CN103924748B - 一种生态保温屋面施工方法 - Google Patents

一种生态保温屋面施工方法 Download PDF

Info

Publication number
CN103924748B
CN103924748B CN201410138865.4A CN201410138865A CN103924748B CN 103924748 B CN103924748 B CN 103924748B CN 201410138865 A CN201410138865 A CN 201410138865A CN 103924748 B CN103924748 B CN 103924748B
Authority
CN
China
Prior art keywords
reinforcement net
bamboo
silicon calcium
roofing
bamboo reinforcement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410138865.4A
Other languages
English (en)
Other versions
CN103924748A (zh
Inventor
葛加君
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Tianyi Construction Engineering Co Ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410138865.4A priority Critical patent/CN103924748B/zh
Publication of CN103924748A publication Critical patent/CN103924748A/zh
Application granted granted Critical
Publication of CN103924748B publication Critical patent/CN103924748B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种生态保温屋面施工方法,包括碳硅钙材料制作、生物胶制作、竹筋网制作、屋面模板安装、竹筋网铺设、浇筑、保养、拆模、粘贴铝锡锑合金卷材等步骤。本发明不仅能够就地取材,节约资源,而且施工操作方便,又且起到节能保温作用;施工方法具有集成性技术特点,现浇生态保温屋面施工方法中采集了碳硅钙材料制作技术与现浇屋面模板安装技术,现浇屋面混凝土技术,屋面保温施工技术。本发明适用于不同区域房屋建筑,不同类型房屋建筑,不同用途房屋建筑。

Description

一种生态保温屋面施工方法
技术领域
本发明涉及一种现浇生态保温屋面施工方法。
背景技术
屋面保温是房屋建筑保温的核心部分,而屋面保温技术,目前国内外采用松散保温材料包括膨胀烧石,膨胀珍珠岩,高炉熔渣等和板状保温材料包括泡沫塑料类板材,微孔混凝土壳板材,膨胀烧石板材,膨胀珍珠岩板材,当然采用以上保温材料进行屋面保温施工起到一定效果,但材料资源比较少,成本较高。
发明内容
本发明的目的在于提供一种施工方便,节能保温的生态保温屋面施工方法。
本发明的技术解决方案是:
一种生态保温屋面施工方法,其特征是:包括下列步骤:
(1)碳硅钙材料制作
碳硅钙材料为一种生态性材料,是由秸秆草丝、木碳粉、泥土粉、石灰粉组成;秸秆草丝的长度≤4mm,细度为1mm以内,秸秆草丝含水率≤5%;木碳粉采用木竹烧制成木碳,木碳通过粉碎过筛,细度≤1mm;泥土粉采用普通黄土、砂土或粘土,晒干或烘干后进行碾磨过筛,细度为微米级;石灰粉通过过筛,细度为微米级;当上述原材料处理加工后,按秸秆草丝︰木碳粉︰泥土粉︰石灰粉=25︰13︰32︰30的重量比进行均匀搅拌,形成碳硅钙材料,装袋备用;
(2)生物胶制作:生物胶是由糯米、小麦粉、榆树皮粉组成;先将糯米进行粉碎成粉,然后按糯米粉:小麦粉:榆树皮粉=45︰42︰13的重量比进行配置,配置后加水,每1kg混合粉剂加水100公斤,进行水煮,并不断搅动,直至煮沸后30分钟,成胶状,装桶,密封待用;
(3)竹筋网制作:竹筋网制作材料选用5年生青竹,削成竹片,竹片厚度为3mm,宽度为10-15mm,采用十字穿编法,网眼规格为50-60mm;
(4)屋面模板安装:当建筑工程主体结束后,进行屋面模板安装;
(5)竹筋网铺设:竹筋网铺设采用满铺法,搭接处≥50mm,竹筋网铺设时在底模板上放置支撑体,使竹筋网在浇筑层中间位置;
(6)浇筑:浇筑前将碳硅钙材料与粒径为20-30mm的骨料、生物胶及水按碳硅钙材料:骨料:生物胶:水=35︰40︰10︰15的重量比进行配置,均匀搅拌,然后投料浇筑,并振捣密实;所述骨料为石子和建筑垃圾块,石子和建筑垃圾块的重量比例为1:2;
(7)保养:当屋面浇筑后应进行保养,保养时期为15天以上,保养期间设置覆盖物,应避免雨害、冻害、晒害;
(8)拆模:当生态混凝土屋面浇筑保养期满后进行拆模;
(9)粘贴铝锡锑合金卷材:采用焊缝法与粘胶式在浇筑的生态保温屋面体上粘贴铝锡锑合金卷材,铺设时平实、不空鼓、缝口<5mm。
本发明不仅能够就地取材,节约资源,而且施工操作方便,又且起到节能保温作用;施工工法,具有集成性技术特点,现浇生态保温屋面施工工法中采集了碳硅钙材料制作技术与现浇屋面模板安装技术,现浇屋面混凝土技术,屋面保温施工技术。本发明适用于不同区域房屋建筑,不同类型房屋建筑,不同用途房屋建筑。
下面结合实施例对本发明作进一步说明。
具体实施方式
一种生态保温屋面施工方法,包括下列步骤:
(1)碳硅钙材料制作
碳硅钙材料为一种生态性材料,是由秸秆草丝、木碳粉、泥土粉、石灰粉组成;秸秆草丝的长度≤4mm,细度为1mm以内,秸秆草丝含水率≤5%;木碳粉采用木竹烧制成木碳,木碳通过粉碎过筛,细度≤1mm;泥土粉采用普通黄土、砂土或粘土,晒干或烘干后进行碾磨过筛,细度为微米级;石灰粉通过过筛,细度为微米级;当上述原材料处理加工后,按秸秆草丝︰木碳粉︰泥土粉︰石灰粉=25︰13︰32︰30的重量比进行均匀搅拌,形成碳硅钙材料,装袋备用;
(2)生物胶制作:生物胶是由糯米、小麦粉、榆树皮粉组成;先将糯米进行粉碎成粉,然后按糯米粉:小麦粉:榆树皮粉=45︰42︰13的重量比进行配置,配置后加水,每1kg混合粉剂加水100公斤,进行水煮,并不断搅动,直至煮沸后30分钟,成胶状,装桶,密封待用;
(3)竹筋网制作:竹筋网制作材料选用5年生青竹,削成竹片,竹片厚度为3mm,宽度为10-15mm,采用十字穿编法,网眼规格为50-60mm;
(4)屋面模板安装:当建筑工程主体结束后,进行屋面模板安装;
(5)竹筋网铺设:竹筋网铺设采用满铺法,搭接处≥50mm,竹筋网铺设时在底模板上放置支撑体,使竹筋网在浇筑层中间位置;
(6)浇筑:浇筑前将碳硅钙材料与粒径为20-30mm的骨料、生物胶及水按碳硅钙材料:骨料:生物胶:水=35︰40︰10︰15的重量比进行配置,均匀搅拌,然后投料浇筑,并振捣密实;所述骨料为石子和建筑垃圾块,石子和建筑垃圾块的重量比例为1:2;
(7)保养:当屋面浇筑后应进行保养,保养时期为15天以上,保养期间设置覆盖物,应避免雨害、冻害、晒害;
(8)拆模:当生态混凝土屋面浇筑保养期满后进行拆模;
(9)粘贴铝锡锑合金卷材:采用焊缝法与粘胶式在浇筑的生态保温屋面体上粘贴铝锡锑合金卷材,铺设时平实、不空鼓、缝口<5mm。

