CN103880468B - A kind of sound-absorbing aerated bricks and preparation method thereof - Google Patents
A kind of sound-absorbing aerated bricks and preparation method thereof Download PDFInfo
- Publication number
- CN103880468B CN103880468B CN201410046749.XA CN201410046749A CN103880468B CN 103880468 B CN103880468 B CN 103880468B CN 201410046749 A CN201410046749 A CN 201410046749A CN 103880468 B CN103880468 B CN 103880468B
- Authority
- CN
- China
- Prior art keywords
- tailings
- aerated bricks
- sound
- hour
- iron ore
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of sound-absorbing aerated bricks, it is characterized in that, made by the raw material of following weight portion: iron ore tailings 7-9, molybdenum tailings 15-17, aluminium powder 0.3-0.5, cement 7-9, quick lime 15-17, gypsum 5-7, corncob 13-15, cornstalk 12-14, antierythrite waste liquor 3-5, nano silicon nitride aluminium powder 2-5, alkali lignin 1.4-2.6, guar bean flour 0.7-1.3, aluminium hydroxide 2-3.5, alkylolamides 3-5.5, agalloch eaglewood 0.1-0.3, anistree 0.3-0.5, auxiliary agent 3-6, suitable quantity of water; The present invention taking iron ore tailings, molybdenum tailings as major ingredient, to have cost low, the feature such as easy to use; And added straw ash and the Chinese medicine slag after calcining modification, and there is antibiotic property on the one hand, put forward on the other hand the sound insulation of aerated bricks, heat insulation and heat-insulating property, market prospects are wide.
Description
Technical field
The present invention relates to aerated bricks technical field, be specifically related to a kind of sound-absorbing aerated bricks and preparation method thereof.
Background technology
In recent years, along with the quickening of process of industrialization and the raising of the level of urbanization, also various environmental pressures and problem have been brought, the various solid wastes that industrial processes produce and urban construction are removed and are remake the solid waste brought etc. and perplexing always resident's living environment, the present invention adds in aerated bricks solid waste as raw material, realize the cyclic utilization of waste, reduced the pollution to environment, met strategy of sustainable development requirement.
Aerated bricks is the air-entrained concrete building block of producing by autoclave at high temperature apparatus and process. Air-entrained concrete building block is taking cement, slag, sand, lime etc. as primary raw material, add foaming agent, the solid block forming through stirring moulding, steam press maintenance, air entrained concrete is by purposes, can be divided into five kinds, non-bearing building block, bearing building block, heat insulating block, wallboard and roof boarding.
Tradition solid clay brick weight is large, not only wastes outside national clay resource, price height, and cannot meet the requirement of some special buildings brick, and therefore common brick use has been completely forbidden in present many advanced areas, replaces and advocates energetically aerated bricks. Compare with normal concrete brick with traditional clay brick, aerated bricks is not only lightweight, also has insulation, an advantage such as sound insulation value is excellent, shock resistance is strong, good processability, resistance to elevated temperatures are good, strong adaptability. But China, about the production technology of aerated bricks is ripe not enough, makes aerated bricks Development Technology slow at present, also cannot meet the demand of multiple market.
Summary of the invention
Object of the present invention is just to provide a kind of sound-absorbing aerated bricks and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of sound-absorbing aerated bricks, it is characterized in that, made by the raw material of following weight portion: iron ore tailings 7-9, molybdenum tailings 15-17, aluminium powder 0.3-0.5, cement 7-9, quick lime 15-17, gypsum 5-7, corncob 13-15, cornstalk 12-14, antierythrite waste liquor 3-5, nano silicon nitride aluminium powder 2-5, alkali lignin 1.4-2.6, guar bean flour 0.7-1.3, aluminium hydroxide 2-3.5, alkylolamides 3-5.5, agalloch eaglewood 0.1-0.3, anistree 0.3-0.5, auxiliary agent 3-6, suitable quantity of water; Described auxiliary agent is made up of following raw materials in part by weight: polyphenylene oxide 0.03-0.05, CNT 0.1-0.4, APEO 0.02-0.04, sodium metasilicate 0.2-0.5, triethylamine 1.4-2.7, wollastonite in powder 1-3, methenamine 0.01-0.02, camphor 0.1-0.3, cedar wood oil 1-3, peanut shell 2-4, trichloroethyl phosphate 1.2-2.3, its preparation method is that each crushing material is mixed, be heated to 70-80 DEG C, stirring reaction 30-40 minute, to obtain final product.
The preparation method of described a kind of sound-absorbing aerated bricks, is characterized in that comprising the following steps:
(1) agalloch eaglewood, anise are decocted together in water to filtration in 2-3 hour, gained filtrate Vacuum Concentration extracts, and obtains Chinese medical extract;
(2) after the filter residue of step (1) and iron ore tailings, molybdenum tailings, corncob, cornstalk are mixed, at 650-800 DEG C, calcine 3-4 hour, cooling, grind, add antierythrite waste liquor, alkali lignin, guar bean flour to stir;
(3) by step (1), (2) reaction mass and other residual components, drop in mixer and be uniformly mixed 8-10 minute, obtain mixed slurry;
(4) gained mixed slurry is poured into the mold moulding, precuring 1-3 hour at 46-53 DEG C, the demoulding, cutting, obtains building block base; Again building block base is put into reactor steam press maintenance 13-15 hour, put in storage and get final product.
