CN103965814B - High-strength toughness reinforcing glue and method for making and A2 level inorganic mineral scutum method for making - Google Patents
High-strength toughness reinforcing glue and method for making and A2 level inorganic mineral scutum method for making Download PDFInfo
- Publication number
- CN103965814B CN103965814B CN201410168914.9A CN201410168914A CN103965814B CN 103965814 B CN103965814 B CN 103965814B CN 201410168914 A CN201410168914 A CN 201410168914A CN 103965814 B CN103965814 B CN 103965814B
- Authority
- CN
- China
- Prior art keywords
- baking
- time
- storing temperature
- weight parts
- toughness reinforcing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of preparation method and high-strength toughness reinforcing glue and preparation method thereof of A2 level inorganic mineral scutum, choose the powder of following parts by weight: aluminium hydroxide: 15 ~ 30 weight parts, magnesium hydroxide: 10 ~ 20 weight parts, silicon powder: 40 ~ 50 weight parts, quartz sand: 60 ~ 70 weight parts, diatomite: 10 ~ 20 weight parts, clay: 10 ~ 20 weight parts, talcum powder: 10 ~ 15 weight parts, glass fibre: 2 ~ 3 weight parts, add high-strength toughness reinforcing glue and water carries out and expects, the rolling carrying out repetition by heating up gradually after stirring and baking can obtain.The present invention, by the high-strength toughness reinforcing glue of self-control, makes the stickup of glue good; Adopt inorganic mineral to prepare sheet material, asepsis environment-protecting, improve the security of sheet material, and raw material sources are extensive, reduce production cost, by repeating baking and rolling, make the air in plate be easy to discharge sheet material, rolling is tight, and production technique is simple, is easy to produce.
Description
Technical field
The present invention relates to a kind of building materials and ornaments class, particularly a kind of high-strength toughness reinforcing glue and preparation method thereof and the method adopting high-strength toughness reinforcing glue to prepare A2 level inorganic mineral scutum.
Background technology
The plate used in existing decorative building material is mainly composited aluminum and plastic decking, copper-plastic composite board, stainless steel and composite panel of plastic material; the basic production technique of these plates is as follows: first; to once former grain or recycled plastic granules put into screw extrusion press and extrude; sheet material is formed again by bistrique; thickness of slab is controlled by three epicycles; by adding cooling by water plate temperature in place, normal temperature batches, and makes material.
Existing plastics (PE) core is shaped afterwards and aluminium plate, stainless steel materials, copper coin material carry out compound, finally makes finished product supply market.There is following shortcoming in this sheet material: PE fusing point is low, fire line is poor; The fusing point of PE, at 112 DEG C-140 DEG C, when decomposition combustion easy in temperature is 300 DEG C, produces a large amount of toxic gases, easily jeopardizes the safety of life and property of human consumer during burning.
Summary of the invention
Technical problem to be solved by this invention is for the deficiencies in the prior art, provides a kind of reasonable in design, easy to use, provides the high-strength toughness reinforcing glue of excellent adhering.
Another technical problem to be solved by this invention is for the deficiencies in the prior art, provides a kind of reasonable in design, the preparation method of the simple high-strength toughness reinforcing glue of technique.
A technical problem more to be solved by this invention is for the deficiencies in the prior art, and provide a kind of reasonable in design, raw material sources are wide, improve the preparation method of the A2 level inorganic mineral scutum of security.
Technical problem to be solved by this invention is realized by following technical scheme, the present invention is a kind of high-strength toughness reinforcing glue, be characterized in, the weight percent of this glue consists of: ACRYLIC EMULSION: 60% ~ 80%, Vltra tears or Xylo-Mucine: 4% ~ 12%, simethicone emulsion: 0.1% ~ 0.7%, surplus is water.
Technical problem to be solved by this invention can also be realized further by following technical scheme, in above-described high-strength toughness reinforcing glue: the weight percent of this glue consists of: ACRYLIC EMULSION: 68% ~ 72%, Vltra tears or Xylo-Mucine: 6% ~ 10%, simethicone emulsion: 0.3% ~ 0.5%, surplus is water.
