CN103881513B - 环保型橡胶密封条快干涂料 - Google Patents
环保型橡胶密封条快干涂料 Download PDFInfo
- Publication number
- CN103881513B CN103881513B CN201410088788.6A CN201410088788A CN103881513B CN 103881513 B CN103881513 B CN 103881513B CN 201410088788 A CN201410088788 A CN 201410088788A CN 103881513 B CN103881513 B CN 103881513B
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- sealing strip
- rubber sealing
- quick drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种环保型橡胶密封条快干涂料，包括如下组分：聚共轭二烯基甲基硅烷树脂、硅烷偶联剂、异氰酸酯；在紫外光和空气中自由基氧的作用下，聚共轭二烯基甲基硅烷树脂、硅烷偶联剂和异氰酸酯不仅发生链增长反应，还与橡胶表面的不饱和双健、未完全硫化的硫原子、活性氢原子之间形成大量的共价键。其次涂料分子中的氨酯基、羟基与橡胶中的氢原子形成氢健。共价键与氢健的双重效应使涂层与橡胶表面附着力非常好。因为聚共轭二烯基甲基硅烷树脂，硅烷偶联剂，异氰酸酯在空气中分子链快速增长，并与空气中水份反应，从而达到快干的效果。
Description
技术领域
本发明涉及一种涂料，尤其涉及一种环保型橡胶密封条快干涂料。
背景技术
橡胶密封条的喷涂工艺，行业内通常有两种喷涂方式，一种是传统的离线手工喷涂，一种是越来越多厂家采用的在线自动喷涂。离线喷涂工序较多，产品质量的稳定性难以保证；比起离线手工喷涂，在线自动喷涂方式喷涂膜厚更均匀，成膜更坚密，附着力更佳，光泽更自然美观，质量更趋稳定。
汽车橡胶密封条，因其表面能低，对其表面涂装，现有工艺工序非常复杂。一般要进行：表面清洁→等离子处理→预加热→喷涂→高温烘烤。此工艺对流水线生产的直条有工业价值，但对很小的接角件，会浪费大量人力和能源。
目前，用于橡胶密封条的涂料主要有水性双组份耐磨涂料和油性耐磨橡胶油漆。水性双组份耐磨涂料是近几年发展的新技术，中国专利CN101845267A公布了一种水性双组份耐磨涂料，具有环保、耐磨性好的优点，但是施工工艺复杂，对橡胶表面要等离子处理、预烘烤，涂装前温度要达到80-100度，涂装后要高温烘烤，温度230-300度。油性耐磨橡胶油漆为溶剂型橡胶涂层，其优点是不需要高温烘烤，耐磨性较好；但是该涂料涂装前要对橡胶表面等离子处理，涂装后要低温60-100度烘干，因其含有大量的苯类有害溶剂，会造成环境污染，烘烤时易燃易爆，若自然干燥，固化时间很长，表干30分钟以上，交联固化需更长时间，影响生产效率，另外与橡胶的附着力不好，经过高温低温，冷热循环易脱落。
基于以上分析，有必要开发一种环境友好、施工简单、用于喷涂橡胶密封条的涂料。
发明内容
针对背景技术中存在的问题，本发明提供一种环保型橡胶密封条快干涂料，具有施工简单、干燥快速、涂层附着力好、耐磨、抗污染和耐候性好等优点。
本发明提供的环保型橡胶密封条快干涂料，按重量配比，包括如下组分：
聚共轭二烯基甲基硅烷树脂 2-10份（优选4-8份，更优选5-6份）；
硅烷偶联剂 1-6份（优选2-5份，更优选3-4份）；
异氰酸酯 3-15份（优选5-12份，更优选7-9份）。
上述一种环保型橡胶密封条快干涂料中，所述聚共轭二烯基甲基硅烷树脂的数均分子量优选为25000-60000。
