CN103884688A - 一种玻璃微珠逆反射系数检验方法 - Google Patents
一种玻璃微珠逆反射系数检验方法 Download PDFInfo
- Publication number
- CN103884688A CN103884688A CN201410070161.8A CN201410070161A CN103884688A CN 103884688 A CN103884688 A CN 103884688A CN 201410070161 A CN201410070161 A CN 201410070161A CN 103884688 A CN103884688 A CN 103884688A
- Authority
- CN
- China
- Prior art keywords
- glass microballoon
- pearl
- retro
- glued membrane
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种玻璃微珠逆反射系数检验方法，它包括以下步骤：S1、植珠胶膜的制备；S2、植珠；S3、镀铝；S4、复合胶膜的制备；S5、复合并剥离PET薄膜；S6、测试。本发明的有益效果是：本发明虽然分为6步，但其中最繁琐、最难控制、最受实验人员影响的胶膜制备全部采用涂布复合生产线完成，确保了涂布间隙的稳定性。只需占用生产少量时间即可供实验室长时间测试用。实验人员只需要植珠、镀铝、复合后即可测试。由于保证了涂布间隙的稳定性，不同批次的玻璃微珠测试数值对比性更好，得到的数值更具准确性，避免了因操作者不同而导致的偏差，重复性很好。实验人员不必涂布胶粘剂，减少了溶剂的伤害。
Description
技术领域
本发明涉一种玻璃微珠逆反射系数检验方法。
背景技术
玻璃微珠是制作反光材料的主要核心元件，要求其不仅要有良好的透明性、圆度、低失透率还要有优异的逆反射系数。逆反射系数的快速准确的测试显得尤为重要。
中国专利201210295093.6公开了玻璃微珠逆反射性能的检测方法，先将玻璃微珠放入100～150℃烘箱保持5～10分钟，然后将胶膜放入100～150℃烘箱中使胶膜软化，去除胶膜放于平台上，然后在胶膜上撒上玻璃微珠形成植珠膜，植珠膜镀铝后在镀铝面涂布复合胶并放入烘箱中干燥，最后将胶膜剥离，使用逆反射测试仪测试玻璃微珠的逆反射系数。此方法使用的胶膜为PET-PE复合膜，在烘箱拿出来放到平台上时膜会受冷收缩，卷曲，玻璃微珠撒上去珠子不能完成沉降过程。另外此检测方法会受到操作者不同的影响，重复性差。
中国专利201210295088.5公开了一种玻璃微珠逆反射性能的检测方法，先在镀铝薄膜的镀铝面涂布胶粘剂后放入烘箱干燥，在涂胶面上撒上玻璃微珠，并使玻璃微珠均匀、水平、密集分布在胶面上形成植珠膜，将其放入烘箱中干燥后取出，用逆反射系数测试仪测试其分布有玻璃微珠一侧表面的逆反射系数。此方法测试的数值和实际生产有很大的差距，主要原因是镀铝层在薄膜平面上没有在玻璃微珠球面上，光线进入玻璃微珠后不能完成整个逆反射过程，故此法只能做出横向的对比，只能对产品提供一定的参考，不能判断该玻璃微珠实际逆反射系数的大小。
发明内容
本发明的目的在于克服现有技术的缺点，提供一种快速、稳定、准确的玻璃微珠逆反射系数检验方法。
本发明的目的通过以下技术方案来实现：一种玻璃微珠逆反射系数检验方法，它包括以下步骤：
S1、植珠胶膜的制备：首先在PET薄膜上涂布植珠胶，经烘道烘干后和单面涂硅离型膜复合在一起得到植珠胶膜；
S2、植珠：取上述植珠胶膜，揭去单面涂硅离型膜，然后撒上玻璃微珠，使玻璃微珠均匀铺展并附着在植珠胶膜上，然后放入100～120℃烘箱烘干2～3min，取出得到植珠膜；
S3、镀铝：在植珠膜的玻璃微珠面镀铝，形成镀铝植珠膜；
S4、复合胶膜的制备：在化纤基布上涂布复合胶经烘道烘干后和单面涂硅离型膜复合在一起得到复合胶膜；
S5、复合并剥离PET薄膜：取复合胶膜，揭去单面涂硅离型膜，与镀铝植珠膜复合在一起，剥离PET薄膜，得到样品；
S6、测试：用逆反射系数测试仪测试样品逆反射系数值。