Technical problem to be solved by this invention can also be realized further by following technical scheme, in above-described high-strength toughness reinforcing glue: the weight percent of this glue consists of: ACRYLIC EMULSION: 70%, Vltra tears or Xylo-Mucine: 8%, simethicone emulsion: 0.4%, surplus is water.
Technical problem to be solved by this invention is realized by following technical scheme, the present invention is a kind of preparation method of high-strength toughness reinforcing glue, be characterized in, its step is as follows: first add water in ACRYLIC EMULSION, stir after reaching 30% ~ 40% to solid content, stopping adds water, heating propylene yogurt liquid, heating is stopped after ACRYLIC EMULSION viscosity to 180 ~ 220cP to be heated, in the ACRYLIC EMULSION after heating, Vltra tears or Xylo-Mucine is added by described weight proportion, abundant stirring, make material even, leave standstill and be cooled to room temperature, add simethicone emulsion wherein again, fully namely stirring obtains high-strength toughness reinforcing glue again.
Technical problem to be solved by this invention can also be realized further by following technical scheme, in the preparation method of above-described high-strength toughness reinforcing glue: described in add water operation time ACRYLIC EMULSION solid content reach after 34% ~ 36% and stop adding water, during heating operation ACRYLIC EMULSION viscosity to 190 ~ 210cP after stop heating.
Technical problem to be solved by this invention can also be realized further by following technical scheme, in the preparation method of above-described high-strength toughness reinforcing glue: described in add water operation time ACRYLIC EMULSION solid content reach after 35% and stop adding water, during heating operation, the viscosity of ACRYLIC EMULSION stops heating to 200cP.
Technical problem to be solved by this invention is realized by following technical scheme, the present invention is a kind of method using high-strength toughness reinforcing glue as above or the high-strength toughness reinforcing glue that adopts method described above to obtain to prepare A2 level inorganic mineral scutum, be characterized in, its step is as follows:
(1) select materials: the powder choosing following parts by weight: aluminium hydroxide: 15 ~ 30 weight parts, magnesium hydroxide: 10 ~ 20 weight parts, silicon powder: 40 ~ 50 weight parts, quartz sand: 60 ~ 70 weight parts, diatomite: 10 ~ 20 weight parts, clay: 10 ~ 20 weight parts, talcum powder: 10 ~ 15 weight parts, glass fibre: 2 ~ 3 weight parts;
(2) and material: the powder of above-mentioned weight part is put into stirrer and stirs, the high-strength toughness reinforcing glue that weight part as above is 45 ~ 55 is added in the powder stirred, progressively add appropriate water again, carry out secondary stirring, good mixture to be mixed is stop after fluid paste adding water;
(3) making sheet: the centre that the mixture in fluid paste puts into some layers of non-woven fabrics through the setting gauge of stirrer is carried out coated, coatedly continues or intermittently to carry out, coated good material is carried out first time rolling through milling train, roll rear feeding roaster and carry out first time baking, storing temperature is 75 DEG C ~ 85 DEG C, baking time is 8 ~ 12min, obtain and once toast slab, once will toast slab feeding milling train and carry out second time rolling, roll rear feeding roaster and carry out second time baking, storing temperature is 85 DEG C ~ 95 DEG C, baking time is 8 ~ 12min, obtain secondary baking slab, secondary baking slab is sent into milling train and carries out third time rolling, roll rear feeding roaster and carry out third time baking, storing temperature is 95 DEG C ~ 105 DEG C, baking time is 4 ~ 6min, obtain three baking slabs, three baking slabs are sent into milling train and carries out the 4th rolling, roll rear feeding roaster and carry out the 4th baking, storing temperature is 105 DEG C ~ 115 DEG C, baking time is 4 ~ 6min, obtain four baking slabs, four baking slabs are sent into milling train and carries out the 5th rolling, roll rear feeding roaster and carry out the 5th baking, storing temperature is 125 DEG C ~ 135 DEG C, baking time is 4 ~ 6min, obtain five baking slabs, five baking slabs are sent into roaster and carries out the 6th baking, storing temperature is 145 DEG C ~ 155 DEG C, baking time is 4 ~ 6min, obtain six baking slabs, six baking slabs are sent into roaster and carries out the 7th baking, storing temperature is 165 DEG C ~ 175 DEG C, baking time is 4 ~ 6min, obtain seven baking slabs, room temperature is cooled to after slab drying, batch to obtain finished product sheet material.
