CN103834327A - 一种抗静电无醛胶粘剂 - Google Patents

一种抗静电无醛胶粘剂 Download PDF

Info

Publication number
CN103834327A
CN103834327A CN201410059338.4A CN201410059338A CN103834327A CN 103834327 A CN103834327 A CN 103834327A CN 201410059338 A CN201410059338 A CN 201410059338A CN 103834327 A CN103834327 A CN 103834327A
Authority
CN
China
Prior art keywords
carbon black
antistatic
xie
adhesive
vinyl acetate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410059338.4A
Other languages
English (en)
Other versions
CN103834327B (zh
Inventor
赵永轩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DEQING YUNFENG ZHONGHUANJIA SCIENCE & TECHNOLOGY Co Ltd
Original Assignee
DEQING YUNFENG ZHONGHUANJIA SCIENCE & TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DEQING YUNFENG ZHONGHUANJIA SCIENCE & TECHNOLOGY Co Ltd filed Critical DEQING YUNFENG ZHONGHUANJIA SCIENCE & TECHNOLOGY Co Ltd
Priority to CN201410059338.4A priority Critical patent/CN103834327B/zh
Publication of CN103834327A publication Critical patent/CN103834327A/zh
Application granted granted Critical
Publication of CN103834327B publication Critical patent/CN103834327B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗静电无醛胶粘剂，该胶粘剂按重量百分比计由以下组分构成：醋酸乙烯：40%；甲基丙烯酸甲酯：10%；聚乙烯醇：5%；邻苯二甲酸二丁酯：1-3%；谢尔炭黑：1-5%；其余为水。制备方法包括以下步骤：在装有电动搅拌器、恒压滴液漏斗、冷凝器、温度计的四口瓶中，加入聚乙烯醇和水，升温至65℃，加入自由基引发剂，然后升温至75℃，滴加醋酸乙烯与甲基丙烯酸甲酯，保持温度5小时；降温，将谢尔炭黑与邻苯二甲酸二丁酯缓慢加入，搅拌均匀，即得产品。由于加入了适量的谢尔炭黑，使得胶粘剂良好的抗静电性能，在保证胶粘剂具有足够大剪切强度的基础上使胶粘剂储存期间具备良好的稳定性。