所述的步骤S1中PET薄膜上涂布的植珠胶经烘道烘干后得到的干胶厚度为2～10μm。
所述的步骤S2中使玻璃微珠均匀铺展并附着在植珠胶膜上的具体操作为：将玻璃微珠倒在植珠胶膜的一端，用手提起有玻璃微珠的该端让玻璃微珠自由落下直至铺满整个胶面。
所述的步骤S3中在植珠膜的玻璃微珠面镀铝的具体操作为将植珠膜放入小型镀铝机镀铝，镀铝的厚度为390～410埃。
所述的步骤S4中化纤基布上涂布的复合胶经烘道烘干后得到的干胶厚度为20～50μm。
所述的在PET上涂布配制好的植珠胶和在化纤基布上涂布复合胶的操作均使用涂布复合生产线制备。
经步骤S1得到植珠胶膜后和经步骤S4得到复合胶膜后，得到的植珠胶膜和复合胶膜均由分切机分切成20cm宽的卷。
所述步骤S2为取分切好的20cm的植珠胶膜一段进行植珠，所述步骤S5为取分切好的20cm宽的复合胶膜一段与镀铝植珠膜复合。
本发明具有以下优点：本发明虽然分为6步，但其中最繁琐、最难控制、最受实验人员影响的胶膜制备全部采用涂布复合生产线完成，确保了涂布间隙的稳定性。只需占用生产少量时间即可供实验室长时间测试用。实验人员只需要植珠、镀铝、复合后即可测试。由于保证了涂布间隙的稳定性，不同批次的玻璃微珠测试数值对比性更好，得到的数值更具准确性，避免了因操作者不同而导致的偏差，重复性很好。实验人员不必涂布胶粘剂，减少了溶剂的伤害。
具体实施方式
下面结合实施例对本发明做进一步的描述，本发明的保护范围不局限于以下所述：
实施例1：
一种玻璃微珠逆反射系数检验方法，它包括以下步骤：
S1、植珠胶膜的制备：为了减少实验室繁琐重复的涂布过程，本发明使用涂布复合生产线制备植珠胶膜，可供长时间使用，节约人工成本。涂布复合生产线为市售。首先在PET薄膜上涂布植珠胶，植珠胶为市售，经烘道烘干后（干胶厚度5μm）和单面涂硅离型膜复合在一起，由分切机分切成20cm宽的卷，供长时间使用。
S2、植珠：取分切好的20cm的植珠胶膜一段，揭去单面涂硅离型膜，将玻璃微珠倒在一段，用手提起有玻璃微珠的一段让其自由落下直至铺满整个胶面，使玻璃微珠均匀铺展并附着在植珠胶膜上，放入110℃烘箱烘干2.5min，然后取出。
S3、镀铝：将植珠膜放入小型镀铝机镀铝，得到镀铝植珠膜，镀铝的厚度为400埃。
S4、复合胶膜的制备：复合胶膜同样使用涂布复合生产线制备，确保涂层厚度的一致性均匀性，同时减少了实验人员工作。在化纤基布上涂布复合胶，该复合胶为市售，本实施例采用的复合胶采用如下组分：北京高盟生产的代号为FG-608 100份，铝粉3份，KH560 0.5份，乙酯适量，调节固体含量为30%配制而成，此复合胶不添加固化剂，其余助剂用量和实际生产一致，经烘道烘干后（干胶厚度35微米）和单面涂硅离型膜复合在一起，由分切机分切成20cm宽的卷，供长时间使用。
S5、复合并剥离PET薄膜：取分切好的20cm宽的复合胶膜一段，揭去单面涂硅离型膜，与镀铝植珠膜复合在一起，剥离PET薄膜，得到样品。
S6、测试：用逆反射系数测试仪测试样品逆反射系数值。
实施例2：
一种玻璃微珠逆反射系数检验方法，它包括以下步骤：
S1、植珠胶膜的制备：为了减少实验室繁琐重复的涂布过程，本发明使用涂布复合生产线制备植珠胶膜，可供长时间使用，节约人工成本。涂布复合生产线为市售。首先在PET薄膜上涂布植珠胶，植珠胶为市售，经烘道烘干后（干胶厚度10μm）和单面涂硅离型膜复合在一起，由分切机分切成20cm宽的卷，供长时间使用。
S2、植珠：取分切好的20cm的植珠胶膜一段，揭去单面涂硅离型膜，将玻璃微珠倒在一段，用手提起有玻璃微珠的一段让其自由落下直至铺满整个胶面，使玻璃微珠均匀铺展并附着在植珠胶膜上，放入120℃烘箱烘干2min，然后取出。
S3、镀铝：将植珠膜放入小型镀铝机镀铝，得到镀铝植珠膜，镀铝的厚度为410埃。
S4、复合胶膜的制备：复合胶膜同样使用涂布复合生产线制备，确保涂层厚度的一致性均匀性，同时减少了实验人员工作。在化纤基布上涂布复合胶，该复合胶为市售，本实施例采用的复合胶采用如下组分：北京高盟生产的代号为FG-608 100份，铝粉3份，KH560 0.5份，乙酯适量，调节固体含量为30%配制而成，此复合胶不添加固化剂，其余助剂用量和实际生产一致，经烘道烘干后（干胶厚度50微米）和单面涂硅离型膜复合在一起，由分切机分切成20cm宽的卷，供长时间使用。