Technical problem to be solved by this invention can also be realized further by following technical scheme, in the method for the above-described A2 of preparation level inorganic mineral scutum: storing temperature is 78 DEG C ~ 82 DEG C for the first time, and baking time is 9 ~ 11min; Second time storing temperature is 88 DEG C ~ 92 DEG C, and baking time is 9 ~ 11min; Third time, storing temperature was 98 DEG C ~ 102 DEG C, and baking time is 9 ~ 11min; 4th time storing temperature is 108 DEG C ~ 112 DEG C, and baking time is 5min; 5th time storing temperature is 128 DEG C ~ 132 DEG C, and baking time is 5min; 6th time storing temperature is 148 DEG C ~ 152 DEG C, and baking time is 5min; 7th time storing temperature is 168 DEG C ~ 172 DEG C, and baking time is 5min.
Technical problem to be solved by this invention can also be realized further by following technical scheme, in the method for the above-described A2 of preparation level inorganic mineral scutum: storing temperature is 80 DEG C for the first time, and baking time is 10min; Second time storing temperature is 90 DEG C, and baking time is 10min; Third time, storing temperature was 100 DEG C, and baking time is 5min; 4th time storing temperature is 110 DEG C, and baking time is 5min; 5th time storing temperature is 130 DEG C, and baking time is 5min; 6th time storing temperature is 150 DEG C, and baking time is 5min; 7th time storing temperature is 170 DEG C, and baking time is 5min.
Technical problem to be solved by this invention can also be realized further by following technical scheme, in the method for the above-described A2 of preparation level inorganic mineral scutum: described non-woven fabrics is set to 2 ~ 4 layers.
The present invention, by the high-strength toughness reinforcing glue of self-control, makes the stickup of glue good; Adopt inorganic mineral to prepare sheet material, reach good fire protection requirement, also without the release of toxic gas, environmental protection, avoid the safety of life and property jeopardizing human consumer, improve the security of sheet material, and inorganic mineral is at China's rich reserves, raw material sources are extensive, can reduce production cost, be 2.2MJ/kg through self-inspection combustion heat value, without density flaming droplet/particle in 600S, without flame during product cigarette, and flue gas toxity reaches the A2 grade standard in GB GB8624-2006; When preparing sheet material, repeat baking and rolled plate by heating up gradually, make the air in plate be easy to discharge sheet material, rolling is tight, and production technique is simple, is easy to produce.Compared with prior art, high-strength toughness reinforcing glue has good pastes power, and preparation method is simple; Use above-mentioned high-strength toughness reinforcing glue to prepare sheet material, plate rolling is tight, improves the quality of sheet material, and sheet material raw material sources are wide, and have good fire line, asepsis environment-protecting, ensured good property and personnel safety, mask-making technology is simple.
Embodiment
Further describe concrete technical scheme of the present invention below, so that those skilled in the art understands the present invention further, and do not form the restriction to its right.
Embodiment 1, a kind of high-strength toughness reinforcing glue, the weight percent of this glue consists of: ACRYLIC EMULSION: 60%, Vltra tears or Xylo-Mucine: 4%, simethicone emulsion: 0.1%, and surplus is water.
Embodiment 2, the high-strength toughness reinforcing glue described in embodiment 1, the weight percent of this glue consists of: ACRYLIC EMULSION: 68%, Vltra tears or Xylo-Mucine: 6%, simethicone emulsion: 0.3%, and surplus is water.
