CN103943218B - 传感器用电线电缆 - Google Patents
传感器用电线电缆 Download PDFInfo
- Publication number
- CN103943218B CN103943218B CN201410175228.4A CN201410175228A CN103943218B CN 103943218 B CN103943218 B CN 103943218B CN 201410175228 A CN201410175228 A CN 201410175228A CN 103943218 B CN103943218 B CN 103943218B
- Authority
- CN
- China
- Prior art keywords
- layer
- coated
- groups
- braiding
- mineral filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种传感器用电线电缆，包括有六根导线，六根导线两两组成一组形成三组线芯，每组线芯内的两根导线外分别包覆有氟塑料绝缘层，三组线芯外分部包覆有由纺织包带重叠绕包构成的绕包层，三组线芯之间设有多模光纤束，所述的三组线芯以多模光纤束外包覆有高阻燃纤维带编织隔离层，高阻燃纤维带编织隔离层外包覆有胶带粘连层，胶带粘连层外依次包覆有镀锡铜丝编织构成的屏蔽层、涤纶丝编织构成的抗撕裂层及外护套层；胶带粘连层与镀锡铜丝编织构成的屏蔽层之间填充有耐高温氧化镁陶瓷粉末。本发明结构改进简单，设有绕包隔离屏蔽层，屏蔽效果好，信号传输安全，且设有抗撕裂层使得线缆整体的抗压性强。
Description
技术领域：
本发明涉及电缆，尤其涉及一种传感器用电线电缆。
背景技术：
传感器是一种检测装置，能感受到被测量的信息，并能将感受到的信息，按一定规律变换成为电信号或其他所需形式的信息输出，以满足信息的传输、处理、存储、显示、记录和控制等要求。因而对于传感器用电线电缆，要求其信号传输稳定则需要电线电缆具有好的隔离屏蔽效果，且电线电缆本身具有一定的抗压力性，保证使用寿命长。传统的电缆护套料存在着耐水性差的缺点。
发明内容：
本发明所要解决的技术问题是提供一种传感器用电线电缆，其结构改进简单，设有绕包隔离屏蔽层，屏蔽效果好，信号传输安全，且设有抗撕裂层使得线缆整体的抗压性强。本发明的电缆外护套料耐水性好。
为解决上述技术问题，本发明采用的技术方案是：
一种传感器用电线电缆，包括有六根导线，其特征在于：所述的六根导线两两组成一组形成三组线芯，所述每组线芯内的两根导线外分别包覆有氟塑料绝缘层，所述三组线芯外分部包覆有由纺织包带重叠绕包构成的绕包层，所述三组线芯之间设有多模光纤束，所述的三组线芯以多模光纤束为中心绞合成束且外包覆有高阻燃纤维带编织隔离层，所述的高阻燃纤维带编织隔离层外包覆有胶带粘连层，所述的胶带粘连层外依次包覆有镀锡铜丝编织构成的屏蔽层、涤纶丝编织构成的抗撕裂层及外护套层；所述的胶带粘连层与镀锡铜丝编织构成的屏蔽层之间填充有耐高温氧化镁陶瓷粉末，耐高温氧化镁陶瓷粉末中有钢绳。
所述的外护套层材料由以下重量份的原料制成：高密度聚乙烯65-85、聚苯硫醚15-25、聚对苯二甲酸乙二醇酯10-20、三氧化二锑12-18、硼酸锌5-10、炭黑N66020-30、氧化聚乙烯蜡3-5、钙锌复合稳定剂1-2、钛白粉4-6、轻质碳酸钙10-15、硬脂酸2-3、改性矿物填料8-16、对苯二甲酸二辛酯10-15、癸二酸二正丁酯5-10、蓖麻油6-12、对羟基苯甲酸甲酯2-4、抗氧剂10351-2；
