CN107337991A - A kind of bonding coating of water conservancy gate and preparation method thereof - Google Patents
A kind of bonding coating of water conservancy gate and preparation method thereof Download PDFInfo
- Publication number
- CN107337991A CN107337991A CN201710587319.2A CN201710587319A CN107337991A CN 107337991 A CN107337991 A CN 107337991A CN 201710587319 A CN201710587319 A CN 201710587319A CN 107337991 A CN107337991 A CN 107337991A
- Authority
- CN
- China
- Prior art keywords
- parts
- water conservancy
- bonding coating
- conservancy gate
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of bonding coating of water conservancy gate, it is related to engineering protection equipment production technical field, it is characterised in that：It is made up of the material of following parts by weight, 23 28 parts of resin, 6 10 parts of defoamer, 48 parts of coupling agent, 13 parts of aerosil, 11 15 parts of modification infusorial earth, 13 parts of calcium stearate, 25 parts of Tert-butyl Methacrylate, 49 parts of age resistor, 48 parts of oxaloacetic acid, 38 parts of pigment, 30 36 parts of clear water.The inventive method is rationally, product caking property is strong, has decay resistance.
Description
Technical field
The present invention relates to engineering protection equipment production technical field, and in particular to a kind of bonding coating of water conservancy gate and its
Preparation method.
Background technology
Water conservancy gate, namely what is often called gate, and gate is to be used to closing and opening the control facility for letting out and (putting) aquaporin.Water
The important component of work building, it can be used to intercept current, controlling water level, regulation flow, discharge silt and drift etc..
Gate is classified：(1) divided by making material.Mainly have wooden gate, wooden boards Steel Structure gate, cast-iron lock gate,
Reinforced concrete gate and steel-slag sand.(2) divided by gate Men Dingyu horizontal planes relative position.Mainly have extended-top type gate and
Submergence type gate.(3) divided by job specification.Mainly there are main gate, emergency gate and bulkhead gate.(4) gate opening/closing is pressed
Method divides.The gate and opened using the change control of water pressure suffered by gate during fluctuation in stage that main useful mechanically actuated opens and closes
The Hydro-automatic gate closed.(5) by the different supporting form division of gate flap.Mainly by bulkhead gate gate, hinged bearing gate, cunning
Gate, roller chain gate, string free roller gate, roller gate etc. of road supporting.
Structure composition：
Gate is mainly made up of three parts：
1. subject activity part, to close or open aperture, it is generally called gate, also known as gate flap；
2. bury solid part；
3. opening and closing device.
Movable part includes the weighing structure such as panel girder system, supporting walking part, guiding and antipriming and hanger etc..Bury
Part part includes backbone, guide rail, free bearing, lintel, ground sill, sealing seat etc., and they are embedded in aperture periphery, are built with dowel and water conservancy project
The concrete for building thing firmly connects, respectively formation and supporting walking part and sealing face on gate flap, so as to which log type gate leaf is held
The loads such as the water pressure received pass to hydraulic structure, and obtain good gate sealing performance.Open/close machinery and gate flap hanger
Connection, with the position of operational control movable part, but also there are a small number of gates to be opened and closed by hydraulic automatism control operation.
Formal character：, it is necessary to according to gate job specification, set location, service condition lock during progress gate formal character
Hole span, hoisting capacity and construction costs etc., with reference to the characteristics of gate, with reference to existing operative practice experience, pass through Technological Economy
Compare determination.Wherein plane gate and gates of segmental shape are commonly used door shapes.The work lock of large and medium-sized extended-top type and submergence type
Door uses gates of segmental shape, the particularly conventional gates of segmental shape of high water head deep hole main gate mostly.When as emergency gate and maintenance lock
Men Shi, mostly using plane gate.Set up before main gate and put bulkhead gate and emergency gate.To high water head sluicing main gate
Due to the operation of frequent start water or local unlatching, it should try to reduce radial gate vibration and cavitation phenomenon, improve gate hydraulics, press
Different parts considers the influence of power, and the rigidity and dynamic characteristic of door body are analyzed and researched.To gate flap and embedded part
Manufacture, installation accuracy all should be controlled strictly, when gate slot border fluidised form is complicated or the bodily form is special, except refer to have run into
Work(is tested, and should also solve vibration, the Cavitation that may occur by hydraulic model test, to select the suitable gate slot bodily form.
