CN103992868A - High temperature resistant high speed wire drawing oil - Google Patents
High temperature resistant high speed wire drawing oil Download PDFInfo
- Publication number
- CN103992868A CN103992868A CN201410174126.0A CN201410174126A CN103992868A CN 103992868 A CN103992868 A CN 103992868A CN 201410174126 A CN201410174126 A CN 201410174126A CN 103992868 A CN103992868 A CN 103992868A
- Authority
- CN
- China
- Prior art keywords
- wire drawing
- oil
- parts
- drawing oil
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a wire drawing oil, and in particular relates to a high temperature resistant high speed wire drawing oil; the high temperature resistant high speed wire drawing oil comprises the following raw materials by weight: 2-3 parts of stearic acid, 10-12 parts of 2-octyldodecanol, 2-4 parts of trimethylolpropane, 60-80 parts of di-iso-octyl sebacate, 65-70 parts of hydrogenated polydecylene, 5-6 parts of hydrogenated castor oil, 5-8 parts of sulfurized cottonseed oil, 1-2 parts of fatty acid methyl ester, 0.2-0.5 part of octyl isothiazolinone, 1-2 parts of butyl hydroxy anisd and 2-3 parts of an assistant; the high temperature resistant high speed wire drawing oil uses the di-iso-octyl sebacate and the hydrogenated polydecylene as base oil, by combination with the hydrogenated castor oil, sulfurized cottonseed oil, the trimethylolpropane and other additives, extreme pressure antiwear performance of the wire drawing oil can be greatly improved, the octyl isothiazolinone is a green bactericidal anti-corrosion compound, and makes the wire drawing oil more resistant to storage, the prepared wire drawing oil is particularly prominent in thermal stability, and is especially suitable for high speed wire drawing and drawing process needs.
Description
Technical field
The present invention relates to a kind of wire drawing oil, be specifically related to a kind of high temperature-resistant high-speed wire drawing oil and preparation technology thereof.
Background technology
Wire drawing oil is the important industrial auxiliary agent of a class, in wire drawing, drawing process process, does efficient lubricant oil use, has lubricated, cleaning, the effect such as cooling, antirust, assists metal flow, avoids mould to drag colored bracing wire, improves yield rate, reduces production loss.Existing wire drawing oil is mainly divided into oiliness wire drawing oil and water-based wire drawing oil, this two classes wire drawing oil cuts both ways in the time that reality is used, as oiliness wire drawing oil exists heat dispersion poor, cleaning chip removal difficulty, the problems such as waste liquid difficult degradation, and although the wire drawing oil heat dispersion of water-based is good compared with oiliness wire drawing oil, but lubricant effect is not fully up to expectations, the wire drawing that is difficult to meet various metals line is drawn and is dialled processing requirement, therefore for improve enterprise machining level, reduce production costs, need to improve wire drawing oil formula and technique, make it reach good use properties.
Summary of the invention
The object of the invention is to, a kind of high temperature-resistant high-speed wire drawing oil is provided, to improve the resistance toheat of wire drawing oil, improve drawing speed, to achieve these goals, the technical solution used in the present invention is as follows:
A kind of high temperature-resistant high-speed wire drawing oil, it is characterized in that, material of the present invention is made up of the raw material of following weight part: stearic acid 2-3,2-Standamul G 10-12, TriMethylolPropane(TMP) 2-4, diisooctyl sebacate 60-80, hydrogenation poly-certain herbaceous plants with big flowers alkene 65-70, hydrogenated castor oil 5-6, sulfuration Oleum Gossypii semen 5-8, fatty acid methyl ester 1-2, octyl group isothiazolinone 0.2-0.5, butylated hydroxy anisole 1-2, auxiliary agent 2-3; Described auxiliary agent is made up of the raw material of following weight part: butyl stearate 12-15, Graphene 1-2, Starso 1-2, xanthan gum 10-12, ethoxylated dodecyl alcohol 4-5, deionized water are appropriate; Preparation method is: first will in butyl stearate, add ethoxylated dodecyl alcohol, Graphene, under 1000-1500 rev/min, stir 20-30min, make emulsion for subsequent use, again xanthan gum is mixed with appropriate deionized water, be mixed with the xanthan gum solution that mass concentration is 60-70%, finally the aqueous solution, emulsion and other remaining component mixed, continue to stir 15-20min with 1000-1500 rev/min of rotating speed, stirring finishes rear standing 2-4h, to obtain final product.
Described a kind of high temperature-resistant high-speed wire drawing oil, its preparation technology is:
(1) first stearic acid, 2-Standamul G, TriMethylolPropane(TMP) are mixed, fully stir 20-30min, mixture is for subsequent use;
(2) hydrogenated castor oil is heated to 75-85 DEG C, add the mixture of diisooctyl sebacate, the poly-certain herbaceous plants with big flowers alkene of hydrogenation, sulfuration Oleum Gossypii semen and step (1) gained, stir 20-30min, leave standstill after 10-15min, add again other remaining component, continue to stir 50-60min, after stirring finishes, naturally cool to room temperature, get product.