所述改性矿物填料的制备方法如下：a、按重量比5-10:3-6:2-4:1称取硅灰石、高岭土、叶腊石、铝矾土混合均匀，粉碎，过200-300目筛，650-750℃煅烧20-30min，自然冷却至室温；b、将上述煅烧处理的复合矿物填料加水打浆制成浓度为35-45％的悬浮液，用浓度为15-20％的盐酸溶液调节PH至4-5，水浴加热至70-80℃,1500-2000rpm高速研磨10-15min，然后用浓度为10-15％的氢氧化钠溶液中和至中性，静置20-30min，过滤，滤渣用蒸馏水洗涤2-3次，烘干后加入混合机中，在500-1000rpm高速搅拌下，取相当于复合矿物填料重量3-5％的甲氧基聚乙二醇单甲基丙烯酸酯、0.5-1％的双(二辛氧基焦磷酸酯基)乙撑钛酸酯、2-4％的聚马来酸混合均匀后以雾状或液滴态缓缓加入复合矿物填料中，在40-60℃温度下搅拌10-20min，烘干；c、取相当于复合矿物填料重量30-40％的乙烯-醋酸乙烯共聚物、25-35％的聚酯型聚氨酯、3-5％的双季戊四醇辛醇酯、2-4％的2,4,4’-三氯-2’-羟基二苯醚、4-6％的硬脂酸丁酯与步骤b处理的复合矿物填料混合均匀后一同投入双螺杆挤出机进行熔融共混，然后挤出造粒，自然冷却至室温，即为改性复合矿物填料。
所述的外护套层材料的制备方法，包括以下步骤：
(1)将高密度聚乙烯、聚苯硫醚、聚对苯二甲酸乙二醇酯投入捏合机内混合均匀，然后加入对苯二甲酸二辛酯、癸二酸二正丁酯搅拌片刻，待增塑剂被基本吸收后，加入钙锌复合稳定剂、氧化聚乙烯蜡、硬脂酸，靠摩擦热使料温升到75-85℃，再加入余下原料，料温升至95-105℃时，将料卸到冷却混合机中降温，至40-45℃以下时出料；
(2)将上述捏合好的原料投入双螺杆挤出机中挤出造粒，螺杆转速40-60r/min，加工温度为145-175℃；
(3)经计量后包装即可。
本发明的优点是：
本发明结构改进简单，设有绕包隔离屏蔽层，屏蔽效果好，信号传输安全，且设有抗撕裂层使得线缆整体的抗压性强。本发明电缆外护套料吸水率低，耐水性好,收缩率低，尺寸稳定性好，耐腐蚀性能好，且具有防霉菌功能。
附图说明：
图1为本发明的结构示意图。
具体实施方式：
参见图1，一种传感器用电线电缆，包括有六根导线1，所述的六根导线1两两组成一组形成三组线芯，所述每组线芯内的两根导线1外分别包覆有氟塑料绝缘层2，所述三组线芯外分部包覆有由纺织包带重叠绕包构成的绕包层3，所述三组线芯之间设有多模光纤束4，所述的三组线芯以多模光纤束为中心绞合成束且外包覆有高阻燃纤维带编织隔离层5，所述的高阻燃纤维带编织隔离层5外包覆有胶带粘连层6，所述的胶带粘连层6外依次包覆有镀锡铜丝编织构成的屏蔽层7、涤纶丝编织构成的抗撕裂层8及外护套层9；所述的胶带粘连层6与镀锡铜丝编织构成的屏蔽层7之间填充有耐高温氧化镁陶瓷粉末10，耐高温氧化镁陶瓷粉末10中有钢绳11。
所述的外护套层9材料由以下重量(kg)的原料制成：高密度聚乙烯75、聚苯硫醚15、聚对苯二甲酸乙二醇酯10、三氧化二锑14、硼酸锌8、炭黑N66025、氧化聚乙烯蜡4、钙锌复合稳定剂1.5、钛白粉5、轻质碳酸钙12、硬脂酸2.5、改性矿物填料12、对苯二甲酸二辛酯10、癸二酸二正丁酯8、蓖麻油9、对羟基苯甲酸甲酯3、抗氧剂10351；
所述改性矿物填料的制备方法如下：a、按重量比6:3:2:1称取硅灰石、高岭土、叶腊石、铝矾土混合均匀，粉碎，过200目筛，650℃煅烧20min，自然冷却至室温；b、将上述煅烧处理的复合矿物填料加水打浆制成浓度为45％的悬浮液，用浓度为20％的盐酸溶液调节PH至4.5，水浴加热至70℃,1500rpm高速研磨15min，然后用浓度为15％的氢氧化钠溶液中和至中性，静置20min，过滤，滤渣用蒸馏水洗涤3次，烘干后加入混合机中，在1000rpm高速搅拌下，取相当于复合矿物填料重量3％的甲氧基聚乙二醇单甲基丙烯酸酯、0.5％的双(二辛氧基焦磷酸酯基)乙撑钛酸酯、2％的聚马来酸混合均匀后以雾状或液滴态缓缓加入复合矿物填料中，在60℃温度下搅拌10min，烘干；c、取相当于复合矿物填料重量35％的乙烯-醋酸乙烯共聚物、30％的聚酯型聚氨酯、4％的双季戊四醇辛醇酯、3％的2,4,4’-三氯-2’-羟基二苯醚、56％的硬脂酸丁酯与步骤b处理的复合矿物填料混合均匀后一同投入双螺杆挤出机进行熔融共混，然后挤出造粒，自然冷却至室温，即为改性复合矿物填料。
