CN103897506B - A kind of waterborne flame retardant anticorrosive paint - Google Patents
A kind of waterborne flame retardant anticorrosive paint Download PDFInfo
- Publication number
- CN103897506B CN103897506B CN201310521603.1A CN201310521603A CN103897506B CN 103897506 B CN103897506 B CN 103897506B CN 201310521603 A CN201310521603 A CN 201310521603A CN 103897506 B CN103897506 B CN 103897506B
- Authority
- CN
- China
- Prior art keywords
- parts
- flame retardant
- anticorrosive paint
- agent
- waterborne flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of waterborne flame retardant anticorrosive paint, the parts by weight of its each component are: benzene emulsion 10 ~ 13 parts, modified Nano diatomite in powder 4 ~ 7 parts, 3 ~ 6 parts, aluminium hydroxide, 12 ~ 15 parts, water, iron mica 5 ~ 8 parts, Synolac 3 ~ 6 parts, vinyl cyanide 12 ~ 15 parts, polyvinyl chloride (PVC) RESINS 4 ~ 6 parts, 11 ~ 16 parts, aminoresin, epoxy resin 1 ~ 4 part, silicone antifoam agent 2 ~ 4 parts, rust-preventive agent 5 ~ 8 parts, 5 ~ 8 parts, solidifying agent, non-blushing thinner 2 ~ 7 parts.Waterborne flame retardant anticorrosive paint of the present invention, has good corrosion resistance, and water-tolerant, flame retardant properties are good, to the strong adhesion of base material, and simultaneously environmental protection, free from environmental pollution, be environmental protection paint, be widely used in the antirust and protection decorative operation in the surface of iron structure.
Description
Technical field
The present invention relates to a kind of paint, particularly a kind of waterborne flame retardant anticorrosive paint.
Background technology
Along with the development of society, the enhancing of the environmental consciousness of people, aqueous paint is used by increasing people, aqueous paint is exactly take water as thinner, not containing the coating of organic solvent, not containing benzene,toluene,xylene, formaldehyde, free TDI toxic heavy metal, nontoxic non-stimulated smell, harmless, free from environmental pollution, paint film plentiful, sparkling and crystal-clear bright, snappiness good and it is water-fast to have, wear-resisting, ageing-resistant, color inhibition, fast drying, the feature such as easy to use.But the fire retardant performance that existing aqueous paint forms paint film is not fine, and poor water resistance, therefore needs to develop a kind of water-tolerant, the waterborne anti-rust paint of good flame resistance.
Summary of the invention
The object of this invention is to provide one and there is heat-resisting, flame retardant properties, and strong adhesion, the waterborne flame retardant anticorrosive paint that water tolerance is high.
For achieving the above object, the present invention is achieved by the following technical solutions: a kind of waterborne flame retardant anticorrosive paint, and the parts by weight of its each component are: benzene emulsion 10 ~ 13 parts, modified Nano diatomite in powder 4 ~ 7 parts, 3 ~ 6 parts, aluminium hydroxide, 12 ~ 15 parts, water, iron mica 5 ~ 8 parts, Synolac 3 ~ 6 parts, vinyl cyanide 12 ~ 15 parts, polyvinyl chloride (PVC) RESINS 4 ~ 6 parts, 11 ~ 16 parts, aminoresin, epoxy resin 1 ~ 4 part, silicone antifoam agent 2 ~ 4 parts, rust-preventive agent 5 ~ 8 parts, 5 ~ 8 parts, solidifying agent, non-blushing thinner 2 ~ 7 parts.
Further, described rust-preventive agent is by the mixture of a kind of in citric acid, nano silicon, zinc phosphate, zinc molybdate or at least two kinds.
Further, described solidifying agent is by polyamine or isocyanic ester or urethane.
Further, described non-blushing thinner is mixed according to the ratio of 1:3 by calcium oxide, iron powder.
The invention has the beneficial effects as follows: the invention provides a kind of waterborne flame retardant anticorrosive paint; there is good corrosion resistance; water-tolerant, flame retardant properties are good; to the strong adhesion of base material; environmental protection simultaneously; free from environmental pollution, be environmental protection paint, be widely used in the antirust and protection decorative operation in the surface of iron structure.
