CN103981348A - 一种16Co14Ni10Cr2Mo钢大型零件热处理变形控制方法 - Google Patents

一种16Co14Ni10Cr2Mo钢大型零件热处理变形控制方法 Download PDF

Info

Publication number
CN103981348A
CN103981348A CN201410156364.9A CN201410156364A CN103981348A CN 103981348 A CN103981348 A CN 103981348A CN 201410156364 A CN201410156364 A CN 201410156364A CN 103981348 A CN103981348 A CN 103981348A
Authority
CN
China
Prior art keywords
temperature
carrying
tempering
treatment
air
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410156364.9A
Other languages
English (en)
Other versions
CN103981348B (zh
Inventor
杨旭
金建军
焦清洋
崔灿
景绿路
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenyang Aircraft Design and Research Institute Aviation Industry of China AVIC
Original Assignee
Shenyang Aircraft Design and Research Institute Aviation Industry of China AVIC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Aircraft Design and Research Institute Aviation Industry of China AVIC filed Critical Shenyang Aircraft Design and Research Institute Aviation Industry of China AVIC
Priority to CN201410156364.9A priority Critical patent/CN103981348B/zh
Publication of CN103981348A publication Critical patent/CN103981348A/zh
Application granted granted Critical
Publication of CN103981348B publication Critical patent/CN103981348B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于超高强度钢的热处理领域，涉及一种16Co14Ni10Cr2Mo钢大型零件的热处理变形控制方法。其特征在于，第一，气冷淬火：零件在真空热处理炉中加热至820-840℃，保温55-65分钟后，在压强不小于4×104Pa高纯氩气中进行淬火；第二，冷处理：在零件淬火后3小时内进行冷处理，冷处理温度为零下（65-81）℃，保温55-65分钟后，在空气中回温；第三，低温回火：冷处理后进行低温回火，回火加热温度为140-160℃，保温3-5小时后在空气中冷却；低温回火后对零件进行校形；第四，最终回火：零件校形后，进行最终的回火处理，回火加热温度为505-515℃，保温4-6小时后在空气中冷却。本发明优点：零件淬火后变形量小，且易于进行校形，有效的控制了零件的热处理变形程度。

Description

一种16Co14Ni10Cr2Mo钢大型零件热处理变形控制方法
技术领域
本发明属于超高强度钢的热处理领域，涉及一种16Co14Ni10Cr2Mo钢大型零件的热处理变形控制方法。
背景技术
16Co14Ni10Cr2Mo是一种具有高强高韧的可焊性结构钢，适合用于制造大型的长寿命结构零件。结构钢零件在热处理后由于组织转变会产生变形，特别是对于大型的复杂零件，变形不可避免。
由于16Co14Ni10Cr2Mo钢在热处理后的抗拉强度与屈服强度较为接近，抗拉强度约为1700MPa左右，屈服强度可达1620MPa以上。热处理后若对零件进行校形时，加载力不易控制，特别是对于形状较为复杂的零件，控制不好容易使零件出现过载（超过抗拉强度）而开裂报废。同时材料在热处理后的硬度较高（HRC≥48），机械加工困难，若零件预留加工余量，后续精加工的难度将大幅度增加。
目前，国内外尚没有对16Co14Ni10Cr2Mo高韧性超高强度钢大型零件有效的热处理变形控制方法。
发明内容
本发明的目的是：针对上述背景技术中存在的问题，提出一种16Co14Ni10Cr2Mo钢零件的热处理变形控制方法。
本发明的技术方案是：一种16Co14Ni10Cr2Mo钢零件的热处理变形控制方法，其特征在于步骤如下：
第一，气冷淬火：零件在真空热处理炉中加热至820-840℃，保温55-65分钟后，在压强不小于4×104Pa高纯氩气中进行淬火；
第二，冷处理：在零件淬火后3小时内进行冷处理，冷处理温度为零下（65-81）℃，保温55-65分钟后，在空气中回温；
第三，低温回火：冷处理后进行低温回火，回火加热温度为140-160℃，保温3-5小时后在空气中冷却；低温回火后对零件进行校形；
第四，最终回火：零件校形后，进行最终的回火处理，回火加热温度为505-515℃，保温4-6小时后在空气中冷却。
本发明的优点是：零件淬火后变形量小，且易于进行校形，有效的控制了零件的热处理变形程度。
具体实施方式
下面通过具体的实施例对本发明作进一步详细的描述。
一种16Co14Ni10Cr2Mo钢零件的热处理变形控制方法，其特征在于步骤如下：
第一，气冷淬火：零件在真空热处理炉中加热至820-840℃，保温55-65分钟后，在压强不小于4×104Pa高纯氩气中进行淬火；
第二，冷处理：在零件淬火后3小时内进行冷处理，冷处理温度为零下（65-81）℃，保温55-65分钟后，在空气中回温；
第三，低温回火：冷处理后进行低温回火，回火加热温度为140-160℃，保温3-5小时后在空气中冷却；低温回火后对零件进行校形；
第四，最终回火：零件校形后，进行最终的回火处理，回火加热温度为505-515℃，保温4-6小时后在空气中冷却。

Claims (1)

1.一种16Co14Ni10Cr2Mo钢大型零件热处理变形控制方法，其特征在于，包括如下步骤：
第一，气冷淬火：零件在真空热处理炉中加热至820-840℃，保温55-65分钟后，在压强不小于4×104Pa高纯氩气中进行淬火；
第二，冷处理：在零件淬火后3小时内进行冷处理，冷处理温度为零下（65-81）℃，保温55-65分钟后，在空气中回温；
第三，低温回火：冷处理后进行低温回火，回火加热温度为140-160℃，保温3-5小时后在空气中冷却；低温回火后对零件进行校形；
第四，最终回火：零件校形后，进行最终的回火处理，回火加热温度为505-515℃，保温4-6小时后在空气中冷却。
CN201410156364.9A 2014-04-17 2014-04-17 一种16Co14Ni10Cr2Mo钢大型零件热处理变形控制方法 Active CN103981348B (zh)