Embodiment 3, the high-strength toughness reinforcing glue described in embodiment 1, the weight percent of this glue consists of: ACRYLIC EMULSION: 70%, Vltra tears or Xylo-Mucine: 8%, simethicone emulsion: 0.4%, and surplus is water.
Embodiment 4, the high-strength toughness reinforcing glue described in embodiment 1, the weight percent of this glue consists of: ACRYLIC EMULSION: 72%, Vltra tears or Xylo-Mucine: 10%, simethicone emulsion: 0.5%, and surplus is water.
Embodiment 5, the high-strength toughness reinforcing glue described in embodiment 1, the weight percent of this glue consists of: ACRYLIC EMULSION: 80%, Vltra tears or Xylo-Mucine: 12%, simethicone emulsion: 0.7%, and surplus is water.
Embodiment 6, the preparation method of the high-strength toughness reinforcing glue of embodiment 1-5 described in any one, its step is as follows: first add water in ACRYLIC EMULSION, stir after reaching 30% to solid content, stopping adds water, heating propylene yogurt liquid, ACRYLIC EMULSION viscosity to be heated stops heating to 180cP, in the ACRYLIC EMULSION after heating, Vltra tears or Xylo-Mucine is added by described weight proportion, abundant stirring, make material even, leave standstill and be cooled to room temperature, add simethicone emulsion wherein again, fully namely stirring obtains high-strength toughness reinforcing glue again.
Embodiment 7, in the preparation method of the high-strength toughness reinforcing glue described in embodiment 6: described in add water operation time ACRYLIC EMULSION solid content reach after 34% and stop adding water, during heating operation, the viscosity of ACRYLIC EMULSION stops heating to 190cP.
Embodiment 8, in the preparation method of the high-strength toughness reinforcing glue described in embodiment 6: described in add water operation time ACRYLIC EMULSION solid content reach after 35% and stop adding water, during heating operation, the viscosity of ACRYLIC EMULSION stops heating to 200cP.
Embodiment 9, in the preparation method of the high-strength toughness reinforcing glue described in embodiment 6: described in add water operation time ACRYLIC EMULSION solid content reach after 36% and stop adding water, during heating operation, the viscosity of ACRYLIC EMULSION stops heating to 210cP.
Embodiment 10, the method for A2 level inorganic mineral scutum prepared by a kind of high-strength toughness reinforcing glue using the high-strength toughness reinforcing glue of embodiment 1-5 described in any one or adopt embodiment 6-9 method described in any one to obtain, and be characterized in, its step is as follows:
(1) select materials: the powder choosing following parts by weight: aluminium hydroxide: 15 weight parts, magnesium hydroxide: 10 weight parts, silicon powder: 40 weight parts, quartz sand: 60 weight parts, diatomite: 10 weight parts, clay: 10 weight parts, talcum powder: 10 weight parts, glass fibre: 2 weight parts;
(2) and material: the powder of above-mentioned weight part is put into stirrer and stirs, the high-strength toughness reinforcing glue that the weight part of embodiment 1-9 described in any one is 45 is added in the powder stirred, progressively add appropriate water again, carry out secondary stirring, good mixture to be mixed is stop after fluid paste adding water;
(3) making sheet: the centre that the mixture in fluid paste puts into some layers of non-woven fabrics through the setting gauge of stirrer is carried out coated, coatedly continues or intermittently to carry out, coated good material is carried out first time rolling through milling train, roll the interior baking of roaster that rear feeding storing temperature is 75 DEG C, baking time is 12min, obtain and once toast slab, once will toast slab feeding milling train and carry out second time rolling, roll the interior baking of roaster that rear feeding storing temperature is 85 DEG C, baking time is 12min, obtain secondary baking slab, secondary baking slab is sent into milling train and carries out third time rolling, roll the interior baking of roaster that rear feeding storing temperature is 98 DEG C, baking time is 4min, obtain three baking slabs, three baking slabs are sent into milling train and carries out the 4th rolling, roll the interior baking of roaster that rear feeding storing temperature is 105 DEG C, baking time is 4min, obtain four baking slabs, four baking slabs are sent into milling train and carries out the 5th rolling, roll the interior baking of roaster that rear feeding storing temperature is 125 DEG C, baking time is 4min, obtain five baking slabs, it is toast in the roaster of 145 DEG C that five baking slabs are sent into storing temperature, baking time is 4min, obtain six baking slabs, it is toast in the roaster of 165 DEG C that six baking slabs are sent into storing temperature, baking time is 4min, obtain seven baking slabs, room temperature is cooled to after slab drying, batch to obtain finished product sheet material.