Claims (1)

1.一种生态保温屋面施工方法,其特征是:包括下列步骤:
(1)碳硅钙材料制作
碳硅钙材料为一种生态性材料,是由秸秆草丝、木碳粉、泥土粉、石灰粉组成;秸秆草丝的长度≤4mm,细度为1mm以内,秸秆草丝含水率≤5%;木碳粉采用木竹烧制成木碳,木碳通过粉碎过筛,细度≤1mm;泥土粉采用普通黄土、砂土或粘土,晒干或烘干后进行碾磨过筛,细度为微米级;石灰粉通过过筛,细度为微米级;当上述原材料处理加工后,按秸秆草丝︰木碳粉︰泥土粉︰石灰粉=25︰13︰32︰30的重量比进行均匀搅拌,形成碳硅钙材料,装袋备用;
(2)生物胶制作:生物胶是由糯米、小麦粉、榆树皮粉组成;先将糯米进行粉碎成粉,然后按糯米粉:小麦粉:榆树皮粉=45︰42︰13的重量比进行配置,配置后加水,每1kg混合粉剂加水100公斤,进行水煮,并不断搅动,直至煮沸后30分钟,成胶状,装桶,密封待用;
(3)竹筋网制作:竹筋网制作材料选用5年生青竹,削成竹片,竹片厚度为3mm,宽度为10-15mm,采用十字穿编法,网眼规格为50-60mm;
(4)屋面模板安装:当建筑工程主体结束后,进行屋面模板安装;
(5)竹筋网铺设:竹筋网铺设采用满铺法,搭接处≥50mm,竹筋网铺设时在底模板上放置支撑体,使竹筋网在浇筑层中间位置;
(6)浇筑:浇筑前将碳硅钙材料与粒径为20-30mm的骨料、生物胶及水按碳硅钙材料:骨料:生物胶:水=35︰40︰10︰15的重量比进行配置,均匀搅拌,然后投料浇筑,并振捣密实;所述骨料为石子和建筑垃圾块,石子和建筑垃圾块的重量比例为1:2;
(7)保养:当屋面浇筑后应进行保养,保养时期为15天以上,保养期间设置覆盖物,应避免雨害、冻害、晒害;
(8)拆模:当生态混凝土屋面浇筑保养期满后进行拆模;
(9)粘贴铝锡锑合金卷材:采用焊缝法与粘胶式在浇筑的生态保温屋面体上粘贴铝锡锑合金卷材,铺设时平实、不空鼓、缝口<5mm。
CN201410138865.4A 2014-04-09 2014-04-09 一种生态保温屋面施工方法 Expired - Fee Related CN103924748B (zh)