CN104098344B - 一种陶瓷纤维加气砖及其制备方法 - Google Patents

一种陶瓷纤维加气砖及其制备方法 Download PDF

Info

Publication number
CN104098344B
CN104098344B CN201410271954.6A CN201410271954A CN104098344B CN 104098344 B CN104098344 B CN 104098344B CN 201410271954 A CN201410271954 A CN 201410271954A CN 104098344 B CN104098344 B CN 104098344B
Authority
CN
China
Prior art keywords
ceramic fiber
aerated bricks
powder
water
rice husk
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410271954.6A
Other languages
English (en)
Other versions
CN104098344A (zh
Inventor
盛蕾
盛志义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHIZHOU XINLEI GREEN BUILDING MATERIAL Co Ltd
Original Assignee
CHIZHOU XINLEI GREEN BUILDING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHIZHOU XINLEI GREEN BUILDING MATERIAL Co Ltd filed Critical CHIZHOU XINLEI GREEN BUILDING MATERIAL Co Ltd
Priority to CN201410271954.6A priority Critical patent/CN104098344B/zh
Publication of CN104098344A publication Critical patent/CN104098344A/zh
Application granted granted Critical
Publication of CN104098344B publication Critical patent/CN104098344B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种陶瓷纤维加气砖,由下列重量份的原料制成:尿素0.5-0.8、羟基羧酸盐1-2、卡波姆1-1.4、生石灰11-13、改性稻壳9-11、石膏6-8、粉煤灰45-50、加气铝粉7-8、水泥10-12、二氧化锰3-5、陶瓷纤维2-3、松脂岩粉末4-7、铁屑膨胀剂0.4-0.7、水适量;本发明加气砖通过使用陶瓷纤维,增加了加气砖的强度,同时增加了耐磨性、耐火性,由于陶瓷纤维导热率低,所以增加了加气砖的保温性,而且加气砖干燥收缩率低,不易吸湿膨胀,增加了建筑物安全性;通过使用改性稻壳,增强了隔热效果,耐水性好,减轻了重量,增加了抗震性能,同时减水效果好。

Description

一种陶瓷纤维加气砖及其制备方法
技术领域
[0001] 本发明属于砖领域,尤其涉及一种陶瓷纤维加气砖及其制备方法。
背景技术
[0002] 加气砖也叫做加气混凝土砌块,应用非常的广泛,主要用在机械厂房和民用建筑中的墙体材料、填充墙、楼板和屋面板等承重墙材以及非承重材料和周围的填充围墙。
[0003]目前加气砖已成为建筑材料行业的主导产品,国家已经逐步禁止使用粘土实心砖,逐渐取而代之的就是加气混凝土砌块,蒸压砖。
[0004] 加气砖具有重量轻、保温隔热性能好、抗震能力强、加工性能好、具有一定的耐高温性、隔音性能好、适应性强的特点,可根据当地不同原材料,不同条件来量身定造,原材料来源广泛,可选择河沙、粉煤灰、矿砂等,因地制宜,可以废物利用,有利环保,真正变废为宝。
[0005] 但是随着建筑行业的发展,建筑物越来越高、造型越来越奇特,对加气砖的强度、密度、收缩值、抗冻性等要求都有所提高,另外随着人们生活水平的不断提高,对环境的要求也越来越高,对建筑物的保温性能、吸音性能、放射性都有更高的要求,甚至要求建筑物具有有益身体健康的性能,因此根据需要,研制更加性能优异的加气砖势在必行。
发明内容
[0006] 本发明的目的在于提供一种陶瓷纤维加气砖及其制备方法,该加气砖强度高,耐磨性好,耐火性好,保温性个,不易吸湿膨胀。
[0007] 本发明的技术方案如下:
[0008] 一种陶瓷纤维加气砖,其特征在于由下列重量份的原料制成:尿素0.5-0.8、羟基羧酸盐1-2、卡波姆1-1.4、生石灰11-13、改性稻壳9-11、石膏6-8、粉煤灰45-50、加气铝粉7-8、水泥10-12、二氧化锰3-5、陶瓷纤维2-3、松脂岩粉末4_7、铁肩膨胀剂0.4-0.7、水适量;
[0009] 所述改性稻壳由下列重量份的原料制成:稻壳13-15、亚硫酸钠0.5-0.7、远红外陶瓷粉1-2、庚酸烯丙酯0.5-0.7、2_甲基咪唑0.1-0.2、芳香族聚氨酯丙烯酸酯1_2、丙烯酸羟乙酯1-2、聚羧酸高效减水剂1-2、玻璃粉1-2、过硫酸铵0.01-0.02、海藻酸钙0.4-0.7、霞石粉1-2、三丹油0.5-0.7、地沟油2-3 ;制作方法为:将稻壳粉碎成50-100目颗粒,边搅拌边喷入三丹油、地沟油,混合均匀后放置5-7个小时,再与其他剩余成分混合,加热至75-800C,分散研磨30-40分钟,即得。
[0010] 所述的陶瓷纤维加气砖的制备方法,其特征在于包括以下步骤:
[0011] (I)将水泥、生石灰、石膏、松脂岩粉末、粉煤灰混合,送入球磨机中研磨成50-100目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57-0.58加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料;
[0012] (2)将第(I)步得到的浆料倒入模具中,得到砖胚体;
[0013] (3)将砖胚体放入蒸养釜进行抽真空,然后在1.7-1.9小时内均匀地通入蒸汽,使蒸养室内的温度升至170-180°C,压力达到ll_13MPa,保持恒定9_12小时;
[0014] (4)在1.7-1.9小时内均匀地放出蒸汽,使蒸养室内的温度降至70°C以下,出釜,放置28-30天即得。
[0015] 本发明的有益效果
[0016] 本发明加气砖通过使用陶瓷纤维,增加了加气砖的强度,同时增加了耐磨性、耐火性,由于陶瓷纤维导热率低,所以增加了加气砖的保温性,而且加气砖干燥收缩率低,不易吸湿膨胀,增加了建筑物安全性;通过使用改性稻壳,增强了隔热效果,耐水性好,减轻了重量,增加了抗震性能,同时减水效果好。
具体实施方式
[0017] 一种陶瓷纤维加气砖,由下列重量份(公斤)的原料制成:尿素0.7、羟基羧酸盐1.6、卡波姆1.2、生石灰12、改性稻壳10、石膏7、粉煤灰48、加气铝粉7、水泥11、二氧化锰4、陶瓷纤维2.5、松脂岩粉末6、铁肩膨胀剂0.5、水适量;
[0018] 所述改性稻壳由下列重量份(公斤)的原料制成:稻壳14、亚硫酸钠0.6、远红外陶瓷粉1.6、庚酸烯丙酯0.6,2-甲基咪唑0.1、芳香族聚氨酯丙烯酸酯1.5、丙烯酸羟乙酯
1.5、聚羧酸高效减水剂1.5、玻璃粉1.5、过硫酸铵0.01、海藻酸钙0.6、霞石粉1.6、三丹油
0.6、地沟油2.6 ;制作方法为:将稻壳粉碎成80目颗粒,边搅拌边喷入三丹油、地沟油,混合均匀后放置6个小时,再与其他剩余成分混合,加热至77°C,分散研磨35分钟,即得。
[0019] 所述的陶瓷纤维加气砖的制备方法,包括以下步骤:
[0020] (I)将水泥、生石灰、石膏、松脂岩粉末、粉煤灰混合,送入球磨机中研磨成70目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料;
[0021] (2)将第(I)步得到的浆料倒入模具中,得到砖胚体;
[0022] (3)将砖胚体放入蒸养釜进行抽真空,然后在1.8小时内均匀地通入蒸汽,使蒸养室内的温度升至176°C,压力达到12MPa,保持恒定11小时;
[0023] (4)在1.8小时内均匀地放出蒸汽,使蒸养室内的温度降至70°C,出盖,放置30天即得。
[0024] 实验数据:
[0025] 该加气砖的密度为640kg/m3,耐火温度为680°C,导热系数为0.21W / (m.°C ),采用淋浴喷头分别向240mm厚的粘土砖墙和加气砖墙喷淋,粘土砖墙12小时后全部浸透,加气砖墙喷淋72小时后渗水深度为60mm,抗压强度为6.9Mpa,吸声系数0.25。

