CN103964808A - 一种复合涂料及其制造方法 - Google Patents

一种复合涂料及其制造方法 Download PDF

Info

Publication number
CN103964808A
CN103964808A CN201310031089.3A CN201310031089A CN103964808A CN 103964808 A CN103964808 A CN 103964808A CN 201310031089 A CN201310031089 A CN 201310031089A CN 103964808 A CN103964808 A CN 103964808A
Authority
CN
China
Prior art keywords
mass parts
parts
alumina
composite coating
ripe
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310031089.3A
Other languages
English (en)
Inventor
李军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310031089.3A priority Critical patent/CN103964808A/zh
Publication of CN103964808A publication Critical patent/CN103964808A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种复合涂料及其制造方法，该涂料的质量份是高铝质熟粉料5～45质量份、高铝质熟骨料10～40质量份、石英砂15～40质量份、水玻璃100质量份、粘土5～10质量份、沸石3～8质量份、石英砂10～40质量份。按各原料的质量份比例倒入容器中加水15～20质量份搅拌均匀，搅成浆糊状，涂刷到修合处修复。本发明不含有毒有害成分，耐高温，不易开裂，能有效防止漏风，使用后节能降耗20以上，可用于填补窑炉漏缝、墙体、窑车，节能效果显著，无副作用，使用方便。

Description

一种复合涂料及其制造方法
技术领域
本发明涉及一种复合密封涂料，特别涉及一种复合涂料及其制造方法。
背景技术
现有的烧结砖瓦的轮窑和隧道窑，窑炉长时间使用后会产生开裂漏风漏气和散热严重，由此造成的热量损失通常占总热耗的20％以上，同时也给产品质量的进一步提高带来了困难，使烧结砖瓦热耗上升，造成能源浪费，这不仅增加了砖厂的生产成本，严重的甚至影响产品质量，缩短窑炉使用寿命。传统的方法是将窑炉进行整修，更换耐火材料，这种方法成本高、时间长，增加了企业的负担。人们迫切希望能有一种密封性好、能耐高温、施工方便简单的窑炉修复涂料。
发明内容
为了解决以上所述技术问题，本发明提供一种密封效果好、耐高温、施工简单、成本较低的一种复合密封涂料。
本发明的技术解决方案是这样的，一种复合涂料，其特征在于该涂料高铝质熟粉料为5～45质量份、高铝质熟骨料15～40质量份、石英砂10～40质量份、水玻璃10～35质量份、粘土5～10质量份、清水10～25质量份、沸石3～5质量份。
该复合涂料的质量份为：高铝质熟粉料为20质量份、高铝质熟骨料30质量份、石英砂25质量份、水玻璃30质量份、粘土10质量份、清水15质量份、沸石3质量份。
高铝质熟粉料为20～50目，高铝质熟骨料中Al2O3含量占比例10～50％，石英砂为10～50目，粘土10～30目、沸石5～8目。
高铝质熟粉料为30目，高铝质熟骨料中Al2O3含量为40％以上，粘土为20目、沸石30目。
将高铝质熟粉料为20质量份、高铝质熟骨料30质量份、石英砂25质量份、水玻璃30质量份、粘土10质量份倒入容器内，沸石6质量份加入清水15质量份搅拌成稀浆状，然后用泵接上喷枪喷涂至接合处，和/或用人工涂刷，涂料厚度为1～10mm。
本发明的有益效果是：本产品不含有毒有害成分，耐高温，不易开裂，能有效防止漏风，使用后节能降耗20％以上，对窑炉既可填补漏线，又可修补窑炉渣、窑炉车。
具体实施方式
实施例1，本实施方式的复合材料高铝质熟粉料10～30质量份(粒度0.078mm，Al2O3含量50％)、高铝质熟骨料30-35质量份(Al2O3含量60％，20目、40目各占30％，30目40％)、石英砂20～25质量份过30目、沸石3～5质量份、水玻璃15～25质量份，按以上重量比将原料倒入容器中，加入15～20％清水搅拌成稀浆状，用喷枪或人工喷涂密封窑炉内壁，粘土2质量份，喷涂厚度5mm。
实施例2，本实施方式的复合涂料高铝质熟粉料25～40质量份(粒度0.08mm，Al2O3含量50％)、高铝质熟骨料20～30质量份(Al2O3含量60％，20目、40目各占30％，30目40％)、石英砂(30目)20-30质量份、沸石3质量份、水玻璃25-35质量份，按以上重量比将原料倒入容器中，加入5～20质量份清水、粘土3质量份搅拌成稀浆状，用喷枪或人工喷涂密封窑炉内壁，喷涂厚度4mm。
实施例3，本实施方式复合涂料高铝质熟粉料15-35质量份(粒度0.08mm，Al2O3含量50％)、高铝质熟骨料25-33质量份(Al2O3含量60％，沸石5质量份。20目、40目各占30％，30目40％)、石英砂22-28质量份(30目)、水玻璃20-30质量份，按以上重量比将原料倒入容器中，加入15-20质量份清水、粘土15～20质量份搅拌成稀浆状，用喷枪或人工喷涂密封窑炉内壁，喷涂厚度2mm。
实施例4，本实施方式复合涂料高铝质熟粉料30质量份(粒度0.08mm，Al2O3含量50％)、高铝质熟骨料25质量份(Al2O3含量60％，20目、40目各占30％，30目40％)、石英砂25质量份(30目)、水玻璃20质量份，沸石6质量份、粘土4质量份，按以上重量比将原料倒入容器中，加入15-20质量份清水搅拌成稀浆状，用喷枪或人工喷涂密封窑炉内壁，喷涂厚度6mm。
实施例5，本实施方式复合涂料高铝质熟粉料10质量份(粒度0.08mm，Al2O3含量50％)、高铝质熟骨料35质量份(Al2O3含量60％，20目、40目各占30％，30目40％)、石英砂20质量份(30目)、水玻璃35质量份，沸石8质量份、粘土5质量份，按以上重量比将原料倒入容器中，加入15-20质量份清水搅拌成稀浆状，用喷枪或人工喷涂密封窑炉内壁，喷涂厚度2mm。
实施例6，本实施方式复合涂料组合物原料质量份和重量比为：高铝质熟粉料40质量份(粒度0.08mm，Al2O3含量50％)、高铝质熟骨料20质量份(Al2O3含量60％，20目、40目各占30％，30目40％)、沸石8质量份、石英砂25质量份(30目)、水玻璃15质量份，粘土1质量份，按以上质量份也将原料倒入容器中，加入15-20质量份清水搅拌成稀浆状，用喷枪或人工喷涂密封窑炉内壁，喷涂厚度2～5mm。

