CN103895084A - Method for manufacturing intensified paint door - Google Patents
Method for manufacturing intensified paint door Download PDFInfo
- Publication number
- CN103895084A CN103895084A CN201210575895.2A CN201210575895A CN103895084A CN 103895084 A CN103895084 A CN 103895084A CN 201210575895 A CN201210575895 A CN 201210575895A CN 103895084 A CN103895084 A CN 103895084A
- Authority
- CN
- China
- Prior art keywords
- paint
- panel
- edge sealing
- moulding
- door
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A method for manufacturing an intensified paint door includes the steps that upper wood veneer adheres to a panel, seal primer is made, color is made, finishing coat is made, temperature raising and pressurizing are performed by a hot press, an oil paint panel is made, cutting and trimming are performed so as to make door leaves, grooves are formed in the two sides of the formed door leaves for molding, edge sealing wood bars are placed in the grooves, and edge sealing is completed. The technological process of the method is opposite to a traditional technological process, cutting is performed after all the parts are coated with the finishing coat, then, fine sawing and edge sealing are performed, the painted face coated with finishing coat is good in hardness and can not be scratched or scraped by iron wires or iron nails easily, and materials can be prepared on a large scale in advance.
Description
Technical field
The present invention relates to a kind of paint door technique, especially a kind of method of manufacturing strengthening paint door.
Background technology
In the industry, the technological process of strengthening paint door is generally japanning after first sawing sheet, and lacquer painting hardness easily scratches, scratches like this.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of method of manufacturing strengthening paint door, is difficult for scratching, scratching through the lacquer painting of the method processing.
In order to solve the problems of the technologies described above, a kind of method of manufacturing strengthening paint door of the present invention, it comprises as follows
Step: 1) stick solid wood veneer with 7.7mm panel;
2) through paint machine, the panel that posts wooden skin is carried out to seal coat uv;
3) panel of carrying out uv priming paint is placed on and on hot press, does color and finish paint;
4) carry out after color and finish paint, hot press temperature rises to 250 degree-300 degree, and pressure is arranged on 250 tons, is first poured on panel after deployed even to paint raw materials and color, then covers paint film pressing 8-10 minutes;
5) carry out after paint panel, length and width are each on request goes out greatly 10mm size and carries out sawing sheet, as output one long be 2010mm, wide is the rectangular panel of 810mm;
6) rectangular panel after two sawing sheets is pressed together on respectively to the tow sides of door-core frame, more unnecessary panel is amputated to the long 2000mm of being of rectangular panel, wide is 800mm, so far door leaf moulding;
7) by two side moulding of moulding door leaf, i.e. the monosymmetric rectangular channel of outputing;
8) use sawed two of sizing saw machine to carry out the edge sealing batten of paint, and by the moulding of edge sealing batten, itself and rectangular channel are matched;
9) finally edge sealing batten is put into glue, by kludge, edge sealing batten is put into rectangular channel fixing, complete edge sealing work.
Technological process of the present invention is with traditional contrary, makes each parts carry out after finish paint just sawing sheet, then finishing mandrel edge sealing, carry out like this lacquer painting after finish paint for hardness iron wire, iron nail be all not easy to scratch, scratch, get in enormous quantities material ready but also can shift to an earlier date.
Accompanying drawing explanation
Below in conjunction with the drawings and specific embodiments, the present invention is further detailed explanation:
Fig. 1 is the structural representation of hot press pressing panel;
Fig. 2 is the structural representation of moulding door leaf;
Fig. 3 is the structural representation after moulding door leaf fluting;
Fig. 4 is the structural representation of edge sealing batten;
Fig. 5 is the door leaf structure schematic diagram after japanning edge sealing.
The specific embodiment
A kind of method of manufacturing strengthening paint door of the present invention, it comprises the steps:
1) stick solid wood veneer with 7.7mm panel 1;
2) through paint machine, the panel 1 that posts wooden skin is carried out to seal coat uv;
3) panel 1 of carrying out uv priming paint is placed on and on hot press 2, does color and finish paint;
4) carry out after color and finish paint, hot press 2 temperature rise to 250 degree-300 degree, and pressure is arranged on 250 tons, are first poured on panel 1 after deployed even to paint raw materials and color, then cover paint film 3 pressing 8-10 minutes, as shown in Figure 1; Wherein, when hot press 2 pressure reach 250 tons, when temperature requirement is spent at 250 degree 1, the high temperature resistant thickness of paint film 3 of employing must be greater than 1mm;
5) carry out after paint panel 1, length and width are each on request goes out greatly 10mm size and carries out sawing sheet, as output one long be 2010mm, wide is the rectangular panel 4 of 810mm;
6) rectangular panel 4 after two sawing sheets is pressed together on respectively to the tow sides of door-core frame 5, more unnecessary panel is amputated to the long 2000mm of being of rectangular panel 4, wide is 800mm, so far door leaf moulding, as shown in Figure 2;
7) by two side moulding of moulding door leaf, i.e. the monosymmetric rectangular channel 6 of outputing, as shown in Figure 3;
8) use sawed two of sizing saw machine to carry out the edge sealing batten 7 of paint, and by 7 moulding of edge sealing batten, itself and rectangular channel 6 are matched, as shown in Figure 4;
9) as shown in Figure 5, finally edge sealing batten 7 is put into glue, its edge sealing glue used is two component splicing adhesives, and its ratio is 1:0.2, then by kludge, edge sealing batten 7 is put into rectangular channel 6 fixing, completes edge sealing work.
In sum, content of the present invention is not limited in the above-described embodiment, and those skilled in the art can propose other embodiment within technological guidance's thought of the present invention, but this embodiment comprises within the scope of the present invention.
Claims (1)
1. a method of manufacturing strengthening paint door, is characterized in that:
1) stick solid wood veneer with 7.7mm panel (1);
2) through paint machine, the panel (1) that posts wooden skin is carried out to seal coat uv;
3) panel (1) of carrying out uv priming paint is placed on hot press (2) and does color and finish paint;
4) carry out after color and finish paint, hot press (2) temperature rises to 250 degree-300 degree, and pressure is arranged on 250 tons, is poured on panel (1) after first paint raw materials and color is evenly deployed to go up, then covers paint film (3) pressing 8--10 minute;
5) carry out after paint panel (1), length and width are each on request goes out greatly 10mm size and carries out sawing sheet, as output one long be 2010mm, wide is the rectangular panel (4) of 810mm;
6) rectangular panel (4) after two sawing sheets is pressed together on respectively to the tow sides of door-core frame (5), more unnecessary panel is amputated to the long 2000mm of being of rectangular panel (4), wide is 800mm, so far door leaf moulding;
7) by two side moulding of moulding door leaf, i.e. the monosymmetric rectangular channel (6) of outputing;
8) use sawed two of sizing saw machine to carry out the edge sealing batten (7) of paint, and by edge sealing batten (7) moulding, itself and rectangular channel (6) are matched;
9) finally edge sealing batten (7) is put into glue, by kludge, edge sealing batten (7) is put into rectangular channel (6) fixing, complete edge sealing work.