CN103964819A - 锰矿渣新型节能环保烧结砖及其制造方法 - Google Patents
锰矿渣新型节能环保烧结砖及其制造方法 Download PDFInfo
- Publication number
- CN103964819A CN103964819A CN201410172209.6A CN201410172209A CN103964819A CN 103964819 A CN103964819 A CN 103964819A CN 201410172209 A CN201410172209 A CN 201410172209A CN 103964819 A CN103964819 A CN 103964819A
- Authority
- CN
- China
- Prior art keywords
- brick
- manganese slag
- manganese
- environment
- novel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明锰矿渣新型节能环保烧结砖及其制造方法,其原料为锰渣25%—45%、页岩50%-75%、煤5%、水2%-3%;其中锰渣是锰矿提炼出来的。取锰渣25%—45%、页岩50%-75%、煤5%,放入粉碎机粉碎,通过滚筒把搅拌好的料送入料仓,在水2%-3%进行3次搅拌;将搅拌好的料送真空砖机加压挤出机挤出成型制成砖坯;把砖坯进行风干,把风干好的砖坯进行1100°C高温培烧,检测合格后制成成品砖。本发明的目的是为综合利用、治理环境,利用冶炼后的废弃物锰渣为主原料生产出一种新型的墙体建筑材料锰矿渣新型节能环保烧结砖取代粘土砖。可以实现经济增长与环境保护共同发展,具有显著的经济效益和社会效益。
Description
技术领域
本发明涉及一种建筑材料,具体地是锰矿渣新型节能环保烧结砖及其制造方法。
背景技术
锰是炼钢工业不可缺少的原料,在自然界中主要以软锰矿形式存在,锰渣就是冶炼后的废弃物,里面的锰含量很高,其来源可以是采用酸性渣法或偏酸性渣法生产高碳锰铁时的附产品。目前国内建筑业的墙体材料砖需求量大,已工业化的烧结砖有粘土烧结砖(即红砖)、粘土粉煤灰烧结砖、煤矸石烧结砖三种,还有无粘土粉砖灰烧 结砖及无粘土硼泥烧结砖。生产粘土烧结砖约生产100万块砖就要毁田 —亩。国家提倡要提高资源的利用率,可以把锰渣制作成新型节能环保烧结砖。
发明内容
本发明的目的是为综合利用、治理环境,利用冶炼后的废弃物锰渣为主原料生产出一种新型的墙体建筑材料锰矿渣新型节能环保烧结砖取代粘土砖。
本发明锰矿渣新型节能环保烧结砖及其制造方法内容简述:
本发明锰矿渣新型节能环保烧结砖及其制造方法,其原料为锰渣25%—45%、页岩50%-75%、煤5%、水2%-3%;其中,锰渣是锰矿提炼出来的。
其制造方法为:取锰渣25%—45%、页岩50%-75%、煤5%,放入粉碎机粉碎,通过滚筒把搅拌好的料送入料仓,在水2%-3%进行3次搅拌;将搅拌好的的料送真空砖机加压挤出机挤出成型制成砖坯;把砖坯进行风干,把风干好的砖坯进行1100°C高温培烧,检测合格后制成成品砖。
本发明的目的是为综合利用、治理环境,利用冶炼后的废弃物锰渣为主原料生产出一种新型的墙体建筑材料锰矿渣新型节能环保烧结砖取代粘土砖。可以实现经济增长与环境保护共同发展,具有显著的经济效益和社会效益。
具体实施方式
实施例:
取锰矿提炼出来的锰渣25%—45%、页岩50%-75%、煤5%,放入粉碎机粉碎,通过滚筒把搅拌好的料送入料仓,在水2%-3%进行3次搅拌;将搅拌好的的料送真空砖机加压挤出机挤出成型制成砖坯;把砖坯进行风干,把风干好的砖坯进行1100°C高温培烧,检测合格后制成成品砖。
以上所述仅为本发明的具有代表性的实施例,不以任何方式限制本发明,凡在本发明的精神和原则之内所作的任何修改、等同替换或改进等,均应包含在本发明的保护范围之内。
Claims (2)
1.锰矿渣新型节能环保烧结砖及其制造方法,其特征在于:锰渣25%—45%、页岩50%-75%、煤5%、水2%-3%。
2. 根据权利要求1所述锰矿渣新型节能环保烧结砖及其制造方法,其特征在于:取锰渣25%—45%、页岩50%-75%、煤5%,放入粉碎机粉碎,通过滚筒把搅拌好的料送入料仓,在水2%-3%进行3次搅拌;将搅拌好的的料送真空砖机加压挤出机挤出成型制成砖坯;把砖坯进行风干,把风干好的砖坯进行1100°C高温培烧,检测合格后制成成品砖。