Patents

环保海竿坠及其制备方法 Download PDF

Info

Publication number
CN104026088A
CN104026088A CN201310080515.2A CN201310080515A CN104026088A CN 104026088 A CN104026088 A CN 104026088A CN 201310080515 A CN201310080515 A CN 201310080515A CN 104026088 A CN104026088 A CN 104026088A
Authority
CN
China
Prior art keywords
iron ore
environmental protection
semi
cement
finished product
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310080515.2A
Other languages
English (en)
Other versions
CN104026088B (zh
Inventor
王国正
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310080515.2A priority Critical patent/CN104026088B/zh
Publication of CN104026088A publication Critical patent/CN104026088A/zh
Application granted granted Critical
Publication of CN104026088B publication Critical patent/CN104026088B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种环保海竿坠，包括坠体，该坠体内部设有贯穿该坠体的管子，按重量份计，所述坠体的组分包括：铁矿石粉5～8份，水泥1～3份，粘土矿粉1～2份。优化后，按重量份计，所述坠体的组分包括：铁矿石粉7份，水泥2份，粘土矿粉1份；所述管子为塑料管。本发明所具有的优点是：极为环保且制备成本较低。本发明还公开了该环保海竿坠的制备方法。

Description

环保海竿坠及其制备方法
技术领域
本发明涉及钓具技术领域，尤其是涉及一种环保海竿坠。本发明还涉及该环保海竿坠的制备方法。
背景技术
使用海竿钓鱼极富乐趣，因此海竿坠作为耗材大量使用。目前市场上的海竿坠包括30g、60g、80g等多种规格，但是均为铅制品。由于海竿坠在使用时会不可避免的大量掉落于水中，比如，黄河小浪底库区中每年掉入的铅制海竿坠高达2吨，从而海竿坠对水质造成极大污染。同时，铅的成本较高，造成海竿坠的制备成本居高不下。
发明内容
本发明的目的是提供一种环保海竿坠，它具有极为环保且制备成本较低的特点。本发明还公开了该环保海竿坠的制备方法。
本发明所采用的技术方案是：环保海竿坠，包括坠体，该坠体内部设有贯穿该坠体的管子，按重量份计，所述坠体的组分包括：铁矿石粉5～8份，水泥1～3份，粘土矿粉1～2份。
按重量份计，所述坠体的组分包括：铁矿石粉7份，水泥2份，粘土矿粉1份。
所述管子为塑料管。
本发明环保海竿坠所具有的优点是：极为环保且制备成本较低。本发明的环保海竿坠避免对铅的使用，替代以常见的铁矿石粉、水泥以及粘土矿等原料制备，从而不会对水质造成铅污染。同时，这些原料相对于铅而言，价格极低，从而极大的降低了海竿坠的制备成本。
本发明的环保海竿坠的制备方法，包括如下步骤：
A)按比例取铁矿石、水泥和粘土矿，并将铁矿石和粘土矿粉碎为至少80目后分别形成铁矿石粉和粘土矿粉；
B)将铁矿石粉、水泥、粘土矿粉搅拌均匀，且伴随添加水，所添加水量以原料不至于散开为准，最终形成湿状混合原料；
C)将湿状混合原料放置入液压成型机中在12～18T的压力、180～220℃的温度下压制形成第一半成品；
D)将第一半成品中穿入管子形成第二半成品；
E)将第二半成品存放晾干至少20天形成成品。
所述步骤C)中液压成型机的压力为：15T，温度为：200℃。
所述步骤E)中第二半成品存放晾干时间至少为30天。
本发明制备方法采用极为常见的设备即可实现，从而操作简单，不会增加海竿坠的制备成本。
附图说明
下面结合附图和实施例对本发明进一步说明：
图1是本发明的实施例的环保海竿坠的主视剖视图。
图中：10、坠体；20、管子。
具体实施方式
实施例1，见图1所示：环保海竿坠，包括坠体10，该坠体10内部设有贯穿该坠体10的管子20。该管子20可以是常见的金属管等任何材质制备的管子，优化的，为了更为环保和易于制备，该管子20采取塑料管。
该环保海竿坠通过以下步骤制备：
A)按照比例取铁矿石5kg、水泥1kg和粘土矿1kg，并将铁矿石和粘土矿粉碎为80目后分别形成铁矿石粉和粘土矿粉。其中，铁矿石可以是常见的磁铁矿(Fe3O4)、赤铁矿(Fe2O3)和菱铁矿(FeCO3)等；水泥采用任何标号的硅酸盐水泥均可；粘土矿可以是常见的高岭石族、伊利石族、蒙脱石族、蛭石族以及海泡石族等矿物。
B)将铁矿石粉、水泥、粘土矿粉搅拌均匀，且伴随添加水，所添加水量以原料不至于散开为准，最终形成湿状混合原料。
C)将湿状混合原料放置入液压成型机中在12T的压力、180℃的温度下压制形成第一半成品。需要说明的是，将以上湿状混合原料放置入合适大小模具中之后，方才放置入液压成型机中成型。从而，所形成的第一半成品根据需要具有合适的体积和形状。
D)将第一半成品中穿入管子形成第二半成品；
E)将第二半成品存放晾干20天形成成品。
实施例2，与实施例1的区别仅在于：
步骤A)中按比例取铁矿石7kg、水泥2kg和粘土矿1kg，并将铁矿石和粘土矿粉碎为100目后分别形成铁矿石粉和粘土矿粉。
步骤C)中液压成型机的压力为：15T，温度为：200℃。
步骤E)中第二半成品存放晾干时间为30天。
实施例3，与实施例1的区别仅在于：
步骤A)中按比例取铁矿石8kg、水泥3kg和粘土矿1.5kg，并将铁矿石和粘土矿粉碎为120目分别形成铁矿石粉和粘土矿粉。
步骤C)中液压成型机的压力为：18T，温度为：220℃。
步骤E)中第二半成品存放晾干时间为35天。
实施例4，与实施例1的区别仅在于：
步骤A)中按比例取铁矿石8kg、水泥3kg和粘土矿2kg，并将铁矿石和粘土矿粉碎为100目分别形成铁矿石粉和粘土矿粉。
步骤C)中液压成型机的压力为：18T，温度为：200℃。
步骤E)中第二半成品存放晾干时间为30天。
效果例：经常规测算，本发明的环保海竿坠的坠体的原料的成本为5000～6000元/T，而铅的价格多在14000元/T左右，从而本发明的环保海竿坠仅在原料成本上而言，已经具有极大的优势。同时，由于本发明的环保海竿坠不含铅，从而不会对水质造成铅污染。
以上所述仅为本发明的优选实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书及附图内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (6)

