CN103952917B - 一种莫代尔梭织面料开纤工艺 - Google Patents

一种莫代尔梭织面料开纤工艺 Download PDF

Info

Publication number
CN103952917B
CN103952917B CN201410183868.XA CN201410183868A CN103952917B CN 103952917 B CN103952917 B CN 103952917B CN 201410183868 A CN201410183868 A CN 201410183868A CN 103952917 B CN103952917 B CN 103952917B
Authority
CN
China
Prior art keywords
cloth
woven fabric
fibrillation
fiber opening
pickling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410183868.XA
Other languages
English (en)
Other versions
CN103952917A (zh
Inventor
吴绍明
胡卫林
李国信
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HANGZHOU XINSHENG PRINTING & DYEING Co Ltd
Original Assignee
HANGZHOU XINSHENG PRINTING & DYEING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HANGZHOU XINSHENG PRINTING & DYEING Co Ltd filed Critical HANGZHOU XINSHENG PRINTING & DYEING Co Ltd
Priority to CN201410183868.XA priority Critical patent/CN103952917B/zh
Publication of CN103952917A publication Critical patent/CN103952917A/zh
Application granted granted Critical
Publication of CN103952917B publication Critical patent/CN103952917B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种莫代尔梭织面料开纤工艺，包括以下工艺步骤：用酶、退浆剂、精练剂和渗透剂冷堆处理坯布，并经水洗和预定型；经过上述处理后的布料在机缸中进行喷压处理，选择水位控制在3.5~4.5吨之间，浴比为1：15~20；将硫酸加入副缸稀释并搅拌均匀，然后缓慢加入上述提到的机缸里，升温，并保温进行酸洗；酸洗后的布料再进行水洗，并用纯碱进行中和，即可得到开纤后的布料，通过此工艺制备的开纤布料克服了现有技术的不足，能将布面毛羽上的杂质毛料去除干净，并且布料的手感柔软、绒感强，该工艺简单易行，实现了去毛和开纤同步进行。