所述的外护套层9材料的制备方法，包括以下步骤：
(1)将高密度聚乙烯、聚苯硫醚、聚对苯二甲酸乙二醇酯投入捏合机内混合均匀，然后加入对苯二甲酸二辛酯、癸二酸二正丁酯搅拌片刻，待增塑剂被基本吸收后，加入钙锌复合稳定剂、氧化聚乙烯蜡、硬脂酸，靠摩擦热使料温升到75-85℃，再加入余下原料，料温升至95-105℃时，将料卸到冷却混合机中降温，至40-45℃以下时出料；
(2)将上述捏合好的原料投入双螺杆挤出机中挤出造粒，螺杆转速40-60r/min，加工温度为145-175℃；
(3)经计量后包装即可。
经检测，制得的所述的外护套层9材料的性能结果如下表：
。
Claims (2)
1.一种传感器用电线电缆，包括有六根导线，其特征在于：所述的六根导线两两组成一组形成三组线芯，所述每组线芯内的两根导线外分别包覆有氟塑料绝缘层，所述三组线芯外分部包覆有由纺织包带重叠绕包构成的绕包层，所述三组线芯之间设有多模光纤束，所述的三组线芯以多模光纤束为中心绞合成束且外包覆有高阻燃纤维带编织隔离层，所述的高阻燃纤维带编织隔离层外包覆有胶带粘连层，所述的胶带粘连层外依次包覆有镀锡铜丝编织构成的屏蔽层、涤纶丝编织构成的抗撕裂层及外护套层；所述的胶带粘连层与镀锡铜丝编织构成的屏蔽层之间填充有耐高温氧化镁陶瓷粉末，耐高温氧化镁陶瓷粉末中有钢绳；
所述的外护套层材料 由以下重量份的原料制成：高密度聚乙烯 65-85、聚苯硫醚 15-25、聚对苯二甲酸乙二醇酯 10-20、三氧化二锑 12-18、硼酸锌 5-10、炭黑N660 20-30、氧化聚乙烯蜡 3-5、钙锌复合稳定剂 1-2、钛白粉 4-6、轻质碳酸钙 10-15、硬脂酸 2-3、改性矿物填料 8-16、对苯二甲酸二辛酯 10-15、癸二酸二正丁酯 5-10、蓖麻油 6-12、对羟基苯甲酸甲酯 2-4、抗氧剂1035 1-2；
所述改性矿物填料的制备方法如下：
a、按重量比5-10:3-6:2-4:1称取硅灰石、高岭土、叶腊石、铝矾土混合均匀，粉碎，过200-300目筛，650-750℃煅烧20-30min，自然冷却至室温；
b、将上述煅烧处理的复合矿物填料加水打浆制成浓度为35-45%的悬浮液，用浓度为15-20%的盐酸溶液调节PH至4-5，水浴加热至70-80℃,1500-2000rpm高速研磨10-15min，然后用浓度为10-15%的氢氧化钠溶液中和至中性，静置20-30min，过滤，滤渣用蒸馏水洗涤2-3次，烘干后加入混合机中，在500-1000rpm高速搅拌下，取相当于复合矿物填料重量3-5%的甲氧基聚乙二醇单甲基丙烯酸酯、0.5-1%的双(二辛氧基焦磷酸酯基)乙撑钛酸酯、 2-4%的聚马来酸混合均匀后以雾状或液滴态缓缓加入复合矿物填料中，在40-60℃温度下搅拌10-20min，烘干；
c、取相当于复合矿物填料重量30-40%的乙烯-醋酸乙烯共聚物、25-35%的聚酯型聚氨酯、3-5%的双季戊四醇辛醇酯、2-4%的2 ,4 ,4’ -三氯 -2’ -羟基二苯醚、4-6%的硬脂酸丁酯与步骤b处理的复合矿物填料混合均匀后一同投入双螺杆挤出机进行熔融共混，然后挤出造粒，自然冷却至室温，即为改性复合矿物填料。
2.根据权利要求1所述的传感器用电线电缆，其特征在于所述的外护套层材料的制备方法，包括以下步骤：
（1）将高密度聚乙烯、聚苯硫醚、聚对苯二甲酸乙二醇酯投入捏合机内混合均匀，然后加入对苯二甲酸二辛酯、癸二酸二正丁酯搅拌片刻，待增塑剂被基本吸收后，加入钙锌复合稳定剂、氧化聚乙烯蜡、硬脂酸，靠摩擦热使料温升到75-85℃，再加入余下原料，料温升至95-105℃时，将料卸到冷却混合机中降温，至40-45℃以下时出料；
（2）将上述捏合好的原料投入双螺杆挤出机中挤出造粒，螺杆转速40-60r/min，加工温度为145-175℃；
（3）经计量后包装即可。