CN1040045A - 中空玻璃用聚硫环氧密封胶 - Google Patents

中空玻璃用聚硫环氧密封胶 Download PDF

Info

Publication number
CN1040045A
CN1040045A CN 87101255 CN87101255A CN1040045A CN 1040045 A CN1040045 A CN 1040045A CN 87101255 CN87101255 CN 87101255 CN 87101255 A CN87101255 A CN 87101255A CN 1040045 A CN1040045 A CN 1040045A
Authority
CN
China
Prior art keywords
component
components
sealing
double glazing
type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 87101255
Other languages
English (en)
Inventor
乔守莲
陈兴远
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINHUANGDAO GLASS ACADEMY STATE BUILDING MATERIALS INDUSTRY BUREAU
Original Assignee
QINHUANGDAO GLASS ACADEMY STATE BUILDING MATERIALS INDUSTRY BUREAU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINHUANGDAO GLASS ACADEMY STATE BUILDING MATERIALS INDUSTRY BUREAU filed Critical QINHUANGDAO GLASS ACADEMY STATE BUILDING MATERIALS INDUSTRY BUREAU
Priority to CN 87101255 priority Critical patent/CN1040045A/zh
Publication of CN1040045A publication Critical patent/CN1040045A/zh
Pending legal-status Critical Current

Abstract

本发明是用环氧树脂改性聚硫橡胶的双组份密封胶，主要用于中空玻璃周边的粘结与密封。两组份都不含增塑剂和其他溶剂。一组份是以液体聚硫橡胶为主，另一组份以环氧树脂为主，使用时，两组份按一定比例混合，固化后可产生良好的弹性和密封性，对玻璃及金属框架具有很高的粘结力，和优异的耐水性及耐紫外线性能。

