CN103833307A - 一种耐高温加气砖及其制作方法 - Google Patents

一种耐高温加气砖及其制作方法 Download PDF

Info

Publication number
CN103833307A
CN103833307A CN201410046866.6A CN201410046866A CN103833307A CN 103833307 A CN103833307 A CN 103833307A CN 201410046866 A CN201410046866 A CN 201410046866A CN 103833307 A CN103833307 A CN 103833307A
Authority
CN
China
Prior art keywords
high temperature
temperature resistant
hour
mixed
aerated bricks
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410046866.6A
Other languages
English (en)
Inventor
晋元龙
陈德全
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xu Junyun
Original Assignee
Ma'an Mountain Bao Long Building Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ma'an Mountain Bao Long Building Material Co Ltd filed Critical Ma'an Mountain Bao Long Building Material Co Ltd
Priority to CN201410046866.6A priority Critical patent/CN103833307A/zh
Publication of CN103833307A publication Critical patent/CN103833307A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐高温加气砖，其特征在于，由下列重量份的原料制成：水泥5-9、生石灰15-18、钢渣7-9、高岭土14-17、硅铁合金0.3-0.5、氢氧化钙12-15、四氧化三铁0.5-0.8、羟丙基甲基纤维素钠0.4-0.6、木质素磺酸钙0.3-0.5、环氧大豆油2-4、交联剂TAC1-2、苹果酸4-6、玫瑰花0.3-0.5、香茅草0.1-0.3、助剂3-5、水适量；本发明通过优化配方用料，本发明砖隔热与隔音性能均好，较现有加气砖有明显提高，成品合格率较高、抗压强度高。

Description

一种耐高温加气砖及其制作方法
技术领域
本发明涉及加气砖技术领域，具体涉及一种耐高温加气砖及其制作方法。
背景技术
 近年来，随着工业化进程的加快和城市化水平的提高，也带来了各种环境压力和问题，工业生产过程产生的各种固废以及城市建设拆迁重造带来的固废等一直困扰着居民的生活环境，本发明将固废作为原材料添加到加气砖中，实现了废物的循环利用，减少了对环境的污染，符合可持续发展战略要求。
加气砖是通过高温蒸压设备工艺生产的加气混凝土砌块。加气混凝土砌块以水泥、矿渣、砂、石灰等为主要原料，加入发气剂，经搅拌成型、蒸压养护而成的实心砌块，加气混凝土按用途，可分为非承重砌块、承重砌块、保温块、墙板与屋面板五种。
传统实心粘土砖重量大，不仅浪费国家粘土资源、价格高外，而且也无法满足一些特殊建筑用砖的要求，因此现在许多先进地区已经全面禁止红砖使用，取而代之大力提倡加气砖。和传统的粘土砖和普通混凝土砖相比，加气砖不仅重量轻，还具有保温隔热、隔音性能优、抗震能力强、加工性能好、耐高温性能佳、适应性强等优点。但是，目前我国有关加气砖的生产技术还不够成熟，使得加气砖发展技术缓慢，还无法满足多元化市场的需求。
发明内容
本发明的目的就是提供一种耐高温加气砖及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种耐高温加气砖，其特征在于，由下列重量份的原料制成：水泥5-9、生石灰15-18、钢渣7-9、高岭土14-17、硅铁合金0.3-0.5、氢氧化钙12-15、四氧化三铁0.5-0.8、羟丙基甲基纤维素钠0.4-0.6、木质素磺酸钙0.3-0.5、环氧大豆油2-4、交联剂TAC1-2、苹果酸4-6、玫瑰花0.3-0.5、香茅草0.1-0.3、助剂3-5、水适量；所述的助剂由下列重量份原料制成：聚苯醚0.03-0.05、碳纳米管0.1-0.4、聚氧乙烯醚0.02-0.04、硅酸钠0.2-0.5、三乙胺1.4-2.7、硅灰石粉1-3、乌洛托品0.01-0.02、樟脑0.1-0.3、柏木油1-3、花生壳2-4、三氯乙基磷酸酯1.2-2.3，其制备方法是将各物料粉碎混合，加热至70-80℃，搅拌反应30-40分钟，即得；
所述的一种耐高温加气砖的制备方法，其特征在于包括以下步骤：
（1）将玫瑰花、香茅草一起在水中煎煮2-3小时过滤，所得滤液真空浓缩提取，得中药提取物；
（2）将步骤（1）的滤渣和高岭土、钢渣混匀后，于600-800℃下煅烧3-4小时，冷却，研磨，加入环氧大豆油、羟丙基甲基纤维素钠、木质素磺酸钙搅拌均匀；
（3）将步骤（1）、（2）反应物料以及其它剩余成分，投入搅拌机里搅拌混合8-10分钟，得混合料浆；
（4）将所得混合料浆浇筑入模成型，于50-60℃下预养1-3 小时，脱模，切割，得砌块坯；再将砌块坯放入反应釜中蒸压养护13-15 小时，入库即得。
本发明有以下有益效果：本发明通过对高岭土及硅铁合金进行改性，减轻了砖的容重，利用钢渣取代了砂的加气混凝土砌块，减少了钢渣对环境的污染，增加了固体废弃物的综合利用率；同时本发明通过优化配方用料，本发明砖隔热与隔音性能均好，较现有加气砖有明显提高，成品合格率较高、抗压强度高。
具体实施方式
所述的一种耐高温加气砖，其特征在于，由下列重量份的原料制成：水泥5、生石灰15、钢渣7、高岭土17、硅铁合金0.35、氢氧化钙15、四氧化三铁0.5、羟丙基甲基纤维素钠0.46、木质素磺酸钙0.35、环氧大豆油2、交联剂TAC 2、苹果酸4、玫瑰花0.35、香茅草0.1、助剂3、水适量；所述的助剂由下列重量份原料制成：聚苯醚0.05、碳纳米管0.14、聚氧乙烯醚0.02、硅酸钠0.25、三乙胺1.4、硅灰石粉1、乌洛托品0.01、樟脑0.13、柏木油3、花生壳2、三氯乙基磷酸酯1.2，其制备方法是将各物料粉碎混合，加热至70-80℃，搅拌反应30-40分钟，即得。
制作方法包括以下步骤：
（1）将玫瑰花、香茅草一起在水中煎煮2-3小时过滤，所得滤液真空浓缩提取，得中药提取物；
（2）将步骤（1）的滤渣和高岭土、钢渣混匀后，于600-800℃下煅烧3-4小时，冷却，研磨，加入环氧大豆油、羟丙基甲基纤维素钠、木质素磺酸钙搅拌均匀；
（3）将步骤（1）、（2）反应物料以及其它剩余成分，投入搅拌机里搅拌混合8-10分钟，得混合料浆；
（4）将所得混合料浆浇筑入模成型，于50-60℃下预养1-3 小时，脱模，切割，得砌块坯；再将砌块坯放入反应釜中蒸压养护13-15 小时，入库即得。
通过上述实施例加工得到的加气砖的性能数据如下：本砌块的平均容重为500-700kg/m3，保温性能好，耐火温度为750℃，在砌块内部具有大量的气孔和微孔，因而有良好的保温隔热性能，平均值抗压强度为7.1-8.5MPa。