Description

一种莫代尔梭织面料开纤工艺
技术领域
本发明属于纺织工业染整工程领域，特别是涉及一种莫代尔梭织面料开纤工艺。
背景技术
莫代尔是高湿模量粘胶纤维的纤维素再生纤维，该纤维的原料采用榉木，先将其制成木浆，再通过专门的纺丝工艺加工成纤维，该产品原料全部为天然材料，对人体无害，并能够自然分解，对环境无害，除此之外，还具有透气性、吸水性良好等优点，因此在现在社会具有广泛的应用。梭织面料是将纱线通过经、纬向的交错而组成，具有结构稳定、布面平整，悬垂时一般不出现驰垂现象等优点，在服装中的使用处于领先地位。而用莫代尔通过梭织的方式生产出来的面料，结合了莫代尔面料和梭织方式两者的优点，更是受到了人们的普遍欢迎。
现有技术中，在处理胚布时，经常会存在开纤时布面毛羽去除不干净，开纤效果和均匀性差，布面手感硬，无绒感等缺点。
发明内容
本发明的目的在于克服现有技术的不足，提供一种具有布面毛羽去除干净，开纤效果好均匀，手感柔软，绒感强的莫代尔梭织面料开纤工艺。
为解决上述技术问题，本发明提供的技术方案为：
一种莫代尔梭织面料的开纤工艺，包括如下工艺步骤：
（1）用酶、退浆剂、精练剂和渗透剂冷堆处理坯布，并经水洗机水洗和预定型；定型用的定型机为立信门富士定型机。
（2）经过步骤（1）处理后的布料在J型机缸中进行喷压处理，选择水位控制在3.5~4.5吨之间，浴比为1：15~20；优选的浴比为1:18；水洗的目的是去除布上的杂质、浆料，面料在机缸运行时通过喷压来调节速度。
（3）先将硫酸加入副缸稀释并搅拌均匀，然后缓慢加入步骤（2）中的机缸里，升温，并保温进行酸洗；
（4）经过步骤（3）酸洗后的布料再进行水洗，并用纯碱进行中和，通过测试PH值判断是否中和完全，即可得到开纤后的布料。
作为优选，所述的酶是淀粉酶，所述的退浆剂为氧化退浆剂，所述的精炼剂为除油精练剂，所述的渗透剂为JFC。
作为优选，所述的硫酸为质量分数98%的浓硫酸，用量为0.6g/L~1.2g/L。
作为优选，所述的升温温度为90~120℃，保温时间为80~120min。
本发明的有益效果是：1）通过此开纤工艺处理的布料，能将布面毛羽上的杂质毛料去除干净，并且布料的手感柔软、绒感强，该工艺简单易行，并且去毛和开纤实现了同步进行。
具体实施方式
为了进一步理解本发明，下面实施例是对本发明优选实施方式进行的描述，但是应当理解，这些描述只是为了进一步说明本发明的特征和优点，而不是对本发明权利要求的限制。
实施例1
用酶、退浆剂、除油精练剂和渗透剂冷堆处理坯布，并用水洗机水洗，用立信门富士定型机进行预定型处理，经过上述处理后的布料在机缸中进行喷压处理，选择水位控制在3.5吨，浴比为1：15，面料在机缸运行时通过喷压来调节速度，然后将98%的浓硫酸，用量为0.6g/L，加入副缸稀释并搅拌均匀，然后缓慢加入上述机缸里，升温到90℃，并保温80min进行酸洗，酸洗后进行水洗，并用纯碱进行中和至中性，后进行染色，定型即可得到开纤后的布料。
实施例2
用酶、退浆剂、除油精练剂和渗透剂冷堆处理坯布，并用水洗机水洗，用立信门富士定型机进行预定型处理，经过上述处理后的布料在机缸中进行喷压处理，选择水位控制在4吨，浴比为1：18，面料在机缸运行时通过喷压来调节速度，然后将98%的浓硫酸，用量为0.9g/L，加入副缸稀释并搅拌均匀，然后缓慢加入上述机缸里，升温到105℃，并保温100min进行酸洗，酸洗后进行水洗，并用纯碱进行中和至中性，后进行染色，定型即可得到开纤后的布料。
实施例3
用酶、退浆剂、除油精练剂和渗透剂冷堆处理坯布，并用水洗机水洗，用立信门富士定型机进行预定型处理，经过上述处理后的布料在机缸中进行喷压处理，选择水位控制在4.5吨，浴比为1：20，面料在机缸运行时通过喷压来调节速度，然后将98%的浓硫酸，用量为1.2g/L，加入副缸稀释并搅拌均匀，然后缓慢加入上述机缸里，升温到120℃，并保温120min进行酸洗，酸洗后进行水洗，并用纯碱进行中和至中性，后进行染色，定型即可得到开纤后的布料。
以上所述仅为本发明的优选实施方式，应当指出，对于本领域的普通技术人员而言，在不脱离本发明的原理前提下，还可以做出多种变形和改进，这也应该视为本发明的保护范围。

Claims (3)

1.一种莫代尔梭织面料开纤工艺，其特征在于：包括如下工艺步骤：
(1)用淀粉酶，氧化退浆剂，除油精炼剂，JFC渗透剂冷堆处理坯布，并用水洗机水洗和预定型；
(2)经过步骤(1)处理后的布料在机缸中进行喷压处理，选择水位控制在3.5-4.5吨之间，浴比在1：15-20；
(3)先将98％硫酸以0.6g/L-1.2g/L的用量加入副缸稀释并搅拌均匀，然后缓慢加入步骤(2)中的机缸里，升温，并保温进行酸洗；
(4)经过步骤(3)酸洗后的布料在经过水洗，并用纯碱进行中和，后进行染色，定型即可得到开纤后的布料。
2.根据权利要求1所述的莫代尔梭织面料开纤工艺，其特征在于：所述的浴比为1：18。
3.根据权利要求1所述的莫代尔梭织面料开纤工艺，其特征在于：所述的升温温度为90-120℃，保温时间为80-120min。
CN201410183868.XA 2014-05-04 2014-05-04 一种莫代尔梭织面料开纤工艺 Expired - Fee Related CN103952917B (zh)