The present invention has following beneficial effect: the present invention taking iron ore tailings, molybdenum tailings as major ingredient, to have cost low, the feature such as easy to use; And added straw ash and the Chinese medicine slag after calcining modification, and there is antibiotic property on the one hand, put forward on the other hand the sound insulation of aerated bricks, heat insulation and heat-insulating property, market prospects are wide.
Detailed description of the invention
Described a kind of sound-absorbing aerated bricks, it is characterized in that, made by the raw material of following weight portion: iron ore tailings 8, molybdenum tailings 16, aluminium powder 0.3, cement 9, quick lime 15, gypsum 5, corncob 13, cornstalk 12, antierythrite waste liquor 3, nano silicon nitride aluminium powder 2, alkali lignin 1.4, guar bean flour 0.7, aluminium hydroxide 2, alkylolamides 3, agalloch eaglewood 0.1-0.3, anistree 0.3-0.5, auxiliary agent 3-6, suitable quantity of water; Described auxiliary agent is made up of following raw materials in part by weight: polyphenylene oxide 0.03-0.05, CNT 0.1-0.4, APEO 0.02-0.04, sodium metasilicate 0.2-0.5, triethylamine 1.4-2.7, wollastonite in powder 1-3, methenamine 0.01-0.02, camphor 0.1-0.3, cedar wood oil 1-3, peanut shell 2-4, trichloroethyl phosphate 1.2-2.3, its preparation method is that each crushing material is mixed, be heated to 70-80 DEG C, stirring reaction 30-40 minute, to obtain final product.
Preparation method comprises the following steps:
(1) agalloch eaglewood, anise are decocted together in water to filtration in 2-3 hour, gained filtrate Vacuum Concentration extracts, and obtains Chinese medical extract;
(2) after the filter residue of step (1) and iron ore tailings, molybdenum tailings, corncob, cornstalk are mixed, at 650-800 DEG C, calcine 3-4 hour, cooling, grind, add antierythrite waste liquor, alkali lignin, guar bean flour to stir;
(3) by step (1), (2) reaction mass and other residual components, drop in mixer and be uniformly mixed 8-10 minute, obtain mixed slurry;
(4) gained mixed slurry is poured into the mold moulding, precuring 1-3 hour at 46-53 DEG C, the demoulding, cutting, obtains building block base; Again building block base is put into reactor steam press maintenance 13-15 hour, put in storage and get final product.
The performance data of processing the aerated bricks obtaining by above-described embodiment is as follows: the average unit weight of this aerated bricks is 515-630kg/m3, there is a large amount of pores and micropore in building block inside, thereby to have good thermal and insulating performance, mean value compression strength be 6.1-7.8MPa.
Claims (1)
1. a sound-absorbing aerated bricks, it is characterized in that, made by the raw material of following weight portion: iron ore tailings 7-9, molybdenum tailings 15-17, aluminium powder 0.3-0.5, cement 7-9, quick lime 15-17, gypsum 5-7, corncob 13-15, cornstalk 12-14, antierythrite waste liquor 3-5, nano silicon nitride aluminium powder 2-5, alkali lignin 1.4-2.6, guar bean flour 0.7-1.3, aluminium hydroxide 2-3.5, alkylolamides 3-5.5, agalloch eaglewood 0.1-0.3, anistree 0.3-0.5, auxiliary agent 3-6, suitable quantity of water; Described auxiliary agent is made up of following raw materials in part by weight: polyphenylene oxide 0.03-0.05, CNT 0.1-0.4, APEO 0.02-0.04, sodium metasilicate 0.2-0.5, triethylamine 1.4-2.7, wollastonite in powder 1-3, methenamine 0.01-0.02, camphor 0.1-0.3, cedar wood oil 1-3, peanut shell 2-4, trichloroethyl phosphate 1.2-2.3, its preparation method is that each crushing material is mixed, be heated to 70-80 DEG C, stirring reaction 30-40 minute, to obtain final product;
The preparation method of described sound-absorbing aerated bricks comprises the following steps:
(1) agalloch eaglewood, anise are decocted together in water to filtration in 2-3 hour, gained filtrate Vacuum Concentration extracts, and obtains Chinese medical extract;
(2) after the filter residue of step (1) and iron ore tailings, molybdenum tailings, corncob, cornstalk are mixed, at 650-800 DEG C, calcine 3-4 hour, cooling, grind, add antierythrite waste liquor, alkali lignin, guar bean flour to stir;
(3) by step (1), step (2) reaction mass and other residual components, drop in mixer and be uniformly mixed 8-10 minute, obtain mixed slurry;
(4) gained mixed slurry is poured into the mold moulding, precuring 1-3 hour at 46-53 DEG C, the demoulding, cutting, obtains building block base; Again building block base is put into reactor steam press maintenance 13-15 hour, put in storage and get final product.