Embodiment
For understanding the present invention better; below by three embodiments, elaboration concrete is further done to the present invention; but unintelligible is limitation of the invention; for some nonessential improvement and adjustment that those skilled in the art does according to foregoing invention content, be also considered as dropping in protection scope of the present invention.
Embodiment 1
A kind of waterborne flame retardant anticorrosive paint of the present embodiment, the parts by weight of its each component are: benzene emulsion 10 ~ 13 parts, modified Nano diatomite in powder 4 parts, 3 parts, aluminium hydroxide, 12 parts, water, iron mica 5 parts, Synolac 3 parts, vinyl cyanide 12 parts, polyvinyl chloride (PVC) RESINS 4 parts, 11 parts, aminoresin, epoxy resin 1 part, silicone antifoam agent 2 parts, rust-preventive agent 5 parts, 5 parts, solidifying agent, non-blushing thinner 2 parts.
Described rust-preventive agent is by the mixture of a kind of in citric acid, nano silicon, zinc phosphate, zinc molybdate or at least two kinds.
Described solidifying agent is by polyamine or isocyanic ester or urethane.
Described non-blushing thinner is mixed according to the ratio of 1:3 by calcium oxide, iron powder.
Embodiment 2
A kind of waterborne flame retardant anticorrosive paint of the present embodiment, the parts by weight of its each component are: benzene emulsion 13 parts, modified Nano diatomite in powder 7 parts, 6 parts, aluminium hydroxide, 15 parts, water, iron mica 8 parts, Synolac 6 parts, vinyl cyanide 15 parts, polyvinyl chloride (PVC) RESINS 6 parts, 16 parts, aminoresin, epoxy resin 4 parts, silicone antifoam agent 4 parts, rust-preventive agent 8 parts, 8 parts, solidifying agent, non-blushing thinner 7 parts.
Described rust-preventive agent is by the mixture of a kind of in citric acid, nano silicon, zinc phosphate, zinc molybdate or at least two kinds.
Described solidifying agent is by polyamine or isocyanic ester or urethane.
Described non-blushing thinner is mixed according to the ratio of 1:3 by calcium oxide, iron powder.
Embodiment 3
A kind of waterborne flame retardant anticorrosive paint of the present embodiment, the parts by weight of its each component are: benzene emulsion 11 parts, modified Nano diatomite in powder 6 parts, 5 parts, aluminium hydroxide, 14 parts, water, iron mica 7 parts, Synolac 5 parts, vinyl cyanide 13 parts, polyvinyl chloride (PVC) RESINS 5 parts, 15 parts, aminoresin, epoxy resin 3 parts, silicone antifoam agent 3 parts, rust-preventive agent 6 parts, 7 parts, solidifying agent, non-blushing thinner 5 parts.
Described rust-preventive agent is by the mixture of a kind of in citric acid, nano silicon, zinc phosphate, zinc molybdate or at least two kinds.
Described solidifying agent is by polyamine or isocyanic ester or urethane.
Described non-blushing thinner is mixed according to the ratio of 1:3 by calcium oxide, iron powder.
Claims (3)
1. a waterborne flame retardant anticorrosive paint, is characterized in that, the parts by weight of its each component are:
Benzene emulsion 10 ~ 13 parts,
Modified Nano diatomite in powder 4 ~ 7 parts,
3 ~ 6 parts, aluminium hydroxide,
12 ~ 15 parts, water,
Iron mica 5 ~ 8 parts,
Synolac 3 ~ 6 parts,
Vinyl cyanide 12 ~ 15 parts,
Polyvinyl chloride (PVC) RESINS 4 ~ 6 parts,
11 ~ 16 parts, aminoresin,
Epoxy resin 1 ~ 4 part,
Silicone antifoam agent 2 ~ 4 parts,
Rust-preventive agent 5 ~ 8 parts,
5 ~ 8 parts, solidifying agent,
Non-blushing thinner 2 ~ 7 parts;
Described rust-preventive agent is by the mixture of a kind of in citric acid, nano silicon, zinc phosphate, zinc molybdate or at least two kinds.
2. a kind of waterborne flame retardant anticorrosive paint according to claim 1, is characterized in that, described solidifying agent is by polyamine or isocyanic ester or urethane.
3. a kind of waterborne flame retardant anticorrosive paint according to claim 1, is characterized in that, described non-blushing thinner is mixed according to the ratio of 1:3 by calcium oxide, iron powder.