Embodiment 11, preparing in the method for A2 level inorganic mineral scutum described in embodiment 10: its step is as follows:
(1) select materials: the powder choosing following parts by weight: aluminium hydroxide: 30 weight parts, magnesium hydroxide: 20 weight parts, silicon powder: 50 weight parts, quartz sand: 70 weight parts, diatomite: 20 weight parts, clay: 20 weight parts, talcum powder: 15 weight parts, glass fibre: 3 weight parts;
(2) and material: the powder of above-mentioned weight part is put into stirrer and stirs, the high-strength toughness reinforcing glue that the weight part of embodiment 1-9 described in any one is 55 is added in the powder stirred, progressively add appropriate water again, carry out secondary stirring, good mixture to be mixed is stop after fluid paste adding water;
(3) making sheet: the centre that the mixture in fluid paste puts into some layers of non-woven fabrics through the setting gauge of stirrer is carried out coated, coatedly continues or intermittently to carry out, coated good material is carried out first time rolling through milling train, roll the interior baking of roaster that rear feeding storing temperature is 80 DEG C, baking time is 10min, obtain and once toast slab, once will toast slab feeding milling train and carry out second time rolling, roll the interior baking of roaster that rear feeding storing temperature is 90 DEG C, baking time is 10min, obtain secondary baking slab, secondary baking slab is sent into milling train and carries out third time rolling, roll the interior baking of roaster that rear feeding storing temperature is 100 DEG C, baking time is 5min, obtain three baking slabs, three baking slabs are sent into milling train and carries out the 4th rolling, roll the interior baking of roaster that rear feeding storing temperature is 110 DEG C, baking time is 5min, obtain four baking slabs, four baking slabs are sent into milling train and carries out the 5th rolling, roll the interior baking of roaster that rear feeding storing temperature is 130 DEG C, baking time is 5min, obtain five baking slabs, it is toast in the roaster of 150 DEG C that five baking slabs are sent into storing temperature, baking time is 5min, obtain six baking slabs, it is toast in the roaster of 170 DEG C that six baking slabs are sent into storing temperature, baking time is 5min, obtain seven baking slabs, room temperature is cooled to after slab drying, batch to obtain finished product sheet material.
Embodiment 12, prepare in the method for A2 level inorganic mineral scutum described in embodiment 10: first time storing temperature be 78 DEG C, baking time is 11min; Second time storing temperature is 88 DEG C, and baking time is 11min; Third time, storing temperature was 98 DEG C, and baking time is 11min; 4th time storing temperature is 108 DEG C, and baking time is 5min; 5th time storing temperature is 128 DEG C, and baking time is 5min; 6th time storing temperature is 148 DEG C, and baking time is 5min; 7th time storing temperature is 168 DEG C, and baking time is 5min.
Embodiment 13, prepare in the method for A2 level inorganic mineral scutum described in embodiment 10: first time storing temperature be 80 DEG C, baking time is 10min; Second time storing temperature is 90 DEG C, and baking time is 10min; Third time, storing temperature was 100 DEG C, and baking time is 5min; 4th time storing temperature is 110 DEG C, and baking time is 5min; 5th time storing temperature is 130 DEG C, and baking time is 5min; 6th time storing temperature is 150 DEG C, and baking time is 5min; 7th time storing temperature is 170 DEG C, and baking time is 5min.
