CN103897298B - 耐腐蚀、耐磨及抗老化改性pvc塑料组合物 - Google Patents

耐腐蚀、耐磨及抗老化改性pvc塑料组合物 Download PDF

Info

Publication number
CN103897298B
CN103897298B CN201410111951.6A CN201410111951A CN103897298B CN 103897298 B CN103897298 B CN 103897298B CN 201410111951 A CN201410111951 A CN 201410111951A CN 103897298 B CN103897298 B CN 103897298B
Authority
CN
China
Prior art keywords
resistant
resisting
corrosion
wear
minute
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410111951.6A
Other languages
English (en)
Other versions
CN103897298A (zh
Inventor
史丽
张璐璐
李凯强
梁德华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Guanhong Plastic Industry Co., Ltd.
Fuyang Institute of product quality supervision and inspection
Original Assignee
Fuyang Institute Of Product Quality Supervision And Inspection
ANHUI GUANHONG PLASTIC INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fuyang Institute Of Product Quality Supervision And Inspection, ANHUI GUANHONG PLASTIC INDUSTRY Co Ltd filed Critical Fuyang Institute Of Product Quality Supervision And Inspection
Priority to CN201410111951.6A priority Critical patent/CN103897298B/zh
Publication of CN103897298A publication Critical patent/CN103897298A/zh
Application granted granted Critical
Publication of CN103897298B publication Critical patent/CN103897298B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种耐腐蚀、耐磨及抗老化改性PVC塑料组合物，涉及塑料技术领域，由以下重量百分比的组分组成：聚氯乙烯树脂90110g，邻苯二甲酸二辛酯2530g，邻苯二甲酸二丁酯2025g，硬脂酸钡0.52g，石蜡.10.5g，硬脂酸镉0.51g，受阻胺光稳定剂0.10.5g，ATO纳米粉体6580g，改性剂810g，复合分散改性剂810g。本发明能够让PVC聚氯乙烯具有耐腐蚀、耐磨、能承受较高压力、不易形成死折并耐一定负压等优异性能。