上述一种环保型橡胶密封条快干涂料中，所述共轭二烯基优选为C4-C20的直链、支化或环状共轭二烯基，更优选为C4-C16的直链、支化或环状共轭二烯基，更优选为C4-C12的直链、支化或环状共轭二烯基，如丁二烯基、戊二烯基、环戊二烯基等。
上述一种环保型橡胶密封条快干涂料中，所述异氰酸酯优选为聚烯烃多异氰酸酯，其分子量优选为1000-2500。
上述一种环保型橡胶密封条快干涂料中，所述硅烷偶联剂包括乙烯基三过氧化叔丁基硅烷、丁二烯基三乙氧基硅烷、异丁基三乙氧基硅烷、甲基丙烯酰氧基丙基三甲氧基硅烷、乙烯基三甲氧基硅烷、氨丙基三乙氧基硅烷、(2,3-环氧丙氧)丙基三甲氧基硅烷中的一种或几种，优选为甲基丙烯酰氧基丙基三甲氧基硅烷。
上述一种环保型橡胶密封条快干涂料中，按重量配比，还包括0-3份的颜料，优选0.5-2.5份，更优选1-2份。
其中，所述颜料包括钛白粉、氧化铁红、碳黑或酞菁蓝中的一种或几种混合物。
上述一种环保型橡胶密封条快干涂料中，按重量配比，还包括40-90份的溶剂，优选50-80份，更优选60-70份。
其中，所述溶剂为酯类溶剂、芳烃类溶剂、醇醚类溶剂、酮类溶剂、醇类溶剂或脂肪烃类溶剂等中的一种或几种的混合物。酯类溶剂可以为乙酸丁酯、乙酸乙酯、碳酸二甲酯或丙二醇甲醚醋酸酯等；芳烃类溶剂可以为甲苯、二甲苯、三甲苯或四甲苯等；醇醚类溶剂可以为乙二醇丙醚、乙二醇丁醚或丙二醇丙醚等；酮类溶剂可以为环己酮或甲乙酮等；醇类溶剂可以为异丙醇、正丁醇或环己醇等；脂肪烃类溶剂可以为正庚烷、环己烷等。
优选地，所述溶剂为乙酸丁酯、乙酸乙酯、乙酸甲酯、环己烷、甲苯和二甲苯中的一种或几种。
上述一种环保型橡胶密封条快干涂料中，还包括1-5份的助剂，优选2-3份。
其中，所述助剂包括分散剂、防沉剂、催干剂、增韧剂、消泡剂、抗结皮剂、流平剂、湿润剂、增稠剂中的一种或几种。
其中，所述流平剂优选为0.4-0.8份，选自丙烯酸酯类共聚物流平剂、有机硅流平剂、改性聚丙烯酸酯流平剂中的一种或几种。
其中，所述消泡剂优选为0.3-0.5份，选自有机硅类消泡剂、矿物油类消泡剂、聚醚类消泡剂、脂肪醇类消泡剂、丙烯酸酯类消泡剂中的一种或几种。
其中，所述防沉剂优选为0.2-0.4份，选自纳米二氧化硅、气相二氧化硅、沉淀二氧化硅、膨润土、聚酰胺蜡、氢化蓖麻油中的一种或几种，优选为纳米二氧化硅防沉剂。
其中，所述分散剂选自三乙基己基磷酸、十二烷基硫酸钠、甲基戊醇、纤维素衍生物、纳米聚酰胺、古尔胶、脂肪酸聚乙二醇酯中的一种或几种，优选为纳米聚酰胺。
施工时，不需要对橡胶密封件进行预处理，直接喷涂，5分钟后自然干燥，60分钟后可装箱入库。
本发明所提供的环保型橡胶密封条快干涂料在不需要对橡胶件预处理的情况下，具有附着力好、耐磨、抗污染、耐候性好和快干等优点。在紫外光和空气中自由基氧的作用下，聚共轭二烯基甲基硅烷树脂、硅烷偶联剂和异氰酸酯不仅发生链增长反应，还与橡胶表面的不饱和双健、未完全硫化的硫原子、活性氢原子之间形成大量的共价键。其次涂料分子中的氨酯基、羟基与橡胶中的氢原子形成氢健。共价键与氢健的双重效应使涂层与橡胶表面附着力非常好。因为聚共轭二烯基甲基硅烷树脂，硅烷偶联剂，异氰酸酯在空气中分子链快速增长，并与空气中水份反应，从而达到快干的效果。
具体实施方式
本发明提供的一种环保型橡胶密封条快干涂料，按重量配比，包括如下组分：
聚共轭二烯基甲基硅烷树脂 2-10份（优选4-8份，更优选5-6份）；
硅烷偶联剂 1-6份（优选2-5份，更优选3-4份）；
异氰酸酯 3-15份（优选5-12份，更优选7-9份）。
上述一种环保型橡胶密封条快干涂料中，按重量配比，还包括0-3份的颜料，优选0.5-2.5份，更优选1-2份。
上述一种环保型橡胶密封条快干涂料中，按重量配比，还包括40-90份的溶剂，优选50-80份，更优选60-70份。