Claims (2)

1.一种耐高温加气砖，其特征在于，由下列重量份的原料制成：水泥5-9、生石灰15-18、钢渣7-9、高岭土14-17、硅铁合金0.3-0.5、氢氧化钙12-15、四氧化三铁0.5-0.8、羟丙基甲基纤维素钠0.4-0.6、木质素磺酸钙0.3-0.5、环氧大豆油2-4、交联剂TAC1-2、苹果酸4-6、玫瑰花0.3-0.5、香茅草0.1-0.3、助剂3-5、水适量；所述的助剂由下列重量份原料制成：聚苯醚0.03-0.05、碳纳米管0.1-0.4、聚氧乙烯醚0.02-0.04、硅酸钠0.2-0.5、三乙胺1.4-2.7、硅灰石粉1-3、乌洛托品0.01-0.02、樟脑0.1-0.3、柏木油1-3、花生壳2-4、三氯乙基磷酸酯1.2-2.3，其制备方法是将各物料粉碎混合，加热至70-80℃，搅拌反应30-40分钟，即得。
2.根据权利要求1所述的一种耐高温加气砖的制作方法，其特征在于包括以下步骤：
（1）将玫瑰花、香茅草一起在水中煎煮2-3小时过滤，所得滤液真空浓缩提取，得中药提取物；
（2）将步骤（1）的滤渣和高岭土、钢渣混匀后，于600-800℃下煅烧3-4小时，冷却，研磨，加入环氧大豆油、羟丙基甲基纤维素钠、木质素磺酸钙搅拌均匀；
（3）将步骤（1）、（2）反应物料以及其它剩余成分，投入搅拌机里搅拌混合8-10分钟，得混合料浆；
（4）将所得混合料浆浇筑入模成型，于50-60℃下预养1-3 小时，脱模，切割，得砌块坯；再将砌块坯放入反应釜中蒸压养护13-15 小时，入库即得。
CN201410046866.6A 2014-02-11 2014-02-11 一种耐高温加气砖及其制作方法 Pending CN103833307A (zh)