CN103866635B - 一种甲基丙烯酸月桂酯湿强剂及其制备方法 - Google Patents
一种甲基丙烯酸月桂酯湿强剂及其制备方法 Download PDFInfo
- Publication number
- CN103866635B CN103866635B CN201410070053.0A CN201410070053A CN103866635B CN 103866635 B CN103866635 B CN 103866635B CN 201410070053 A CN201410070053 A CN 201410070053A CN 103866635 B CN103866635 B CN 103866635B
- Authority
- CN
- China
- Prior art keywords
- parts
- lauryl methacrylate
- wet strength
- strength agent
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种甲基丙烯酸月桂酯湿强剂及其制备方法，甲基丙烯酸月桂酯湿强剂由以下成分按照重量比组成：甲基丙烯酸月桂酯为14～16份、顺丁烯二酸酐为7～11份、三羟甲基丙烷为6～7份、壬二酸为2～4份、环氧丙烯酸酯为2～3份、仲辛醇聚氧乙烯醚为5～10份、水为80～95份。将甲基丙烯酸月桂酯、顺丁烯二酸酐、三羟甲基丙烷、壬二酸、环氧丙烯酸酯、仲辛醇聚氧乙烯醚和水进行复配、混合制备得到本发明的湿强剂。本发明制备得到的湿强剂可以用于造纸工业中，提高成品纸的抗张强度，提高纸品的品质。
Description
技术领域
本发明涉及一种湿强剂及其制备方法，特别是涉及一种可以提高纸张抗张强度的甲基丙烯酸月桂酯湿强剂及其制备方法。
背景技术
造纸行业中用到的湿强剂的种类较多，不同种类的湿强剂其作用和效果都不尽相同。湿强剂作为一种造纸助剂，被广泛的应用于植物纤维纸张中。湿强剂与织物纤维形成一个结合网络，网络的结构非常复杂，湿强剂成分之间会有相互的连接，同时湿强剂成分与织物纤维之间也会有相互的连接，这些结构提高了纸张的抗张强度。
以甲基丙烯酸月桂酯作为主要成分的湿强剂并不多见，如果甲基丙烯酸月桂酯湿强剂可以有效的提高纸张的抗张强度，可以作为一种新型的湿强剂被应用到造纸行业中。
发明内容
要解决的技术问题：普通的湿强剂不能有效的提高纸张的湿强抗张强度和干强抗张强度，降低了纸张的抗张强度的问题。
技术方案：本发明公开了一种甲基丙烯酸月桂酯湿强剂及其制备方法，甲基丙烯酸月桂酯湿强剂由以下成分按照重量比组成：甲基丙烯酸月桂酯为14～16份、顺丁烯二酸酐为7～11份、三羟甲基丙烷为6～7份、壬二酸为2～4份、环氧丙烯酸酯为2～3份、仲辛醇聚氧乙烯醚为5～10份、水为80～95份。
一种甲基丙烯酸月桂酯湿强剂的制备方法，制备方法包括如下步骤：（1）分别称取甲基丙烯酸月桂酯为14～16份、顺丁烯二酸酐为7～11份、三羟甲基丙烷为6～7份、壬二酸为2～4份、环氧丙烯酸酯为2～3份、仲辛醇聚氧乙烯醚为5～10份、水为80～95份；（2）调节反应釜温度为55℃，将80～95份的水放入反应釜中，搅拌的同时加入仲辛醇聚氧乙烯醚为5～10份、壬二酸为2～4份，搅拌混合均匀；（3）待搅拌均匀后再向反应釜中加入甲基丙烯酸月桂酯为14～16份、顺丁烯二酸酐为7～11份、三羟甲基丙烷为6～7份，再次进行搅拌、搅拌均匀；（4）最后加入环氧丙烯酸酯为2～3份，低速搅拌2h，搅拌结束后冷却，制备得到甲基丙烯酸月桂酯湿强剂。
甲基丙烯酸月桂酯湿强剂制备时加入的甲基丙烯酸月桂酯优选为15～16份。
甲基丙烯酸月桂酯湿强剂制备时加入的环氧丙烯酸酯优选为3份。
甲基丙烯酸月桂酯湿强剂制备时加入的三羟甲基丙烷优选为7份。
有益效果：制备得到甲基丙烯酸月桂酯湿强剂后，将其应用到造纸的过程中，得到的纸张湿强抗张强度和干强抗张强度得到增大，湿强抗张强度从12.4N·m/g增大至33.1至34.2N·m/g，干强抗张强度从29.8N·m/g增大至65.7至67.2N·m/g，纸张的抗张强度得到了明显的增大，提高了纸张的物理强度。
具体实施方式
实施例1