Description

耐腐蚀、耐磨及抗老化改性PVC塑料组合物
技术领域
本发明涉及塑料技术领域，具体涉及一种耐腐蚀、耐磨及抗老化改性PVC塑料组合物。
背景技术
PVC材料即聚氯乙烯，它是世界上产量最大的塑料产品之一，价格便宜，应用广泛，聚氯乙烯树脂为白色或浅黄色粉末。根据不同的用途可以加入不同的添加剂，聚氯乙烯塑料可呈现不同的物理性能和力学性能。在聚氯乙烯树脂中加入适量的增塑剂，可制成多种硬质、软质和透明制品。随着社会城市化、科技化、人性化的发展，PVC行业的高速发展，PVC材料越来越贴近人们的生活，随之而来的是PVC使用量的增加，和PVC材料大多耐热性不好、易燃。且燃烧时伴随着浓烟易产生刺激性气味和有毒气体，危害使用者身心健康。
PVC，全名为Polyvinylchloride，主要成份为聚氯乙烯，另外加入其他成分来增强其耐热性，韧性，延展性等。据统计，仅仅1995年一年，PVC在欧洲的生产量就有五百万吨左右，而其消费量则为五百三十万吨。在德国，PVC的生产量和消费量平均为一百四十万吨。PVC正以4%的增长速度在全世界范围内得到生产和应用。PVC在东南亚的增长速度尤为显著，这要归功于东南亚各国都有进行基础设施建设的迫切需求。在可以生产三维表面膜的材料中，PVC是最适合的材料。而随着人性化理念的普及，及新型和谐社会的构成，设计一种耐热阻燃PVC的方法是非常必要的。
现有的耐热PVC材料综合性能不佳，成本普遍都较高，不能满足耐腐蚀、耐磨及抗老化的高要求。
发明内容
本发明所要解决的技术问题在于提供一种耐腐蚀、耐磨及抗老化改性PVC塑料组合物。
本发明所要解决的技术问题采用以下技术方案来实现：
一种耐腐蚀、耐磨及抗老化改性PVC塑料组合物，由以下重量百分比的组分组成，
各组分的最佳重量百分比为：
所述ATO纳米粉体，其粒径为3—50nm，松密度为0.4—1.5g/cm3，其锑掺杂摩尔百分含量为3-25%；
所述复合分散改性剂为纳米粉体复合分散改性剂，或者由油酸和PVP按质量比为0.5—3复合而成。
1）按照所述组份重量百比称取各种原料；
2）将聚氯乙烯树脂与石蜡混合3-5分钟，加入受阻胺光稳定剂并升温至90-100℃混合5-lO分钟；
3）加入其余组分，升温至120—130℃混合5-lO分钟，使各组分分散均匀，降温至40-50℃出料，在室温中冷却4-6小时；
4）将冷却后的物料投放到双螺杆挤出机中，挤出造粒。
本发明的有益效果是：本发明能够让PVC聚氯乙烯具有耐腐蚀、耐磨、能承受较高压力、不易形成死折并耐一定负压等优异性能。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
一种耐腐蚀、耐磨及抗老化改性PVC塑料组合物，由以下重量百分比的组分组成，
所述ATO纳米粉体，其粒径为3—50nm，松密度为0.4—1.5g/cm3，其锑掺杂摩尔百分含量为3-25%；
所述复合分散改性剂为纳米粉体复合分散改性剂，或者由油酸和PVP按质量比为0.5—3复合而成。
1）按照所述组份重量百比称取各种原料；
2）将聚氯乙烯树脂与石蜡混合3-5分钟，加入受阻胺光稳定剂并升温至90-100℃混合5-lO分钟；
3）加入其余组分，升温至120—130℃混合5-lO分钟，使各组分分散均匀，降温至40-50℃出料，在室温中冷却4-6小时；
4）将冷却后的物料投放到双螺杆挤出机中，挤出造粒。
实施例2
一种耐腐蚀、耐磨及抗老化改性PVC塑料组合物，由以下重量百分比的组分组成，
1）按照所述组份重量百比称取各种原料；
2）将聚氯乙烯树脂与石蜡混合3-5分钟，加入受阻胺光稳定剂并升温至90-100℃混合5-lO分钟；
3）加入其余组分，升温至120—130℃混合5-lO分钟，使各组分分散均匀，降温至40-50℃出料，在室温中冷却4-6小时；
4）将冷却后的物料投放到双螺杆挤出机中，挤出造粒。
实施例3
一种耐腐蚀、耐磨及抗老化改性PVC塑料组合物，由以下重量百分比的组分组成，
所述ATO纳米粉体，其粒径为3—50nm，松密度为0.4—1.5g/cm3，其锑掺杂摩尔百分含量为3-25%；
所述复合分散改性剂为纳米粉体复合分散改性剂，或者由油酸和PVP按质量比为0.5—3复合而成。
1）按照所述组份重量百比称取各种原料；
2）将聚氯乙烯树脂与石蜡混合3-5分钟，加入受阻胺光稳定剂并升温至90-100℃混合5-lO分钟；
3）加入其余组分，升温至120—130℃混合5-lO分钟，使各组分分散均匀，降温至40-50℃出料，在室温中冷却4-6小时；
4）将冷却后的物料投放到双螺杆挤出机中，挤出造粒。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (1)

1.一种耐腐蚀、耐磨及抗老化改性PVC塑料组合物，其特征在于，由以下重量的组分制成：
所述ATO纳米粉体，其粒径为3-50nm，松密度为0.4-1.5g/cm3，其锑掺杂摩尔百分含量为3-25％；
所述复合分散改性剂由油酸和PVP按质量比为0.5-3复合而成；
制备方法如下：
1)按照所述组分重量称取各种原料；
2)将聚氯乙烯树脂与石蜡混合3-5分钟，加入受阻胺光稳定剂并升温至90-100℃混合5-10分钟；
3)加入其余组分，升温至120-130℃混合5-10分钟，使各组分分散均匀，降温至40-50℃出料，在室温中冷却4-6小时；
4)将冷却后的物料投放到双螺杆挤出机中，挤出造粒。
CN201410111951.6A 2014-03-24 2014-03-24 耐腐蚀、耐磨及抗老化改性pvc塑料组合物 Expired - Fee Related CN103897298B (zh)