CN103979863A - 一种耐腐蚀加气砖及其制备方法 - Google Patents

一种耐腐蚀加气砖及其制备方法 Download PDF

Info

Publication number
CN103979863A
CN103979863A CN201410149700.7A CN201410149700A CN103979863A CN 103979863 A CN103979863 A CN 103979863A CN 201410149700 A CN201410149700 A CN 201410149700A CN 103979863 A CN103979863 A CN 103979863A
Authority
CN
China
Prior art keywords
parts
corrosion
sawdust
steam
hour
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410149700.7A
Other languages
English (en)
Other versions
CN103979863B (zh
Inventor
晋元龙
陈德全
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Dongling New Building Materials Co., Ltd.
Original Assignee
Ma'an Mountain Bao Long Building Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ma'an Mountain Bao Long Building Material Co Ltd filed Critical Ma'an Mountain Bao Long Building Material Co Ltd
Priority to CN201410149700.7A priority Critical patent/CN103979863B/zh
Publication of CN103979863A publication Critical patent/CN103979863A/zh
Application granted granted Critical
Publication of CN103979863B publication Critical patent/CN103979863B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种耐腐蚀加气砖，由下列重量份的原料制成：水泥8-10、生石灰12-15、苯甲酸单乙醇胺0.4-0.7、改性锯末8-11、石膏4-6、粉煤灰55-60、聚苯乙烯泡沫颗粒1-2、甘油单酯3-4、聚氨酯树脂乳液2-4、铝粉膏0.09-0.13、松香1-2、贝壳粉2-3、磷酸二氢铝1-2、超细硫酸钡0.5-1、无水铝酸钙1-2、琼脂1-2、水适量；本发明加气砖通过使用苯甲酸单乙醇胺，增强了加气砖的耐腐蚀性能，防止腐蚀钢筋；通过使用超细硫酸钡、聚氨酯树脂乳液、磷酸二氢铝，增加了强度、防止开裂；通过使用改性锯末，减小干密度和干燥收缩值，而且通过废机油处理的锯末，提高了加气砖的耐水性。

Description

一种耐腐蚀加气砖及其制备方法
技术领域
本发明属于砖领域，尤其涉及一种耐腐蚀加气砖及其制备方法。
背景技术
加气砖也叫做加气混凝土砌块，应用非常的广泛，主要用在机械厂房和民用建筑中的墙体材料、填充墙、楼板和屋面板等承重墙材以及非承重材料和周围的填充围墙。
目前加气砖已成为建筑材料行业的主导产品，国家已经逐步禁止使用粘土实心砖，逐渐取而代之的就是加气混凝土砌块，蒸压砖。
加气砖具有重量轻、保温隔热性能好、抗震能力强、加工性能好、具有一定的耐高温性、隔音性能好、适应性强的特点，可根据当地不同原材料，不同条件来量身定造，原材料来源广泛，可选择河沙、粉煤灰、矿砂等，因地制宜，可以废物利用，有利环保，真正变废为宝。
但是随着建筑行业的发展，建筑物越来越高、造型越来越奇特，对加气砖的强度、密度、收缩值、抗冻性等要求都有所提高，另外随着人们生活水平的不断提高，对环境的要求也越来越高，对建筑物的保温性能、吸音性能、放射性都有更高的要求，甚至要求建筑物具有有益身体健康的性能，因此根据需要，研制更加性能优异的加气砖势在必行。
发明内容
本发明的目的在于提供一种耐腐蚀加气砖及其制备方法，该加气砖耐腐蚀性好，防止腐蚀钢筋，强度高，不易开裂。
本发明的技术方案如下：
一种耐腐蚀加气砖,其特征在于由下列重量份的原料制成：水泥8-10、生石灰12-15、苯甲酸单乙醇胺0.4-0.7、改性锯末8-11、石膏4-6、粉煤灰55-60、聚苯乙烯泡沫颗粒1-2、甘油单酯3-4、聚氨酯树脂乳液2-4、铝粉膏0.09-0.13、松香1-2、贝壳粉2-3、磷酸二氢铝1-2、超细硫酸钡0.5-1、无水铝酸钙1-2、琼脂1-2、水适量；
    所述改性锯末由下列重量份的原料制成：海泡石绒2-3、锯末10-13、二氧化硅气凝胶1-2、木胶粉0.4-0.7、异佛尔酮二异氰酸酯0.8-1.2、三乙胺0.06-0.09、含氢硅油乳液0.5-0.8、羟基硅油乳液0.5-0.8、硫酸铜0.01-0.02、聚乙烯醇0.5-1.2、氢氧化钾0.6-0.7、硬脂酸1-2、氯化钙1-2、粉煤灰3-5、氧化聚乙烯蜡0.8-1、废机油1-1.5；制作方法为：将锯末粉碎成50-100目颗粒，边搅拌边喷入氧化聚乙烯蜡、废机油，混合均匀后放置5-7个小时，再与其他剩余成分混合，加热至75-80℃，分散研磨20-30分钟，即得。
所述的耐腐蚀加气砖的制备方法，其特征在于包括以下步骤：
（1）将水泥、生石灰、石膏、粉煤灰混合，送入球磨机中研磨成50-100目颗粒，再与除铝粉膏之外的成分混合，按水料比为0.57-0.58加入水，搅拌均匀，再加入铝粉膏，搅拌均匀得到浆料；
（2）将第（1）步得到的浆料倒入模具中，得到砖胚体；
（3）将砖胚体放入蒸养室进行抽真空，然后在1.7-1.9小时内均匀地通入蒸汽，使蒸养室内的温度升至170-180℃，压力达到11-13MPa，保持恒定9-12小时；
（4）在1.7-1.9小时内均匀地放出蒸汽，使蒸养室内的温度降至70℃以下，出釜，放置28-30天即得。
本发明的有益效果
本发明加气砖通过使用苯甲酸单乙醇胺，增强了加气砖的耐腐蚀性能，防止腐蚀钢筋；通过使用超细硫酸钡、聚氨酯树脂乳液、磷酸二氢铝，增加了强度、防止开裂；通过使用改性锯末，减小干密度和干燥收缩值，而且通过废机油处理的锯末，提高了加气砖的耐水性。
具体实施方式
一种耐腐蚀加气砖,由下列重量份(公斤)的原料制成：水泥9、生石灰14、苯甲酸单乙醇胺0.5、改性锯末9、石膏5、粉煤灰58、聚苯乙烯泡沫颗粒1.5、甘油单酯3.5、聚氨酯树脂乳液3、铝粉膏0.11、松香1.5、贝壳粉2.5、磷酸二氢铝1.5、超细硫酸钡0.8、无水铝酸钙1.5、琼脂1.5、水适量；
    所述改性锯末由下列重量份（公斤）的原料制成：海泡石绒2.5、锯末12、二氧化硅气凝胶1.5、木胶粉0.5、异佛尔酮二异氰酸酯1、三乙胺0.07、含氢硅油乳液0.7、羟基硅油乳液0.7、硫酸铜0.02、聚乙烯醇0.8、氢氧化钾0.6、硬脂酸1.5、氯化钙1.5、粉煤灰4、氧化聚乙烯蜡0.9、废机油1.3；制作方法为：将锯末粉碎成80目颗粒，边搅拌边喷入氧化聚乙烯蜡、废机油，混合均匀后放置6个小时，再与其他剩余成分混合，加热至78℃，分散研磨25分钟，即得。
所述的耐腐蚀加气砖的制备方法，包括以下步骤：
（1）将水泥、生石灰、石膏、粉煤灰混合，送入球磨机中研磨成80目颗粒，再与除铝粉膏之外的成分混合，按水料比为0.57加入水，搅拌均匀，再加入铝粉膏，搅拌均匀得到浆料；
（2）将第（1）步得到的浆料倒入模具中，得到砖胚体；
（3）将砖胚体放入蒸养室进行抽真空，然后在1.8小时内均匀地通入蒸汽，使蒸养室内的温度升至175℃，压力达到12MPa，保持恒定11小时；
（4）在1.8小时内均匀地放出蒸汽，使蒸养室内的温度降至70℃，出釜，放置28天即得。
实验数据：
该加气砖的密度为600kg/m3，耐火温度为680℃，导热系数为0.13W /(m·℃），采用淋浴喷头分别向240mm厚的粘土砖墙和加气砖墙喷淋，粘土砖墙12小时后全部浸透，加气砖墙喷淋72小时后渗水深度为80mm，抗压强度为 5.9Mpa，吸声系数0.46。

