CN103937053A - 一种橡胶电容器密封垫及其制备方法 - Google Patents

一种橡胶电容器密封垫及其制备方法 Download PDF

Info

Publication number
CN103937053A
CN103937053A CN201410146397.5A CN201410146397A CN103937053A CN 103937053 A CN103937053 A CN 103937053A CN 201410146397 A CN201410146397 A CN 201410146397A CN 103937053 A CN103937053 A CN 103937053A
Authority
CN
China
Prior art keywords
parts
sealing gasket
mixing
rubber
attapulgite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410146397.5A
Other languages
English (en)
Other versions
CN103937053B (zh
Inventor
郑颖
褚诗泉
马永新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Jiangwei Precision Manufacturing Co Ltd
Original Assignee
Anhui Jiangwei Precision Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Jiangwei Precision Manufacturing Co Ltd filed Critical Anhui Jiangwei Precision Manufacturing Co Ltd
Priority to CN201410146397.5A priority Critical patent/CN103937053B/zh
Publication of CN103937053A publication Critical patent/CN103937053A/zh
Application granted granted Critical
Publication of CN103937053B publication Critical patent/CN103937053B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种橡胶电容器密封垫，其特征在于，由下列重量份的原料制成：丁腈橡胶286576-80、二辛酯10-12、硫磺2-3、防老剂RD1-2、促进剂DM1-2、炭黑33030-34、硅烷偶联剂KH5501～4、四硼酸钠3-4、硬脂酸锌1.5-2.5、三甘醇二异辛酸酯5-8、羟基氟硅油3.5-4、石蜡2-4、改性凹凸棒土12-15；本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明配方合理，工艺简单，生产成本低，生产的密封垫具有良好的力学性能以及耐油性，经久耐用。

Description

一种橡胶电容器密封垫及其制备方法
技术领域
本发明涉及橡胶复合材料加工领域，特别是一种橡胶电容器密封垫及其制备方法。
背景技术
电容器通常简称为电容，是电子设备中大量使用的电子元件之一，广泛应用于电路的隔直通交、耦合、旁路、滤波、调谐回路、能量转换、控制等方面。电容器由壳体、电容芯子、端盖及接线端子组成，电容器壳体内装有浸渍介质，浸渍介质一般为植物油或矿物油，电容器的密封部位均设有密封垫或密封圈，由于电容器的工作环境千差万别，有的电容器需要在恶劣的环境下工作，电容器密封垫需要耐高温、耐寒、耐酸碱、耐盐雾等有不同要求。
发明内容
本发明的目的是提供一种橡胶电容器密封垫及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种橡胶电容器密封垫，由下列重量份的原料制成：丁腈橡胶286576-80、二辛酯10-12、硫磺2-3、防老剂RD1-2、促进剂DM1-2、炭黑33030-34、硅烷偶联剂KH5501～4、四硼酸钠3-4、硬脂酸锌1.5-2.5、三甘醇二异辛酸酯5-8、羟基氟硅油3.5-4、石蜡2-4、改性凹凸棒土12-15；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土30-34、二苯基甲烷二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯3-4、三聚磷酸钠5-6、玉石4-5、硅烷偶联剂KH-5501-2、碳化硅4-5、2，6-二叔丁基对甲酚1-2、吗啉1-2、硫醇丁基锡1-2、当归油1-2；制备方法是将凹凸棒土、玉石放混合入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述橡胶电容器密封垫，由以下具体步骤制成：将丁腈橡胶2865、二辛酯、三甘醇二异辛酸酯加入密炼机中，加热至80-85℃，混炼3-5min；然后升温至110-130℃，再加入硫磺、防老剂RD、促进剂DM、炭黑330、硅烷偶联剂KH550、四硼酸钠，混炼6-8min，再加入硬脂酸锌、羟基氟硅油、石蜡继续混炼4-6min；加入其余剩余成分混炼5-6min，即得本发明橡胶料。
本发明的优异效果是：本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明配方合理，工艺简单，生产成本低，生产的密封垫具有良好的力学性能以及耐油性，经久耐用。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种橡胶电容器密封垫，由下列重量份（公斤）的原料制成：丁腈橡胶286576、二辛酯10、硫磺2、防老剂RD1、促进剂DM1、炭黑33030、硅烷偶联剂KH5501、四硼酸钠3、硬脂酸锌1.5、三甘醇二异辛酸酯5、羟基氟硅油3.5、石蜡2、改性凹凸棒土12；
所述改性凹凸棒土由下列重量份（公斤）的原料制成：凹凸棒土30、二苯基甲烷二异氰酸酯3、二缩三丙二醇二丙烯酸酯3、三聚磷酸钠5、玉石4、硅烷偶联剂KH-5501、碳化硅4、2，6-二叔丁基对甲酚1、吗啉1、硫醇丁基锡1、当归油1；制备方法是将凹凸棒土、玉石放混合入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述橡胶电容器密封垫，由以下具体步骤制成：将丁腈橡胶2865、二辛酯、三甘醇二异辛酸酯加入密炼机中，加热至80-85℃，混炼3-5min；然后升温至110-130℃，再加入硫磺、防老剂RD、促进剂DM、炭黑330、硅烷偶联剂KH550、四硼酸钠，混炼6-8min，再加入硬脂酸锌、羟基氟硅油、石蜡继续混炼4-6min；加入其余剩余成分混炼5-6min，即得本发明橡胶料。
用本发明的耐腐蚀橡胶密封垫与普通胶料物理性能对比如下表。
从表中可以看出用本发明的橡胶密封垫产品，综合性能比较好。

Claims (2)

1.一种橡胶电容器密封垫，其特征在于，由下列重量份的原料制成：丁腈橡胶2865 76-80、二辛酯10-12、硫磺2-3、防老剂RD1-2、促进剂DM1-2、炭黑330 30-34、硅烷偶联剂KH550 1～4、四硼酸钠3-4、硬脂酸锌1.5-2.5、三甘醇二异辛酸酯5-8、羟基氟硅油 3.5-4、石蜡2-4、改性凹凸棒土12-15；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土30-34、二苯基甲烷二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯3-4、三聚磷酸钠5-6、玉石4-5、硅烷偶联剂KH-550 1-2、碳化硅4-5、2，6- 二叔丁基对甲酚1-2、吗啉1-2、硫醇丁基锡1-2、当归油1-2；制备方法是将凹凸棒土、玉石放混合入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
2.根据权利要求1所述橡胶电容器密封垫，其特征在于，由以下具体步骤制成：将丁腈橡胶2865、二辛酯、三甘醇二异辛酸酯加入密炼机中，加热至80-85℃，混炼3-5min；然后升温至110-130℃，再加入硫磺、防老剂RD、促进剂DM、炭黑330、硅烷偶联剂KH550、四硼酸钠，混炼6-8min，再加入硬脂酸锌、羟基氟硅油、石蜡继续混炼4-6min；加入其余剩余成分混炼5-6min，即得本发明橡胶料。
CN201410146397.5A 2014-04-12 2014-04-12 一种橡胶电容器密封垫及其制备方法 Expired - Fee Related CN103937053B (zh)