CN103911760B - The preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops - Google Patents
The preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops Download PDFInfo
- Publication number
- CN103911760B CN103911760B CN201410111562.3A CN201410111562A CN103911760B CN 103911760 B CN103911760 B CN 103911760B CN 201410111562 A CN201410111562 A CN 201410111562A CN 103911760 B CN103911760 B CN 103911760B
- Authority
- CN
- China
- Prior art keywords
- fabric
- speed
- preparation
- fiber crops
- ultra dense
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The preparation method who the present invention relates to the grey fabric of a kind of slim ultra dense windproof napping fiber crops, comprising: plush yarn is selected 100D/144F modified dacron, connection yarn is selected 75D/72F low elastic polyester filament, selects 36G large circle machine to weave; Idiographic flow comprises: join cylinder, dyeing, soft sizing, plucking, middle sizing, carding, cropping, water-proof finish, plucking, cropping, the final shaping. Technique of the present invention is simple, and cost is low, and the fabric obtaining is frivolous, have concurrently simultaneously comfortable and easy to wear, feel is fine and smooth, soft, smooth, final light base grammes per square metre 205g/m2, permeability CFM value 60-70, waterproof effect is more than 90 points, and after many these washings, waterproof effect still can reach 80 points, has a good application prospect.
Description
Technical field
The invention belongs to double-sided plush fabric field, particularly the preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops.
Background technology
Double-sided plush fabric, because it has good windproof, ventilative, soft, warming characteristic, is subject to consumer's happiness always deeplyLike. Along with the raising of people's quality of the life, the consumption demand of knitted double-sided velvet fabric is not met merely basic windproofHeat-preserving function. People improve constantly snugness of fit, Functional Requirement, impel people to adopt various new technologies to improveThe properties of fabric.
The windproof suede class fabric of grabbing on international market generally has two kinds at present, and one is composite material, and compound form has veryMany, be essentially thriple decker sandwich's structure, significantly improve the wind-proof performance of fabric by middle blooming; Another is closeSuede class, utilizes the density of fabric self to reach protection effect, grabs suede density by what improve fabric, increases the anti-of fabricWind performance. But two kinds of equal defectiveness of in the market this, though complex class fabric wind-proof performance is good, but compression performance andFeel is bad; Close suede class fabric is generally more thick and heavy, and grammes per square metre is all at 260g/m2Above.
Summary of the invention
Technical problem to be solved by this invention is to provide the preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops, the partyMethod technique is simple, and cost is low, and the fabric obtaining is frivolous, have concurrently simultaneously comfortable and easy to wear, feel is fine and smooth, soft, smooth,Whole light base grammes per square metre 205g/m2，Permeability CFM value 60-70, waterproof effect is more than 90 points, and after many these washings, waterproof is imitatedFruit still can reach 80 points, has a good application prospect.
The preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops of the present invention, comprising:
Plush yarn is selected 100D/144F modified dacron, and connection yarn is selected 75D/72F low elastic polyester filament, selects high plane No. 36GLarge circle machine is weaved; Idiographic flow comprises: join cylinder, dyeing, soft sizing, plucking, middle sizing, carding, cropping, anti-Water arrangement, plucking, cropping, the final shaping.
Described dyeing is: fabric is placed in to HTHP Jet Dyeing Machine, and bath raio is 1:10-30, adopts disperse dyesAnd cationic dyeing, add 2-5g/l saltcake, 1.0～2.0% high temperature levelling agents, 1.0～2.5g/l glacial acetic acid, 0.5～1.5g/lGlacial acetic acid, is warming up to 120-130 DEG C, running 20～60min; Be cooled to 80 DEG C of discharge opeings. Then fabric is carried out to reduction cleaning,Add 1.0～3.0g/l acidic reduction cleaner, be warming up to 70～90 DEG C and process 10～30min.
Described soft setting process is: fabric is padded to softening agent, enter forming machine, forming machine temperature arranges 130 DEG C, clothSpeed is 10-20m/min.
Described brushing process is: fabric is carried out to plucking 4 times, and looper speed is 120-150RPM, and staight needle speed is110-130RPM, cloth speed is 10-20m/min, and crimping bar speed is 280-320RPM, and clearer speed is 560-640RPM,Main rotor speed is 140-160RPM, and draw-out roller speed is 5-10m/min.
In the middle of described, setting process is: fabric is carried out to centre sizing, and forming machine temperature setting is set to 150-165 DEG C, and cloth speed is30-60m/min。
Described carding process is: fabric is carried out to carding, and looper speed is 40-60RPM, and staight needle speed is 40-60RPM,Cloth speed is 15-30m/min, and clearer speed is 560-640RPM, and main rotor speed is 140-160RPM.
Described cropping technique is: fabric is carried out to cropping, and cloth speed is 5-15m/min, and cutter speed is 800-1000RPM.