Description

一种抗静电无醛胶粘剂
技术领域
本发明属于胶粘剂领域，具体涉及抗静电无醛胶粘剂及其制备方法。
背景技术
    随着电子技术的广泛应用，促进了科技的发展与经济的繁荣。但同时也造成了静电积聚和静电放电现象的频繁发生，给工业生产和生态环境带来众多危害。所以抗静电无醛胶粘剂作为静电场所的粘接材料日益受到人们的重视。现用的抗静电胶粘剂都是在通用粘合剂中掺入金属粉等得到。但金属粉和胶粘剂聚合物树脂的相克性差，使得粘合剂的储存稳定性差。
发明内容
本发明所要解决的技术问题是：针对现有技术存在的不足，提供一种抗静电效果佳，储存稳定性好的抗静电无醛胶粘剂及其制备方法。
为实现本发明之目的，采用以下技术方案予以实现：一种抗静电无醛胶粘剂，该胶粘剂按重量百分比计由以下组分构成：
醋酸乙烯40%；
甲基丙烯酸甲酯：10%；
聚乙烯醇：5%；
邻苯二甲酸二丁酯：1-3%；
谢尔炭黑：1-5%；
其余为水。
作为优选方案：所述的谢尔炭黑含量为2%。
    本发明还提供一种上述胶粘剂的制备方法，包括以下步骤：在装有电动搅拌器、恒压滴液漏斗、冷凝器、温度计的四口瓶中，加入聚乙烯醇和水，升温至650C，加入自由基引发剂，然后升温至750C，滴加醋酸乙烯与甲基丙烯酸甲酯，保持温度5小时；降温，将谢尔炭黑与邻苯二甲酸二丁酯缓慢加入，搅拌均匀，即得产品。
    与现有技术相比较，本发明的有益效果是：由于加入了适量的谢尔炭黑，使得胶粘剂良好的抗静电性能，在保证胶粘剂具有足够大剪切强度的基础上使胶粘剂储存期间具备良好的稳定性。
具体实施方式
实施例1
一种抗静电无醛胶粘剂，该胶粘剂按重量百分比计由以下组分构成：
醋酸乙烯40%；
甲基丙烯酸甲酯：10%；
聚乙烯醇：5%；
邻苯二甲酸二丁酯：1%；
谢尔炭黑：1%；
其余为水。
本发明胶粘剂的制备方法包括以下步骤：在装有电动搅拌器、恒压滴液漏斗、冷凝器、温度计的四口瓶中，加入聚乙烯醇和水，升温至650C，加入自由基引发剂，然后升温至750C，滴加醋酸乙烯与甲基丙烯酸甲酯，保持温度5小时；降温，将谢尔炭黑与邻苯二甲酸二丁酯缓慢加入，搅拌均匀，即得产品。
实施例2
一种抗静电无醛胶粘剂，该胶粘剂按重量百分比计由以下组分构成：
醋酸乙烯40%；
甲基丙烯酸甲酯：10%；
聚乙烯醇：5%；
邻苯二甲酸二丁酯：2%；
谢尔炭黑：2%；
其余为水。
本发明胶粘剂的制备方法包括以下步骤：在装有电动搅拌器、恒压滴液漏斗、冷凝器、温度计的四口瓶中，加入聚乙烯醇和水，升温至650C，加入自由基引发剂，然后升温至750C，滴加醋酸乙烯与甲基丙烯酸甲酯，保持温度5小时；降温，将谢尔炭黑与邻苯二甲酸二丁酯缓慢加入，搅拌均匀，即得产品。
实施例3
一种抗静电无醛胶粘剂，该胶粘剂按重量百分比计由以下组分构成：
醋酸乙烯40%；
甲基丙烯酸甲酯：10%；
聚乙烯醇：5%；
邻苯二甲酸二丁酯：3%；
谢尔炭黑：5%；
其余为水。
本发明胶粘剂的制备方法包括以下步骤：在装有电动搅拌器、恒压滴液漏斗、冷凝器、温度计的四口瓶中，加入聚乙烯醇和水，升温至650C，加入自由基引发剂，然后升温至750C，滴加醋酸乙烯与甲基丙烯酸甲酯，保持温度5小时；降温，将谢尔炭黑与邻苯二甲酸二丁酯缓慢加入，搅拌均匀，即得产品。
    下表为谢尔炭黑加入量对本发明胶粘剂固化后表面电阻的影响：
炭黑重量百分数（%） 固化后的表面电阻（Ω）
0 ＞1011
1 8×109
2 2×108
3 5×107
4 5×106
5 3×105
由上表可知：随着胶粘剂中谢尔炭黑的增加，聚合树脂固化后的电阻明显降低，当聚合树脂中的谢尔炭黑量高于2%时，即能达到抗静电要求。
另外，由于谢尔炭黑的加入对胶粘剂的剪切强度会产生影响，在保证胶粘剂抗静电性能的同时，需要控制谢尔炭黑的含量不得过高。
下表为谢尔炭黑加入量对胶粘剂剪切强度的影响
炭黑重量百分数（%） 剪切强度（MPa）
0 2.77
1 2.53
2 2.38
3 2.19
4 2.08
5 1.97
由上表可知，随着聚合树脂中谢尔炭黑的增加，聚合树脂的剪切强度逐渐降低，这与谢尔炭黑本身的聚集状态有关，谢尔炭黑是空壳状，具有优异的导电性能，但机械强度较低，所以随着谢尔炭黑加入量的增加胶粘剂的剪切强度降低。
可见实施例2采用的方案能够最合理地保证胶粘剂的抗静电性能的同时，保证胶粘剂足够大的剪切强度。

Claims (3)

1.一种抗静电无醛胶粘剂，其特征在于：该胶粘剂按重量百分比计由以下组分构成：
醋酸乙烯40%；
甲基丙烯酸甲酯：10%；
聚乙烯醇：5%；
邻苯二甲酸二丁酯：1-3%；
谢尔炭黑：1-5%；
其余为水。
2. 根据权利要求1所述的一种抗静电无醛胶粘剂，其特征在于：所述的谢尔炭黑含量为2%。
3. 一种如权利要求1所述胶粘剂的制备方法，其特征在于包括以下步骤：在装有电动搅拌器、恒压滴液漏斗、冷凝器、温度计的四口瓶中，加入聚乙烯醇和水，升温至650C，加入自由基引发剂，然后升温至750C，滴加醋酸乙烯与甲基丙烯酸甲酯，保持温度5小时；降温，将谢尔炭黑与邻苯二甲酸二丁酯缓慢加入，搅拌均匀，即得产品。
CN201410059338.4A 2014-02-21 2014-02-21 一种抗静电无醛胶粘剂 Expired - Fee Related CN103834327B (zh)