CN112745722A - High-adhesion water-based vinylidene chloride metal paint and preparation method thereof - Google Patents
High-adhesion water-based vinylidene chloride metal paint and preparation method thereof Download PDFInfo
- Publication number
- CN112745722A CN112745722A CN202011606058.2A CN202011606058A CN112745722A CN 112745722 A CN112745722 A CN 112745722A CN 202011606058 A CN202011606058 A CN 202011606058A CN 112745722 A CN112745722 A CN 112745722A
- Authority
- CN
- China
- Prior art keywords
- vinylidene chloride
- weight
- parts
- resin
- metallic paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of corrosion prevention, and particularly relates to a preparation method of a high-adhesion waterborne vinylidene chloride metallic paint, which comprises a film forming substance, an auxiliary agent, an antirust pigment and a filler, wherein the film forming substance is a vinylidene chloride copolymer and a waterborne single-component epoxy resin, the vinylidene chloride copolymer accounts for 30-45 parts by weight of the total formula amount, and the waterborne single-component epoxy resin accounts for 5-20 parts by weight of the total formula amount. The metallic paint is environment-friendly and simple in construction; the film-forming material adopts vinylidene chloride resin and aqueous single-component epoxy resin, not only retains the excellent barrier property of the vinylidene chloride resin, but also has good adhesive force of the epoxy resin to a metal base material.
Description
Technical Field
The invention belongs to the technical field of corrosion prevention, and particularly relates to preparation of a high-adhesion water-based vinylidene chloride metal paint.
Background
The metal is subject to chemical, electrochemical or physical interaction with the environment medium in which the metal is located, so that the metal is deteriorated and deteriorated, namely metal corrosion, which is quite common. From a thermodynamic point of view, the corrosion of metals is generally a spontaneous process, except for very few precious metals (Au, Pt, etc.). It has been recognized that the metals used are rarely damaged by simple mechanical factors (such as tension, compression, impact, fatigue, fracture and abrasion) or other physical factors (such as thermal energy, light energy, etc.), and that the damage to most metallic materials is related to their corrosion factors, and therefore corrosion of metallic materials has become a significant problem that is not negligible today.
The epoxy resin has a large number of hydroxyl groups, can generate strong binding power with a metal substrate, and the thermosetting resin with the performance after the epoxy resin and the curing agent are crosslinked has good corrosion resistance.
The water-based vinylidene chloride copolymer emulsion does not contain organic solvent, has no pollution to the environment when being applied to the field of water-based paint, and does not cause harm to human bodies. The aqueous polyvinylidene chloride resin applied to the field of metal corrosion resistance has two basic performances, namely good barrier performance and strong adhesive force. The polyvinylidene chloride resin with high VDC content and better barrier property has poor emulsion stability and film forming property, low adhesive force with metal and easy shedding.
Compared with the waterborne epoxy resin, the waterborne PVDC coating omits the use of zinc powder paint in the construction process due to the excellent barrier property of PVDC, so that the cost of the whole coating is reduced.
Vinylidene chloride resin has good barrier properties, but has poor adhesion to metal surfaces. The water-based epoxy resin has good adhesive force with a metal base material, but the epoxy resin with strong corrosion resistance is generally double-component, and in the actual application process, the double-component coating has high requirements on construction technology and equipment, so that the application of the double-component coating is limited.
Patent document 1 provides an aqueous paint, a preparation method and an application thereof, wherein the aqueous resin comprises 30-50 parts by weight of aqueous acrylic acid modified epoxy emulsion, 2-15 parts by weight of silica sol and 5-10 parts by weight of polyvinylidene chloride emulsion, and the film forming substance in the invention also uses the compounding of aqueous vinylidene chloride and epoxy resin, but the content of the vinylidene chloride emulsion is less, and the epoxy resin is acrylic acid modified emulsion and is a main component, and the content of the vinylidene chloride emulsion is lower, so that excellent barrier property cannot be achieved;
patent document 2 discloses a water-based single-component rust-bearing construction steel structure primer and a preparation method and application thereof. Wherein the film-forming substance is high-solid water-based modified epoxy ester resin and water-based vinylidene chloride modified acrylic resin. The waterborne vinylidene chloride modified acrylic resin mainly comprises acrylic acid, and compared with macromolecular waterborne epoxy resin, the waterborne epoxy ester resin has smaller molecular weight and weaker relative corrosion resistance.
