CN102826798B - 一种煤矸石砖及其生产方法 - Google Patents
一种煤矸石砖及其生产方法 Download PDFInfo
- Publication number
- CN102826798B CN102826798B CN201210266731.1A CN201210266731A CN102826798B CN 102826798 B CN102826798 B CN 102826798B CN 201210266731 A CN201210266731 A CN 201210266731A CN 102826798 B CN102826798 B CN 102826798B
- Authority
- CN
- China
- Prior art keywords
- powder
- production method
- coal gangue
- colliery
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种煤矸石砖及其生产方法煤矸石粉20-30、水泥5-10、铝粉3-8、石膏3-5、刚玉莫来石2-5、皂角粉3-5、细沙20-25、石灰8-12和膨胀珍珠岩8-12。本发明配方合理，具有工艺设计合理、操作简单、节省能源、废物综合利用、保护耕地、占地少投资少等特点，具有很好的推广使用价值。
Description
技术领域
本发明涉及一种石砖的生产方法，具体涉及一种煤矸石砖及其生产方法。
背景技术
随着社会的发展，石砖的需求量不断的增加，在过去的几年中，大量地使用粘土生产建筑用砖人为地破坏了很多良田耕地，在城市和城乡村建设中，砖瓦在与新型建筑材料的竞争中，仍然是重要的建筑材料，所以研究砖瓦的生产工艺，仍然具有相当重要意义。
发明内容
为了缓解现有技术的不足和缺陷，本发明的目的在于提供一种煤矸石砖及其生产方法，本发明配方合理，具有工艺设计合理、操作简单、节省能源、废物综合利用、保护耕地、占地少投资少等特点，具有很好的推广使用价值。
为了实现上述目的本发明采用如下技术方案：
一种煤矸石砖，其特征在于其组成原料的重量份为：煤矸石粉20-30、水泥5-10、铝粉3-8、石膏3-5、刚玉莫来石2-5、皂角粉3-5、细沙20-25、石灰8-12和膨胀珍珠岩8-12。
所述的煤矸石砖，其特征在于其组成原料的重量份如下表：
煤矸石砖的生产方法，包括以下步骤：按组成原料的重量份称取各原料，然后将煤矸石粉兑水和石膏一起制浆，再打到存浆罐，加热到38-42℃，再将石灰，水泥，铝粉，皂角粉，细沙，刚玉莫来石和膨胀珍珠岩浇铸进去再搅拌5-6分钟，再预养2小时，切割，再进蒸压釜蒸养8-10小时，得到煤矸石砖。
本发明的有益效果：
本发明配方合理，具有工艺设计合理、操作简单、节省能源、废物综合利用、保护耕地、占地少投资少等特点，具有很好的推广使用价值。
具体实施方式
实施例1：一种煤矸石砖，其组成原料的重量份如下表：
煤矸石砖的生产方法，包括以下步骤：按组成原料的重量份称取各原料，然后将煤矸石粉兑水和石膏一起制浆，再打到存浆罐，加热到40℃，再将石灰，水泥，铝粉，皂角粉，细沙，刚玉莫来石和膨胀珍珠岩浇铸进去再搅拌5-6分钟，再预养2小时，切割，再进蒸压釜蒸养9小时，得到煤矸石砖。
抗拉强度为210kg/cm2，抗冷合格，煤矸石砖发热量为1300-1700kj/kg的范围内，莫氏硬度为3-8，合格率达到95%以上，而且使用寿命明显增长，保温效果明显。
Claims (1)
1.一种煤矸石砖，其特征在于其组成原料的重量份为：煤矸石粉20-30、水泥5-10、铝粉3-8、石膏3-5、刚玉莫来石2-5、皂角粉3-5、细沙20-25、石灰8-12和膨胀珍珠岩8-12；
所述的煤矸石砖的生产方法包括以下步骤：按组成原料的重量份称取各原料，然后将煤矸石粉兑水和石膏一起制浆，再打到存浆罐，加热到38-42℃，再将石灰，水泥，铝粉，皂角粉，细沙，刚玉莫来石和膨胀珍珠岩浇铸进去再搅拌5-6分钟，再预养2小时，切割，再进蒸压釜蒸养8-10小时，得到煤矸石砖。