And water conservancy gate is in water body due to soaking for a long time, due to water, hydraulic pressure and other external environmental factors
Reason, usage time is permanent, and external structure easily comes off, and thus brings potential safety hazard, very dangerous.
The content of the invention
The technical problems to be solved by the invention are to overcome existing technological deficiency to provide, and a kind of method is reasonable, product glues
Knot property is strong, has bonding coating of a kind of water conservancy gate of decay resistance and preparation method thereof.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of bonding coating of water conservancy gate, it is characterised in that：It is made up of the material of following parts by weight,
Resin 23-28 parts, defoamer 6-10 parts, coupling agent 4-8 parts, aerosil 1-3 parts, modification infusorial earth 11-
15 parts, calcium stearate 1-3 parts, Tert-butyl Methacrylate 2-5 parts, age resistor 4-9 parts, oxaloacetic acid 4-8 parts, pigment 3-8 parts,
Clear water 30-36 parts；
The resin is one kind in alkyd resin, bisphenol A epoxide resin, phenolic resin, acrylic resin；
The defoamer is silicone emulsion, polyoxyethylene polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxypropylene glycerine
One kind in ether, dimethyl silicone polymer；
The coupling agent is silane resin acceptor kh-550；
The pigment is one kind in cu-zn alloy powder, titanium white, iron oxide red, zinc powder；
The age resistor is 6- ethyoxyls -2,2,4- trimethyls -1,2- dihyaroquinoline, N- phenyl-α-aniline, N- benzene
One kind in base-beta-naphthylamine, N- phenyl-N`- cyclohexyl p-phenylenediamine；
The preparation method of the modification infusorial earth is：Diatomite is ground, 400-500 mesh sieves is crossed, adds 1.5 times of its weight
Pure water, IPDI is added, 12-15 hour is stirred at room temperature, then dried, grind, obtain modification
Diatomite powder；
The IPDI is 1 with diatomaceous mass ratio：1；
A kind of preparation method of the bonding coating of water conservancy gate is,
I is stirred resin, defoamer, aerosil, coupling agent, modification infusorial earth and clear water 15 minutes,
It is then placed in reactor and is stirred 20 minutes at a temperature of 40-45 DEG C；
Material left after II stirring 5 minutes, then adds calcium stearate, Tert-butyl Methacrylate, age resistor, oxalyl
Acetic acid continues stirring 20 minutes；
Then material left after III stirring adds pigment in 10 minutes, be warming up to 50-55 DEG C, be stirred 2 hours i.e.
Can；
The speed of the stirring is 2000-2500r/min.
Beneficial effects of the present invention are：A series of material is mixed and made into product, and product has certain decay resistance,
And protection against the tide, antioxygenic property are good, and have good caking property and adhesive force, are not easy to take off in the presence of external force
Fall.The inventive method is rationally, product caking property is strong, has decay resistance.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, enter below
One step illustrates the present invention.
Embodiment 1
A kind of bonding coating of water conservancy gate, it is characterised in that：It is made up of the material of following parts by weight,
23 parts of resin, 6 parts of defoamer, 4 parts of coupling agent, 1 part of aerosil, 1 part of modification infusorial earth, calcium stearate 1
Part, 2 parts of Tert-butyl Methacrylate, 4 parts of age resistor, 4 parts of oxaloacetic acid, 3 parts of pigment, 30 parts of clear water；
The resin is one kind in alkyd resin, bisphenol A epoxide resin, phenolic resin, acrylic resin；
The defoamer is silicone emulsion, polyoxyethylene polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxypropylene glycerine
One kind in ether, dimethyl silicone polymer；
The coupling agent is silane resin acceptor kh-550；
The age resistor is 6- ethyoxyls -2,2,4- trimethyls -1,2- dihyaroquinoline, N- phenyl-α-aniline, N- benzene
One kind in base-beta-naphthylamine, N- phenyl-N`- cyclohexyl p-phenylenediamine；
The pigment is one kind in cu-zn alloy powder, titanium white, iron oxide red, zinc powder；
The preparation method of the modification infusorial earth is：Diatomite is ground, 400-500 mesh sieves is crossed, adds 1.5 times of its weight
Pure water, IPDI is added, 12-15 hour is stirred at room temperature, then dried, grind, obtain modification
Diatomite powder；
The IPDI is 1 with diatomaceous mass ratio：1；
A kind of preparation method of the bonding coating of water conservancy gate is,
I is stirred resin, defoamer, aerosil, coupling agent, modification infusorial earth and clear water 15 minutes,
It is then placed in reactor and is stirred 20 minutes at a temperature of 40-45 DEG C；
Material left after II stirring 5 minutes, then adds calcium stearate, Tert-butyl Methacrylate, age resistor, oxalyl
Acetic acid continues stirring 20 minutes；
Then material left after III stirring adds pigment in 10 minutes, be warming up to 50-55 DEG C, be stirred 2 hours i.e.