Embodiment 14, prepare in the method for A2 level inorganic mineral scutum described in embodiment 10: first time storing temperature be 82 DEG C, baking time is 9min; Second time storing temperature is 92 DEG C, and baking time is 9min; Third time, storing temperature was 102 DEG C, and baking time is 9min; 4th time storing temperature is 112 DEG C, and baking time is 5min; 5th time storing temperature is 132 DEG C, and baking time is 5min; 6th time storing temperature is 152 DEG C, and baking time is 5min; 7th time storing temperature is 172 DEG C, and baking time is 5min.
Embodiment 15, preparing in the method for A2 level inorganic mineral scutum described in embodiment 10: described non-woven fabrics is set to 2 layers.
Embodiment 16, preparing in the method for A2 level inorganic mineral scutum described in embodiment 10: described non-woven fabrics is set to 4 layers.
Embodiment 17, to prepare thickness for 3mm inorganic mineral scutum, its step is as follows:
(1) select materials: the powder choosing following parts by weight: aluminium hydroxide: 20 weight parts, magnesium hydroxide: 15 weight parts, silicon powder: 45 weight parts, quartz sand: 65 weight parts, diatomite: 15 weight parts, clay: 15 weight parts, talcum powder: 13 weight parts, glass fibre: 2.5 weight parts;
(2) and material: the powder of above-mentioned weight part is put into stirrer and stirs, the high-strength toughness reinforcing glue of self-control that weight part is 47 is added in the powder stirred, progressively add water again, carry out secondary stirring, good mixture to be mixed is stop after fluid paste adding water;
(3) making sheet: the centre that the mixture in fluid paste puts into four layers of non-woven fabrics through the setting gauge of stirrer is carried out coated, coatedly continues or intermittently to carry out; Be that the milling train of 4.2mm carries out first time rolling through Rolling roller gap by coated good material, roll the 1st, No. 2 roasters bakings of rear feeding, storing temperature is 80 DEG C, and baking time is 10min; The milling train being 3.6mm by the sheet material feeding Rolling roller gap after first time baking carries out second time rolling, and roll the 3rd, No. 4 roasters bakings of rear feeding, storing temperature is 90 DEG C, and baking time is 10min; The milling train being 3.2mm by the sheet material feeding Rolling roller gap after second time baking carries out third time rolling, and roll No. 5 roaster baking of rear feeding, storing temperature is 100 DEG C, and baking time is 5min; The milling train being 3.0mm by the sheet material feeding Rolling roller gap after third time baking carries out the 4th rolling, and roll No. 6 roaster baking of rear feeding, storing temperature is 110 DEG C, and baking time is 5min; Sheet material feeding Rolling roller gap after toasting the 4th time is that the milling train of 2.8mm carries out the 5th rolling, and roll No. 7 roaster baking of rear feeding, storing temperature is 130 DEG C, and baking time is 5min; No. 8 roaster baking sent into by sheet material after toasting the 5th time, and storing temperature is 150 DEG C, and baking time is 5min; No. 9 roaster baking sent into by sheet material after toasting the 6th time, and storing temperature is 170 DEG C, and baking time is 5min; After sheet material drying, be cooled to room temperature, batched to obtain finished product sheet material.