一种甲基丙烯酸月桂酯湿强剂的制备方法，制备方法包括如下步骤：（1）分别称取甲基丙烯酸月桂酯为15kg、顺丁烯二酸酐为7kg、三羟甲基丙烷为6kg、壬二酸为4kg、环氧丙烯酸酯为2kg、仲辛醇聚氧乙烯醚为10kg、水为95份；（2）调节反应釜温度为55℃，将95份的水放入反应釜中，搅拌的同时加入仲辛醇聚氧乙烯醚为10kg、壬二酸为4kg，搅拌混合均匀；（3）待搅拌均匀后再向反应釜中加入甲基丙烯酸月桂酯为15kg、顺丁烯二酸酐为7kg、三羟甲基丙烷为6kg，再次进行搅拌、搅拌均匀；（4）最后加入环氧丙烯酸酯为2kg，低速搅拌2h，搅拌结束后冷却，制备得到甲基丙烯酸月桂酯湿强剂。
实施例2
一种甲基丙烯酸月桂酯湿强剂的制备方法，制备方法包括如下步骤：（1）分别称取甲基丙烯酸月桂酯为14kg、顺丁烯二酸酐为9kg、三羟甲基丙烷为7kg、壬二酸为2kg、环氧丙烯酸酯为2kg、仲辛醇聚氧乙烯醚为5kg、水为87份；（2）调节反应釜温度为55℃，将87份的水放入反应釜中，搅拌的同时加入仲辛醇聚氧乙烯醚为5kg、壬二酸为2kg，搅拌混合均匀；（3）待搅拌均匀后再向反应釜中加入甲基丙烯酸月桂酯为14kg、顺丁烯二酸酐为9kg、三羟甲基丙烷为7kg，再次进行搅拌、搅拌均匀；（4）最后加入环氧丙烯酸酯为2kg，低速搅拌2h，搅拌结束后冷却，制备得到甲基丙烯酸月桂酯湿强剂。
实施例3
一种甲基丙烯酸月桂酯湿强剂的制备方法，制备方法包括如下步骤：（1）分别称取甲基丙烯酸月桂酯为16kg、顺丁烯二酸酐为11kg、三羟甲基丙烷为6kg、壬二酸为3kg、环氧丙烯酸酯为3kg、仲辛醇聚氧乙烯醚为8kg、水为80份；（2）调节反应釜温度为55℃，将80份的水放入反应釜中，搅拌的同时加入仲辛醇聚氧乙烯醚为8kg、壬二酸为3kg，搅拌混合均匀；（3）待搅拌均匀后再向反应釜中加入甲基丙烯酸月桂酯为16kg、顺丁烯二酸酐为11kg、三羟甲基丙烷为6kg，再次进行搅拌、搅拌均匀；（4）最后加入环氧丙烯酸酯为3kg，低速搅拌2h，搅拌结束后冷却，制备得到甲基丙烯酸月桂酯湿强剂。
将实施例1、实施例2、实施例3的湿强剂分别稀释5倍，备用。
将浓度为10wt%的针叶浆料放在容器中进行机械搅拌，机械搅拌后向针叶浆料中分别加实施例1、实施例2、实施例3制备得到的甲基丙烯酸月桂酯湿强剂的5倍稀释液，稀释液添加量为纸张重量的2wt%，加入浆料中后搅拌，搅拌后将纸页放入纸页成型器中抄片，纸张定量为70g/m2，将纸张进行干燥后再进行熟化，熟化温度为90℃，熟化时间为12min，熟化后冷却至室温，室温条件下测定纸张的湿强抗张强度和干强抗张强度，测定仪器为抗张强度测定仪。同时进行对比实验，对比实验实验条件与实施例相同，但未添加湿强剂，结果如下。
| 对比实验 | 实施例1 | 实施例2 | 实施例3 | |
| 湿强抗张强度（N·m/g） | 12.4 | 33.8 | 33.1 | 34.2 |
| 干强抗张强度（N·m/g） | 29.8 | 66.5 | 65.7 | 67.2 |
从表中抗张强度数值的变化我们可以观察到，本发明的以甲基丙烯酸月桂酯为主要成分的湿强剂可以提高纸张的抗张强度，提高纸张的物理强度。
Claims (5)
1.一种甲基丙烯酸月桂酯湿强剂，其特征在于甲基丙烯酸月桂酯湿强剂由以下成分按照重量份组成：甲基丙烯酸月桂酯为14～16份、顺丁烯二酸酐为7～11份、三羟甲基丙烷为6～7份、壬二酸为2～4份、环氧丙烯酸酯为2～3份、仲辛醇聚氧乙烯醚为5～10份、水为80～95份。
2.一种甲基丙烯酸月桂酯湿强剂的制备方法，其特征在于制备方法包括如下步骤：（1）分别称取甲基丙烯酸月桂酯为14～16份、顺丁烯二酸酐为7～11份、三羟甲基丙烷为6～7份、壬二酸为2～4份、环氧丙烯酸酯为2～3份、仲辛醇聚氧乙烯醚为5～10份、水为80～95份；（2）调节反应釜温度为55℃，将80～95份的水放入反应釜中，搅拌的同时加入仲辛醇聚氧乙烯醚为5～10份、壬二酸为2～4份，搅拌混合均匀；（3）待搅拌均匀后再向反应釜中加入甲基丙烯酸月桂酯为14～16份、顺丁烯二酸酐为7～11份、三羟甲基丙烷为6～7份，再次进行搅拌、搅拌均匀；（4）最后加入环氧丙烯酸酯为2～3份，低速搅拌2h，搅拌结束后冷却，制备得到甲基丙烯酸月桂酯湿强剂。
3.根据权利要求2所述的一种甲基丙烯酸月桂酯湿强剂的制备方法，其特征在于制备时加入的甲基丙烯酸月桂酯为15～16份。
4.根据权利要求2所述的一种甲基丙烯酸月桂酯湿强剂的制备方法，其特征在于制备时加入的环氧丙烯酸酯为3份。
5.根据权利要求2所述的一种甲基丙烯酸月桂酯湿强剂的制备方法，其特征在于制备时加入的三羟甲基丙烷为7份。