CN103948211A - 一种防穿刺鞋底及其制造方法 - Google Patents
一种防穿刺鞋底及其制造方法 Download PDFInfo
- Publication number
- CN103948211A CN103948211A CN201410224065.4A CN201410224065A CN103948211A CN 103948211 A CN103948211 A CN 103948211A CN 201410224065 A CN201410224065 A CN 201410224065A CN 103948211 A CN103948211 A CN 103948211A
- Authority
- CN
- China
- Prior art keywords
- parts
- lower glue
- gluing
- sole
- charcoal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种防穿刺鞋底,其特征在于包括上胶底层、下胶底层和炭纤布,所述炭纤布位于所述上胶底层和下胶底层之间,与上胶底层、下胶底层粘连。本发明运用炭纤网结合橡胶材料制成的鞋底,结构简单,成本低廉,可以有效的加强鞋底的防穿刺性,同时具有橡胶鞋底弹性强,耐磨损等优点。
Description
技术领域
本发明涉及一种鞋底的领域,尤其涉及一种防穿刺鞋底的领域。
背景技术
橡胶鞋底具有高耐寒、高弹力等特性,且造价低廉,非常受欢迎。但同时橡胶耐穿刺力较差,很多场合对鞋底的耐穿刺能力又有很高的要求,比如士兵在山地训练,或在复杂的地面作战时,很容易被刺穿扎伤脚。
发明内容
发明目的: 本发明目的在于针对现有技术的不足,提供一种能有效提高防穿刺能力,同时还能保持橡胶优点的防穿刺鞋底。
技术方案: 本发明所述的防穿刺鞋底包括上胶底层、下胶底层和炭纤布,所述炭纤布位于所述上胶底层和下胶底层之间,与上胶底层、下胶底层粘连。
作为优选,本发明所述的上胶底层、下胶底层包括如下组分:
标胶 60~80份;
顺丁橡胶 20~40份;
炭黑N200 50~55份;
白油 15~25份;
古马隆树脂 5~15份;
氧化锌 3~7份;
硬脂酸 1~2份;
促进剂M 0.5~1份;
促进剂DM 1~2份;
防老剂4010 0.5~1.5份;
防老剂RD 0.5~1.5份;
硫磺 2~2.4份;
促进剂TT 0.01~0.03份
以重量份计。
作为优选,本发明所述的上胶底层、下胶底层包括如下组分:
标胶 70份;
顺丁橡胶 30份;
炭黑N200 52份;
白油 20份;
古马隆树脂 10份;
氧化锌 5份;
硬脂酸 1.5份;
促进剂M 0.8份;
促进剂DM 1.5份;
防老剂4010 1份;
防老剂RD 1份;
硫磺 2.2份;
促进剂TT 0.02份。
本发明所述的防穿刺鞋底的制造方法包括以下步骤:
①:将由常用橡胶制成方法制成的上胶底层、下胶底层冲压成各尺码的片料,炭纤布冲压成于上胶底层、下胶底层一致的形状;
②:将制好的上胶底层、下胶底层刷上胶浆,送到烘房停放24小时,烘房温度35~45℃;
③:将炭纤布放在上胶底层和下胶底层中间,与上胶底层、下胶底层粘连在一起,放在模具中;
④:将模具送入硫化机硫化,硫化机温度140~160℃,时间350~400秒,机台压力140~150Mpa。
有益效果:本发明运用炭纤网结合橡胶材料制成的鞋底,结构简单,成本低廉,可以有效的加强鞋底的防穿刺性,同时具有橡胶鞋底弹性强,耐磨损等优点。
附图说明
图1为本发明鞋底结构示意图。
具体实施方式
下面通过附图对本发明技术方案进行详细说明,但是本发明的保护范围不局限于所述实施例。
本发明实施例中使用的原料均为市售产品,来源如下:标胶(东莞南冠生胶片有限公司);顺丁橡胶(东莞南冠生胶片有限公司);炭黑N220(广州力本橡胶原料有限公司);白油(无锡市新苏油脂有限公司产工业级白油);古马隆树脂(南京向前化工有限公司);氧化锌(广州拓亿贸易有限公司产品间接法99.7%锌氧粉);硬脂酸(广州市天河区大观智业化工产品1801硬脂酸);促进剂M(上海美华化工有限公司);促进剂DM(上海美华化工有限公司);防老剂4010(山东圣奥化工股份有限公司);防老剂RD(山东圣奥化工股份有限公司);硫磺(中国石化集团北京燕山化工有限公司);促进剂TT(上海美华化工有限公司)。