Claims (5)

1.一种复合涂料，其特征在于该涂料高铝质熟粉料为5～45质量份、高铝质熟骨料15～40质量份、石英砂10～40质量份、水玻璃10～35质量份、粘土5～10质量份、清水10～25质量份。
2.根据权利要求1所述的一种复合涂料，其特征在于该该复合涂料的确质量份为：高铝质熟粉料为20质量份、高铝质熟骨料30质量份、石英砂25质量份、水玻璃30质量份、粘土10质量份、清水15质量份。
3.一种复合涂料的制造方法，其特征在于高铝质熟粉料为20～50目粘度，高铝质熟骨料中Al2O3含量占比例10～50％，石英砂为10～50目粘度，粘土10～30目粘度。
4.一种复合涂料的制造方法，其特征在于高铝质熟粉料为30目粘度，高铝质熟骨料中Al2O3含量为40％以上，粘土为20目粘度。
5.根据权利要求1或3所述的一种复合涂料及其制造方法，其特征在于将高铝质熟粉料为20质量份、高铝质熟骨料30质量份、石英砂25质量份、水玻璃30质量份、粘土10质量份倒入容器内，加入清水15质量份搅拌成稀浆状，然后用泵接上喷枪喷涂至接合处。
CN201310031089.3A 2013-01-28 2013-01-28 一种复合涂料及其制造方法 Pending CN103964808A (zh)