CN103613897A - 一种丁腈橡胶电容器密封垫及其制备方法 - Google Patents

一种丁腈橡胶电容器密封垫及其制备方法 Download PDF

Info

Publication number
CN103613897A
CN103613897A CN201310549547.2A CN201310549547A CN103613897A CN 103613897 A CN103613897 A CN 103613897A CN 201310549547 A CN201310549547 A CN 201310549547A CN 103613897 A CN103613897 A CN 103613897A
Authority
CN
China
Prior art keywords
parts
nitrile rubber
sealing pad
mixing
paracril
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310549547.2A
Other languages
English (en)
Inventor
杨爱军
张和平
王海松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Jiangwei Precision Manufacturing Co Ltd
Original Assignee
Anhui Jiangwei Precision Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Jiangwei Precision Manufacturing Co Ltd filed Critical Anhui Jiangwei Precision Manufacturing Co Ltd
Priority to CN201310549547.2A priority Critical patent/CN103613897A/zh
Publication of CN103613897A publication Critical patent/CN103613897A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种丁腈橡胶电容器密封垫，其特征在于，由下列重量份的原料制成：丁腈橡胶334580-85、防老剂SP2-3、防老剂MB1-2、硬脂酸2-3、硫磺粉1-2、棕榈蜡5-7、氧化锌2-3、促进剂TMTD1-2、二乙烯基三胺0.4-0.7、水滑石粉14-18、磷酸二氢铵1-2、硅橡胶15-25、碳黑N33045-50、甲基丙烯酸甲酯5-15、改性凹凸棒土12-15；本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明密封垫工艺性能好，工艺简单，生产成本低，耐磨、耐油性能好，具有良好的经济效益以及市场前景性。

Description

一种丁腈橡胶电容器密封垫及其制备方法
技术领域
本发明涉及橡胶复合材料加工领域，特别是一种丁腈橡胶电容器密封垫及其制备方法。
背景技术
电容器通常简称为电容，是电子设备中大量使用的电子元件之一，广泛应用于电路的隔直通交、耦合、旁路、滤波、调谐回路、能量转换、控制等方面。电容器由壳体、电容芯子、端盖及接线端子组成，电容器壳体内装有浸渍介质，浸渍介质一般为植物油或矿物油，电容器的密封部位均设有密封垫或密封圈，由于电容器的工作环境千差万别，有的电容器需要在恶劣的环境下工作，电容器密封垫需要耐高温、耐寒、耐酸碱、耐盐雾等有不同要求。
发明内容
本发明的目的是提供一种丁腈橡胶电容器密封垫及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种丁腈橡胶电容器密封垫，由下列重量份的原料制成：丁腈橡胶334580-85、防老剂SP2-3、防老剂MB1-2、硬脂酸2-3、硫磺粉1-2、棕榈蜡5-7、氧化锌2-3、促进剂TMTD1-2、二乙烯基三胺0.4-0.7、水滑石粉14-18、磷酸二氢铵1-2、硅橡胶15-25、碳黑N33045-50、甲基丙烯酸甲酯5-15、改性凹凸棒土12-15；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土30-35、1,6-己二异氰酸酯4-5、二缩三丙二醇二丙烯酸酯2-3、氧化锌5-6、玉石4-5、3-氨丙基三甲氧基硅烷2-3、氮化铝粉4-5、秸秆灰烬1-2、吗啉1-2、二甲基氧化锡1-2、茶多酚1-2；制备方法是将凹凸棒土、玉石混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述丁腈橡胶电容器密封垫，由以下具体步骤制成：将丁腈橡胶3345、防老剂SP、防老剂MB、硬脂酸、甲基丙烯酸甲酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-130℃，再加入硫磺粉、棕榈蜡、氧化锌、促进剂TMTD、二乙烯基三胺，混炼6-8min，再加入水滑石粉、磷酸二氢铵、碳黑N330继续混炼4-6min；加入其余剩余成分混炼6-8min，即得本发明橡胶材料。
本发明的优异效果是：本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明密封垫工艺性能好，工艺简单，生产成本低，耐磨、耐油性能好，具有良好的经济效益以及市场前景性。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种丁腈橡胶电容器密封垫，由下列重量份（公斤）的原料制成：丁腈橡胶334580、防老剂SP2、防老剂MB1、硬脂酸2、硫磺粉1、棕榈蜡5、氧化锌2、促进剂TMTD1、二乙烯基三胺0.4、水滑石粉14、磷酸二氢铵1、硅橡胶15、碳黑N33045、甲基丙烯酸甲酯5、改性凹凸棒土12；
所述改性凹凸棒土由下列重量份（公斤）的原料制成：凹凸棒土30、1,6-己二异氰酸酯4、二缩三丙二醇二丙烯酸酯2、氧化锌5、玉石4、3-氨丙基三甲氧基硅烷2、氮化铝粉4、秸秆灰烬1、吗啉1、二甲基氧化锡1、茶多酚1；制备方法是将凹凸棒土、玉石混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述丁腈橡胶电容器密封垫，由以下具体步骤制成：将丁腈橡胶3345、防老剂SP、防老剂MB、硬脂酸、甲基丙烯酸甲酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-130℃，再加入硫磺粉、棕榈蜡、氧化锌、促进剂TMTD、二乙烯基三胺，混炼6-8min，再加入水滑石粉、磷酸二氢铵、碳黑N330继续混炼4-6min；加入其余剩余成分混炼6-8min，即得本发明橡胶材料。
用本发明的耐腐蚀橡胶密封垫与普通胶料物理性能对比如下表。
Figure BDA0000409432890000031
从表中可以看出用本发明的橡胶密封垫产品，综合性能比较好。

Claims (2)

1.一种丁腈橡胶电容器密封垫，其特征在于，由下列重量份的原料制成：丁腈橡胶3345 80-85、防老剂SP2-3、防老剂MB 1-2、硬脂酸2-3、硫磺粉1-2、棕榈蜡5-7、氧化锌2-3、促进剂TMTD 1-2、二乙烯基三胺0.4-0.7、水滑石粉14-18、磷酸二氢铵1-2、硅橡胶15-25、碳黑N330 45-50、甲基丙烯酸甲酯5-15、改性凹凸棒土12-15；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土30-35、1,6-己二异氰酸酯4-5、二缩三丙二醇二丙烯酸酯2-3、氧化锌5-6、玉石4-5、3-氨丙基三甲氧基硅烷2-3、氮化铝粉4-5、秸秆灰烬1-2、吗啉1-2、二甲基氧化锡1-2、茶多酚1-2；制备方法是将凹凸棒土、玉石混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
2.根据权利要求1所述丁腈橡胶电容器密封垫，其特征在于，由以下具体步骤制成：将丁腈橡胶3345、防老剂SP、防老剂MB、硬脂酸、甲基丙烯酸甲酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-130℃，再加入硫磺粉、棕榈蜡、氧化锌、促进剂TMTD、二乙烯基三胺，混炼6-8min，再加入水滑石粉、磷酸二氢铵、碳黑N330继续混炼4-6min；加入其余剩余成分混炼6-8min，即得本发明橡胶材料。
CN201310549547.2A 2013-11-06 2013-11-06 一种丁腈橡胶电容器密封垫及其制备方法 Pending CN103613897A (zh)