The polyvinylidene chloride metal protective paint is prepared by using polyvinylidene chloride emulsion and aqueous single-component epoxy resin as main film forming substances, and has high adhesive force and no influence on high barrier property.
Documents of the prior art
Patent document
Patent document 1: CN201710539364.0
Patent document 2: CN201710942453.X
Disclosure of Invention
Technical problem to be solved by the invention
The pure polyvinylidene chloride emulsion has good barrier property, but has poor adhesive force on metal base materials; the aqueous epoxy resin has a large amount of hydroxyl groups, can generate strong adhesive force with a metal substrate, but mainly comprises two components, is complex to construct and has higher requirements on equipment. The invention aims to obtain the single-component water-based metal protective paint with high adhesive force and high barrier property by taking polyvinylidene chloride resin and water-based epoxy resin as main film forming substances and complementing the advantages of the polyvinylidene chloride resin and the water-based epoxy resin.
Means for solving the technical problem
Aiming at the problems, the vinylidene chloride metal paint with high barrier property and high adhesive force is prepared by compounding vinylidene chloride resin and single-component waterborne epoxy resin.
According to one embodiment of the invention, the high-adhesion water-based vinylidene chloride metallic paint comprises a film-forming substance, an auxiliary agent, an antirust pigment and a filler, wherein the film-forming substance is a vinylidene chloride copolymer and a water-based single-component epoxy resin, the vinylidene chloride copolymer accounts for 30-45 parts by weight, and the water-based single-component epoxy resin accounts for 5-20 parts by weight.
In a preferred embodiment, the adjuvants include thickeners, defoamers, stabilizers, wetting agents, dispersants, color pastes, flash rust inhibitors, and film forming aids.
In a preferred embodiment, the thickener is bentonite in an amount of 0.1 to 0.5 parts by weight; the defoaming agent is one or a combination of a plurality of materials selected from basf foamasterMO2134AC, Digao Tego Foamex K3, BYK-032 of Germany bike and EASYTECH DF-677 of the mulberry well chemical industry, and the dosage is 0.1-0.5 part by weight; the defoaming agent is polyether siloxane, and the using amount is 0.1-1.5 parts by weight; the stabilizer is one or a combination of F87 and Dazhucheng TR-WA, and is prepared into 25 percent aqueous solution for use, and the dosage of the stabilizer solution is 2 to 7 parts by weight; the wetting agent is Surfynol 104E with the dosage of 0.2-0.8 weight part; the dispersant is anionic wetting dispersant of sodium polyacrylate series, and the dosage is 0.3-1 weight part; the color paste is black color paste with the fineness less than 10 mu m, the concentration of the carbon black is 35 percent, and the using amount is 1 to 3 weight parts; the flash rust prevention auxiliary agent is 15% sodium nitrite solution, and the using amount is 0.2-1 part by weight; the film-forming assistant is one or a combination of more of ethylene glycol butyl ether, alcohol ester 12, dipropylene glycol methyl ether and propylene glycol methyl ether, and the dosage is 1-5 parts by weight.
In a preferred embodiment, the defoaming agent is one or a combination of TEGO901W, TEGO902W and TEGO 904W; the Dispersant is TEGO715W, Dispersant-9100, Claine 6100, Pasteur Sokalan PA 30;
in a preferred embodiment, the metal paint formulation can also be added with an anti-rust pigment, wherein the anti-rust pigment is aluminum tripolyphosphate modified by zinc ions and is used in an amount of 4-10 parts by weight.
In a preferred embodiment, the rust inhibitive pigment is K-white105, APW-2
In a preferred embodiment, the metallic paint formulation can also be added with a filler, wherein the filler is one or more of talcum powder, barium sulfate, mica and kaolin, and the total amount is 8-25 parts by weight.