Embodiment 18, to prepare thickness for 5mm inorganic mineral scutum, its step is as follows:
(1) select materials: the powder choosing following parts by weight: aluminium hydroxide: 30 weight parts, magnesium hydroxide: 20 weight parts, silicon powder: 47 weight parts, quartz sand: 60 weight parts, diatomite: 20 weight parts, clay: 20 weight parts, talcum powder: 15 weight parts, glass fibre: 3 weight parts;
(2) and material: the powder of above-mentioned weight part is put into stirrer and stirs, the high-strength toughness reinforcing glue of self-control that weight part is 50 is added in the powder stirred, progressively add water again, carry out secondary stirring, good mixture to be mixed is stop after fluid paste adding water;
(3) making sheet: the centre that the mixture in fluid paste puts into four layers of non-woven fabrics through the setting gauge of stirrer is carried out coated, coatedly continues or intermittently to carry out; Be that the milling train of 6.0mm carries out first time rolling through Rolling roller gap by coated good material, roll the 1st, No. 2 roasters bakings of rear feeding, storing temperature is 80 DEG C, and baking time is 15min; The milling train being 5.8mm by the sheet material feeding Rolling roller gap after first time baking carries out second time rolling, and roll the 3rd, No. 4 roasters bakings of rear feeding, storing temperature is 90 DEG C, and baking time is 15min; The milling train being 5.4mm by the sheet material feeding Rolling roller gap after second time baking carries out third time rolling, and roll No. 5 roaster baking of rear feeding, storing temperature is 100 DEG C, and baking time is 5min; The milling train being 5.2mm by the sheet material feeding Rolling roller gap after third time baking carries out the 4th rolling, and roll No. 6 roaster baking of rear feeding, storing temperature is 110 DEG C, and baking time is 5min; Sheet material feeding Rolling roller gap after toasting the 4th time is that the milling train of 4.8mm carries out the 5th rolling, and roll No. 7 roaster baking of rear feeding, storing temperature is 130 DEG C, and baking time is 5min; No. 8 roaster baking sent into by sheet material after toasting the 5th time, and storing temperature is 150 DEG C, and baking time is 5min; No. 9 roaster baking sent into by sheet material after toasting the 6th time, and storing temperature is 170 DEG C, and baking time is 5min; After sheet material drying, be cooled to room temperature, batched to obtain finished product sheet material.
Above-mentioned Vltra tears or Xylo-Mucine and simethicone emulsion are all product disclosed in prior art.
Claims (10)
1. a high-strength toughness reinforcing glue, is characterized in that: the weight percent of this glue consists of: ACRYLIC EMULSION: 60% ~ 80%, Vltra tears or Xylo-Mucine: 4% ~ 12%, simethicone emulsion: 0.1% ~ 0.7%, surplus is water.
2. high-strength toughness reinforcing glue according to claim 1, it is characterized in that: the weight percent of this glue consists of: ACRYLIC EMULSION: 68% ~ 72%, Vltra tears or Xylo-Mucine: 6% ~ 10%, simethicone emulsion: 0.3% ~ 0.5%, surplus is water.
3. high-strength toughness reinforcing glue according to claim 1, is characterized in that: the weight percent of this glue consists of: ACRYLIC EMULSION: 70%, Vltra tears or Xylo-Mucine: 8%, simethicone emulsion: 0.4%, and surplus is water.
4. the preparation method of the high-strength toughness reinforcing glue as described in claim 1 or 2 or 3, it is characterized in that: its step is as follows: first add water in ACRYLIC EMULSION, stir after reaching 30% ~ 40% to solid content, stopping adds water, heating propylene yogurt liquid, heating is stopped after ACRYLIC EMULSION viscosity to 180 ~ 220cP to be heated, in the ACRYLIC EMULSION after heating, Vltra tears or Xylo-Mucine is added by described weight proportion, abundant stirring, make material even, leave standstill and be cooled to room temperature, add simethicone emulsion wherein again, fully namely stirring obtains high-strength toughness reinforcing glue again.
5. the preparation method of high-strength toughness reinforcing glue according to claim 4, it is characterized in that: described in add water operation time ACRYLIC EMULSION solid content reach after 34% ~ 36% and stop adding water, during heating operation ACRYLIC EMULSION viscosity to 190 ~ 210cP after stop heating.
6. the preparation method of high-strength toughness reinforcing glue according to claim 4, is characterized in that: described in add water operation time ACRYLIC EMULSION solid content reach after 35% and stop adding water, during heating operation, the viscosity of ACRYLIC EMULSION stops heating to 200cP.