Claims (1)

1.一种陶瓷纤维加气砖,其特征在于由下列重量份的原料制成:尿素0.5-0.8、羟基羧酸盐1-2、卡波姆1-1.4、生石灰11-13、改性稻壳9-11、石膏6-8、粉煤灰45-50、加气铝粉7-8、水泥10-12、二氧化锰3-5、陶瓷纤维2-3、松脂岩粉末4_7、铁肩膨胀剂0.4-0.7、水适量; 所述改性稻壳由下列重量份的原料制成:稻壳13-15、亚硫酸钠0.5-0.7、远红外陶瓷粉1-2、庚酸烯丙酯0.5-0.7、2_甲基咪唑0.1-0.2、芳香族聚氨酯丙烯酸酯1_2、丙烯酸羟乙酯1-2、聚羧酸高效减水剂1-2、玻璃粉1-2、过硫酸铵0.01-0.02、海藻酸钙0.4-0.7、霞石粉1-2、三丹油0.5-0.7、地沟油2-3 ;该改性稻壳的制作方法为:将稻壳粉碎成50-100目颗粒,边搅拌边喷入三丹油、地沟油,混合均匀后放置5-7个小时,再与其他剩余成分混合,加热至75-80 °C,分散研磨30-40分钟,即得; 所述的陶瓷纤维加气砖的制备方法,包括以下步骤: (1)将水泥、生石灰、石膏、松脂岩粉末、粉煤灰混合,送入球磨机中研磨成50-100目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57-0.58加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料; (2)将第(I)步得到的浆料倒入模具中,得到砖坯体; (3)将砖坯体放入蒸养釜进行抽真空,然后在1.7-1.9小时内均匀地通入蒸汽,使蒸养室内的温度升至170-180°C,压力达到ll_13MPa,保持恒定9_12小时; (4)在1.7-1.9小时内均匀地放出蒸汽,使蒸养室内的温度降至70°C以下,出釜,放置28-30天即得。
CN201410271954.6A 2014-06-18 2014-06-18 一种陶瓷纤维加气砖及其制备方法 Active CN104098344B (zh)