According to a second aspect of the present invention, there is provided a method for preparing the above high adhesion aqueous vinylidene chloride metallic paint, comprising the steps of:
the first step is that deionized water is added into a paint mixing tank, then a thickening agent bentonite is slowly added under the stirring state, and the mixture is dispersed at a high speed until the mixture is completely dissolved;
secondly, sequentially adding a defoaming agent, a stabilizing agent, a wetting agent and a dispersing agent into the bentonite solution under a stirring state, and uniformly dispersing at a high speed;
thirdly, adding the anti-rust pigment, the color paste and the filler into the solution under the stirring state, dispersing at a high speed or sanding until the fineness is less than 35 mu m, and cooling the slurry for later use;
fourthly, the pH value of the vinylidene chloride resin is pre-adjusted, the resin is filtered by 200-mesh filter cloth, and the pH value of the resin is adjusted to 4 for standby application by ammonia water under the condition of slow stirring;
fifthly, slowly adding the resin adjusted in the fourth step into the single-component water-based epoxy resin under stirring;
and sixthly, slowly adding the mixed resin obtained in the fifth step into the slurry obtained in the third step under the stirring condition, then adding the flash rust inhibitor and the film-forming assistant, and uniformly stirring.
The invention has the advantages of
The water-based resin is selected and is a single component, so that the environment is protected, and the construction is simple; the film-forming material adopts vinylidene chloride resin and aqueous single-component epoxy resin, not only retains the excellent barrier property of the vinylidene chloride resin, but also has good adhesive force of the epoxy resin to a metal base material.
Further features of the present invention will become apparent from the following description of exemplary embodiments.
Detailed Description
One embodiment of the present disclosure will be specifically described below, but the present disclosure is not limited thereto.
The film forming substances of the prepared high-adhesion waterborne vinylidene chloride metal paint are vinylidene chloride copolymer and waterborne single-component epoxy resin, and the metal protective paint with high vinylidene chloride barrier property and excellent adhesion of the epoxy resin to metal base materials is prepared by selecting the auxiliary agent and the pigment and filler.
The preparation process comprises the following steps:
the first step is that deionized water with the formula amount is added into a paint mixing tank, then bentonite is slowly added under the stirring state, and the bentonite is dispersed at high speed until the bentonite is completely dissolved;
secondly, sequentially adding a defoaming agent, a stabilizing agent, a wetting agent and a dispersing agent into the bentonite solution under a stirring state, and uniformly dispersing at a high speed;
thirdly, adding the anti-rust pigment, the color paste and the filler into the solution under the stirring state, dispersing at a high speed or sanding until the fineness is less than 35 mu m, and cooling the slurry for later use;
fourthly, the pH value of the vinylidene chloride resin is pre-adjusted, the resin is filtered by 200-mesh filter cloth, and the pH value of the resin is adjusted to 4 for standby application by ammonia water under the condition of slow stirring;
fifthly, weighing the single-component waterborne epoxy resin with the formula amount, and then slowly adding the resin adjusted in the fourth step into the waterborne epoxy resin under low-speed stirring;
and sixthly, slowly adding the mixed resin obtained in the fifth step into the slurry obtained in the third step under the condition of low-speed stirring, then adding the flash rust inhibitor and the film-forming assistant, and uniformly stirring at a low speed.
According to the scheme, the specific technological process and technological conditions are as follows:
a high adhesion aqueous vinylidene chloride metallic paint, wherein the film forming material comprises a and b two resins, wherein the a aqueous resin is one or more of vinylidene chloride copolymer such as Haloflex202 of Dismann (DSM), Diofan P530 of Suwei (Solvay), Aquaguard P107 of Valspar, Permax801, Permax803 and Permax805 of Lubrizol in 30-45 weight parts, the b aqueous resin is one or two of single-component epoxy resin emulsion such as H-502-42W and H-505-42W of Japanese DIC, 4020 aqueous epoxy resin dispersion and DP42 single-component aqueous epoxy resin emulsion in 5-20 weight parts;
the bentonite is a thickening agent, and the using amount is 0.1-0.5 weight part;
