CN104016627B - A kind of straw ash thermal insulation mortar and utilize its method preparing warming plate - Google Patents

A kind of straw ash thermal insulation mortar and utilize its method preparing warming plate Download PDF

Info

Publication number
CN104016627B
CN104016627B CN201410256083.0A CN201410256083A CN104016627B CN 104016627 B CN104016627 B CN 104016627B CN 201410256083 A CN201410256083 A CN 201410256083A CN 104016627 B CN104016627 B CN 104016627B
Authority
CN
China
Prior art keywords
parts
straw ash
warming plate
thermal insulation
component
Prior art date
Application number
CN201410256083.0A
Other languages
Chinese (zh)
Other versions
CN104016627A (en
Inventor
杨峰
Original Assignee
杨峰
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 杨峰 filed Critical 杨峰
Priority to CN201410256083.0A priority Critical patent/CN104016627B/en
Publication of CN104016627A publication Critical patent/CN104016627A/en
Application granted granted Critical
Publication of CN104016627B publication Critical patent/CN104016627B/en

Abstract

The present invention discloses a kind of straw ash thermal insulation mortar, it is according to parts by weight, and each component is: straw ash: 70��130 parts, flyash: 10��130 parts, cement: 150��170 parts, water reducer: 1��2 part, HPMC:2��4 part, rubber powder: 10��16 parts, polypropylene chopped strand: 1��3 part, wood fibre: 2��4 parts, calcining coal gangue: 0��60 part. The invention also discloses the preparation method of a kind of straw ash warming plate, first the above-mentioned each component of straw ash thermal insulation mortar and a small amount of water are carried out mix and blend, be then shaped by making sheet mould and compacting pressure mechanism plate.

Description

A kind of straw ash thermal insulation mortar and utilize its method preparing warming plate

Technical field

The present invention relates to a kind of straw ash thermal insulation mortar; The present invention also relates to a kind of method utilizing straw ash thermal insulation mortar to prepare warming plate, belongs to material of construction and receives.

Background technology

At present, building energy conservation career development is rapid, and External Walls Heating Insulation starts widespread use. But, more or less there is certain defect in existing external wall outer insulation material, as: poly-third particle, EPS (XPS) warming plate easily fire, the quality problems such as glass bead, cement foam board etc. easily occur ftractureing, come off, crack. And, existing external-wall heat-insulation material is technical process complexity, labor strength height, construction costs cost height in engineering is constructed.

Consequently, it is desirable to a kind of new technical scheme solves the problems of the technologies described above.

Summary of the invention

It is an object of the invention to provide a kind of straw ash thermal insulation mortar, it has light weight, high insulating effect, sound insulation, anti-cracking, antidetonation, does not burn, lower-price characteristic, and it is refuse reclamation, belongs to energy saving and environment friendly material.

The present invention also provides a kind of method utilizing straw ash thermal insulation mortar to prepare warming plate, the method makes simple, the warming plate of making has light weight, without the need to ageing, high insulating effect, do not ftracture, not crack, do not peel off, do not burn, the feature such as easy construction, decoration are strong.

The technical solution used in the present invention is:

A kind of straw ash thermal insulation mortar, it is according to parts by weight, and each component is: straw ash: 70��130 parts, flyash: 10��130 parts, cement: 150��170 parts, water reducer: 1��2 part, HPMC:2��4 part, rubber powder: 10��16 parts, polypropylene chopped strand: 1��3 part, wood fibre: 2��4 parts, calcining coal gangue: 0��60 part.

Preferably, a kind of straw ash thermal insulation mortar, it is according to parts by weight, and each component is: straw ash: 70��90 parts, flyash: 110��130 parts, cement: 150��170 parts, water reducer: 1��2 part, HPMC:2��4 part, rubber powder: 10��16 parts, polypropylene chopped strand: 1��3 part, wood fibre: 2��4 parts.

Preferably, a kind of straw ash thermal insulation mortar, it is according to parts by weight, and each component is: straw ash: 110��130 parts, flyash: 10��20 parts, cement: 150��170 parts, water reducer: 1��2 part, HPMC:2��4 part, rubber powder: 10��16 parts, polypropylene chopped strand: 1��3 part, wood fibre: 2��4 parts, calcining coal gangue: 40��60 parts.

A preparation method for straw ash warming plate, first carries out mix and blend by the above-mentioned each component of straw ash thermal insulation mortar and a small amount of water, is then shaped by making sheet mould and compacting pressure mechanism plate.

Further, the add-on of described water is 20��35 parts.

Further, described board making process can also embed alkali-proof glass fiber mesh in warming plate.

Further, described board making process can also embed aluminium alloy panel or marble panel on the decorative cover of warming plate.

The present invention adopts straw ash to be main raw material, and it takes from the dead meal of heat power plant, is reasonably recycled by waste material, protection of the environment while save energy; The flyash adopted can the obviously intensity of reinforced mortar and shock resistance.