Claims (2)

1.一种耐腐蚀加气砖,其特征在于由下列重量份的原料制成：水泥8-10、生石灰12-15、苯甲酸单乙醇胺0.4-0.7、改性锯末8-11、石膏4-6、粉煤灰55-60、聚苯乙烯泡沫颗粒1-2、甘油单酯3-4、聚氨酯树脂乳液2-4、铝粉膏0.09-0.13、松香1-2、贝壳粉2-3、磷酸二氢铝1-2、超细硫酸钡0.5-1、无水铝酸钙1-2、琼脂1-2、水适量；
    所述改性锯末由下列重量份的原料制成：海泡石绒2-3、锯末10-13、二氧化硅气凝胶1-2、木胶粉0.4-0.7、异佛尔酮二异氰酸酯0.8-1.2、三乙胺0.06-0.09、含氢硅油乳液0.5-0.8、羟基硅油乳液0.5-0.8、硫酸铜0.01-0.02、聚乙烯醇0.5-1.2、氢氧化钾0.6-0.7、硬脂酸1-2、氯化钙1-2、粉煤灰3-5、氧化聚乙烯蜡0.8-1、废机油1-1.5；制作方法为：将锯末粉碎成50-100目颗粒，边搅拌边喷入氧化聚乙烯蜡、废机油，混合均匀后放置5-7个小时，再与其他剩余成分混合，加热至75-80℃，分散研磨20-30分钟，即得。
2.根据权利要求1所述的耐腐蚀加气砖的制备方法，其特征在于包括以下步骤：
（1）将水泥、生石灰、石膏、粉煤灰混合，送入球磨机中研磨成50-100目颗粒，再与除铝粉膏之外的成分混合，按水料比为0.57-0.58加入水，搅拌均匀，再加入铝粉膏，搅拌均匀得到浆料；
（2）将第（1）步得到的浆料倒入模具中，得到砖胚体；
（3）将砖胚体放入蒸养室进行抽真空，然后在1.7-1.9小时内均匀地通入蒸汽，使蒸养室内的温度升至170-180℃，压力达到11-13MPa，保持恒定9-12小时；
（4）在1.7-1.9小时内均匀地放出蒸汽，使蒸养室内的温度降至70℃以下，出釜，放置28-30天即得。
CN201410149700.7A 2014-04-15 2014-04-15 一种耐腐蚀加气砖及其制备方法 Active CN103979863B (zh)