the defoaming agent is mineral oil defoaming agent, such as Pasteur foamer MO2134AC, Digao Tego Foamex K3, BYK-032 of Germany Bike, EASYTECH DF-677 of Morus chemical industry, etc., and the dosage is 0.1-0.5 weight part;
the defoaming agent is polyether siloxane, such as TEGO901W, TEGO902W and TEGO904W, and the dosage is 0.1-1.5 parts by weight;
the stabilizer is F87, Dazhuchongsheng TR-WA, the stabilizer is prepared into 25% aqueous solution, and the dosage of the stabilizer solution is 2-7 parts by weight;
the wetting agent is Surfynol 104E, an acetylenic diol Germini nonionic surfactant. Due to the special structure, the product has multiple functions of wetting, defoaming, improving dispersibility, improving flowing and leveling property and the like, can effectively reduce surface tension, control foam and stabilize consistency and viscosity. The dosage is 0.2 to 0.8 weight portion;
the dispersant is an anionic wetting dispersant of a polyacrylic acid sodium salt series. For example TEGO715W, Dispersant-9100, Claine 6100, Pasteur Sokalan PA30, etc. in an amount of 0.3 to 1 part by weight;
the anti-rust pigment is aluminum tripolyphosphate modified by zinc ions, such as K-white105, APW-2 and the like, and the dosage of the anti-rust pigment is 4-10 parts by weight;
the filler is one or more of talcum powder, barium sulfate, mica and kaolin, and the using amount is 8-25 parts by weight;
the color paste is black color paste with the fineness less than 10 mu m, the concentration of the carbon black is 35 percent, and the using amount is 1 to 3 weight parts;
the flash rust prevention auxiliary agent is 15% sodium nitrite solution, and the using amount is 0.2-1 part by weight;
the film-forming assistant is one or two of ethylene glycol butyl ether, alcohol ester 12, dipropylene glycol methyl ether, propylene glycol methyl ether and the like, and the dosage is 1-5%.
Examples
The present invention is described in more detail by way of examples, but the present invention is not limited to the following examples.
Example 1
A high-adhesion water-based vinylidene chloride metallic paint comprises the following components: 18 parts of deionized water, 20240 parts of vinylidene chloride copolymer Haloflex, 10 parts of aqueous single-component epoxy resin H-502-42W, 0.2 part of bentonite LT, 0.3 part of Pasteur Foamaster MO2134AC, 0.4 part of digao 901W, 5 parts of 25% TR-WA aqueous solution, 0.5 part of Yingchuang Surfynol 104E, 0.6 part of digao 715W, 1.5 parts of black paste, 15 parts of talcum powder, 5 parts of K-White 1055, 0.7 part of 15% sodium nitrite solution and 3 parts of ethylene glycol butyl ether.
During preparation, firstly, bentonite is dissolved and dispersed in deionized water, then, basf foamasterMO2134AC, digao 901W, a 25% TR-WA aqueous solution, Yingchuang Surfynol 104E, digao 715W, self-made black paste, talcum powder and K-White105 are added, high-speed dispersion is carried out until the fineness is less than 35 mu m, and slurry is cooled for later use. And then filtering Haloflex202 by using 200-mesh filter cloth, adjusting the pH value to 4 by using ammonia water, adding the Haloflex202 with the adjusted pH value into H-502-42W under a low-speed stirring state, slowly adding mixed resin into the slurry, finally adding 15% sodium nitrite solution and ethylene glycol monobutyl ether, and uniformly stirring and mixing at a low speed to obtain the high-adhesion waterborne vinylidene chloride metallic paint.
Example 2
A high-adhesion water-based vinylidene chloride metallic paint comprises the following components: 17 parts of deionized water, 15 parts of a vinylidene chloride copolymer Permax 80535, 15 parts of 4020 aqueous epoxy resin dispersion, 0.3 part of bentonite LT, 30.4 parts of Digao Foamex K, 0.3 part of Digao 902W, 5.6 parts of a 25% F-87 aqueous solution, 0.6 part of Yingchuang Surfynol 104E, 300.8 parts of Pasteur Sokalan PA, 2 parts of self-made black paste, 13 parts of barium sulfate, 6 parts of K-White 1056 parts, 1790.5 parts of an anti-flash agent and 4 parts of alcohol ester twelve.
The preparation method comprises the steps of dissolving and dispersing bentonite into deionized water, adding Pasteur Foamex K3, digao 902W, a 25% F-87 aqueous solution, Yingchuang Surfynol 104E, Pasteur Sokalan PA30, self-made black paste, barium sulfate and K-White105, dispersing at a high speed until the fineness is less than 35 mu m, and cooling the slurry for later use. Then filtering Permax805 by using 200-mesh filter cloth, adjusting the pH value to 4 by using ammonia water, adding the Permax805 with the adjusted pH value into 4020 under the low-speed stirring state, then slowly adding mixed resin into the slurry, finally adding 179 and alcohol ester twelve, and uniformly stirring and mixing at low speed to obtain the high-adhesion waterborne vinylidene chloride metallic paint.