It is an advantage of the invention that: straw ash thermal insulation mortar has light weight, high insulating effect, sound insulation, anti-cracking, antidetonation, do not burn, lower-price characteristic; The warming plate utilizing straw ash thermal insulation mortar to prepare has light weight, without the need to ageing, high insulating effect, do not ftracture, not crack, do not peel off, do not burn, the feature such as easy construction, decoration are strong.

Embodiment

Embodiment 1

A kind of straw ash thermal insulation mortar, it is according to parts by weight, and each component is: straw ash 70 parts, 130 parts, flyash, cement: 170 parts, water reducer: 2 parts, HPMC:4 part, rubber powder 16 parts, polypropylene chopped strand 3 parts, wood fibre 4 parts.

Embodiment 2

A kind of straw ash thermal insulation mortar, it is according to parts by weight, and each component is: straw ash 80 parts, 120 parts, flyash, cement 160 parts, water reducer 1.6 parts, HPMC3 part, rubber powder 15 parts, polypropylene chopped strand 2 parts, wood fibre 3 parts.

Embodiment 3

A kind of straw ash thermal insulation mortar, it is according to parts by weight, and each component is: straw ash 90 parts, 110 parts, flyash, cement 150 parts, water reducer 1 part, HPMC2 part, rubber powder 10 parts, polypropylene chopped strand 1 part, wood fibre 2 parts.

Embodiment 4

A kind of straw ash thermal insulation mortar, it is according to parts by weight, and each component is: straw ash 110 parts, 10 parts, flyash, cement 150 parts, water reducer 1 part, HPMC2 part, rubber powder 10 parts, polypropylene chopped strand 1 part, wood fibre 2 parts, calcining coal gangue 40 parts.

Embodiment 5

A kind of straw ash thermal insulation mortar, it is according to parts by weight, and each component is: straw ash 130 parts, 20 parts, flyash, cement 170 parts, water reducer 2 parts, HPMC4 part, rubber powder 16 parts, polypropylene chopped strand 3 parts, wood fibre 4 parts, calcining coal gangue 60 parts.

Embodiment 6

A kind of straw ash thermal insulation mortar, it is according to parts by weight, and each component is: straw ash 120 parts, 15 parts, flyash, cement 160 parts, water reducer 1.5 parts, HPMC3 part, rubber powder 15 parts, polypropylene chopped strand 2 parts, wood fibre 3 parts, calcining coal gangue 50 parts.

Embodiment 7

The preparation method of a kind of straw ash warming plate, first the water of the above-mentioned each component of straw ash thermal insulation mortar and 20��35 parts is carried out mix and blend, then it is shaped by making sheet mould and compacting pressure mechanism plate, board making process can also embed alkali-proof glass fiber mesh in warming plate, the decorative cover of warming plate embeds aluminium alloy panel or marble panel.

Claims (5)

1. the preparation method of a straw ash warming plate, it is characterized in that: it is according to parts by weight, each component is: straw ash: 70��130 parts, flyash: 10��130 parts, cement: 150��170 parts, water reducer: 1��2 part, HPMC:2��4 part, rubber powder: 10��16 parts, polypropylene chopped strand: 1��3 part, wood fibre: 2��4 parts, calcining coal gangue: 0��60 part;First the water of above-mentioned each component and 20��35 parts is carried out mix and blend, then it is shaped by making sheet mould and compacting pressure mechanism plate.
2. the preparation method of a kind of straw ash warming plate according to claim 1, it is characterized in that: it is according to parts by weight, each component is: straw ash: 70��90 parts, flyash: 110��130 parts, cement: 150��170 parts, water reducer: 1��2 part, HPMC:2��4 part, rubber powder: 10��16 parts, polypropylene chopped strand: 1��3 part, wood fibre: 2��4 parts.
3. the preparation method of a kind of straw ash warming plate according to claim 1, it is characterized in that: it is according to parts by weight, each component is: straw ash: 110��130 parts, flyash: 10��20 parts, cement: 150��170 parts, water reducer: 1��2 part, HPMC:2��4 part, rubber powder: 10��16 parts, polypropylene chopped strand: 1��3 part, wood fibre: 2��4 parts, calcining coal gangue: 40��60 parts.
4. the preparation method of a kind of straw ash warming plate according to claim 1, it is characterised in that: described board making process can also embed alkali-proof glass fiber mesh in warming plate.
5. the preparation method of a kind of straw ash warming plate according to claim 1, it is characterised in that: described board making process can also embed aluminium alloy panel or marble panel on the decorative cover of warming plate.
CN201410256083.0A 2014-06-06 2014-06-06 A kind of straw ash thermal insulation mortar and utilize its method preparing warming plate CN104016627B (en)