1.环保海竿坠，包括坠体，该坠体内部设有贯穿该坠体的管子，其特征在于：按重量份计，所述坠体的组分包括：铁矿石粉5～8份，水泥1～3份，粘土矿粉1～2份。
2.根据权利要求1所述的环保海竿坠，其特征在于：按重量份计，所述坠体的组分包括：铁矿石粉7份，水泥2份，粘土矿粉1份。
3.根据权利要求1或2所述的环保海竿坠，其特征在于：所述管子为塑料管。
4.根据权利要求1所述的环保海竿坠的制备方法，包括如下步骤：
A)按比例取铁矿石、水泥和粘土矿，并将铁矿石和粘土矿粉碎为至少80目后分别形成铁矿石粉和粘土矿粉；
B)将铁矿石粉、水泥、粘土矿粉搅拌均匀，且伴随添加水，所添加水量以原料不至于散开为准，最终形成湿状混合原料；
C)将湿状混合原料放置入液压成型机中在12～18T的压力、180～220℃的温度下压制形成第一半成品；
D)将第一半成品中穿入管子形成第二半成品；
E)将第二半成品存放晾干至少20天形成成品。
5.根据权利要求4所述的环保海竿坠的制备方法，其特征在于：所述步骤C)中液压成型机的压力为：15T，温度为：200℃。
6.根据权利要求4所述的环保海竿坠的制备方法，其特征在于：所述步骤E)中第二半成品存放晾干时间至少为30天。
CN201310080515.2A 2013-03-07 2013-03-07 环保海竿坠的制备方法 Active CN104026088B (zh)