Comparative example
A high-adhesion water-based vinylidene chloride metallic paint comprises the following components: 18 parts of deionized water, 20250 parts of vinylidene chloride copolymer Haloflex, 0.2 part of bentonite LT, 0.3 part of Pasteur Foamaster MO2134AC, 0.4 part of digao 901W, 5 parts of 25% TR-WA aqueous solution, 0.5 part of Yingchuang Surfynol 104E, 0.6 part of digao 715W, 1.5 parts of self-made black paste, 15 parts of talcum powder, 5 parts of K-White 1055, 0.7 part of 15% sodium nitrite solution and 3 parts of ethylene glycol butyl ether.
During preparation, firstly, bentonite is dissolved and dispersed in deionized water, then, basf foamasterMO2134AC, digao 901W, a 25% TR-WA aqueous solution, Yingchuang Surfynol 104E, digao 715W, self-made black paste, talcum powder and K-White105 are added, high-speed dispersion is carried out until the fineness is less than 35 mu m, and slurry is cooled for later use. And then filtering Haloflex202 by using 200-mesh filter cloth, adjusting the pH to 4 by using ammonia water, slowly adding the resin with the adjusted pH into the slurry, finally adding 15% sodium nitrite solution and ethylene glycol monobutyl ether, and uniformly stirring and mixing at a low speed to obtain the high-adhesion waterborne vinylidene chloride metallic paint.
The examples and comparative examples were tested for their performance, the metallic paint was sprayed on a polished cold rolled steel sheet to a dry film thickness of 30 ± 3 μm, and the performance was tested after 7 days of room temperature curing, the specific performance test results are given in the following table:
TABLE 1 Performance test results of aqueous vinylidene chloride metallic paints
Item | Example 1 | Example 2 | Comparative example |
Time to surface dry (min) | 25 | 22 | 40 |
Hardness of pencil | 2H | 3H | 2B |
Adhesion force | Level 0 | Level 0 | Stage 2 |
Neutral salt fog resistance | No abnormal condition after 800h | No abnormal condition after 800h | Rusting after more than 600h |
The comparison in Table 1 shows that the thickness of the paint film is about 30 μm, the hardness of the pure vinylidene chloride metallic paint is lower, the drying speed is lower, and the adhesive force can not meet the requirement, while when the vinylidene chloride resin is matched with the single-component water-based epoxy resin for use, the adhesive force can meet the requirement, the drying speed of the paint film is high, the hardness is higher, the excellent corrosion resistance of the vinylidene chloride resin and the single-component water-based epoxy resin are complemented, and the salt spray resistance is improved from 600h to more than 800 h.
Industrial applicability
The invention aims to improve the adhesive force of the vinylidene chloride copolymer serving as a metal protective paint on the metal surface, and the prepared vinylidene chloride metal paint has excellent barrier property of vinylidene chloride and good adhesive force of epoxy resin to a metal base material. The paint can be dried at room temperature or baked at low temperature, and can be sprayed or brushed according to construction requirements. The thickness of the dry film is 30-50 μm, and after curing, the salt spray resistance can reach more than 800 h. The mechanical property is good: impact resistance is that the height of a heavy hammer is 50cm, and no matter the heavy hammer is positively or reversely punched, the coating is not damaged; secondly, performing adhesion test by using a Baige method, observing through a magnifying lens, wherein the cut part of the coating is smooth and has no drop, and the adhesion is 0 grade; thirdly, testing the flexibility of the coating by using a conical bending resistance tester, wherein the testing result is less than or equal to 1 mm. The paint is directly sprayed on a steel structure base material for 20-30min to achieve surface drying without a curing agent. The resin is suitable for various petroleum equipment, chemical equipment, electric equipment, hydraulic equipment and fire-fighting equipment; large and medium-sized mechanical equipment such as railways, bridges, pipelines, automobile parts, cranes, excavators and machine tools; and (4) antirust coating of other metals such as castings, forgings and the like.
