CN103820788B - 一种含有改性莫来石粉的防锈剂 - Google Patents
一种含有改性莫来石粉的防锈剂 Download PDFInfo
- Publication number
- CN103820788B CN103820788B CN201410057005.8A CN201410057005A CN103820788B CN 103820788 B CN103820788 B CN 103820788B CN 201410057005 A CN201410057005 A CN 201410057005A CN 103820788 B CN103820788 B CN 103820788B
- Authority
- CN
- China
- Prior art keywords
- parts
- mullite powder
- film
- antirust agent
- prepared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种含有改性莫来石粉的防锈剂，由下列重量份的原料制得：蓖麻油80‑100份、羊毛脂金属皂3‑5份、硬脂酸铝8‑10份、二茂铁1‑3份、聚异丁烯0.8‑1.0份、2‑氰乙基甲酰胺1‑2份、四氮唑0.5‑1.0份、2‑氨乙基十七烯基咪唑啉0.8‑1.2份、N‑苯基‑2‑萘胺1.0‑1.5份、二烷基二硫代磷酸锌1‑3份、聚乙烯醇1‑3份、柠檬酸钠5‑8份、硼酸铵8‑10份、十二烷基苯磺酸钠2‑4份、成膜树脂5‑6份、改性莫来石粉1‑3份。本发明通过添加改性莫来石粉，调整配方，制备一种具有很好的气相防锈效果的防锈剂，本发明的防锈剂具有优越的防锈性能，使用方便，而且生产工艺简单。
Description
技术领域
本发明涉及金属防锈技术领域，尤其涉及一种含有改性莫来石粉的防锈剂。
背景技术
金属加工件在生产加工及运输的过程中，很容易生锈，需要使用防锈油在金属表面形成一层薄膜，防止金属锈蚀的化学品。机械在运行和贮存中很难不与空气中的氧、湿气或其它腐蚀性介质接触，这些物质在金属表面将发生电化学腐蚀而生锈，要防止锈蚀就得阻止以上物质与金属接触。防锈剂属于防锈产品的一种。
但是，有些工件具有细长弯曲的小孔，或有窄细盲孔，往往涂油也难以防锈，如果用气相防锈剂就能轻而易举地完成防锈措施。其实，气相防锈剂是一种主动防锈材料，只要密封环境许可、防锈剂还在，他就能够将防锈状态继续下去，他不想防锈油和涂料，涂层破坏了防锈功能就失去了。因此，它的防锈保护期非常长久，军事上常用它作武器防锈，最长防锈期可达12-20年。它的使用保护和去除非常方便，只要将工件与它放在一起，再加上塑料袋等密封就完成防锈保护，去除时打开密封袋，拿出来就能用。气相防锈剂的用途和用量将会越来越大，可以预见，不久的将来，气相防锈剂会成为钢铁的主要防锈材料之一。
发明内容
本发明的目的是克服现有技术的不足，提供一种具有很好的气相防锈效果、优越的防锈性能、使用方便、生产工艺简单的含有改性莫来石粉的防锈剂。
为了实现上述目的本发明采用如下技术方案：
一种含有改性莫来石粉的防锈剂，由下列重量份的原料制得：蓖麻油80-100份、羊毛脂金属皂3-5份、硬脂酸铝8-10份、二茂铁1-3份、聚异丁烯0.8-1.0份、2-氰乙基甲酰胺1-2份、四氮唑0.5-1.0份、2-氨乙基十七烯基咪唑啉0.8-1.2份、N-苯基-2-萘胺1.0-1.5份、二烷基二硫代磷酸锌1-3份、聚乙烯醇1-3份、柠檬酸钠5-8份、硼酸铵8-10份、十二烷基苯磺酸钠2-4份、成膜树脂5-6份、改性莫来石粉1-3份；
所述的成膜树脂由以下重量份的原料制备而成：松香5-8份、尿素2-5份、锌粉1-2份、二甲基硅油3-5份、液化石蜡15-18份、3-氨丙基三甲氧基硅烷3-5份、乙酰柠檬酸三酯10-15份、环氧大豆油10-13份、二甲苯10-15份、聚乙烯醇5-8份。
所述的改性莫来石粉的制备方法为：莫来石于500-800℃下煅烧3-4小时后，磨成粉末，用10-15％双氧水浸泡3-5小时，去离子水洗涤，烘干，在其中加入相当于其重量1-2％的2,4,6-三苯酚、2-3％的α-氰基丙烯酸乙酯、1-2％的交联剂TAC，高速4500-4800转/分搅拌20-30分钟，烘干粉碎过200-400目筛，即可。
所述的含有改性莫来石粉的防锈剂的制备方法，包括以下制备步骤：
(1)制备成膜树脂：将二甲基硅油、液化石蜡、3-氨丙基三甲氧基硅烷、乙酰柠檬酸三酯、环氧大豆油、二甲苯、聚乙烯醇按上述重量份比例加入不锈钢反应釜，升温至100-115℃，搅拌，加入其余制备成膜树脂的原料，混匀，然后以30-40℃/小时的速率升温至200-220℃,1-2小时后停止加热，放至稀释釜，冷却到60-75℃，即得成膜树脂；