7. use the high-strength toughness reinforcing glue described in claim 1 or 2 or 3 or the high-strength toughness reinforcing glue that adopts method described in claim 4 or 5 or 6 to obtain to prepare a method for A2 level inorganic mineral scutum, it is characterized in that: its step is as follows:
(1) select materials: the powder choosing following parts by weight: aluminium hydroxide: 15 ~ 30 weight parts, magnesium hydroxide: 10 ~ 20 weight parts, silicon powder: 40 ~ 50 weight parts, quartz sand: 60 ~ 70 weight parts, diatomite: 10 ~ 20 weight parts, clay: 10 ~ 20 weight parts, talcum powder: 10 ~ 15 weight parts, glass fibre: 2 ~ 3 weight parts;
(2) and material: the powder of above-mentioned weight part is put into stirrer and stirs, add in the powder stirred as the weight part of claim 1-6 as described in any one be 45 ~ 55 high-strength toughness reinforcing glue, progressively add appropriate water again, carry out secondary stirring, good mixture to be mixed is stop after fluid paste adding water;
(3) making sheet: the centre that the mixture in fluid paste puts into some layers of non-woven fabrics through the setting gauge of stirrer is carried out coated, coatedly continues or intermittently to carry out, coated good material is carried out first time rolling through milling train, roll rear feeding roaster and carry out first time baking, storing temperature is 75 DEG C ~ 85 DEG C, baking time is 8 ~ 12min, obtain and once toast slab, once will toast slab feeding milling train and carry out second time rolling, roll rear feeding roaster and carry out second time baking, storing temperature is 85 DEG C ~ 95 DEG C, baking time is 8 ~ 12min, obtain secondary baking slab, secondary baking slab is sent into milling train and carries out third time rolling, roll rear feeding roaster and carry out third time baking, storing temperature is 95 DEG C ~ 105 DEG C, baking time is 4 ~ 6min, obtain three baking slabs, three baking slabs are sent into milling train and carries out the 4th rolling, roll rear feeding roaster and carry out the 4th baking, storing temperature is 105 DEG C ~ 115 DEG C, baking time is 4 ~ 6min, obtain four baking slabs, four baking slabs are sent into milling train and carries out the 5th rolling, roll rear feeding roaster and carry out the 5th baking, storing temperature is 125 DEG C ~ 135 DEG C, baking time is 4 ~ 6min, obtain five baking slabs, five baking slabs are sent into roaster and carries out the 6th baking, storing temperature is 145 DEG C ~ 155 DEG C, baking time is 4 ~ 6min, obtain six baking slabs, six baking slabs are sent into roaster and carries out the 7th baking, storing temperature is 165 DEG C ~ 175 DEG C, baking time is 4 ~ 6min, obtain seven baking slabs, room temperature is cooled to after slab drying, batch to obtain finished product sheet material.
8. the method preparing A2 level inorganic mineral scutum according to claim 7, is characterized in that: storing temperature is 78 DEG C ~ 82 DEG C for the first time, and baking time is 9 ~ 11min; Second time storing temperature is 88 DEG C ~ 92 DEG C, and baking time is 9 ~ 11min; Third time, storing temperature was 98 DEG C ~ 102 DEG C, and baking time is 9 ~ 11min; 4th time storing temperature is 108 DEG C ~ 112 DEG C, and baking time is 5min; 5th time storing temperature is 128 DEG C ~ 132 DEG C, and baking time is 5min; 6th time storing temperature is 148 DEG C ~ 152 DEG C, and baking time is 5min; 7th time storing temperature is 168 DEG C ~ 172 DEG C, and baking time is 5min.
9. the method preparing A2 level inorganic mineral scutum according to claim 7, is characterized in that: storing temperature is 80 DEG C for the first time, and baking time is 10min; Second time storing temperature is 90 DEG C, and baking time is 10min; Third time, storing temperature was 100 DEG C, and baking time is 5min; 4th time storing temperature is 110 DEG C, and baking time is 5min; 5th time storing temperature is 130 DEG C, and baking time is 5min; 6th time storing temperature is 150 DEG C, and baking time is 5min; 7th time storing temperature is 170 DEG C, and baking time is 5min.
10. the method preparing A2 level inorganic mineral scutum according to claim 7, is characterized in that: described non-woven fabrics is set to 2 ~ 4 layers.