The present invention is not limited to the above embodiments, and any changes or substitutions that can be easily made by those skilled in the art within the technical scope of the present invention are also within the scope of the present invention. Therefore, the protection scope of the present invention shall be subject to the protection scope of the claims.
Claims (8)
1. The high-adhesion water-based vinylidene chloride metallic paint is characterized in that: the antirust paint comprises a film forming substance, an auxiliary agent, an antirust pigment and a filler, wherein the film forming substance is a vinylidene chloride copolymer and a water-based single-component epoxy resin, the dosage of the vinylidene chloride copolymer is 30-45 parts by weight, and the dosage of the water-based single-component epoxy resin is 5-20 parts by weight.
2. The aqueous vinylidene chloride metallic paint of claim 1 wherein the additives include thickeners, defoamers, stabilizers, wetting agents, dispersants, color pastes, flash rust inhibitors, and film forming additives.
3. The aqueous vinylidene chloride metallic paint according to claim 2, characterized in that: the thickening agent is bentonite, and the using amount is 0.1-0.5 weight part; the defoaming agent is one or a mixture of a plurality of materials selected from basf foamasterMO2134AC, Digao Tego Foamex K3, BYK-032 of Germany bike and EASYTECH DF-677 of the mulberry well chemical industry, and the dosage is 0.1-0.5 part by weight; the defoaming agent is polyether siloxane, and the using amount is 0.1-1.5 parts by weight; the stabilizer is one or more of F87, Dazhuchongsheng TR-WA, and is prepared into 25% aqueous solution, and the amount of the stabilizer solution is 2-7 parts by weight; the wetting agent is Surfynol 104E with the dosage of 0.2-0.8 weight part; the dispersant is anionic wetting dispersant of sodium polyacrylate series, and the dosage is 0.3-1 weight part; the color paste is black color paste with the fineness less than 10 mu m, the concentration of the carbon black is 35 percent, and the using amount is 1 to 3 weight parts; the flash rust prevention auxiliary agent is 15% sodium nitrite solution, and the using amount is 0.2-1 part by weight; the film-forming assistant is one or two of ethylene glycol butyl ether, alcohol ester 12, dipropylene glycol methyl ether and propylene glycol methyl ether, and the dosage is 1-5 parts by weight.
4. The aqueous vinylidene chloride metallic paint according to claim 2, characterized in that: the defoaming agent is further specifically one or a combination of more of TEGO901W, TEGO902W and TEGO 904W; the dispersing agent is further specifically one or a combination of more of TEGO715W, Dispersant-9100, Claine 6100 and Basff Sokalan PA 30.
5. The aqueous vinylidene chloride metallic paint according to claim 2, characterized in that: the anti-rust pigment is aluminum tripolyphosphate modified by zinc ions, and the using amount of the anti-rust pigment is 4-10 parts by weight.
6. The aqueous vinylidene chloride metallic paint according to claim 5, characterized in that: the antirust pigment is K-white105 or APW-2.
7. The aqueous vinylidene chloride metallic paint according to claim 2, characterized in that: the metallic paint further comprises a filler, wherein the filler is one or more of talcum powder, barium sulfate, mica and kaolin, and the using amount of the filler is 8-25 parts by weight.
8. The method for preparing a high-adhesion aqueous vinylidene chloride metallic paint according to any one of claims 1 to 7, comprising the steps of:
the first step is that deionized water is added into a paint mixing tank, then bentonite is added under the stirring state, and the bentonite is dispersed until the bentonite is completely dissolved;
secondly, sequentially adding a defoaming agent, a stabilizing agent, a wetting agent and a dispersing agent into the bentonite solution under the stirring state, and uniformly dispersing;
thirdly, adding the anti-rust pigment, the color paste and the filler into the solution under the stirring state, dispersing at high speed or sanding until the fineness is less than 35 mu m, and cooling the slurry for later use;
fourthly, the pH value of the vinylidene chloride resin is pre-adjusted, the resin is filtered by 200-mesh filter cloth, and the pH value of the resin is adjusted to 4 for standby application by ammonia water under the stirring condition;
fifthly, adding the resin adjusted in the fourth step into the single-component water-based epoxy resin under stirring;
and sixthly, under the stirring condition, adding the mixed resin obtained in the fifth step into the slurry obtained in the third step, then adding the flash rust inhibitor and the film-forming assistant, and uniformly stirring.