Described water-proof finish technique is: fabric is carried out to water-proofing treatment, and employing one is soaked one and rolled method, adds waterproofing agent while padding,Forming machine temperature setting is set to 150-165 DEG C, and cloth speed is 10-20m/min.
Described the final shaping technique is: fabric is carried out to the final shaping, and the front four casees temperature settings of forming machine are set to 150-160 DEG C,Rear four casees temperature are 170-178 DEG C, and cloth speed is 10-30m/min.
The object of the invention is a kind of slim windproof double-sided plush fabric of exploitation, adopts superfine fibre, uses high plane No. loom to weave,Solve special rear arrangement problem, developed the open air that integrates ultralight, windproof, ventilative, waterproof, warming, easy cleaningSportswear fabric, market prospects are wide. And outdoor exercises become the leisure way of the emerging fashion of developed country, leisureization, motionChange the trend that is leading global garment material consumption market, slim windproof double-sided plush product is just becoming the favorite in market.
Beneficial effect
Technique of the present invention is simple, and cost is low, and the fabric obtaining is frivolous, have concurrently simultaneously comfortable and easy to wear, feel is fine and smooth, soft,Smooth, final light base grammes per square metre 205g/m2, permeability CFM value 60-70, waterproof effect is more than 90 points, through many these washingsRear waterproof effect still can reach 80 points, has a good application prospect.
Detailed description of the invention
Below in conjunction with specific embodiment, further set forth the present invention. Should be understood that these embodiment are only for illustrating the present inventionBe not used in and limit the scope of the invention. In addition should be understood that after having read the content of the present invention's instruction art technology peopleMember can make various changes or modifications the present invention, and these equivalent form of values fall within equally the application's appended claims and limitScope.
Embodiment 1
Plush yarn is selected 100D/144F modified dacron, and connection yarn is selected 75D/72F low elastic polyester filament, selects 36G large circle machineWeave; Idiographic flow comprises: join cylinder, dyeing, soft sizing, plucking, middle sizing, carding, cropping, water-proof finish,Plucking, cropping, the final shaping.
(1) dyeing is: fabric is placed in to HTHP Jet Dyeing Machine, and bath raio is 1:10, adopts disperse dyes and sunIonic dye dyeing, adds 2g/l saltcake, 1.0% high temperature levelling agent, 1.0g/l glacial acetic acid, 0.5g/l glacial acetic acid, is warming up to120 DEG C, running 20min; Be cooled to 80 DEG C of discharge opeings. Then fabric is carried out to reduction cleaning, add 1.0g/l acidic reduction clearLotion, is warming up to 70 DEG C and processes 10～30min.
(2) soft setting process is: fabric is padded to softening agent, enter forming machine, forming machine temperature arranges 130 DEG C, and cloth speed is10m/min。
(3) brushing process is: fabric is carried out to plucking 4 times, and looper speed is 130RPM, and staight needle speed is 120RPM, clothSpeed is 10m/min, and crimping bar speed is 280RPM, and clearer speed is 560RPM, and main rotor speed is 140RPM,Draw-out roller speed is 5m/min.
(4) in the middle of, setting process is: fabric is carried out to centre sizing, and forming machine temperature setting is set to 150 DEG C, and cloth speed is 30m/min.(5) carding process is: fabric is carried out to carding, and looper speed is 40RPM, and staight needle speed is 40RPM, and cloth speed is15m/min, clearer speed is 560RPM, main rotor speed is 140RPM.
(6) cropping technique is: fabric is carried out to cropping, and cloth speed is 5m/min, and cutter speed is 800RPM.
(7) water-proof finish technique is: fabric is carried out to water-proofing treatment, and employing one is soaked one and rolled method, adds waterproofing agent while padding, fixedType machine temperature setting is set to 150 DEG C, and cloth speed is 10m/min.
(8) the final shaping technique is: fabric is carried out to the final shaping, and the front four casees temperature settings of forming machine are set to 150 DEG C, rear four casees temperatureDegree is 170 DEG C, and cloth speed is 10m/min.
Gained fabric light base grammes per square metre 205g/m2, permeability CFM value 60, waterproof effect is more than 90 points, through many these washingsRear waterproof effect still can reach 80 points, frivolous comfortable, soft fine and smooth.
Embodiment 2
Plush yarn is selected 100D/144F modified dacron, and connection yarn is selected 75D/72F low elastic polyester filament, selects 36G large circle machineWeave; Idiographic flow comprises: join cylinder, dyeing, soft sizing, plucking, middle sizing, carding, cropping, water-proof finish,Plucking, cropping, the final shaping.
(1) fabric is placed in to HTHP Jet Dyeing Machine, bath raio is 1:30, adopts disperse dyes and cationic dyeing,Add 5g/l saltcake, 2.0% high temperature levelling agent, 2.5g/l glacial acetic acid, 1.5g/l glacial acetic acid, be warming up to 130 DEG C, running 60min;Be cooled to 80 DEG C of discharge opeings. Then fabric is carried out to reduction cleaning, add 3.0g/l acidic reduction cleaner, be warming up to 90 DEG C and locateReason 30min.