Wire drawing oil advantage prepared by the present invention is: use the poly-certain herbaceous plants with big flowers alkene of resistant to elevated temperatures diisooctyl sebacate and hydrogenation as base oil, give wire drawing oil good resistance to elevated temperatures, go back cost economical rationality simultaneously, lubricant effect is good, coordinate again hydrogenated castor oil, sulfuration Oleum Gossypii semen and stearic acid, the additives such as TriMethylolPropane(TMP), improve greatly the extreme pressure and antiwear behavior of wire drawing oil, not oxidizable, good heat stability, octyl group isothiazolinone is a kind of sterilization and anticorrosion compound of green, make the more resistance to storage of wire drawing oil of preparation, in sum, wire drawing oil of the present invention shows particularly outstanding on thermal stability, can be applicable to the wire drawing of various metals wire rod, drawing process is used, especially can meet high-speed wire-drawing, the demand of drawing process.
Embodiment
Embodiment
The present embodiment wire drawing oil by following weight part (kilogram) raw material make: the poly-certain herbaceous plants with big flowers alkene 70 of stearic acid 2,2-Standamul G 12, TriMethylolPropane(TMP) 4, diisooctyl sebacate 80, hydrogenation, hydrogenated castor oil 5, sulfuration Oleum Gossypii semen 8, fatty acid methyl ester 1, octyl group isothiazolinone 0.5, butylated hydroxy anisole 1, auxiliary agent 3; Described auxiliary agent is made up of the raw material of following weight part: butyl stearate 15, Graphene 1, Starso 2, xanthan gum 10, ethoxylated dodecyl alcohol 4, deionized water are appropriate; Preparation method is: first will in butyl stearate, add ethoxylated dodecyl alcohol, Graphene, under 1500 revs/min, stir 20min, make emulsion for subsequent use, again xanthan gum is mixed with appropriate deionized water, be mixed with mass concentration and be 70% xanthan gum solution, finally the aqueous solution, emulsion and other remaining component are mixed, continue to stir 15min with 1500 revs/min of rotating speeds, stirring finishes rear standing 3h, to obtain final product.
Described a kind of high temperature-resistant high-speed wire drawing oil, its preparation technology is:
(1) first stearic acid, 2-Standamul G, TriMethylolPropane(TMP) are mixed, fully stir 30min, mixture is for subsequent use;
(2) hydrogenated castor oil is heated to 75-85 DEG C, add the mixture of diisooctyl sebacate, the poly-certain herbaceous plants with big flowers alkene of hydrogenation, sulfuration Oleum Gossypii semen and step (1) gained, stir 30min, leave standstill after 10min, add again other remaining component, continue to stir 60min, after stirring finishes, naturally cool to room temperature, get product.
Wire drawing oil of the present invention can stablize at ambient temperature deposit at least one year, during this time without precipitating, demixing phenomenon; Concrete each performance index are as follows:
Claims (2)
1. a high temperature-resistant high-speed wire drawing oil, it is characterized in that, this wire drawing oil is made up of the raw material of following weight part: stearic acid 2-3,2-Standamul G 10-12, TriMethylolPropane(TMP) 2-4, diisooctyl sebacate 60-80, hydrogenation poly-certain herbaceous plants with big flowers alkene 65-70, hydrogenated castor oil 5-6, sulfuration Oleum Gossypii semen 5-8, fatty acid methyl ester 1-2, octyl group isothiazolinone 0.2-0.5, butylated hydroxy anisole 1-2, auxiliary agent 2-3; Described auxiliary agent is made up of the raw material of following weight part: butyl stearate 12-15, Graphene 1-2, Starso 1-2, xanthan gum 10-12, ethoxylated dodecyl alcohol 4-5, deionized water are appropriate; Preparation method is: first will in butyl stearate, add ethoxylated dodecyl alcohol, Graphene, under 1000-1500 rev/min, stir 20-30min, make emulsion for subsequent use, again xanthan gum is mixed with appropriate deionized water, be mixed with the xanthan gum solution that mass concentration is 60-70%, finally the aqueous solution, emulsion and other remaining component mixed, continue to stir 15-20min with 1000-1500 rev/min of rotating speed, stirring finishes rear standing 2-4h, to obtain final product.
2. a kind of high temperature-resistant high-speed wire drawing oil as claimed in claim 1, its preparation technology is as follows:
(1) first stearic acid, 2-Standamul G, TriMethylolPropane(TMP) are mixed, fully stir 20-30min, mixture is for subsequent use;
(2) hydrogenated castor oil is heated to 75-85 DEG C, add the mixture of diisooctyl sebacate, the poly-certain herbaceous plants with big flowers alkene of hydrogenation, sulfuration Oleum Gossypii semen and step (1) gained, stir 20-30min, leave standstill after 10-15min, add again other remaining component, continue to stir 50-60min, after stirring finishes, naturally cool to room temperature, get product.