S5、复合并剥离PET薄膜：取分切好的20cm宽的复合胶膜一段，揭去单面涂硅离型膜，与镀铝植珠膜复合在一起，剥离PET薄膜，得到样品。
S6、测试：用逆反射系数测试仪测试样品逆反射系数值。
实施例3：
一种玻璃微珠逆反射系数检验方法，它包括以下步骤：
S1、植珠胶膜的制备：为了减少实验室繁琐重复的涂布过程，本发明使用涂布复合生产线制备植珠胶膜，可供长时间使用，节约人工成本。涂布复合生产线为市售。首先在PET薄膜上涂布植珠胶，植珠胶为市售，经烘道烘干后（干胶厚度2μm）和单面涂硅离型膜复合在一起，由分切机分切成20cm宽的卷，供长时间使用。
S2、植珠：取分切好的20cm的植珠胶膜一段，揭去单面涂硅离型膜，将玻璃微珠倒在一段，用手提起有玻璃微珠的一段让其自由落下直至铺满整个胶面，使玻璃微珠均匀铺展并附着在植珠胶膜上，放入100℃烘箱烘干3min，然后取出。
S3、镀铝：将植珠膜放入小型镀铝机镀铝，得到镀铝植珠膜，镀铝的厚度为390埃。
S4、复合胶膜的制备：复合胶膜同样使用涂布复合生产线制备，确保涂层厚度的一致性均匀性，同时减少了实验人员工作。在化纤基布上涂布复合胶，该复合胶为市售，本实施例采用的复合胶采用如下组分：北京高盟生产的代号为FG-608 100份，铝粉3份，KH560 0.5份，乙酯适量，调节固体含量为30%配制而成，此复合胶不添加固化剂，其余助剂用量和实际生产一致，经烘道烘干后（干胶厚度20微米）和单面涂硅离型膜复合在一起，由分切机分切成20cm宽的卷，供长时间使用。
S5、复合并剥离PET薄膜：取分切好的20cm宽的复合胶膜一段，揭去单面涂硅离型膜，与镀铝植珠膜复合在一起，剥离PET薄膜，得到样品。
S6、测试：用逆反射系数测试仪测试样品逆反射系数值。
Claims (8)
1.一种玻璃微珠逆反射系数检验方法，其特征在于：它包括以下步骤：
S1、植珠胶膜的制备：首先在PET薄膜上涂布植珠胶，经烘道烘干后和单面涂硅离型膜复合在一起得到植珠胶膜；
S2、植珠：取上述植珠胶膜，揭去单面涂硅离型膜，然后撒上玻璃微珠，使玻璃微珠均匀铺展并附着在植珠胶膜上，然后放入100～120℃烘箱烘干2～3min，取出得到植珠膜；
S3、镀铝：在植珠膜的玻璃微珠面镀铝，形成镀铝植珠膜；
S4、复合胶膜的制备：在化纤基布上涂布复合胶经烘道烘干后和单面涂硅离型膜复合在一起得到复合胶膜；
S5、复合并剥离PET薄膜：取复合胶膜，揭去单面涂硅离型膜，与镀铝植珠膜复合在一起，剥离PET薄膜，得到样品；
S6、测试：用逆反射系数测试仪测试样品逆反射系数值。
2.根据权利要求1所述的一种玻璃微珠逆反射系数检验方法，其特征在于：所述的步骤S1中PET薄膜上涂布的植珠胶经烘道烘干后得到的干胶厚度为2～10μm。
3.根据权利要求1所述的一种玻璃微珠逆反射系数检验方法，其特征在于：所述的步骤S2中使玻璃微珠均匀铺展并附着在植珠胶膜上的具体操作为：将玻璃微珠倒在植珠胶膜的一端，用手提起有玻璃微珠的该端让玻璃微珠自由落下直至铺满整个胶面。
4.根据权利要求1所述的一种玻璃微珠逆反射系数检验方法，其特征在于：所述的步骤S3中在植珠膜的玻璃微珠面镀铝的具体操作为将植珠膜放入小型镀铝机镀铝，镀铝的厚度为390～410埃。
5.根据权利要求1所述的一种玻璃微珠逆反射系数检验方法，其特征在于：所述的步骤S4中化纤基布上涂布的复合胶经烘道烘干后得到的干胶厚度为20～50μm。
6.根据权利要求1所述的一种玻璃微珠逆反射系数检验方法，其特征在于：所述的在PET上涂布配制好的植珠胶和在化纤基布上涂布复合胶的操作均使用涂布复合生产线制备。
7.根据权利要求1所述的一种玻璃微珠逆反射系数检验方法，其特征在于：经步骤S1得到植珠胶膜后和经步骤S4得到复合胶膜后，得到的植珠胶膜和复合胶膜均由分切机分切成20cm宽的卷。
8.根据权利要求7所述的一种玻璃微珠逆反射系数检验方法，其特征在于：所述步骤S2为取分切好的20cm的植珠胶膜一段进行植珠，所述步骤S5为取分切好的20cm宽的复合胶膜一段与镀铝植珠膜复合。