CN103922702B - A kind of ceramic cup of glazing - Google Patents
A kind of ceramic cup of glazing Download PDFInfo
- Publication number
- CN103922702B CN103922702B CN201410139810.5A CN201410139810A CN103922702B CN 103922702 B CN103922702 B CN 103922702B CN 201410139810 A CN201410139810 A CN 201410139810A CN 103922702 B CN103922702 B CN 103922702B
- Authority
- CN
- China
- Prior art keywords
- glazing
- ceramic cup
- mud
- cup
- reed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A ceramic cup for glazing, be made up of the raw material of following weight percent: grey 5-20%, glacial drift rock 35-80% after the burning of unslaked lime raw ore 10-30%, the mud 5-15% planting reed, straw, each raw material weight per-cent sum is 100%; Described mud weight of planting reed is in butt.The ceramic cup of the glazing of the present invention, iron content is enriched, and plumbous and cadmium mass content is up to state standards≤0.3 ‰, does not contain harmful material, uses its splendid attire to contain the beverage of water, cup can with water molecule reaction, make the mouthfeel of beverage better.If with this cup splendid attire clear water, the mouthfeel of clear water more alcohol and.
Description
Technical field
The present invention relates to a kind of ceramic cup, especially relate to a kind of ceramic cup of glazing.
Background technology
Pottery take clay as the material and various goods that main raw material and various natural mineral pass through that pulverizing is mixing, shaping and calcining is obtained.People potter's clay be made in special kiln high-temperature firing article pottery.The traditional concept of pottery refers to all artificial Industrial products being raw material with Inorganic nonmetal mineral such as clays.The major production areas of pottery is the ground such as Jing Dezhen, Gao An, Fengcheng, Pingxiang, Foshan, Chaozhou, Dehua, Liling, Zibo.
Common pottery is that earth sintering forms, and in prior art, be a kind of processing of low side to the processing majority of pottery, the ceramic product processed generally only plays the effect of splendid attire product (especially food).In recent years, people more and more pay close attention to the outward appearance of ceramic product, but up to now, can not improve the ceramic product of Foods or drinks mouthfeel.
Summary of the invention
The technical problem to be solved in the present invention is, overcomes the deficiencies in the prior art, provides a kind of ceramic cup that can improve the glazing of Foods or drinks mouthfeel.
The technical scheme that the present invention solves the employing of its technical problem is, a kind of ceramic cup of glazing, be made up of the raw material of following weight percent: grey 5-20%, glacial drift rock 35-80% after the burning of unslaked lime raw ore 10-30%, the mud 5-15% planting reed, straw, each raw material weight per-cent sum is 100%; Described mud weight of planting reed is in butt.
Preferred weight percent is: grey 7-15%, glacial drift rock 46-71% after the burning of unslaked lime raw ore 15-25%, the mud 7-14% planting reed, straw.
Its preparation technology, comprises the following steps:
Glacial drift rock is crushed to 50-80 order, then ball milling 8-15 hour, then adds unslaked lime raw ore, planted the mud of reed, ash after straw burning, then ball milling 4-10 hour, control water content is 50-70wt%, obtains glaze water; Glazing is in the ceramic cup inwall sintered (outer wall also can glazing, but does not affect the mouthfeel of beverage or clear water etc.) again, and control glazed thickness is 0.05-0.15mm, at sintering temperature is 1000-1500 DEG C, sinter 10-15 hour.
The present invention adds the ash after straw burning, can increase the smooth finish of glaze layer; Add the mud of planting reed, the sticking power of glaze layer can be increased; Add unslaked lime raw ore, the temperature that after can reducing glazing, ceramic cup sinters.
The ceramic cup of the glazing of the present invention, iron content is enriched, and plumbous and cadmium mass content is up to state standards≤0.3 ‰, does not contain harmful material, uses its splendid attire to contain the beverage of water, cup can with water molecule reaction, make the mouthfeel of beverage better.If with this cup splendid attire clear water, the mouthfeel of clear water more alcohol and.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment 1
The ceramic cup of the glazing of the present embodiment, is made up of the raw material of following weight percent: ash 20%, glacial drift rock 55% after the burning of unslaked lime raw ore 10%, the mud 15% of planting reed, straw; Described mud weight of planting reed is in butt.
The ceramic cup of the glazing of the present embodiment, its preparation technology comprises the following steps:
Glacial drift rock is crushed to 50 orders, then ball milling 8 hours, then adds unslaked lime raw ore, planted the mud of reed, ash after straw burning, then ball milling 10 hours, control water content is 50wt%, obtains glaze water; Glazing is in the ceramic cup inwall sintered again, controls glazed thickness at 0.05mm, at sintering temperature is 1000 DEG C, sinters 15 hours.
The ceramic cup of the glazing of the present embodiment, iron content is enriched, and plumbous and cadmium mass content is up to state standards≤0.3 ‰, does not contain harmful material, uses its splendid attire to contain the beverage of water, cup can with water molecule reaction, make the mouthfeel of beverage better.If with this cup splendid attire clear water, the mouthfeel of clear water more alcohol and.
Embodiment 2
The ceramic cup of the glazing of the present embodiment, be made up of the raw material of following weight percent: ash 5%, glacial drift rock 70% after the burning of unslaked lime raw ore 20%, the mud 5% of planting reed, straw, described mud weight of planting reed is in butt.