Description

本发明的密封胶是用环氧树脂改性聚硫橡胶的双组份密封胶，主要用于中空玻璃周边的粘结与密封。
目前，无论是进口的或国产的中空玻璃聚硫密封剂都是两组份的，一是以液体聚硫橡胶为主，加入填充剂CaCO3，和增塑剂邻苯二甲酸脂类;另一组份则为固化剂，是由金属氧化物、活性炭和增塑剂配制而成。
由于两组份中均含有大量增塑剂，在贮存过程中。增塑剂游离在表面而产生分层现象，而且耐紫外线性能和粘结强度以及耐水性都受到影响，这种基本配方的密封剂贮存安全期一般为4～6个月。
本发明的目的是提供一种不含增塑剂及其他溶剂的聚硫密封胶，使其既保留了聚硫橡胶的良好弹性和密封性，又大幅度提高对玻璃和金属的粘结强度，并可获得优异的耐紫外线性能和耐水性能。
本发明的密封胶是由两组份组成，A组份是以聚硫橡胶为主，加触变剂二氧化硅，填充剂二氧化钛，炭黑（或碳酸钙），和催化剂2.4.6-三（二甲氨基甲基）苯酚，以及硫磺和硬脂酸组成。B组份（即固化剂）是以环氧树脂与活性氧化锰为主要成分。
A组份中的液体聚硫橡胶是保证良好弹性和气密性的物质，其分子量控制在2000～3500范围内较适宜;二氧化硅选用36～5型，它有促进密封胶具有触变性的作用;二氧化钛是提高密封胶的延展性，改善粘附作用，并能吸收紫外线，选用金红石型;炭黑一方面可大量吸收紫外线，提高密封胶的耐紫外线性能和户外大气老化性能，另一方面可增加聚硫橡胶的补强效果，选用半补强炭黑，这种炭黑可赋予固化后的密封胶以耐曲挠性和优良的回弹性，对吸收紫外线的能力较强;2.4.6-三（二甲氨基甲基）苯酚是作为聚硫橡胶与环氧树脂反应的催化剂，它与液体聚硫橡胶的相溶性很好，当A、B两组份混合后，机械强度在室温下能较快达到最高值;少量硫磺可提高密封胶的弹性;而硬脂酸则可减少粘包辊现象。
这样配制成的A组份为黑色膏状物，由于炭黑是一种很好的表面活性剂，对胶料分散体系的稳定性起很大作用。贮存期可长达2～3年或更长。
B组份（即固化剂），是由环氧树脂与活性氧化锰为主要成份，加上促进剂D、二氧化钛、二氧化硅和硬脂酸组成。
B组份中的环氧树脂选用双酚A型，根据软化点的不同而选用常温为液体状态的610，616和618三种型号，当选用616和618型时，在室温下即可操作，而选用610型时，则需加热到30～35℃。环氧值（即当量/100克树脂）在0.48～0.56之间为宜，其用量为聚硫橡胶的14～40（重量份数）;若低于14重量份数，则粘结强度提高不大，若高于40重量份数，则固化后的弹性差，且硬度大。活性氧化锰是聚硫橡胶的固化剂，其用量取决于环氧树脂的用量，一般为4～12（重量份数）;促进剂D-二苯胍，起促进硫化速度的作用，达到室温固化的目的，其他组份的作用与A组份中的相同。
A·B两组份各种物质的用量范围如下：
A组份为：（黑色膏状物）        用量（重量份数）
液体聚硫橡胶（分子量2000～3500）        200～220
二氧化钛（金红石型）        5～15
二氧化硅（36～5型）        10～30
半补强炭黑        40～70
2.4.6-三（二甲氨基甲基）苯酚        3～10
硫磺        0～0.6
硬脂酸        0～0.5
B组份为：（棕褐色膏状物）        用量（重量份数）
环氧树脂（环氧值0.48～0.56）        28～80
二氧化钛（金红石型）        0～1
二氧化硅（36～5型）        0.6～1.1
活性二氧化锰        4～12
硬脂酸        0.1～0.2
促进剂D        0.6～1.4
欲使本发明的密封胶达到最佳性能，必需严格控制A·B两组份的配制工艺。
生产密封胶主要使用混胶设备-三辊研磨机，A·B两组份必需分别按一次投料的配比重量份数准确称量各种物料，经初混后再放入混炼机，控制混炼温度在40～55℃，第一次混炼后的粒度要求在20μ以下，第二、三次混炼后的粒度要求在5μ以下，最好为0，第四次则使物料快速通过，A·B两组份需分别贮存备用。
使用时A·B两组份的配比如下：
按重量份数        A∶B＝8.3～9.5∶1
按体积份数        A∶B＝8～9∶1
两组份混合后，表面不粘手的时间为1～2小时，硫化时间4～8小时，室温固化24小时后的硬度（邵A）为40～55。
若将A组份中填充剂炭黑改用碳酸钙，即可配制成白色膏状物，用炭黑配制成的A组份与用碳酸钙配制成的A组份，它们分别与B组份配成的密封胶比较。用炭黑配制的密封胶其优点是比重小（1.25g/cm3），硬度低、弹性、韧性好，贮存稳定期长。而用碳酸钙配制的密封胶比重大（1.70g/cm3），这样生产同样规格的中空玻璃，用炭黑配制的密封胶比用碳酸钙配制的密封胶可节省胶量的1/3。
本发明的密封胶不仅可用于制造中空玻璃，而且还可用于汽车风挡玻璃的粘结与密封，又可根据使用的要求，改变A·B两组份的使用配比，可作为金属、玻璃、陶瓷、水泥的防水、防震粘结剂和密封材料，用溶剂稀释后，还可作防水涂料。
本发明与目前进口的或国产的中空玻璃聚硫密封剂相比，具有以下优点：
1、对金属和玻璃的粘结强度提高一倍或更多。
2、耐水性能明显提高，经30±2℃海水、自来水浸泡31天后剥离强度没有下降趋势。
3、耐紫外线性能优异，由于配方中没有任何溶剂和增塑剂，聚硫橡胶与环氧树脂反应没有付产物产生，经紫外线长期照射不会产生化学雾状物或油状物。
4、以聚硫橡胶为主的A组份贮存期可长达2～3年或更长。以环氧树脂为主的B组份贮存期可达8个月或更
长，而不产生分层现象。
实施例：
组份A（黑色膏状物）        重量份数
液体聚硫橡胶        220
二氧化钛（金红石型）        7
二氧化硅（沉淀法36～5型）        14
炭黑（半补强）        68
2.4.6-三（二甲氨基甲基）苯酚        5
硫磺        0～0.3
硬脂酸        0.2
组份B（棕褐色膏状物）
环氧树脂        33
二氧化钛（金红石型）        0.4
二氧化硅（沉淀法36～5型）        0.8
二氧化锰（活性）        10
硬脂酸        0.1
促进剂D        1.2
将A·B两组份按A∶B＝9∶1的重量份数配合，按上述 工艺混炼后，即可用于中空玻璃周边的粘结与密封，室温固化后，剥离强度可达到7.6kg/cm2，扯断伸长率466%，扯断强度23kg/cm2，经海水、自来水浸泡31天后，剥离强度未见下降趋势。

Claims (4)

1、本发明是用环氧树脂改性聚硫橡胶的双组份密封胶，主要用于中空玻璃周边的粘结与密封，本发明的特点是：两组份中均不含增塑剂和其他溶剂，两组份的组成为：
A组份：                                                                                                                    重量份数
①液体聚硫橡胶(分子量为2000～3500)        200～220
②二氧化钛(金红石型)                                                                5～15
③二氧化硅(36～5型)                                                                    10～30
④半补强炭黑                                                                                                40～70
⑤2.4.6-三(二甲氨基甲基)苯酚                                3～10
⑥硫磺                                                                                                                        0～0.6
⑦硬脂酸                                                                                                                0～0.5
B组份：
①液体环氧树脂(环氧值0.48～0.56)                28～80
②二氧化钛(金红石型)                                                                0～1
③二氧化硅(36～5型)                                                                    0.6～1
④活性氧化锰                                                                                                5～12
⑤硬脂酸                                                                                                                0.1～0.2
⑥促进剂D                                                                                                            0.6～1.4
2、如权利要求1的密封胶，其特点是：混炼温度为40～55℃，胶料粒度为5μ以下。
3、如权利要求1的密封胶，其特点是：不仅可用于中空玻璃;还可用于汽车风挡玻璃的粘结与密封;并可改变A.B两组份的配比，作为金属、玻璃、陶瓷、水泥的防水、防震粘结剂和密封材料;用溶剂稀释后还可作防水涂料。
CN 87101255 1987-12-28 1987-12-28 中空玻璃用聚硫环氧密封胶 Pending CN1040045A (zh)