上述一种环保型橡胶密封条快干涂料中，还包括1-5份的助剂，助剂包括分散剂、防沉剂、催干剂、增韧剂、消泡剂、抗结皮剂、流平剂、湿润剂、增稠剂等中的一种或几种。
下面通过具体实施例对本发明进行详细和具体的介绍，以使更好的理解本发明，但是下述实施例并不限制本发明范围。
实施例1
本实施例中，一种环保型橡胶密封条快干涂料，包括组分：
利用上述实施例中的涂料施工时，不需要对橡胶密封件进行预处理，直接喷涂，3.5分钟后自然干燥，60分钟后可装箱入库。
实施例2
本实施例中，一种环保型橡胶密封条快干涂料，包括组分：
利用上述实施例中的涂料施工时，不需要对橡胶密封件进行预处理，直接喷涂，4分钟后自然干燥，60分钟后可装箱入库。
实施例3
本实施例中，一种环保型橡胶密封条快干涂料，包括组分：
利用上述实施例中的涂料施工时，不需要对橡胶密封件进行预处理，直接喷涂，4分钟后自然干燥，60分钟后可装箱入库。
实施例4
本实施例中，一种环保型橡胶密封条快干涂料，包括组分：
利用上述实施例中的涂料施工时，不需要对橡胶密封件进行预处理，直接喷涂，5分钟后自然干燥，60分钟后可装箱入库。
实施例5
本实施例中，一种环保型橡胶密封条快干涂料，包括组分：
利用上述实施例中的涂料施工时，不需要对橡胶密封件进行预处理，直接喷涂，4分钟后自然干燥，60分钟后可装箱入库。
本发明所提供的环保型橡胶密封条快干涂料在不需要对橡胶件预处理的情况下，具有附着力好、耐磨、抗污染、耐候性好和快干等优点。使用上述实施例中的涂料得到的漆膜性能与利用现有橡胶涂料得到的漆膜相比，漆膜性能差异不大，但是施工工艺大为简化，施工时间和干燥时间大大缩短，干燥时间仅为5分钟，可以明显的提高生产效率、降低生产成本。
以上对本发明的具体实施例进行了详细描述，但其只是作为范例，本发明并不限制于以上描述的具体实施例。对于本领域技术人员而言，任何对本发明进行的等同修改和替代也都在本发明的范畴之中。因此，在不脱离本发明的精神和范围下所作的均等变换和修改，都应涵盖在本发明的范围内。
Claims (9)
1.一种环保型橡胶密封条快干涂料，其特征在于，按重量配比，包括如下组分：
聚共轭二烯基甲基硅烷树脂 2-10份；
硅烷偶联剂 1-6份；
异氰酸酯 3-15份；
其中，所述异氰酸酯为聚烯烃多异氰酸酯，其分子量为1000-2500；
其中，在紫外光和空气中自由基氧的作用下，聚共轭二烯基甲基硅烷树脂、硅烷偶联剂和异氰酸酯发生链增长反应。
2.根据权利要求1所述的一种环保型橡胶密封条快干涂料，其特征在于，按重量配比，包括如下组分：
聚共轭二烯基甲基硅烷树脂 4-8份；
硅烷偶联剂 2-5份；
异氰酸酯 5-12份。
3.根据权利要求1所述的一种环保型橡胶密封条快干涂料，其特征在于，按重量配比，包括如下组分：
聚共轭二烯基甲基硅烷树脂 5-6份；
硅烷偶联剂 3-4份；
异氰酸酯 7-9份。
4.根据权利要求1所述的一种环保型橡胶密封条快干涂料，其特征在于，所述聚共轭二烯基甲基硅烷树脂的数均分子量为25000-60000。
5.根据权利要求1所述的一种环保型橡胶密封条快干涂料，其特征在于，按重量配比，还包括0-3份的颜料。
6.根据权利要求1所述的一种环保型橡胶密封条快干涂料，其特征在于，按重量配比，还包括40-90份的溶剂。
7.根据权利要求6所述的一种环保型橡胶密封条快干涂料，其特征在于，所述溶剂为酯类溶剂、芳烃类溶剂、醇醚类溶剂、酮类溶剂、醇类溶剂或脂肪烃类溶剂中的一种或几种的混合物。
8.根据权利要求1所述的一种环保型橡胶密封条快干涂料，其特征在于，按重量配比，还包括1-5份的助剂。
9.根据权利要求8所述的一种环保型橡胶密封条快干涂料，其特征在于，所述助剂包括分散剂、防沉剂、催干剂、增韧剂、消泡剂、抗结皮剂、流平剂、湿润剂、增稠剂中的一种或几种。