(2) soft setting process is: fabric is padded to softening agent, enter forming machine, forming machine temperature arranges 130 DEG C, and cloth speed is20m/min。
(3) brushing process is: fabric is carried out to plucking 4 times, and looper speed is 150RPM, and staight needle speed is 130RPM, clothSpeed is 20m/min, and crimping bar speed is 320RPM, and clearer speed is 640RPM, and main rotor speed is 150RPM,Draw-out roller speed is 10m/min.
(4) in the middle of, setting process is: fabric is carried out to centre sizing, and forming machine temperature setting is set to 165 DEG C, and cloth speed is 60m/min.
(5) carding process is: fabric is carried out to carding, and looper speed is 60RPM, and staight needle speed is 60RPM, and cloth speed is30m/min, clearer speed is 640RPM, main rotor speed is 160RPM.
(6) cropping technique is: fabric is carried out to cropping, and cloth speed is 15m/min, and cutter speed is 1000RPM.
(7) water-proof finish technique is: fabric is carried out to water-proofing treatment, and employing one is soaked one and rolled method, adds waterproofing agent while padding, fixedType machine temperature setting is set to 150 DEG C, and cloth speed is 10m/min.
(8) the final shaping technique is: fabric is carried out to the final shaping, and the front four casees temperature settings of forming machine are set to 150 DEG C, rear four casees temperatureDegree is 170 DEG C, and cloth speed is 10m/min.
Gained fabric light base grammes per square metre 205g/m2, permeability CFM value 70, waterproof effect is more than 90 points, through many these washingsRear waterproof effect still can reach 80 points, frivolous comfortable, soft fine and smooth.
Claims (8)
1. a preparation method for the grey fabric of slim ultra dense windproof napping fiber crops, comprising:
Plush yarn is selected 100D/144F modified dacron, and connection yarn is selected 75D/72F low elastic polyester filament, selects 36G great circle wovenMake; Idiographic flow comprises: join cylinder, dyeing, soft sizing, plucking, middle sizing, carding, cropping, water-proof finish, drawHair, cropping, the final shaping; Wherein, dyeing is: fabric is placed in to HTHP Jet Dyeing Machine, and bath raio is 1:10-30,Adopt disperse dyes and cationic dyeing, add 2-5g/l saltcake, 1.0～2.0% high temperature levelling agents, 1.0～2.5g/l glacial acetic acid,0.5～1.5g/l glacial acetic acid, is warming up to 120-130 DEG C, running 20～60min; Be cooled to 80 DEG C of discharge opeings; Then fabric is carried outReduction cleaning, adds 1.0～3.0g/l acidic reduction cleaner, is warming up to 70～90 DEG C and processes 10～30min.
2. the preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops according to claim 1, is characterized in that: described softSoft setting process is: fabric is padded to softening agent, enter forming machine, forming machine temperature arranges 130 DEG C, and cloth speed is 10-20m/min.
3. the preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops according to claim 1, is characterized in that: described in drawHair technique is: fabric is carried out to plucking 4 times, and looper speed is 120-150RPM, and staight needle speed is 110-130RPM, cloth speedFor 10-20m/min, crimping bar speed is 280-320RPM, and clearer speed is 560-640RPM, and main rotor speed is140-160RPM, draw-out roller speed is 5-10m/min.
4. the preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops according to claim 1, is characterized in that: in describedBetween setting process be: fabric is carried out to centre sizing, and forming machine temperature setting is set to 150-165 DEG C, and cloth speed is 30-60m/min.
5. the preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops according to claim 1, is characterized in that: described combHair technique is: fabric is carried out to carding, and looper speed is 40-60RPM, and staight needle speed is 40-60RPM, and cloth speed is15-30m/min, clearer speed is 560-640RPM, main rotor speed is 140-160RPM.
6. the preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops according to claim 1, is characterized in that: described in cutHair technique is: fabric is carried out to cropping, and cloth speed is 5-15m/min, and cutter speed is 800-1000RPM.
7. the preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops according to claim 1, is characterized in that: described anti-Water finishing technique is: fabric is carried out to water-proofing treatment, and employing one is soaked one and rolled method, adds waterproofing agent, forming machine temperature setting while paddingBe set to 150-165 DEG C, cloth speed is 10-20m/min.
8. the preparation method of the grey fabric of a kind of slim ultra dense windproof napping fiber crops according to claim 1, is characterized in that: describedWhole setting process is: fabric is carried out to the final shaping, and the front four casees temperature settings of forming machine are set to 150-160 DEG C, and rear four casees temperature are170-178 DEG C, cloth speed is 10-30m/min.