(2)将步骤(1)制得的成膜树脂和其他各原料按上述重量份比例混合，80-100℃下搅拌30-40分钟，然后保温1-2小时后，冷却，即可。
与已有技术相比，本发明的有益效果如下：
本发明通过添加改性莫来石粉，调整配方，制备一种具有很好的气相防锈效果的防锈剂，本发明的防锈剂具有优越的防锈性能，使用方便，而且生产工艺简单。
具体实施方式
下面结合实施例对本发明作进一步的描述。
实施例：
一种含有改性莫来石粉的防锈剂，由下列重量份的原料制得：蓖麻油80份、羊毛脂金属皂5份、硬脂酸铝8份、二茂铁2份、聚异丁烯0.8份、2-氰乙基甲酰胺2份、四氮唑0.6份、2-氨乙基十七烯基咪唑啉1.2份、N-苯基-2-萘胺1.2份、二烷基二硫代磷酸锌2份、聚乙烯醇2份、柠檬酸钠7份、硼酸铵8份、十二烷基苯磺酸钠3份、成膜树脂5份、改性莫来石粉2份；
所述的成膜树脂由以下重量份的原料制备而成：松香6份、尿素3份、锌粉2份、二甲基硅油4份、液化石蜡16份、3-氨丙基三甲氧基硅烷4份、乙酰柠檬酸三酯10份、环氧大豆油10份、二甲苯12份、聚乙烯醇6份。
所述的改性莫来石粉的制备方法为：莫来石于700℃下煅烧3小时后，磨成粉末，用13％双氧水浸泡4小时，去离子水洗涤，烘干，在其中加入相当于其重量2％的2,4,6-三苯酚、3％的α-氰基丙烯酸乙酯、2％的交联剂TAC，高速4600转/分搅拌30分钟，烘干粉碎过200目筛，即可。
所述的含有改性莫来石粉的防锈剂的制备方法，包括以下制备步骤：
(1)制备成膜树脂：将二甲基硅油、液化石蜡、3-氨丙基三甲氧基硅烷、乙酰柠檬酸三酯、环氧大豆油、二甲苯、聚乙烯醇按上述重量份比例加入不锈钢反应釜，升温至100℃，搅拌，加入其余制备成膜树脂的原料，混匀，然后以40℃/小时的速率升温至200℃,2小时后停止加热，放至稀释釜，冷却到70℃，即得成膜树脂；
(2)将步骤(1)制得的成膜树脂和其他各原料按上述重量份比例混合，100℃下搅拌30分钟，然后保温2小时后，冷却，即可。
试验例：
本发明防锈剂的性能试验：
静态不接触加速试验
分别将5ml和10ml的本实施例放在小烧杯中，将金属试片(50mm×25mm×2mm)按GB/T4879-1999规定的方法处理后置于烧杯正上方，然后将含有HCO3 -1000mg/L、SO4 2-2500mg/L、Cl-1500mg/L的电解质溶液放入一个大烧杯中，电解质溶液保持为40℃，将放有本实施例的小烧杯置于大烧杯中，将大烧杯和小烧杯和正上方的金属试片都置于一个密封装置中，装置上端设置一个透气孔，室温下观察各材料出现腐蚀的时间。另外，不放防锈剂作为空白的试验。试验结果如下表1：
表1静态不接触加速试验结果
由表1可知本发明的防锈剂防锈效果明显，对钢类以及黄铜都具有良好的防锈效果。
Claims (2)
1.一种含有改性莫来石粉的防锈剂，其特征在于：由下列重量份的原料制得：蓖麻油80-100份、羊毛脂金属皂3-5份、硬脂酸铝8-10份、二茂铁1-3份、聚异丁烯0.8-1.0份、2-氰乙基甲酰胺1-2份、四氮唑0.5-1.0份、2-氨乙基十七烯基咪唑啉0.8-1.2份、N-苯基-2-萘胺1.0-1.5份、二烷基二硫代磷酸锌1-3份、聚乙烯醇1-3份、柠檬酸钠5-8份、硼酸铵8-10份、十二烷基苯磺酸钠2-4份、成膜树脂5-6份、改性莫来石粉1-3份；
所述的成膜树脂由以下重量份的原料制备而成：松香5-8份、尿素2-5份、锌粉1-2份、二甲基硅油3-5份、液化石蜡15-18份、3-氨丙基三甲氧基硅烷3-5份、乙酰柠檬酸三酯10-15份、环氧大豆油10-13份、二甲苯10-15份、聚乙烯醇5-8份；
所述的改性莫来石粉的制备方法为：莫来石于500-800℃下煅烧3-4小时后，磨成粉末，用10-15％双氧水浸泡3-5小时，去离子水洗涤，烘干，在其中加入相当于其重量1-2％的2,4,6-三苯酚、2-3％的α-氰基丙烯酸乙酯、1-2％的交联剂TAC，高速4500-4800转/分搅拌20-30分钟，烘干粉碎过200-400目筛，即可。
2.一种如权利要求1所述的含有改性莫来石粉的防锈剂的制备方法，其特征在于：包括以下制备步骤：
(1)制备成膜树脂：将二甲基硅油、液化石蜡、3-氨丙基三甲氧基硅烷、乙酰柠檬酸三酯、环氧大豆油、二甲苯、聚乙烯醇按上述重量份比例加入不锈钢反应釜，升温至100-115℃，搅拌，加入其余制备成膜树脂的原料，混匀，然后以30-40℃/小时的速率升温至200-220℃,1-2小时后停止加热，放至稀释釜，冷却到60-75℃，即得成膜树脂；
(2)将步骤(1)制得的成膜树脂和其他各原料按上述重量份比例混合，80-100℃下搅拌30-40分钟，然后保温1-2小时后，冷却，即可。