实施例1:一种防穿刺鞋底,如图1所示,包括上胶底层1、下胶底层2和炭纤布3, 所述上胶底层1、下胶底层2的组分为:
标胶 60份;
顺丁橡胶 20份;
炭黑N200 50份;
白油 15份;
古马隆树脂 5份;
氧化锌 3份;
硬脂酸 1份;
促进剂M 0.5份;
促进剂DM 1份;
防老剂4010 0.5份;
防老剂RD 0.5份;
硫磺 2份;
促进剂TT 0.01份
以重量份计,
将上胶底层1、下胶底层2和炭纤布3冲压成形状一致的片料;将制好的上胶底层1、下胶底层2刷上胶浆,送到烘房停放24小时,烘房温度35℃;将炭纤布3放在上胶底层1和下胶底层2中间,与上胶底层1、下胶底层2粘连在一起,放在模具中;将模具送入硫化机硫化,硫化机温度140℃,时间350秒,机台压力140Mpa,得到所述防穿刺鞋底。
实施例2:一种防穿刺鞋底,如图1所示,包括上胶底层1、下胶底层2和炭纤布3, 所述上胶底层1、下胶底层2的组分为:
标胶 80份;
顺丁橡胶 40份;
炭黑N200 55份;
白油 25份;
古马隆树脂 15份;
氧化锌 7份;
硬脂酸 2份;
促进剂M 1份;
促进剂DM 2份;
防老剂4010 1.5份;
防老剂RD 1.5份;
硫磺 2.4份;
促进剂TT 0.03份
以重量份计,
将上胶底层1、下胶底层2和炭纤布3冲压成形状一致的片料;将制好的上胶底层1、下胶底层2刷上胶浆,送到烘房停放24小时,烘房温度45℃;将炭纤布3放在上胶底层1和下胶底层2中间,与上胶底层1、下胶底层2粘连在一起,放在模具中;将模具送入硫化机硫化,硫化机温度160℃,时间400秒,机台压力150Mpa,得到所述防穿刺鞋底。
实施例3:一种防穿刺鞋底,如图1所示,包括上胶底层1、下胶底层2和炭纤布3, 所述上胶底层1、下胶底层2的组分为:
标胶 70份;
顺丁橡胶 30份;
炭黑N200 52份;
白油 20份;
古马隆树脂 10份;
氧化锌 5份;
硬脂酸 1.5份;
促进剂M 0.8份;
促进剂DM 1.5份;
防老剂4010 1份;
防老剂RD 1份;
硫磺 2.2份;
促进剂TT 0.02份;
以重量份计,
将上胶底层1、下胶底层2和炭纤布3冲压成形状一致的片料;将制好的上胶底层1、下胶底层2刷上胶浆,送到烘房停放24小时,烘房温度40℃;将炭纤布3放在上胶底层1和下胶底层2中间,与上胶底层1、下胶底层2粘连在一起,放在模具中;将模具送入硫化机硫化,硫化机温度150℃,时间370秒,机台压力145Mpa,得到所述防穿刺鞋底。
Claims (4)
1.一种防穿刺鞋底,其特征在于包括上胶底层、下胶底层和炭纤布,所述炭纤布位于所述上胶底层和下胶底层之间,与上胶底层、下胶底层粘连。
2.根据权利要求1所述的防穿刺鞋底,其特征在于:所述上胶底层、下胶底层包括如下组分:
标胶 60~80份;
顺丁橡胶 20~40份;
炭黑N200 50~55份;
白油 15~25份;
古马隆树脂 5~15份;
氧化锌 3~7份;
硬脂酸 1~2份;
促进剂M 0.5~1份;
促进剂DM 1~2份;
防老剂4010 0.5~1.5份;
防老剂RD 0.5~1.5份;
硫磺 2~2.4份;
促进剂TT 0.01~0.03份
以重量份计。
3.根据权利要求2所述的防穿刺鞋底,其特征在于:所述上胶底层、下胶底层包括如下组分:
标胶 70份;
顺丁橡胶 30份;
炭黑N200 52份;
白油 20份;
古马隆树脂 10份;
氧化锌 5份;
硬脂酸 1.5份;
促进剂M 0.8份;
促进剂DM 1.5份;
防老剂4010 1份;
防老剂RD 1份;
硫磺 2.2份;
促进剂TT 0.02份。
4.根据权利要求1~3任意一项所述的防穿刺鞋底的制造方法,其特征在于包括以下步骤:
①:将上胶底层、下胶底层冲压成各尺码的片料,炭纤布冲压成与上胶底层、下胶底层一致的形状;
②:将制好的上胶底层、下胶底层刷上胶浆,送到烘房停放24小时,烘房温度35~45℃;
③:将炭纤布放在上胶底层和下胶底层中间,与上胶底层、下胶底层粘连在一起,放在模具中;
④:将模具送入硫化机硫化,硫化机温度140~160℃,时间350~400秒,机台压力140~150Mpa。