Can；
The speed of the stirring is 2000-2500r/min.
Embodiment 2
A kind of bonding coating of water conservancy gate, it is characterised in that：It is made up of the material of following parts by weight,
28 parts of resin, 10 parts of defoamer, 8 parts of coupling agent, 3 parts of aerosil, 15 parts of modification infusorial earth, calcium stearate
3 parts, 5 parts of Tert-butyl Methacrylate, 9 parts of age resistor, 8 parts of oxaloacetic acid, 8 parts of pigment, 36 parts of clear water；
The age resistor is 6- ethyoxyls -2,2,4- trimethyls -1,2- dihyaroquinoline, N- phenyl-α-aniline, N- benzene
One kind in base-beta-naphthylamine, N- phenyl-N`- cyclohexyl p-phenylenediamine；
The resin is one kind in alkyd resin, bisphenol A epoxide resin, phenolic resin, acrylic resin；
The defoamer is silicone emulsion, polyoxyethylene polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxypropylene glycerine
One kind in ether, dimethyl silicone polymer；
The coupling agent is silane resin acceptor kh-550；
The pigment is one kind in cu-zn alloy powder, titanium white, iron oxide red, zinc powder；
The preparation method of the modification infusorial earth is：Diatomite is ground, 400-500 mesh sieves is crossed, adds 1.5 times of its weight
Pure water, IPDI is added, 12-15 hour is stirred at room temperature, then dried, grind, obtain modification
Diatomite powder；
The IPDI is 1 with diatomaceous mass ratio：1；
A kind of preparation method of the bonding coating of water conservancy gate is,
I is stirred resin, defoamer, aerosil, coupling agent, modification infusorial earth and clear water 15 minutes,
It is then placed in reactor and is stirred 20 minutes at a temperature of 40-45 DEG C；
Material left after II stirring 5 minutes, then adds calcium stearate, Tert-butyl Methacrylate, age resistor, oxalyl
Acetic acid continues stirring 20 minutes；
Then material left after III stirring adds pigment in 10 minutes, be warming up to 50-55 DEG C, be stirred 2 hours i.e.
Can；
The speed of the stirring is 2000-2500r/min.
Embodiment 3
A kind of bonding coating of water conservancy gate, it is characterised in that：It is made up of the material of following parts by weight,
25 parts of resin, 8 parts of defoamer, 5 parts of coupling agent, 2 parts of aerosil, 13 parts of modification infusorial earth, calcium stearate 3
Part, 4 parts of Tert-butyl Methacrylate, 7 parts of age resistor, 6 parts of oxaloacetic acid, 5 parts of pigment, 33 parts of clear water；
The age resistor is 6- ethyoxyls -2,2,4- trimethyls -1,2- dihyaroquinoline, N- phenyl-α-aniline, N- benzene
One kind in base-beta-naphthylamine, N- phenyl-N`- cyclohexyl p-phenylenediamine；
The resin is one kind in alkyd resin, bisphenol A epoxide resin, phenolic resin, acrylic resin；
The defoamer is silicone emulsion, polyoxyethylene polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxypropylene glycerine
One kind in ether, dimethyl silicone polymer；
The coupling agent is silane resin acceptor kh-550；
The pigment is one kind in cu-zn alloy powder, titanium white, iron oxide red, zinc powder；
The preparation method of the modification infusorial earth is：Diatomite is ground, 400-500 mesh sieves is crossed, adds 1.5 times of its weight
Pure water, IPDI is added, 12-15 hour is stirred at room temperature, then dried, grind, obtain modification
Diatomite powder；
The IPDI is 1 with diatomaceous mass ratio：1；
A kind of preparation method of the bonding coating of water conservancy gate is,
I is stirred resin, defoamer, aerosil, coupling agent, modification infusorial earth and clear water 15 minutes,
It is then placed in reactor and is stirred 20 minutes at a temperature of 40-45 DEG C；
Material left after II stirring 5 minutes, then adds calcium stearate, Tert-butyl Methacrylate, age resistor, oxalyl
Acetic acid continues stirring 20 minutes；
Then material left after III stirring adds pigment in 10 minutes, be warming up to 50-55 DEG C, be stirred 2 hours i.e.