The ceramic cup of the glazing of the present embodiment, its preparation technology comprises the following steps:
Glacial drift rock is crushed to 80 orders, then ball milling 15 hours, then adds unslaked lime raw ore, planted the mud of reed, ash after straw burning, then ball milling 10 hours, control water content is 70wt%, obtains glaze water; Glazing is in the ceramic cup inner and outer wall sintered again, controls glazed thickness at 0.15mm, at sintering temperature is 1500 DEG C, sinters 10 hours.
The ceramic cup of the glazing of the present embodiment, iron content is enriched, and plumbous and cadmium mass content is up to state standards≤0.3 ‰, does not contain harmful material, uses its splendid attire to contain the beverage of water, cup can with water molecule reaction, make the mouthfeel of beverage better.If with this cup splendid attire clear water, the mouthfeel of clear water more alcohol and.
Embodiment 3
The ceramic cup of the glazing of the present embodiment, be made up of the raw material of following weight percent: ash 10%, glacial drift rock 51% after the burning of unslaked lime raw ore 30%, the mud 9% of planting reed, straw, described mud weight of planting reed is in butt.
The ceramic cup of the glazing of the present embodiment, its preparation technology comprises the following steps:
Glacial drift rock is crushed to 60 orders, then ball milling 10 hours, then adds unslaked lime raw ore, planted the mud of reed, ash after straw burning, then ball milling 8 hours, control water content is 60wt%, obtains glaze water; Glazing is in the ceramic cup inwall sintered again, controls glazed thickness at 0.1mm, at sintering temperature is 1200 DEG C, sinters 12 hours.
The ceramic cup of the glazing of the present embodiment, iron content is enriched, and plumbous and cadmium mass content is up to state standards≤0.3 ‰, does not contain harmful material, uses its splendid attire to contain the beverage of water, cup can with water molecule reaction, make the mouthfeel of beverage better.If with this cup splendid attire clear water, the mouthfeel of clear water more alcohol and.
Embodiment 4
The ceramic cup of the glazing of the present embodiment, be made up of the raw material of following weight percent: ash 20%, glacial drift rock 35% after the burning of unslaked lime raw ore 30%, the mud 15% of planting reed, straw, described mud weight of planting reed is in butt.
The ceramic cup of the glazing of the present embodiment, its preparation technology comprises the following steps:
Glacial drift rock is crushed to 70 orders, then ball milling 14 hours, then adds unslaked lime raw ore, planted the mud of reed, ash after straw burning, then ball milling 9 hours, control water content is 65wt%, obtains glaze water; Glazing is in the ceramic cup inwall sintered again, controls glazed thickness at 0.12mm, at sintering temperature is 1400 DEG C, sinters 14 hours.
The ceramic cup of the glazing of the present embodiment, iron content is enriched, and plumbous and cadmium mass content is up to state standards≤0.3 ‰, does not contain harmful material, uses its splendid attire to contain the beverage of water, cup can with water molecule reaction, make the mouthfeel of beverage better.If with this cup splendid attire clear water, the mouthfeel of clear water more alcohol and.
Embodiment 5
The ceramic cup of the glazing of the present embodiment, be made up of the raw material of following weight percent: ash 5%, glacial drift rock 80% after the burning of unslaked lime raw ore 10%, the mud 5% of planting reed, straw, described mud weight of planting reed is in butt.
The ceramic cup of the glazing of the present embodiment, its preparation technology comprises the following steps:
Glacial drift rock is crushed to 65 orders, then ball milling 9 hours, then adds unslaked lime raw ore, planted the mud of reed, ash after straw burning, then ball milling 8 hours, control water content is 60wt%, obtains glaze water; Glazing is in the ceramic cup inwall sintered again, controls glazed thickness at 0.08mm, at sintering temperature is 1300 DEG C, sinters 12 hours.
The ceramic cup of the glazing of the present embodiment, iron content is enriched, and plumbous and cadmium mass content is up to state standards≤0.3 ‰, does not contain harmful material, uses its splendid attire to contain the beverage of water, cup can with water molecule reaction, make the mouthfeel of beverage better.If with this cup splendid attire clear water, the mouthfeel of clear water more alcohol and.
Claims (2)
1. the ceramic cup of a glazing, it is characterized in that, be made up of the raw material of following weight percent: grey 5-20%, glacial drift rock 35-80% after the burning of unslaked lime raw ore 10-30%, the mud 5-15% planting reed, straw, each raw material weight per-cent sum is 100%; Described mud weight of planting reed is in butt;
Its preparation method, comprises the following steps:
Glacial drift rock is crushed to 50-80 order, then ball milling 8-15 hour, then adds unslaked lime raw ore, planted the mud of reed, ash after straw burning, then ball milling 4-10 hour, control water content is 50-70wt%, obtains glaze water; Glazing is in the ceramic cup inwall sintered again, and control glazed thickness is 0.05-0.15mm, at sintering temperature is 1000-1500 DEG C, sinter 10-15 hour.
2. the ceramic cup of glazing according to claim 1, is characterized in that, is made up of the raw material of following weight percent: grey 7-15%, glacial drift rock 46-71% after the burning of unslaked lime raw ore 15-25%, the mud 7-14% planting reed, straw.