Can；
The speed of the stirring is 2000-2500r/min.
Comparative example
A kind of coating includes：20 parts of bisphenol A epoxide resin, 5 parts of silicone emulsion, 5 parts of silane coupler, aerosil
2 parts, 10 parts of diatomite, 4 parts of oxaloacetic acid, 3 parts of pigment, 30 parts of clear water；
Preparation method：Above-mentioned material is put into reactor and stirred at a temperature of 50-60 DEG C with 1000-1500r/min
Mix 2 hours.
Determine performance, the effect such as following table of 1-3 of the embodiment of the present invention and comparative example：
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (9)
- A kind of 1. bonding coating of water conservancy gate, it is characterised in that：It is made up of the material of following parts by weight,Resin 23-28 parts, defoamer 6-10 parts, coupling agent 4-8 parts, aerosil 1-3 parts, modification infusorial earth 11-15 parts, Calcium stearate 1-3 parts, Tert-butyl Methacrylate 2-5 parts, age resistor 4-9 parts, oxaloacetic acid 4-8 parts, pigment 3-8 parts, clear water 30-36 parts.
- A kind of 2. bonding coating of water conservancy gate according to claim 1, it is characterised in that：The resin is alkyd tree One kind in fat, bisphenol A epoxide resin, phenolic resin, acrylic resin.
- A kind of 3. bonding coating of water conservancy gate according to claim 1, it is characterised in that：The defoamer is emulsification silicon One kind in oil, polyoxyethylene polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxypropylene glycerin ether, dimethyl silicone polymer.
- A kind of 4. bonding coating of water conservancy gate according to claim 1, it is characterised in that：The coupling agent is that silane is even Join agent KH-550.
- A kind of 5. bonding coating of water conservancy gate according to claim 1, it is characterised in that：The pigment is ormolu One kind in powder, titanium white, iron oxide red, zinc powder.
- A kind of 6. bonding coating of water conservancy gate according to claim 1, it is characterised in that：The age resistor is 6- ethoxies Base -2,2,4- trimethyls -1,2- dihyaroquinoline, N- phenyl-α-aniline, N- phenyl-β-naphthylamines, N- phenyl-N`- cyclohexyl pair One kind in phenylenediamine.
- A kind of 7. bonding coating of water conservancy gate according to claim 1, it is characterised in that：The system of the modification infusorial earth Preparation Method is：Diatomite is ground, 400-500 mesh sieves is crossed, adds 1.5 times of pure water of its weight, it is different to add isophorone two Cyanate, 12-15 hour is stirred at room temperature, then dries, grind, obtain modification infusorial earth powder.
- A kind of 8. bonding coating of water conservancy gate according to claim 7, it is characterised in that：The isocyanide of isophorone two Acid esters is 1 with diatomaceous mass ratio：1.
- A kind of 9. preparation method of the bonding coating of water conservancy gate according to claim 1, it is characterised in that：I by resin, Defoamer, aerosil, coupling agent, modification infusorial earth and clear water are stirred 15 minutes, are then placed in reactor Stirred 20 minutes at a temperature of 40-45 DEG C；Material left after II stirring 5 minutes, then adds calcium stearate, Tert-butyl Methacrylate, age resistor, oxaloacetic acid Continue stirring 20 minutes；Then material left after III stirring adds pigment in 10 minutes, be warming up to 50-55 DEG C, be stirred 2 hours；The speed of the stirring is 2000-2500r/min.